• 한국초전도ㆍ저온공학회논문지
• /
• 제1권2호
• /
• pp.1-7
• /
• 1999

we evaluated the effects of joining process such as contact method. shape of joined area and pressure on the electrical and mechanical properties of Bi-2223 superconducting tape, Specifically. the current capacity of the jointed tape was measured as a function of uniaxial pressure. and the thermal shock, bonding strength and the thermal of the tape were evaluated and correlated to the microstructural evolution. It was observed that the current capacity was significanrly dependent on the uniaxial pressure The jointed tape, fabricated with a pressure of 1,000-1,600 Mpa. showed the highest value of current capacity results from improvements in core density, contacting area and grain alignment, ect. In addition, the strength of jointed tape was measured to be 86 Mpa, which is about 88% of the unjoined ape's strength. The irreversible strain($\varepsilon$irrev) for the jointed tape was measured to be 0.1%, smaller than that of unjoined tape ($\varepsilon$irrev= 0.3%). The decrease in the strength and irreversible strain for jointed tape is believed to be due to the irregular geometry/morphology of the transition area of the tape.

• 전기학회논문지
• /
• 제59권2호
• /
• pp.352-354
• /
• 2010

The effects of Au addition on the structure and the superconducting properties of Bi system bulk have been investigated. Au exists in the metalic form in above materials. It does not affect the formation and structure of the BiSrCaCuO(2223) phase. The superconducting transition temperature Tc does not change for $Bi_{1.7}Pb_{0.3}Sr_2Ca_2Cu_3O$ composite However Au doping can make the grains smaller. Metallic Au can make gathers on the grains boundary and lead to the increment of critical transport current density. The current density of $Bi_{1.7}Pb_{0.3}Sr_2Ca_2Cu_3Au_{0.5}O$ was 1000A/$cm^2$ at liquid nitrogen temperature.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1992년도 춘계학술대회 논문집
• /
• pp.58-63
• /
• 1992

Effects of the second sintering process on the superconducting characteristics of the (Bi, Pb)SrCaCuO system have been studied. It was found that the optimal calcining temperature of mixed powder may be proper to 820$^{\circ}C$ and the optimal sintering temperture was determined on 845$^{\circ}C$. The 2212 phases transitioned the 2223 phasses during the sintring process and zero resistance was attained at 108 K for the samples sintered for 264 hr. The 2223 phases changed into the 2212 phases and nonsuperconducting phases by the second grinding process. And the 2223 phases did not recover easily by the second sintering process.

• 한국전기전자재료학회논문지
• /
• 제11권11호
• /
• pp.1014-1021
• /
• 1998

We evaluated the effect of processing variables on microstructural evolution interface irregularity between Ag sheath and superconductor core and resultant critical current density(J$_{c}$) of (Bi,Pb)$_2$Sr$_2$Ca$_2$Cu$_3$O$_{x}$(2223) superconductor tape. The value of J$_{c}$ was significantly influenced by the interface irregularity, degree of texturing and relative 2223 content. The interface became more irregular(sausage effect), while the degree of texturing gradually improved as the dimension of tape decreased during forming process. As the dimension of wire/tape were changed from diameter of 3.25 mm to thickness of 0.20 mm, J$_{c}$ value was observed to be increased by 10 times. In addition, optimum sintering temperature for improved J$_{c}$ was observed to be 835$^{\circ}C$ in a ambient atmosphere probably due to combined effect of both improved texturing and high 2223 content. Microstructural investigation showed the degree of texturing was degraded by the existence of both second phases and interface irregularity. It was observed that larger grain size and better texturing was developed near relatively flat interface compared to those inside superconducting core.ting core.

• Transactions on Electrical and Electronic Materials
• /
• 제9권6호
• /
• pp.265-272
• /
• 2008

In this paper, AC losses of long wire Bi-2223 tapes with different twist pitch of superconducting core were fabricated, measured and analyzed. These samples produced by a powder-in-tube method are multi-filamentary tape with Ag matrix. Also, it's produced by non-twist. The critical current measurement was carried out under the environment in Liquid nitrogen and in zero field by 4-prob method. And the Magnetic measurement was carried out under the environment of applied time-varying transport current by transport method. From experiment, the susceptibility measurements were conducted while cooling in a magnetic field. Flux loss measurements were conducted as a function of ramping rate, frequency and field direction. The AC flux loss increases as the twist-pitch of the tapes decreased, in agreement with the Norris Equation. Neutron-diffraction measurements have been carried out investigate the crystal structure, magnetic structures, and magnetic phase transitions in Bi-2223([Bi, Pb]:Sr:Ca:Cu:O).

• KIEE International Transactions on Electrophysics and Applications
• /
• 제3C권6호
• /
• pp.211-215
• /
• 2003

Alternating current (AC) losses of two Bi-2223 ([Bi, Pb] : Sr : Ca : Cu :O = 2:2:2:3) tapes [one untwisted (Tape I, twist-pitch of $\infty$ mm) and the other with a twist-pitch of 8mm (Tape II) ] were measured and compared. These samples, produced by the powder-in-tube (PIT) method, are multi-filamentary and have a Ag/Au and Ag matrix, respectively. Susceptibility measurements were conducted while cooling in a magnetic field. Flux loss measurements were conducted as a function of ramping rate, frequency and field direction. The AC flux loss increases as the twist-pitch of the tapes decreased, in agreement with the Norris Equation.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2000년도 High Temperature Superconductivity Vol.X
• /
• pp.298-303
• /
• 2000

We evaluated the electric properties of Bi-2223 jointed tapes processed by both resistive- and supercondcuting-joint methods. For the resistive-joint, filler materials of wood metal, Pb/Sn, In, and silver paste were used, whereas, for the superconductive-joint, the lap joint method were used. In the resistive-joint tape, it was observed that the electrical properties such as current transport property, n-value, and contact resistance of the tape were significantly related to the resistivity of filler materials. On the other hand, in the superconducting-joint tape, the current transport property was dependent on the uniaxial pressure. Specifically, the current transport property varied 50 to 80% with uniaxial pressure, probably due to the irregular microstructure in the transition region.

• 한국전기전자재료학회논문지
• /
• 제16권6호
• /
• pp.522-531
• /
• 2003

Samples with the nominal composition, B $i_{1.84}$P $b_{0.34}$S $r_{1.91}$C $a_{2.03}$C $u_{3.06}$ $O_{10+{\delta}}$ high- $T_{c}$ superconductors containing MgO as an additive were fabricated by a solid-state reaction method. Samples with MgO of 5~30 wt% each were sintered at 820~86$0^{\circ}C$ for 24 hours. The structural characteristics, critical temperature, grain size and image of mapping with respect to MgO contents were analyzed by XRD(X-Ray Diffraction), SEM(Scanning Electron Microscope) and EDS(Energy dispersive X-ray spectrometer) respectively. As MgO contents increased, intensity of MgO Peaks and ratio of Bi-2212 phase in superconductors intensified and the proportion of the phase transition from Bi-2223 to Bi-2212 was increased.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1991년도 추계학술대회 논문집 학회본부
• /
• pp.311-315
• /
• 1991

The formation and transition of 2212 and 2223 phase have been studied in BPSCCO system. The 2212 phase formed in early sintering state reacts on $Ca_2PbO_4,\;Ca_2CuO_3$ and CuO during sintering process and thus produces the 2223 phase. A long sintering period is need to fabricate the superconductor with large volume fraction of 2223 phase. Also, the thin plate-like grains composed of Bi, Sr, Ca and Cu contribute to 2223 phase formation. Though the sample has lower volume fraction of 2223 phase, the critical temperature is measured highly in case of the grain grown to plate-like shape. In this work, the critical temperature of the sample sintered for 264 hr in air was measured 108 K. Microstructure of the sample was varied with condition of heat treatment after sintering process and the sample annealed with $500^{\circ}C$ for 5 hr showed excellent charateristics of 2223 phase formation.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1993년도 정기총회 및 추계학술대회 논문집 학회본부
• /
• pp.213-215
• /
• 1993

Silver-sheathed Bi-Pb-Sr-Ca-Cu-O wires by the powder-in-tube method were preparated to study on the superconducting properties with cooling conditions. Superconducting wires were cooled down in the furnace, air and liquid $N_2$ after sintering at $840^{\circ}C$. Critical current density of sample cooled in the furnace is $5.1{\times}10^3\;A/cm^2$ at 77K, zero magnetic field and Jc of sample cooled in the air is very low. 2223 high-Tc superconducting phase of sample cooled in the air was distroyed. Therefore, we knew that superconducting wire need to cool slowly to get the high critical current density.