• Journal of the Korean institute of surface engineering
• /
• v.25 no.5
• /
• pp.223-233
• /
• 1992

(Ti, Al)N films were deposited on 304 stainless steel by D.C. magnetron sputtering using Al target and Ti plate. The properties of (Ti, Al)N films such as composition, microhardness, grain size, crystal structure were investigated. The chemical composition of (Ti, Al)N films was similar to the sputter area ratio of titanium to aluminum target by means of EDS and AES survey. The higher bias voltage to substrate and the smaller input of N2 gas showedthe increased microhardness and the finer grain size of the films. The results obtained from this study show, it is belived, that the (Ti, Al)N film by D.C.magne-tron sputtering is promising in the wear resistance use.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.04a
• /
• pp.12-12
• /
• 2006

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.688-694
• /
• 1999

Ti-6Al-4V-N films have been grown onto glass substrates by dc reactive magnetron sputtering from a Ti-6Al-4V-N alloy target at different nitrogen partial pressure, input powers and sputtering times. The influence of various sputtering conditions on structural properties of Ti-6Al-4V-N films was investigated by measuring their X-ray diffraction. The quaternary Ti-6Al-4V-N film is crystallizing in a face centered cubic TiN structure, the lattice parameter is smaller than the TiN parameter as titanium atoms of the TiN lattice are replaced by aluminum and vanadium atoms. The films show the (111) preferred orientation and the (111) peak intensity decreases as the nitrogen partial pressure is increased, but the intensity increases as the sputtering time is increased. The deposition rate and the grain size are alto related with the variation of various sputtering conditions.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.558-564
• /
• 2004

In order to improve the low hardness and low wear resistance of Ti-6Al-4V alloy, plasma carburization treatment and CrN film coating were carried out. Effects of the plasma carburization and CrN coating were analyzed and compared with the non-treated alloy by mechanical and creep tests. After plasma carburization and CrN coating treatments, the carburized layer was about 150 ${\mu}m$ in depth and CrN coated layer was about 7.5 ${\mu}m$ in thickness. Hardness value of about $H_{v}$ 402 of the non-treated alloy was improved to $H_{v}$ 1600 and 1390 by plasma carburization and CrN thin film coating, respectively. Stress exponent(n) was decreased from 9.10 in CrN coating specimen to 8.95 in carburized specimen. However, the activation energy(Q) was increased from 242 to 250 kJ/mol. It can be concluded that the static creep deformation for Ti-6Al-4V alloy is controlled by the dislocation climb over the ranges of the experimental conditions.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.131-132
• /
• 2015

$Ti_{0.26}Al_{0.16}Si_{0.01}N_{0.57}$ (at%) coatings were synthesized on stainless steel 304 by using arc ion plating systems (AIPS). Targets employed for the deposition were Ti, AlSi(67:33at%) and AlSi(82:18at%). The thickness of TiAlSiN coatings is $4{\mu}m$. The oxidation characteristics of the deposited coatings were studied by thermogravimetric analysis (TGA) in air between 800 and $900^{\circ}C$ for 75 hr. The oxide scale formed on the TiAlSiN coatings consisted of $rutile-TiO_2$ layer and ${\alpha}-Al_2O_3$. At $800^{\circ}C$, the coatings oxidized relatively slowly, and the scales were thin and adherent. When oxidized above $900^{\circ}C$, $TiO_2$ grew fast over the mixed oxide layer, and the oxide scale formed on TiAlSiN coatings was prone to spallation. Microstructural changes of the TiAlSiN coatings that occurred during high temperature oxidation were investigated by EPMA, XRD, SEM and TEM.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.207-215
• /
• 1997

Aluminum (Al) thin films were deposited on the Si(100) and TiN(60 nm)/Si (100) substrate by the ionized cluster beam deposition (ICBD) method. The characteristics of thin films were examined by the $\alpha$-step, four-point-probe, Scanning Electron Spectroscopy (SEM), Auger Electron Spectroscopy (AES). The growth rate of the Al thin film increased and the resistivity decreased as the crucible temperature increased. At the crucible temperature $1800^{\circ}C$, the microstructure of Al thin film deposited was smooth and continuous the resistivity decreased as the acceleration voltage increased. Also, the minimum resistivity in Si(100) substrate and TiN(60 nm)/Si(100) substrate were 3.4 $\mu \Omega \textrm {cm}$, 3.6 $\mu \Omega \textrm {cm}$ at the acceleration voltage 4 kV and 2 kV respectively. From the AES spectrumt 14 wasn't detected any impurities In the Al thin film. Therefore the resistivity of Al thin film was affected by the microstructure of film.

• International Journal of Ocean System Engineering
• /
• v.2 no.2
• /
• pp.106-115
• /
• 2012

In the present study, TiN and CrN films were coated by arc ion plating equipment onto aluminum alloy substrate, A2024. The film thickness was about 4.65 ${\mu}m$. TiN and CrN films were analyzed by X-ray diffraction and energy dispersive X-ray equipments. The Young's modulus and the micro-Vickers hardness of aluminum substrate were modified by the ceramic film coatings. The difference in Young's modulus between substrate and coating film would affect on the wear resistance. The critical load, Lc, was 75.8 N for TiN and 85.5 N for CrN. It indicated from the observation of optical micrographs for TiN and CrN films that lots of cracks widely propagated toward the both sides of scratch track in the early stage of MODE I. TiN film began to delaminate completely at MODE II stage. The substrate was finally glittered at MODE III stage. For CrN film, a few crack can be observed at MODE I stage. The delamination of film was not still occurred at MODE II and then was happened at MODE III. This agrees with critical load measurement which the adhesive strength was greater for CrN film than for TiN film. Consequently, it was difficult for CrN to delaminate because the adhesive strength was excellent against Al substrate. The wear process, which the film adheres and the ball transfers, could be enhanced because of the increase in loading. The wear weight of ball was less for CrN than for TiN. This means that the wear damage of ball was greater for TiN than for CrN film. It is also obvious that it was difficult to delaminate because the CrN coating film has high toughness. The coefficient of friction was less for CrN coating film than for TiN film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.06a
• /
• pp.3-3
• /
• 2001

Recently TiN, TiAlN, CrN hardcoatings have adapted many industrial application such as die, mold and cutting tools because of good wear resistant and thermal stability. However, in terms of high speed process, general hard coatings have been limited by oxidation and thermal hardness drop. Especially in the case of PCB drill, high speed cutting and without lubricant process condition have not adapted these coatings until now. Therefore more recently, superhard nanocomposite coating which have superhard and good thermal stability have developed. In previous works, WC-TiAlN new nanocomposite film was investigated by cathodic arc ion plating system. Control of AI concentration, WC-TiAlN multi layer composite coating with controlled microstructure was carried out and provides additional enhancement of mechanical properties as well as oxidation resistance at elevated temperature. It is noted that microhardness ofWC-TiA1N multi layer composite coating increased up to 50 Gpa and got thermal stability about $900^{\circ}C$. In this study WC-TiAlN nanocomposite coating was deposited on PCB drill for enhancement of life time. The parameter was A1 concentration and plasma cleaning time for edge sharpness maintaining. The characteristic of WC-TiAlN film formation and wear behaviors are discussed with data from AlES, XRD, EDS and SEM analysis. Through field test, enhancement of life time for PCB drill was measured.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.05a
• /
• pp.144-144
• /
• 2001

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.9
• /
• pp.681-685
• /
• 2012

We investigated the dry etching characteristics of TiN in $TiN/Al_2O_3$ gate stack using a inductively coupled plasma system. TiN thin film is etched by BCl3/He plasma. The etching parameters are the gas mixing ratio, the RF power, the DC-bias voltages and process pressures. The highest etch rate is in $BCl_3/He$ (25%:75%) plasma. The selectivity of TiN thin film to $Al_2O_3$ is pretty similar with $BCl_3/He$ plasma. The chemical reactions of the etched TiN thin films are investigated by X-ray photoelectron spectroscopy. The intensities of the Ti 2p and the N 1s peaks are modified by $BCl_3$ plasma. Intensity and binding energy of Ti and N could be changed due to a chemical reaction on the surface of TiN thin films. Also we investigated that the non-volatile byproducts such as $TiCl_x$ formed by chemical reaction with Cl radicals on the surface of TiN thin films.