• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.2
• /
• pp.91-97
• /
• 2000

The structure and mechanical properties of TiN and TiCN thin films deposited on STD61 steel substrates by the RF-sputtering methods has been studied by using XPS, XRD, micro-hardness tester, scratch tester, and wear-resistance tester. XPS results showed that the TiCN thin film formed with chemical bonding state. The TiN thin films grew with (111) orientation having the lowest strain energy by compressive stress, whereas the TiCN thin films grew with both (111) and (200) orientation, but (200) orientation having the lowest surface energy becomes dominant as carbon contents increase. The pre-etching treatment of substrate did not affect on the preferred orientation of thin films, but it played an important role in improving mechanical properties of thin films such as the hardness, adhesion and wear- resistance. Especially, the TiCN thin films showed the superior wear resistances due to high hardness and low friction coefficient compared with TiN thin films.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.399-406
• /
• 1996

The orientational cross-over phenomena in an RF sputtering growth of TiN films were studied in an in-situ, real-time synchrotron x-ray scattering experiment. For the films grown with pure Ar sputtering gas, the cross-over from the more strained (002)-oriented grains to the less strained (111)-oriented grains occurred as the film thickness was increased. As the sputtering power was increased, the cross-over thickness, at which the growth orientation changes from the <002> to the <111> direction, was decreased. The addition of $N_2$ besides Ar as sputtering gas suppressed the cross-over, and consequently resulted in the (002) preferred orientation without exhibiting the cross-over. We attribute the observed cross-over phenomena to the competition between the surface and the strain energy. The x-ray powder diffraction, the x-ray reflectivity, and the ex-situ AFM surface topology study consistently suggest that the microscopic growth front was in fact always the (002) planes. In the initial stage of growth, the (002) planes were aligned to the substrate surface to minimize the surface energy. At later stages, however, the (002) growth front tilted away from the surface by about $60^{\circ}$ to relax the strain, which caused the cross-over of the preferred growth direction to the <111> direction.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.2
• /
• pp.79-89
• /
• 2014

The effect of carbon on the microstructure and texture of low carbon steels was investigated in a series of 1.6 Mn-0.3Cr-0.2Mo-0.001B steels with carbon ranging from 0.021 to 0.048%. Intensity of {111} orientation increased with decreasing the carbon content, resulting in the increase in $r_m$ value. The highest $r_m$ value of 1.30 was obtained in 0.021%C steel annealed at $820{\sim}850^{\circ}C$ according to the typical galvannealing heat cycle. Martensite volume fraction was not substantially affected by the annealing temperature. It was found that the fine and uniformly distributed martensite particles which were present in amounts of about 5% volume fraction were desirable for the highest $r_m$ value. The other factor affecting the high $r_m$ value was the preferred epitaxial growth of retained ferrite with {111} orientation into austenite during cooling.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.33 no.4
• /
• pp.157-163
• /
• 1984

The object of this paper is to investigte the gate controlled diode structure for ionic concentration measurement. It includes device fabrication, characterization, device physics and modeling of the gate controlled diode structure. The differences of turn on voltages and surface generation currents in the (100) and (111) silicon crystallographic orientation of the sample device were observed. Therefore the dependence of these two factors of the silicon crystallographic orientation was investigated. It was observed that drifts arose after extended immersion of the sample device in acid or base solutions. The surface generation-recombination velocity of both (100) and (111) increased. The increase in the interfacial traps for both surface, determined by the turn on voltage was directly proportional to the surface generation-recombination velocity increase.

• Journal of the Korean institute of surface engineering
• /
• v.18 no.3
• /
• pp.95-104
• /
• 1985

A study has been made of preferred orientation, crose sectional microstructure, surface morphology and mechanical properties of copper foils fabricated by electrodeposition on 304 stainless steel plate from copper sulfate baths for high speed plating. The preferred orientation of the copper foils changed from the [110] to the [111] to ture with decreasing bath temperature and increasing cathode current density. The foils with the [110] texture had the field oriented texture type structure and the surface of many asperities grooved approximately perpendicular to the subtrate. A specimen with the [111]+[311] texture had the lower strength than one with the [10] texture, if they were obtained under similar electrolysis conditions.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.3
• /
• pp.155-161
• /
• 2009

An investigation of the deformation behavior of ${\gamma}'-Ni_3Al$ single crystals containing fine dispersion of disordered ${\gamma}$ particles was performed for several different crystal orientations. Deformation structures were observed by the weak-beam method of transmission electron microscopy (TEM). The critical resolved shear stress (CRSS) for (111) [$\bar{1}$01] slie. increases with increasing temperature in the temperature range where (111) slip operates. The CRSS for (111) [$\bar{1}$01] slip is dependent on crystal orientation in the corresponding temperature range. The temperature where the strenjlth reaches a maximum is dependent on crystal orientation; the higher the ratio of the Schmid factors of (010) [$\bar{1}$01] to that of (111) [$\bar{1}$01], the higher the peak temperature. The peak temperatures were increased by the precipitation of y particles for the samples of all orientations. Electron microscopy of deformation induced dislocation arrangements under peak temperature has revealed that most of dislocations are straight screw dislocations. The mobility of screw dislocations decreases with increasing temperature. Above the peak temperature, dislocations begin to cross slip from the (111) [$\bar{1}$01] slip system to the (010) [$\bar{1}$01] slip system, thus decreasing the strength.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2000.09a
• /
• pp.377-378
• /
• 2000

• Journal of Families and Better Life
• /
• v.15 no.1
• /
• pp.111-128
• /
• 1997

This study mainly deals with the housewife's value orientation home management strategy and home management satisfaction,. The major results are as follows; 1) The degree of communication and communication frequency in household prove the predictable variables to influence the housewife's value orientation home management strategy and home management satisfaction. 2) Among the value orientation fate control orientation predicts home management strategy. 3) Material orientation shows the negative influence on her home management satisfaction. 4) Among home management strategy the fact that household financial management strategy and housework organization strategy are the important variables in the home management satisfaction suggest that household financial management and everyday repeated housework management cause the deep influence on her life satisfaction. 5) The higher her material orientation and gender equilibrium orientation are the higher housework socialization stra egy frequency is the lower her home management satisfaction is.

• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.313-320
• /
• 1995

We investigated the preferred orientation, electrical and magnetic properties of the Mn-Zn ferrite thin films deposited on SiO2/Si(100) by ion beam sputtering. The Cu-added Mn-Zn ferrite thin films had a preferred orientation of (111) with a weak orientation, (311). While the Zn-added one had a strong (111) preferred orientation. The saturation magnetization of the Cu- or Zn-doped Mn-Zn ferrite films increased with increasing substrate temperature (Ts) due to the increase of grain size and the enhancement of crystallinity. For the same reason the coercivity of Cu- or Zn-doped Mn-Zn ferrite films deposited at low Ts increased with increasing Ts, but those of the films deposited at high Ts slightly decreased not only because the defect density of the films decreases but because more grains have multi-domains with increasing Ts. The resistivity of Cu- or Zn-added Mn-Zn ferrite thin fims measured by complex impedance method decreased with increasing Ts due to the ehhancement of crystallinity as well as due to the increase of grain size.

• Korean Journal of Materials Research
• /
• v.19 no.12
• /
• pp.674-679
• /
• 2009

Yttria stabilized zirconia single crystals show plastic deformation at high temperatures by activating dislocations. The plastic deformation is highly dependent on crystallographic orientation. When the samples were deformed at different orientations, stress-strain curves changed by operating different slip systems. The strength of samples was also highly dependent on crystallographic orientation, i.e., samples without yield drop showed higher strength than that of samples exhibiting yield drop. The slip systems in the sample deformed along <112>, <111> and <001> agreed with the theoretical values of the plastic deformation, following Schmid's Law. Dislocations play a major role in the plastic deformation of this crystal. At the early stages of plastic deformation, all samples exhibited dislocation dipoles and, in the later stages, dislocation interactions occurred by forming nodes, tangles and networks. In this study, three different orientations, [11-2], [111] and [001] were employed to explain the plastic deformation behavior. A microstructural analysis was performed to elucidate the mechanism of the plastic behavior of this crystal.