• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.211-218
• /
• 1990

CA2-based clinker with highly activated surface and hydraulic properties was synthesized at a comparatively lowr temperature than that of conventional synthesis by "hydration-burning method". This consists of calcining the mixture of CaCO3 and Al2O3 to obtain a primary clinker, hydrating the primary clinker and reburning the hydrates to obtain final clinker. Burning of primary clinker above 1200℃ was necessary to eliminate free CaO in it and to obtain it's solid hydrate. However, rising the burning temperature above 1300℃ is ineffective due to the decrease in hydraulic properties of the primary clinker with the temperature. Hydration of primary clinker at the elevated temperature(>35℃) was required to obtain the hydrate with more porous structure and final clinker with more active surface. CA2 was formed and increased with temperature at above 1150℃, finally became a primary phase of the final clinker. However, burning at the temperature above 1300℃ resulted in reverse effect on the hydraulic properties of the final clinker due to rapid decrease in it's surface area with the temperature.

• Journal of the Speleological Society of Korea
• /
• v.19 no.20
• /
• pp.29-62
• /
• 1989

Cheju Island, which was formed by volcanic activity, is an oval in its shape with the major axis 80km and the minor axis of 40km. The island holds in its heart Mt. Hanala rising 1,950m above the sea. Petrological study of this volcanic island has been made actively by Sang-Man Lee, Chong-Kwang Won and Moon-Won Li. The chronological measurements of the island by Chong-Kwan Won and Moon-Won Lee showed that it is composed of Sanbangsan trachytes and Backlokdam trachytes(25,000 year ago). These reports are based on the chemical analysis and the rediometric chronological measurements on the ground. However, there has been no reports about the inside of caves. We made an (composition) analysis of the inside of Manjang Cave by the fundamental parameter method in X-ray fluorescence spectrometry. The fundamental parameter method in X-ray fluorescence spectrometry is nondestructive analysis. and it enables us to make the values processed by a computer. The results obtained by this methods are as follows: SiO$_2$(49％), $Al_2$O$_3$(17％), Fe$_2$O$_3$(13％), CaO(8.1％), MgO(5.5％), Na2O(3.6％), TiO$_2$(2.1％), $K_2$O(0.86％), P$_2$O$_{5}$(0.28％), and MnO(0.20％) respectively. The data obtained by the fundamental parameter method in X-ray fluorescene was compared with the data provided by Chong-Kwan Won and Moon-Won Lee. Our measurement was made by K-Ar-method in cooperation with T. ITAYA. The samples are of 30,000-420,000 years ago. The composition of the values of our underground analysis with the existing values obtained by the analyses on the ground produced new data about Cehju volcanic island.d.

• Journal of the Speleological Society of Korea
• /
• v.21 no.22
• /
• pp.17-56
• /
• 1990

Cheju Island, which was formed by volcanic activity, is an oval in its shape with the major axis of 80km and the minor axis of 40km. The island holds in its heart Mt. Hanla rising 1,950m above the sea. Petrological study of this volcanic island has been made actively by Sang-Man Lee, Chong-Kwan won and Moon-Won Lee. The chronological measurements of the island by Chong-Kwan Won and Moon-Won Lee showed that it is composed of Sanbangsan trachytes and Backlokdam trachytes(25,000 year ago). These reports are based on the chemical analysis and the rediometric chronological measurements on the ground. However, there has been no reports about the inside of caves. We made an (composition) analysis of the inside of Manjang Cave by the fundamental parameter method in X-ray fluorescence spectrometry. The fundamental parameter method in X-ray fluorescence spectrometry is nondestructive analysis, and it enables us to make the values processed by a computer. The results obtained by this methods are as follows : SiO$_2$(49％), $Al_2$O$_3$(17％), Fe$_2$O$_3$(13％), CaO(8.1％), MgO(5.5％), Na$_2$O(3.6％), TiO$_2$(2.1％), $K_2$O(0.86％), P$_2$O$_{5}$(0.28％), and MnO(0.20％), respectively. The data obtained by the fundamental parameter method in X-ray fluorescence was compared with the data provided by Chong-Kwan and Moon-Won Lee. Our measurement was made by K-Ar-method in cooperation with T.ITAYA. The samples are of 30,000～420,000 year ago. The composition of the values of our underground analysis with the existing values obtained by the analyses on the ground produced new data about Cheju volcanic island.d.

• Proceedings of the KSPS conference
• /
• 1997.07a
• /
• pp.11-25
• /
• 1997

This presentation will focus on building basic English Prosodic Skills which are very useful and helpful for Japanese learners of English. The focus first will be on recognizing the seven basic nuclear tones, analysing intonation structures, distinguishing intonation patterns and then on the way of improving speaking ability using sufficient verbal contents of intonation (mini-dialogue). My presentation deals mainly with some difficulties which Japanese learners of English have in the field of RP intonation, It is chiefly concerned with identifying, describing and analysing tone-group sequences. It sometimes happens that Japanese learners of English can pronounce isolated bounds correctly and read phonetic symbols sufficiently, bet have difficult problems in carrying out accurate prosodic features. The use of wrong intonation is sometimes the cause of misunderstanding of speaker's attitude, connotation and shades of meaning, etc.. However accurately students can pronounce the nuclear tone or tone-group of English, they have to learn how to connect tone-groups properly for suitable sequences in respect to meaning or implication. We are faced with the complicated theory of RF intonation on the one hand and difficult realization of it on the other. Japanese learners of English have special difficulties in employing "rising tune" and "falling + rising tune". If students are taught pitch movements by indicating dots graphically between two horizontal lines, they can easily understand the whole shape of pitch movements. In this presentation, I illuminate several tone-group sequences which are very useful for Japanese learning English intonation. Among them, four similar Pitch Patterns, such as, (1) (equation omitted)- type, (2) (equation omitted) - type, (3) (equation omitted) - type and (4) (Rising Head) (equation omitted)- type are clarified and other important tone-group sequences aye also highlighted from the point of view of teaching English as a foreign language. The intonation theory, tone marks and technical terms are, in all essentials, those of Intonation of Colloquial English by O'Connor, J. D. and Arnold, G. F., Longman, 2nd ed., 1982. The changes of tone are shown graphically between two horizontal lines representing the ordinary high and low zones of the utterance. A.C.Gimson (1981:314) : The intonation of English has been studied in greater detail and for longer than that of any other language. No definitive analysis, classifying the features of RP intonation, has yet appeared (though that presented by O'Connor and Arnold (1973) provides the most comprehensive and useful account from the foreign learner's point of view).

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.595-605
• /
• 2000

Dental ceramics have good aesthetics, biocompatibility, low thermal conductivity, abrasion resistance, and color stability. However poor resistance to fracture and shrinkage during firing process have been limiting factors in their use, particularly in multiunit ceramic restorations. A new method for making all-ceramic crowns that have high strength and low processing shrinkage has been developed and is referred to as the Vita In-Ceram method. This study was performed to investigate the effect of $CeO_2$ addition in borosilicate glasses on the strength of alumina-glass composites. Porous alumina compacts were prepared by slip casting and sintered at $1,100^{\circ}C$ for 2 hours. Dense composites were made by infiltration of molten glass into partially sintered alumina at $1,140^{\circ}C$ for 4 hours. Specimens were polished sequentially from #800 to #2000 diamond disk. and the final surface finishing on the tensile side was received an additional polishing sequence through $1{\mu}m$ diamond paste. Biaxial flexure test was conducted by using ball-on-three-ball method at a crosshead speed of 0.5mm/min. To examine the microstructural aspect of crack propagation in the alumina-glass composites, Vickers-produced indentation crack was made on the tensile surface at a load of 98.0 N and dwell time of 15 sec, and the radial crack patterns were examined by an optical microscope and a scanning electron microscope. The results obtained were summarized as follows; 1. The porosity rates of partially sintered alumina decreased with the rising of firing temperature. 2. The maximum biaxial flexure strength of 423.5MPa in alumina-glass composites was obtained with an addition of 3 mol% $CeO_2$ in glass composition and strength values showed the aspect of decrease with the increase of $CeO_2$ content. 3 The biaxial flexure strength values of alumina-glass composites were decreased with rising the firing temperature. 4. Observation of the fracture surfaces of alumina-glass composites indicated that the enhancement of strength in alumina-glass composites was due to the frictional or geometrical inter-locking of rough fracture surfaces and ligamentary bridging by intact islands of materials left behind the fracture front.

• Korean Journal of Environment and Ecology
• /
• v.30 no.5
• /
• pp.803-809
• /
• 2016

In order to elucidate the ecological responses of B. latissimum under global warming situation and prepare the conservation measures, we cultivated the plant within control(ambient $CO_2+$ambient temperature) and treatment(elevated $CO_2+$elevated temperature) from 2010 to 2011. Rising $CO_2$ concentration was treated with 2 times and temperature increased with $2.0^{\circ}C$ above than control. As a result, Growth response has received more the effect of $CO_2+$Temperature rising than light, moisture, nutrients, and it was grow well in $CO_2+$temperature rise sphere when many nutrients, and it was grow well in $CO_2+$temperature rise sphere when many nutrients. No. of leaves were many number in the treated group compared to the control at a low light gradient and high nutrient gradient, leaf width was narrow in the treatment compared to the control in the middle gradient of light and nutrients. Shoot length, petiole length, lamina length was no difference between control and $CO_2+$temperature rise sphere. Based on the results of this study, in order to preserve the B. latissimum in future climate, we should be supply of nutrients(containing ${NH_4}^+$, $NO_3$, $P_2O_5$, $K_2O$, etc.) in the habitat of the B. latissimum, and must ensure that the habitat of B. latissimum is not destroyed. Also, We should be find similar area with habitat of the B. latissimum, restoring, expanding.

• Journal of Environmental Science International
• /
• v.15 no.6
• /
• pp.579-586
• /
• 2006

The purposes of this paper were to monitor the temperature rising courses and spark discharge of the modified granular activated carbon (GAC) by microwave (MW) irradiation and to evaluate absorption of benzene. The GAC coated on $SiO_2$, boron, talc, ferrite was named as the modified GAC. Thermal and spark discharge measurement of virgin GAC and modifed GAC has been carried out using a MW device operating at 2450 MHz under various energy conditions. The results of this paper as follows. First, the modified GAC is more efficient than the virgin GAC in temperature control. Temperature gradient of the modified GAC is more lower than that of virgin GAC. The temperature gradient of GAC was observed in the following order : virgin GAC, Mn-Zn ferrite/GAC, Ni-Zn ferrite,/GAC, $SiO_2/GAC$, Boron/GAC, Talc/GAC. Second, the spark discharge of the modified GAC was diminished, compared with that of virgin GAC. Because of its excellent electrical insulating properties, the coating material prevents the spark discharge. Finally, the benzene adsorption capacity of the modified GAC decreased due to diminishing of adsorption site by the coating material. Considering the temperature gradient and spark discharge of GAC, the GAC coated $SiO_2$ would be appropriate absorbent under irradiation of MW.

• Journal of Korean Medical classics
• /
• v.19 no.2 s.33
• /
• pp.97-107
• /
• 2006

From the study on the relation of voice and O-jang(五臟廳), the conclusion is as follows. The function of breathing out in larynx is involved with lung and kidney. Lung press out the air, at the same time, kidney supports that to maintenance the density of air constantly. So the person who has short breathing can not make strong voice, and also if having a weak kidney in upper Cho[下蕉], their voice will be changed so very softly to cannot make hard type of voice and lingering sounds. Opening and Closing of vocal cords are controled by liver and spleen. when vocal cords are contracted, liver makes tension, whereas spleen does in slackness. So liver is likely to make high-piched sounds in tension of vocal cords, and spleen is the same to do smoothy and husky sounds through relaxing the vocal cords. In the rising condition of liver function, the temp of speech become fast, and more the pronunciation is clearer, it means that the function of thinking by spleen is operated well. Otherwise, indistinct pronunciation means that in the body seup-sa(濕邪) spreads. Also depression of emotion in speech often makes Gi(氣) of heart weaker, whereas it means regular condition of heart including Simpo(心包) that expression of emotion looks happy.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.22-23
• /
• 2016

This study aims to derive the optimal condition that ensures the monolithicity of ultra-high performance concrete (UHPC), through the evaluation of bonding shear performance with respect to the time of cold joint occurrence during the placement. From the direct shear test, while the normalized bonding shear strength reduction of UHPC with the delay time of 15 minutes was the lowest at around 8%, a dramatic degradation of bonding shear performance was observed after 15 minutes. XRD analysis of the middle and surface sections was performed in order to analyze the composition of the thin film formed at the surface of UHPC, and as a result, the main ingredient appeared to be SiO₂ from the XRD pattern of middle and surface sections, which is believed to be the result of the rising of SiO₂-based filler, used as anadmixture in this study, toward the surface, due to its low specific gravity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1992.05a
• /
• pp.97-100
• /
• 1992

The Degradation mechanism of the ZnO-varistor fabricated with the content of a 3-Composition seed grain is discussed using the method of Thermally Stimulated Current (TSC). The spectra of TSC is measured in the temperature range of -130～270$^{\circ}C$ with a various forming electric fields E$\sub$f/, temperature T$\sub$f/ time tf, and a various rising rate of temperature. It is observed that there are appeared the peaks of ${\alpha}$, ${\alpha}$$_2$, ${\beta}$ and ${\gamma}$from high temperature in a TSC spectrum. It seems that ${\alpha}$$_1$ peak is due to thermal depolarization of donor ions forming the space charge in the depletion layer, and ${\alpha}$$_2$peak is due to the detrapping of trapped electrons in deep trap level of intergranular layer, and ${\beta}$ peak is due to the thermal exciting of carrier existing in the donor level of grain itself, and ${\gamma}$ peak is due to the thermal exciting of trapped carrier in all shallow trap site randomly distributed in the inner of sample and/or a intrinsic impurity existing in it.