• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.4
• /
• pp.297-302
• /
• 2011

Recently, low temperature co-fired ceramic (LTCC) technology is widely used in sensors, actuators and microsystems fields because of its very good electrical and mechanical properties, high reliability and stability as well as possibility of making 3D micro structures. In this study, we investigated the effects of sputtering gas ratio and annealing temperature on the crystal structure of $Pb(ZrTi)O_3$ (PZT) thin films deposited on LTCC substrate. The LTCC substrate with thickness of $400\;{\mu}m$ were fabricated by laminating 4 green tapes which consist of alumina and glass particle in an organic binder. The PZT thin films were deposited on Pt / Ti / LTCC substrates by RF magnetron sputtering method. The results showed that the crystallization of the films were enhanced as increasing $O_2$ mixing ratio. At about 25% $O_2$ mixing ratio, was well crystallized in the perovskite structure. PZT thin films was annealed at various temperatures. When the annealing temperature is lower, the PZT thin films become a phyrochlore phase. However, when the annealing temperature is higher than $600^{\circ}C$, the PZT thin films become a perovskite phase. At the annealing temperature of $700^{\circ}C$, perovskite PZT thin films with good quality structure was obtained.

• Journal of the Korean Society of Safety
• /
• v.24 no.4
• /
• pp.22-27
• /
• 2009

In this paper, the minuteness structure, piezoelectric, and dielectric characteristics of $0.95{Pb(Sb_{1/2}Nb_{1/2})_{0.02})_{0.02}(Ni_{1/3}Nb_{2/3})_{0.13}(Zr_{0.48}Ti_{0.52})_{0.85}}O_3+0.05Pb(CO_{1/2}W_{1/2})O_3+0.3%$ $MnO_2+0.3wt%$ CuO ceramics has been systematically investigated as a function of the sintering temperature after manufacturing the specimens with a general method. This study will be very helpful as basic data for developing ceramic materials, More study in a soon time for improving stability of temperature, effect of adds and stability and reality of frequency with improved production condition for specimens will give a powerful potentiality as a applied material of dielectric ceramics.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.3
• /
• pp.220-226
• /
• 2000

The piezoelectric material for piezoelectric transformer needs the high electromechanical coupling factor( $k_{p}$) the piezoelectric constant( $d_{33}$) and the mechanical quality factor( $Q_{m}$)in order to obtain high voltage step-up ratio and low temperature rising. In this study the piezoelectric transformers were fabricated using Pb［$Zr_{0.45}$/ $Ti_{0}$48//L $u_{0.02}$(M $n_{1}$3//S $b_{2}$3/)$_{0.05}$］ $O_3$(PMS-PZT) and Pb［Z $r_{0.25}$/ $Ti_{0.375}$(M $g_{1}$3//N $b_{2}$3/)$_{0.375}$］ $O_3$+0.5wt%Mn $O_2$(PMN-PZT) ceramics. The piezoelectric properties of PMS-PZT and PMN-PZT were measured. The voltage set-up ratios of the piezoelectric transformers using PMS-PZT and PMN-PZT were the value of 15, 20 respectively under 100$_{KΩ}$ in Rosen type transformer.r.ormer.r.r.r.r.r.r.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1991.10a
• /
• pp.68-72
• /
• 1991

In this study, to improve temperature stability 0.05 Pb(Sn$\_$$\frac{1}{2}$/Sb$\_$$\frac{1}{2}$/O$_3$ - 0.35PbTiO$_3$ - 0.60PbZrO$_3$ + 0.4[wt%]MnO$_2$ piezoelctric oeramics of low dielectric constant and large mechanical quality factor were manufactured with the addition of Cr$_2$O$_3$by Hot Press method. And the SAW delay line was fabricated and the propagation characteristics of SAW was investigated, and the SAW filter was fabricated on C4 added by 0.2[wt%] Cr$_2$O$_3$and its frequency characteristics was investigated. The specimen, whose propagation characteristics of surface acoustic wave were the best, was C4 added by 0.2[wt%] Cr$_2$O$_3$, and its electromechanical coupling factor(ks$^2$) was 3.11[%] and its temperature coefficient of the center frequency (C$\_$fo/) was -21.27[ppm/$^{\circ}C$]. The 31[MHz] SAW IF filter of C4 scarcely had diffraction phenomena and its group delay time was 1.4673 ${\pm}$40[ns] in the pass band, and the insertion loss was -24.419[dB] on no impedance matching.

• Journal of Conservation Science
• /
• v.33 no.3
• /
• pp.215-223
• /
• 2017

The purpose of this study is to reveal the characteristics, correlations, and colorant materials of those using the chemical compositions of 30 glasses excavated from the Sarari hall of the Mireuksaji stone pagoda, and to determine the correlations between them and other glass excavated from the Wanggungri site. The results of the chemical analysis of the 11 glass beads show that they are a soda glass group with high contents of $SiO_2$ and $Na_2O$; these can be further subdivided into soda-alumina groups ($Na_2O-Al_2O_3-CaO-Si_2O$). The characteristics of the stabilizer are classified as being of the high alumina glass group (LCHA), except for two glasses. It was concluded that colorant materials affected the coloring for glass beads by various components including Ti, Mn, Fe, Cu and Pb. In addition, we examined six lead glasses which are glass plate and unknown fragments that are of a common lead glass system ($PbO-SiO_2$) with respect to the average contents of PbO (70wt.%) and $SiO_2$ (30wt.%). As a result of comparing these relics with those of the glass beads excavated by Wanggungri, there is a similarity in that they belong to the soda glass group. However, the contents of $Na_2O$ are relatively higher than that of the glass beads in the Mireuksaji pagoda, and most of relics include glasses with a low content of $K_2O$ and CaO. In addition, the PbO and $SiO_2$ contents are slightly different in the lead glass. It seems that the glass relics made at two different sites may have used different raw materials or techniques.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.338-343
• /
• 2002

In this study, $Pb_{0.88}(La_{\alpha}Nd_{1-\alpha})_{0.08}(Mn_{1/3}Sb_{2/3})_{0.02}Ti_{0.98}O_3$ system ceramics with La molar ratio $\alpha$ variation were manufactured for 24 MHz class resonator application. Electromechanical coupling factor, mechanical quality factor and dynamic range of $3^{rd}$ overtone thickness vibration mode were measured as the variations of La and Nd molar ratio. Mechanical quality factor and dynamic range at $\alpha$ = 0.6 composition ceramics showed the highest value of 2691 and 52.37 dB, respectively. The temperature coefficient of resonant frequency measured from $-20^{\circ} to 80^{\circ}$ showed an excellent value of $5ppm/^{\circ}C$ at $\alpha$=1 composition ceramics.

• 보존과학연구
• /
• s.22
• /
• pp.93-114
• /
• 2001

The composition analysis of Danchung pigments at Geunjeongjeon Hall in Gyeongbokgung Palace were carried out by FXRF and MXRD. The analytical result of the inside pigments at Geunjeongjeon showed that these painted in use the mineral pigments. Gold pigment was pure gold(Au).The main composition identified in green pigments were chalcanthite($CuSO_4$.$5H_2O$) and celadonite($K(Mg, Fe, Al)_2$.$(Si, Al)_4O_10(OH)_2$ ). Red pigments werecinnnabar(HgS).The analytical result of the outside pigments at Geunjeongjeon revealed that these applied to the artificial synthetic pigment. Yellow pigment was chromeyellow($PbCrO_4$). The main composition identified in red pigments were red lead($Pb_3O_4$)and hematite($Fe_2O_3$). Green pigments were emeral green($C_2H_3A_s3Cu_2O_8$) and chromegreen($Cr_2O_3$). Blue pigment was lazurite($Na_6Ca2Al_6Si_6O_24(SO_4)_2$), titanium dioxide($TiO_2$) of white pigment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.10
• /
• pp.966-970
• /
• 2006

We reported on characteristics of the piezoelectric ceramic-polymer composite for the application of the thick-film speaker. The PVDF-PZT composites were fabricated to incorporate the advantages of both ceramic and polymer with various mixing ratios by 3-roll mill mixer. The composite solutions were coated by the conventional screen-printing method on ITO electrode coated PET (Polyethylene terephthalate) polymer film. After depositing the top-electrode of silver-paste, 4 kV/mm of DC field was applied at $120^{\circ}C$ for 30 min to poling the composite films. The value of $d_{33}$ (piezoelectric charge constant) was increased when the PZT weight percent was increased. The maximum value of the $d_{33}$ was 24 pC/N at 70 wt% PZT. But the $g{33}$ (piezoelectric voltage constant) showed the maximum value of $32mV{\cdot}m/N$ at 65 wt% of PZT powder. The SPL (sound pressure level) of the speaker fabricated with the 65:35 composite film was about 68 dB at 1 kHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.12
• /
• pp.1077-1082
• /
• 2008

To fabricate a multi-layered piezoelectrics/electrodes structure, the piezoelectrics should be sintered at the temperature lower than $950^{\circ}C$ to use the silver electrode, which is cheaper than the electrodes containing noble metals such as Pd and Pt. Therefore, in this study, we modified the composition of $Pb(Zr,Ti)O_3$-based material as $(Pb_{0.98}Cd_{0.02})(Ni_{1/3}Nb_{2/3})_{0.25}Zr_{0.35}Ti_{0.4}O_3$ to lower the sintering temperature and to improve the piezoelectric properties. Small amount of $MnCO_3$, $SiO_2$, and $Pb_3O_4$ were also added to lower the sintering temperature of the ceramic. The prepared raw powders were mixed by using a ball mill for 24 hours. And then the mixed powders were calcinated for 2 hours at $800^{\circ}C$. The calcinated powders were again crushed with the ball mill for 72 hours. The final powders were pressed for making the shape of ${\emptyset}15\;mm$ disk. The disk-type samples were sintered at temperature range of $850{\sim}950^{\circ}C$. The crystal phases of the sintered specimens were perovskite structure without secondary phases. All of the measured electrical properties such as electromechanical coupling coefficients ($k_p$), mechanical quality factors ($Q_m$), and piezoelectric charge constants ($d_{33}$) were decreased with decreasing the sintering temperatures. The electrical properties measured at the sample sintered at $950^{\circ}C$ were 54% of $k_p$, 503 of $Q_m$, and 390 pC/N of $d_{33}$, respectively. These properties were considered to be fairly good for the application of multi-layered piezoelectric generators or actuators.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.68-69
• /
• 2005

Low temperature ($\leq900^{\circ}C$) sintering piezoelectric ceramics $0.01Pb(Mg_{1/2}W_{1/2})O_3$-0.41Pb$(Ni_{1/3}Nb_{2/3})O_3-0.35PbTiO_3-0.23PbZrO_3+0.1wt%Y_2O_3+xwt%ZnO$ $(0{\leq}x{\leq}2.5)$ have been developed and investigated. The electromechanical coupling coefficient ($k_p$), piezoelectric constant ($d_{33}$), and mechanical quality factor ($Q_m$) have been measured to characterize the piezoelectric materials system. When 2.0 wt% ZnO is added, the properties of the system, $d_{33}$ = 559 pC/N, $k_p$ = 55.0 % and $Q_m$ = 73.4 are obtained which are very suitable for piezoelectric actuators. A bending mode multilayer actuator has been also developed using the materials which size is $27(L)\times9(W)\times1.07(t)mm^3$. The actuators are fabricated by multilayer ceramic (MLC) process and consist of24 layers and each layer thickness is $35{\mu}m$. At this time, the displacement of actuator was $100{\mu}m$ at 28V.