• 한국재료학회지
• /
• 제26권12호
• /
• pp.751-756
• /
• 2016

Graphite was diffusion-bonded by hot-pressing to W-25Re alloy using a Ti interlayer. For the joining, a uniaxial pressure of 25 MPa was applied at $1600^{\circ}C$ for 2 hrs in an argon atmosphere with a heating rate of $10^{\circ}C\;min^{-1}$. The interfacial microstructure and elemental distribution of the W-25Re/Ti/Graphite joints were analyzed by scanning electron microscopy (SEM). Hot-pressed joints appeared to form a stable interlayer without any micro-cracking, pores, or defects. To investigate the high-temperature stability of the W-25Re/Ti/Graphite joint, an oxy-acetylene torch test was conducted for 30 seconds with oxygen and acetylene at a 1.3:1 ratio. Cross-sectional analysis of the joint was performed to compare the thickness of the oxide layer and its chemical composition. The thickness of W-25Re changed from 250 to $20{\mu}m$. In the elemental analysis, a high fraction of rhenium was detected at the surface oxidation layer of W-25Re, while the W-25Re matrix was found to maintain the initial weight ratio. Tungsten was first reacted with oxygen at a torch temperature over $2500^{\circ}C$ to form a tungsten oxide layer on the surface of W-25Re. Then, the remaining rhenium was subsequently reacted with oxygen to form rhenium oxide. The interfacial microstructure of the Ti-containing interlayer was stable after the torch test at a temperature over $2500^{\circ}C$.

• 한국세라믹학회지
• /
• 제37권9호
• /
• pp.915-920
• /
• 2000

합성과 동시에 소결이 이루어지는 HPCS법을 이용하여 TiB$_2$-W 복합체를 텅스텐의 함량 변화에 다라 제조하여 이 복합체의 미세구조 및 기계적 물성에 대하여 연구하였다. 이 연구 결과, 텅스텐의 함량증가에 따라 삼성분 붕화 화합물인 TiWB$_2$의 상이 증가하였으며, 이 상의 증가에 따라 기계적 물성이 향상되었다. 60 MPa의 압력과 130$0^{\circ}C$, 3000 A에서 소결한 TiB$_2$-30vol% W 복합체에서 상대밀도, 강도, 경도 값은 각각 97.2%, 411.5 MPa, 22.36 GPa로 가장 우수한 물성을 얻을 수 있었다.

• 한국세라믹학회지
• /
• 제20권1호
• /
• pp.19-24
• /
• 1983

Dielectrics used as capacitor was studied in the system of $Pb(MgW)_{0.5} O_3-PbTiO_3-PbZrO_3$ Curie tempera-tures of $PbTiO_3 PbZrO_3$ and $Pb[MgW]_{0.5} O_3$ were 49$0^{\circ}C$ 23$0^{\circ}C$ and 39$0^{\circ}C$ respectively. When these materials formed solid solution the more amount of $Pb(MgW)_{0.5}O_3$ was increased the more Curie temperature lowered and dielectric constant increased. Higher dielectric constants were measured in the solid solution of which X-Ray diffraction patterns were changed. Especially Curie temperature and dielectric constant were 85$^{\circ}C$ and 4159 respectively in the composition of 60 $Pb(MgW)_{0.5}O_3-30 PbTiO_3-10PbZrO_3$. Also in this composition ferroeletric material with thermal stability was obtained.

• 한국세라믹학회지
• /
• 제39권11호
• /
• pp.1108-1112
• /
• 2002

산화물 제어봉 물질로서 $Dy_xTi_yO_z$ 소결체를 powder process에 의해 제조하였다. $Dy_2O_3+TiO_2$ 혼합분말의 소결성과 고용체의 상을 TMA와 XRD로써 각각 분석하였으며, 소결체의 비열과 열확산계수를 측정하여 열전도도를 구하였다. $Dy_xTi_yO_z$에서 Dy의 함량에 따라 소결성과 밀도가 변하였고 $3\;g\;Dy/cm^3\;Dy_xTi_yO_z$의 경우 $1580{\circ}C$의 소결온도에서 용융이 일어났다. $4.00\;g\;Dy/cm^3$ 소결체에는 $Dy_2TiO_5+Dy_2Ti_2O_7$의 두 상이 존재하며 $4.54\;g\;Dy/cm^3$의 경우 $Dy_2TiO_5$의 단일 상만이 존재하는 결과를 보였다. $Dy_xTi_yO_z$의 열전도도는 $25~600{\circ}C$ 범위에서 온도에 따라 큰 변화가 없으며 $1600{\circ}C$ 소결체가 1.69∼1.78 W/mK, 1550$^{\circ}C$ 소결체의 경우에는 1.49~1.55 W/mK이었다.

• 한국세라믹학회지
• /
• 제20권3호
• /
• pp.227-235
• /
• 1983

The dielectric and piezoelectic properties in which $(Zr_{0.52} Ti_{0.48})^{+4}$ ions of $Pb(Zr_{0.52} Ti_{0.48})O_3$ are partially substituted for $W^{+6}$ ions were studied. $ZrTiO_4$ was made by coprecipitation. The specimens of disc shape were sintered respectively at 1180$^{\circ}$to 130$0^{\circ}C$ at an intervals of 2$0^{\circ}C$ for 1 hour. The optimum sintering temperature were found to be between 126$0^{\circ}C$ and 128$0^{\circ}C$. PZT solid solutions sintered had the tetragonal structure with c/a=1.025$\pm$0.005 and theoretical densities incre-ased from 8.02 to 8.17g/cm3 with increasing the amount of the partial substitution of $(Zr_{0.52} Ti_{0.48})^{+4}$ ion for $W^{+6}$ ion The grain size and curie temperature decreased with increasing the amount of $WO_3$ while the dielectric constant increased. When $(Zr_{0.52} Ti_{0.48})^{+4}$ ion was substituted for 1 mole% of $W{+6 ]$ion the planar coupling coefficient$(K_P)$ was as high as 0.58 But as the amount of $WO_3$ increased the mechanical quality factor(Qm) decreased considerably.

• 한국정밀공학회지
• /
• 제20권1호
• /
• pp.144-150
• /
• 2003

When WC and group IV elements are added to Ti(C,N)-Ni substrate, microstructures of the cermet is changed. The microstructure gives direct effect on the property of the material. In this study, the amount of WC and group W elements of Ti(C,N) cermet tool was investigated. The composition of WC was changed from 5 to 20wt% to determine the effect of WC on the cutting performance of cermet tool. The more WC was added, the longer the tool life of the cermet tool was. The cermet with 20wt% WC showed the best fracture toughness. The effect of group W elements; ZrC, ZrN and HfC was also investigated by adding each of them to manufacture the cermet tool with fixed l4wt% WC composition. The cermet with 1wt% ZrC and 14wt% WC showed the best cutting performance among the investigated cermet tools.

• 한국대기환경학회지
• /
• 제8권1호
• /
• pp.84-91
• /
• 1992

Hydrodesulfurization of thiophene was studied over $Ni-W/TiO_2-ZrO_2$ catalysts in a fixed bed flow reactor. The ranges of experimental conditions were at the temperatures between 200$^\circ$C and 360$^\circ$C, the pressures between 20 X $10^5$ Pa. The catalysts were reduced with the flow of 10 L/hr of $H_2$ at the temperature of 350$^\circ$C. It was found that $TiO_2-ZrO_2$ supported catalysts had similar activity to $\gamma-Al_2O_3$ supported. The largest surface areas and the highest acidity occured as the binary oxides were mixed with equal molar ratios. The HDS increased with increasing temperatures, pressures and contact times.

• 한국세라믹학회지
• /
• 제30권1호
• /
• pp.1-6
• /
• 1993

Dielectric and piezoelectric porperties of pseudoternary xPb(Al2/3W1/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 (x=1~10mol%) ceramic system have been investigated as a function of the amount of PAW[Pb(Al2/3W1/3)O3] and sintered from 110$0^{\circ}C$ to 120$0^{\circ}C$ for 1hr. As the amount of PAW increases, the c/a of tetragonal structure decreases. The grain size was reduced with increasing the amount of PAW addition. However, the density, dielectric constant and electromechanical coupling factor(kp) exhibited a maximum value at the amount of 5mol% PAW addition.

• 한국분말재료학회지
• /
• 제24권1호
• /
• pp.41-45
• /
• 2017

The effects of the heat treatment temperature and of the atmosphere on the dehydrogenation and hydrogen reduction of ball-milled $TiH_2-WO_3$ powder mixtures are investigated for the synthesis of Ti-W powders with controlled microstructure. Homogeneously mixed powders with refined $TiH_2$ particles are successfully prepared by ball milling for 24h. X-ray diffraction (XRD) analyses show that the powder mixture heat-treated in Ar atmosphere is composed of Ti, $Ti_2O$, and W phases, regardless of the heat treatment temperature. However, XRD results for the powder mixture, heat-treated at $600^{\circ}C$ in a hydrogen atmosphere, show $TiH_2$ and TiH peaks as well as reaction phase peaks of Ti oxides and W, while the powder mixture heat-treated at $900^{\circ}C$ exhibits only XRD peaks attributed to Ti oxides and W. The formation behavior of the reaction phases that are dependent on the heat treatment temperature and on the atmosphere is explained by thermodynamic considerations for the dehydrogenation reaction of $TiH_2$, the hydrogen reduction of $WO_3$ and the partial oxidation of dehydrogenated Ti.

• 한국항행학회논문지
• /
• 제7권2호
• /
• pp.211-216
• /
• 2003

본 논문에서는 오래 전부터 NMOS의 게이트 전극으로 사용된 폴리실리콘을 대체할 수 있는 Ta-Ti 합금의 특성에 대해 연구하였다. 실리콘 기판 위에 열적으로 성장된 $SiO_2$ 위에 Ta과 Ti의 두 타깃을 사용하여 co-sputterring 방법으로 Ta-Ti 합금을 증착하였다. 각각의 타깃은 100W의 sputtering power로 증착하여 시편을 제작하였다. 또한 비교 분석을 위하여 Ta을 100W의 sputtering power로 증착한 시편도 제작하였다. 제작된 Ta-Ti 합금 게이트의 열적/화학적 안정성을 검토하기 위하여 $600^{\circ}C$에서 급속열처리를 수행한 결과 소자의 성능 저하는 나타나지 않았다. 또한 전기적 특성 분석 결과 Ta-Ti 합금은 NMOS에 적합한 일함수인 4.13eV를 산출해 낼 수 있었고, 면저항 역시 폴리실리콘에 비해 낮은 값을 얻을 수 있었다.