• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.228-229
• /
• 2006

본 연구에서는 초음파 모터 등의 고출력 액츄에이터에 응용 가능한 $04Pb(Ni_{1/3}Nb_{2/3})O_3-6Pb(Zr_xTi_{1-x})O_3$ 조성시스템에 소결온도를 달리하여 압전, 유전특성 및 미세구조에 관해 고찰하였다. 본 조성을 $1200^{\circ}C$ 온도에서 2, 4, 6, 8시간 소결하여 시편을 제조하였으며 이의 결정구조 및 미세조직을 분석하였다. 소결시간 증가에 따라 전기기계결합계수와 기계적품질계수는 증가하였으며, 압전상수는 Zr(Zr+Ti)비 0.390까지 증가하였으나 그 이상 증가함에 따라 감소하였다. 압전특성은 $1200^{\circ}C$에서 4시간 소결한 Zr=0.390인 조성에서 ${\varepsilon}_r$ = 4487, $k_p$ = 0.72. $d_{33}$ = 710, $Q_m$ =109의 우수한 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제31권8호
• /
• pp.934-940
• /
• 1994

Fibers of ZrO2-SiO2 system were prepared from the hydrolysis and condensation of Si(OC2H5)4 and Zr(OnC3H7)4 with different H2O/alkoxide molar ratios. It was found that fibers could be drawn in the viscosity range of 1~100 poise from HCl catalyzed solutions with lower water contents of the mole ratio H2O/alkoxide, r 2. The fibrous gels were converted into the corresponding oxide glass fibers by heating at 80$0^{\circ}C$. Mechanical test was performed on E, A and 20ZrO2-80SiO2 glass fibers reinforced cement in order to investigate the flexural strength. The flexural strength value of 20ZrO2-80SiO2 glass fibers reinforced cement was greater than those of E and A. The chemical durability of the fibers in alkaline solutions increased with ZrO2 content. The weight loss due to the corrosion by 2N-NaOH solutions at $25^{\circ}C$ for 160 hours was about 0.31$\times$10-2 mg/dm2 for the 20ZrO2-80SiO2 glass fibers, which was superior to that of Vycor glass.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1165-1172
• /
• 1997

ZrB2 powders were prepared from a mixture of ZrO2, B2O3 and Mg by self-propagating high temperature synthesis method. The combustion product was successfully obtained from a mixture of ZrO2:B2O3:Mg=1:2:8.5 molar ratio. By-product, MgO was effectively removed by leaching with 1M HCl solution at 9$0^{\circ}C$ for over 5hours. After leaching, the Mg content was 0.86~1.42 wt%, and the mean particle size was 4.72${\mu}{\textrm}{m}$. The addition of 7.5 wt%(14Ni:1.0C) as a sintering aid greatly densified ZrB2 bodies compared with that of only Ni. The ZrB2 sintered bodies containing 7.5 wt%(14Ni:1.0C) was 94.3% of the theoretical density. In this case, ZrB2 existed as a major phase and had a bend strength of 300 MPa and a vickers hardness of 2000 kg/$\textrm{mm}^2$.

• 대한금속재료학회지
• /
• 제48권6호
• /
• pp.506-513
• /
• 2010

The composite coatings of $(ZrO_2-8Y_2O_3)$/(Ni-22Cr-10Al-1Y) were prepared by the air plasma spraying method. They consisted of (Ni,Cr)-rich regions,$(ZrO_2-Y_2O_3)$-rich regions, and $Al_2O_3$-rich regions that were formed by oxidation of Al from (Ni-22Cr-10Al-1Y) during spraying. The coatings corroded at 800 and $900^{\circ}C$ in NaCl-$Na_2SO_4$ molten salts up to 50 hr. Ni, Cr and Al oxidized to NiO, $Cr_2O_3$ and ${\alpha}-Al_2O_3$, respectively. These oxides and $(ZrO_2-Y_2O_3)$ were dissolved off into the molten salts during hot corrosion, which resulted in the ever-lasting corrosion of the composite coatings. Chromium diffused out from the (Ni,Cr)-rich regions and oxidized to $Cr_2O_3$, which was most frequently found as surface scales. Aluminum retained in the (Ni,Cr)-rich regions were similarly diffused out.

• 한국재료학회지
• /
• 제8권6호
• /
• pp.505-512
• /
• 1998

플라즈마 용사법을이용하여 AISI 316 스테인레스 금속모재에 0.1mm 두께의 $NiCrAlCoY_{2}O_{3}$금속 결합층과 0.3mm 두께의 $ZrO_{2}(8wt%Y_{2}O_3$) 세라믹층으로 구성된 이층 단열코팅층을 제조하였다. 코팅층의 미세조직, 금속결합층의 산화를 고찰하였으며, $900^{\circ}C$에서 등은 시험과 열반복시험 후, 접합강도시험을 통하여 코팅층의 단사정 상은 열처리시간이 길어질수록 약간 증가하였다. 또한 비변태성 t'의 c/a는 용사상태에서 1.0099이였으며, 100시간 열처리 후에는 1.0115로 약간 증가하였다. 그리고 용사층의 접합강도는 열처리 시간이 길어질수록 감소하였다. 등온열처리 후에는 1.0115로 약간 증가하였다. 그리고 용사층 의 접합강도는 열처리 시간이 길어질수록 감소하였다. 등온열처리 후, 파괴는 주로 세라믹층에서 일어났으며, 반복 열처리되 시편에서는 10회 이후 대부분 금속결합층/세라믹층의 계면에서 일어났다.

• 한국세라믹학회지
• /
• 제29권8호
• /
• pp.630-638
• /
• 1992

Ta2O5 alloying into 3 mol% Y2O3-stabilized tetragonal ZrO2 polycrystals (3Y-TZP) increased the degradation during aging at 265℃ and the fracture toughness; both are determined by the amount of transformed m-ZrO2. It was proposed that the mechanism underlying the t→m transformation when aged at low temperatures is attributed to the reorientation of (Zzr'V ). complexes parallel to [111] lattice direction, which is accompanied by a relaxation of TZP lattice during annealing at low temperature. A small strain which results from the reorientation gives rise to a localized mechanical instability, thus lowering the nucleation barrier so that the t→m phase transformation (degradation) proceeds. The amount of transformed m-ZrO2 during aging becomes greater as the chemical free energy change related to the transformation, ΔGo, increases with increasing the Ta2O5 alloying content.

• Korean Chemical Engineering Research
• /
• 제51권1호
• /
• pp.47-52
• /
• 2013

본 연구는 $Ni/Ce_xZr_{1-x}O_2$ 촉매를 이용하여 프로판의 자열개질반응을 통한 수소제조에 관한 것이다. $Ni/Ce_xZr_{1-x}O_2$ 촉매는 용매로서 물을 사용한 방법(CZ-W), 우레아와 물을 사용한 방법(CZ-UW), 우레아, 에탄올 및 물을 사용한 방법(CZ-UWA)으로 각각 제조하였다. 반응물질의 조성은 $Steam/C_3H_8$=3, $C_3H_8/O_2$=2.70 이었고, 반응은 상압 고정층 유통식 반응기에서 $300{\sim}700^{\circ}C$ 온도범위에서 진행하였다. 촉매제조시 용매에 우레아 및 에탄올을 첨가할 경우 촉매의 활성이 증가하였다. CZ-UW 촉매의 경우 클러스터형태의 탄소생성에 기인한 활성점 피막으로 인해 쉽게 비활성화가 초래됐다. 하지만 CZ-UWA 촉매의 경우 반응 후 탄소가 활성에 영향을 미치지 않는 나노파이버형태로 존재하여 활성저하가 발생되지 않음을 SEM을 통해 확인했다. 또한 $Ni/Ce_{0.75}Zr_{0.25}O_2$ 촉매의 전환율 및 수율이 더 좋게 나타났으며 또한 소량의 Cobalt를 첨가했을 때 탄소에 대한 저항성이 크게 향상됨을 TGA로 확인하였다.

• 한국대기환경학회지
• /
• 제8권1호
• /
• pp.84-91
• /
• 1992

Hydrodesulfurization of thiophene was studied over $Ni-W/TiO_2-ZrO_2$ catalysts in a fixed bed flow reactor. The ranges of experimental conditions were at the temperatures between 200$^\circ$C and 360$^\circ$C, the pressures between 20 X $10^5$ Pa. The catalysts were reduced with the flow of 10 L/hr of $H_2$ at the temperature of 350$^\circ$C. It was found that $TiO_2-ZrO_2$ supported catalysts had similar activity to $\gamma-Al_2O_3$ supported. The largest surface areas and the highest acidity occured as the binary oxides were mixed with equal molar ratios. The HDS increased with increasing temperatures, pressures and contact times.

• 한국재료학회지
• /
• 제8권8호
• /
• pp.699-706
• /
• 1998

현재까지 박막코팅 분야에 주로 이용해 오던 플라즈마 용융분사법을 이용하여 고밀도의 두꺼운 세라믹 침적물을 제조하였다. 용융점이 2910K인 ZrO2-20wt%Y2O3분말을 이용하여 최적조건에서 이론밀도의 약 97%의 침적물을 얻었다. 고밀도 침적에 영향을 미치는 변수는 챔버 내부압력, 플라즈마동력, 플라즈마 가스조성, 분사거리, 분말입자 크기 등이었으며, 침적밀도 및 침적된 splat의 형태는 분말의 용융정도 및 챔버 내부압력에 크게 좌우되었다. 높은 밀도으 침적물을 만들기 위해서는 분말을 완전히 용융시키는 것이 중요하며, 완전히 용융된 조건에서는 챔버 내부압력이 낮고 분말분사거리가 짧은 조건 즉, 분사되는 분말이 높은 모멘텀을 가질수록 침적물의 밀도가 증가함을 알 수 있었다. 실험에서 얻어진 결과는 ANOVA 통계방법으로 분석하여 단일변수의 영향뿐만 아니라 이들 변수가 서로 조합하여 밀도에 미치는 영향도 분석하였다.

• Bulletin of the Korean Chemical Society
• /
• 제31권10호
• /
• pp.2835-2840
• /
• 2010

A series of $MoO_3/CeO_2-ZrO_2$ catalysts with different Mo content (8 - 20 wt %) were prepared by simple co-precipitation followed by impregnation method and were characterized by X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM), energy dispersive spectroscopic (EDS) techniques. The prepared materials were tested for catalytic activity by the synthesis of benzimidazole derivatives using condensation of aromatic aldehydes and o-phenylenediamine by conventional and microwave method. Obtained results reveal that the catalytic activity increases with increase in Mo wt % loading. The best catalytic activity was obtained with 20 wt % $MoO_3/CeO_2-ZrO_2$. The particle size or crystallite size was estimated using Debye-Scherrer equation. After completion of reaction, the catalyst can be recovered efficiently and reused with consistent activity.