• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.685-692
• /
• 1997

Effects of sintering temperature and time on the phase formation, the characteristics of sintering and electrical behaviors of NASICON compounds with Na3Zr2Si2PO12 and Na3.2Zr1.3Si2.2P0.8O10.5 compositions synthesized by solid state reaction were investigated. Maximum relative densities of 96% and 91% were obtained for Na3Zr2Si2PO12 and Na3.2Zr1.3Si2.2P0.8O10.5 compounds, respectively. Complex impedance analysis in a frequency range below 4 MHz was performed to measure the ionic conductivity and migration barrier height of the compounds at RT-30$0^{\circ}C$. The maximum ionic conductivity and the minimum migration barrier height were 0.45 ohm-1cm-1 and 0.07 eV, respectively. The migration barrier height of the high temperature form (space group : R3c) is about 30-40% of that of the low temperature form (space group : C2/c) in two NASICON compounds. Ionic conductivity increases with increasing sinterability, and the presence of glass phase in Na3.2Zr1.3Si2.2P0.8O10.5 compounds lowers significantly ionic conductivity at temperatures above 14$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.719-725
• /
• 1995

ZST powders were synthesized by coprecipitation of (Zr4+, Ti4+)-hydroxide in the presence of SnO2 particles. Zn(NO3)2 was used as a sintering additive, and according to the adding sequence, sintering and dielectric properties were investigated. Sintered densities of ZST prepared by adding Zn(NO3)2 before calcination were a little higher than those added after calcination, and dielectric properties of the specimen added by Zn(NO3)2 after calcination were better (sintered at 125$0^{\circ}C$/2 h ; Q$\times$f(GHz)=49, 000, $\varepsilon$r=41) than before calcination (Q$\times$f(GHz)=42, 000, $\varepsilon$r=39.5). Through the observation of TEM, it was identified that the cause was due to the difference of the degree of Zn2+ diffusion into grains. With increasing sintering time from 2 to 8 hrs, grain size was doubled and dielectric properties were somewhat deteriorated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1993.11a
• /
• pp.10-13
• /
• 1993

ln this study, x PSN - y PT - z PZ ceramics doped with w MnO$_2$were fabricated by the mixed oxide method at 1250[$^{\circ}C$] for 2[hr] and then the dielectric and pyroelectric properties were investigated. In the 0.05 PSN - 0.4 PT - 0.55 PZ specimen with 0.5[wt.%] MnO$_2$, the pyroelectric coefficient was 6.6${\times}$10$\^$-8/[C/cm$^2$$.$$^{\circ}C$], respectibly.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.894-896
• /
• 1999

The $\beta$-SiC+$ZrB_2$ ceramic composites were pressureless-sintered and annealed by adding 4, 8, 12wt% $Al_{2}O_{3}+Y_{2}O_{3}$(6 : 4wt%) powder as a liquid forming additives at $1800^{\circ}C$ for 4h. The relative density is over 79.3% of the theoretical density and phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H, 4H), $ZrB_2$, $Al_{5}Y_{2}O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 301.33MPa for composites added with 8wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed the highest of $3.6979MPa{\cdot}m^{1/2}$ for composites added with 8wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. The electrical resistivity was measured by the Pauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.311-313
• /
• 1997

The effects of porosity on the pressureless sintered $\beta$-SiC-$ZrB_2$ composites with $Al_2O_3$ additions(4, 8, 12wt.%) under argon atmosphere were investigated. Relative density of $\beta$-SiC-$ZrB_2$ composites were decreased with the $Al_2O_3$ content. The relative density and fracture toughness of $\beta$-SiC-$ZrB_2$ with 4wt% $Al_2O_3$ are 93.2%, $1.323MPa{\cdot}m^{1/2}$ respectively. The Vicker's hardness and flexural strength of $\beta$-SiC-$ZrB_2$ with 12wt.% $Al_2O_3$ are 0.492GPa, 261MPa respectively. Fracture toughness of $\beta$-SiC-$ZrB_2$ composites are directly proportional to relative density.

• Electrical & Electronic Materials
• /
• v.9 no.2
• /
• pp.132-137
• /
• 1996

Pb(Zr$_{x}$Ti$_{1-x}$ )O$_{3}$ solutions prepared by sol-gel processing with different Zr/Ti ratio were coated on Pt/SiO$_{2}$/Si substrates using spin coating method. Coated films were annealed by rapid thermal annealing at 650.deg. C for 20sec to fabricate Pb(Zr, Ti)O$_{3}$ ferroelectric thin films. Electrical properties of the films such as dielectric constant and loss, ferroelectric hysteresis, fatigue, switching time, and leakage current were measured. Hysteresis of the films with different Zr/Ti ratio yield Pr ranging 10-21.mu.C/cm$^{2}$, E$_{c}$ ranging 37.5-137.5kV/cm. Hysteresis curve was changed from square-type to slim type according to increasing Zr contents. Switching time was faster than 180ns, and leakage current was about 20.mu.A/cm$^{2}$. The film underwent above 10$^{8}$ cycles of reversed polarization showed fatigue with increased coercive field and decreased remnant polarization.tion.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.310-310
• /
• 2008

본 연구에서는 (1-x) Pb(Zr0.515Ti0.485)$O_3$ - x Pb$(Sb_{1/2}Nb_{1/2})O_3$ + 0.5wt% $MnO_2$ 조성에 Pb$(Sb_{1/2}Nb_{1/2})O_3$ (PSN) (x=0.02, 0.04, 0.06, 0.08) 변화에 따른 미세구조 및 압전, 유전특성에 관해 고찰하였다. PSN 치환량이 증가함에 따라 정방정 (tetragonal)구조에서 삼방정(rhombohedral)구조로 상전이가 일어났으며, 결정립의 크기가 작아지는 것을 확인하였다. 전기기계결합계수 (kp) 는 PSN이 4 mol % 치환됨에 따라 증가하였으며, 더 이상 치환 시 감소하였다. PSN 치환에 따른 전기적 특성은, 결정구조, 결정립의 크기 및 2 차상 등의 미세구조와 긴밀한 관계가 있는 것으로 보여진다. 상경계(Morphotropic Phase Boundary) 영역인 0.96 Pb(Zr0.515Ti0.485)$O_3$ - 0.04 Pb$(Sb_{1/2}Nb_{1/2})O_3$ + 0.5wt% $MnO_2$ 조성에서 $\varepsilon{^T}_{33}/\varepsilon_o$ = 1109, $k_p$= 70.8 (%), $d_{33}$= 325 (pC/N)의 우수한 특성을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.8
• /
• pp.676-680
• /
• 2003

In this study, to develop the low temperature sintering ceramics for piezoelectric transformer, PSN-PNN-PZT system ceramics were manufactured as a function of V$_2$O$_{5}$ addition, that is the low melting point oxide. Its dielectric and piezoelectric characteristics were investigated. With increasing the amount of V$_2$O$_{5}$ addition, electromechanical coupling factor(kp) and mechanical quality factor(Qm) were decreased. For piezoelectric transformer application, the 0.1wt% V$_2$O$_{5}$ added specimen sintered at 1,00$0^{\circ}C$ showed the proper value of $\varepsilon$r=1,590, kp=0.51 and Qm=748.m=748.

• Particle and aerosol research
• /
• v.4 no.1
• /
• pp.21-25
• /
• 2008

$Pb(Zr_{0.53}Ti_{0.47})O_3$ (PZT) was synthesized by a multiple wet dry process. Precipitates prepared from reaction between $ZrOCl_2{\cdot}8H_2O$ and $TiOCl_2$ and $NH_4OH$ in an aqueous solution was dried at $100^{\circ}C$, and calcined at $500^{\circ}C$ and $700^{\circ}C$. The mixture mixed with PbO and as-dried or calcined $Zr_{0.53}Ti_{0.47}O_4$ (ZT) powders was calcined again at 700 and $800^{\circ}C$. Well crystallized ZT and PZT were formed at even $700^{\circ}C$. PZT piezoelectric ceramics of more than 98.5% in a relative density was obtained by sintering at as low as $900^{\circ}C$.

• The Journal of the Petrological Society of Korea
• /
• v.27 no.1
• /
• pp.37-47
• /
• 2018

Volcanic ash samples of historical eruptions from Mt. Baekdu were analyzed for major oxides, trace and rare earth elements by a variety of analytical techniques. The results indicate that the ashes consist of approximately 58.8~71.1 wt.% $SiO_2$, 9.6~16.8 wt.% $Al_2O_3$, 4.5~6.9 wt.% $Fe_2O_{3t}$, 0.1~1.7 wt.% MgO, 0.3~1.6 wt.% CaO, 5.2~6.3 wt.% $Na_2O$, 4.3~5.9 wt.% $K_2O$ and less than 1.2 wt.% $TiO_2$. Thirty two trace metals including Ba, Cu, Cr. Co, Ni, Sr, V, Zn, and Zr were analyzed. The ashes can be divided two groups: group A(1 ka Millennium pumice, 1668 and $190{\underline{3}}$ pumice) and group B(1702 pumice) according to the relative enrichment of HREEs. The abundances of heavy metals such as Cu, Co, Mn, and Zn were relatively low. As compared to the Sakurajima volcanic ash, Baekdusan volcanic ash has low concentrations of Y, Nb, Pb, U, Sc, V, Ni and Cu and high concentrations of Zr, Ba, Hf, Cr, Co, Zn and rare-earth (except Eu).