• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.228-229
• /
• 2006

본 연구에서는 초음파 모터 등의 고출력 액츄에이터에 응용 가능한 $04Pb(Ni_{1/3}Nb_{2/3})O_3-6Pb(Zr_xTi_{1-x})O_3$ 조성시스템에 소결온도를 달리하여 압전, 유전특성 및 미세구조에 관해 고찰하였다. 본 조성을 $1200^{\circ}C$ 온도에서 2, 4, 6, 8시간 소결하여 시편을 제조하였으며 이의 결정구조 및 미세조직을 분석하였다. 소결시간 증가에 따라 전기기계결합계수와 기계적품질계수는 증가하였으며, 압전상수는 Zr(Zr+Ti)비 0.390까지 증가하였으나 그 이상 증가함에 따라 감소하였다. 압전특성은 $1200^{\circ}C$에서 4시간 소결한 Zr=0.390인 조성에서 ${\varepsilon}_r$ = 4487, $k_p$ = 0.72. $d_{33}$ = 710, $Q_m$ =109의 우수한 특성을 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.934-940
• /
• 1994

Fibers of ZrO2-SiO2 system were prepared from the hydrolysis and condensation of Si(OC2H5)4 and Zr(OnC3H7)4 with different H2O/alkoxide molar ratios. It was found that fibers could be drawn in the viscosity range of 1~100 poise from HCl catalyzed solutions with lower water contents of the mole ratio H2O/alkoxide, r 2. The fibrous gels were converted into the corresponding oxide glass fibers by heating at 80$0^{\circ}C$. Mechanical test was performed on E, A and 20ZrO2-80SiO2 glass fibers reinforced cement in order to investigate the flexural strength. The flexural strength value of 20ZrO2-80SiO2 glass fibers reinforced cement was greater than those of E and A. The chemical durability of the fibers in alkaline solutions increased with ZrO2 content. The weight loss due to the corrosion by 2N-NaOH solutions at $25^{\circ}C$ for 160 hours was about 0.31$\times$10-2 mg/dm2 for the 20ZrO2-80SiO2 glass fibers, which was superior to that of Vycor glass.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1165-1172
• /
• 1997

ZrB2 powders were prepared from a mixture of ZrO2, B2O3 and Mg by self-propagating high temperature synthesis method. The combustion product was successfully obtained from a mixture of ZrO2:B2O3:Mg=1:2:8.5 molar ratio. By-product, MgO was effectively removed by leaching with 1M HCl solution at 9$0^{\circ}C$ for over 5hours. After leaching, the Mg content was 0.86~1.42 wt%, and the mean particle size was 4.72${\mu}{\textrm}{m}$. The addition of 7.5 wt%(14Ni:1.0C) as a sintering aid greatly densified ZrB2 bodies compared with that of only Ni. The ZrB2 sintered bodies containing 7.5 wt%(14Ni:1.0C) was 94.3% of the theoretical density. In this case, ZrB2 existed as a major phase and had a bend strength of 300 MPa and a vickers hardness of 2000 kg/$\textrm{mm}^2$.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.506-513
• /
• 2010

The composite coatings of $(ZrO_2-8Y_2O_3)$/(Ni-22Cr-10Al-1Y) were prepared by the air plasma spraying method. They consisted of (Ni,Cr)-rich regions,$(ZrO_2-Y_2O_3)$-rich regions, and $Al_2O_3$-rich regions that were formed by oxidation of Al from (Ni-22Cr-10Al-1Y) during spraying. The coatings corroded at 800 and $900^{\circ}C$ in NaCl-$Na_2SO_4$ molten salts up to 50 hr. Ni, Cr and Al oxidized to NiO, $Cr_2O_3$ and ${\alpha}-Al_2O_3$, respectively. These oxides and $(ZrO_2-Y_2O_3)$ were dissolved off into the molten salts during hot corrosion, which resulted in the ever-lasting corrosion of the composite coatings. Chromium diffused out from the (Ni,Cr)-rich regions and oxidized to $Cr_2O_3$, which was most frequently found as surface scales. Aluminum retained in the (Ni,Cr)-rich regions were similarly diffused out.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.505-512
• /
• 1998

In this study, two-layer thermal barrier coatings composed of plasma sprayed 0.3mm $ZrO_2(8wt% Y_2o_3)$ ceramic coating layer and O.lmm $NiCrAlCoY_20_3$ bond coating layer on AISI 316 were investigated microstructure of the coating, oxidation of the metallic bond coating and adhesive strength to evaluate the durability of coating layer after cyclic and isothermal test at 90$0^{\circ}C$. And quantitative phase analysis of $ZrO_2(8wt% Y_2o_3)$ ceramic coating was performed as a function of thermal exposure time using XRD technique. The results showed that the amount of m - 2rO, phase in the coating was slightly increased with increasing thermal exposure time at 90$0^{\circ}C$. The c/a ratio of t' - $ZrO_2$ in the as-sprayed coating was 1.0099 and slightly increased to 1.0115 after 100 hours heat treatment. It was believed that $Y_2O_3$ in high yttria tetragonaJ(t') was transformed to low yttria tetragonaJ(t) by $Y_2O_3$ diffusion with increasing thermal exposure time. The adhesive strength was gradually decreased as thermal exposure time increased. After the isothermal test, the failure predominantly occured in ceramic coating layer. On the other hand. the specimens after cyclic thermal test were mostly failed at bond coating/ceramic coating interface. The failure was oeeured by decreasing the bond strength between bond coating and oxide scale which were formed by oxidation of the metallic elements within bond coating and by thermal stress due to thermal expansion mismatches between the oxide scale and ceramic coating.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.630-638
• /
• 1992

Ta2O5 alloying into 3 mol% Y2O3-stabilized tetragonal ZrO2 polycrystals (3Y-TZP) increased the degradation during aging at 265℃ and the fracture toughness; both are determined by the amount of transformed m-ZrO2. It was proposed that the mechanism underlying the t→m transformation when aged at low temperatures is attributed to the reorientation of (Zzr'V ). complexes parallel to [111] lattice direction, which is accompanied by a relaxation of TZP lattice during annealing at low temperature. A small strain which results from the reorientation gives rise to a localized mechanical instability, thus lowering the nucleation barrier so that the t→m phase transformation (degradation) proceeds. The amount of transformed m-ZrO2 during aging becomes greater as the chemical free energy change related to the transformation, ΔGo, increases with increasing the Ta2O5 alloying content.

• Korean Chemical Engineering Research
• /
• v.51 no.1
• /
• pp.47-52
• /
• 2013

In this study, the catalytic performance and characterization of $Ni/Ce_xZr_{1-x}O_2$ were investigated using an autothermal reforming (ATR) process for hydrogen production. The $Ni/Ce_xZr_{1-x}O_2$ catalysts were prepared using the following methods: the water method (CZ-W), urea water method (CZ-UW) and urea, water and ethanol method (CZ-UWA). The performance of $Ni/Ce_xZr_{1-x}O_2$ catalysts in autothermal reforming of propane for hydrogen production was studied in a fixed-bed flow reactor. Reaction tests were conducted by using a feed of $H_2O/C_3H_8/O_2$=3/1/0.37 and $300{\sim}700^{\circ}C$. The CZ-UW and CZ-UWA catalysts showed higher propane conversion and hydrogen yield than the CZ-W catalyst. The activity test confirmed that the improvement in the water-ethanol catalyst was due to the low level of carbon deposition. SEM showed that the surface carbon consisted of clusters on the used CZ-UW catalyst, which is incontrast to the nano-fiber morphology observed on the used CZ-UWA catalyst. It was found that the amount of carbon deposition depends on the preparation method. Especially the $Ni/Ce_{0.75}Zr_{0.25}O_2$ was showed higher propane conversion and hydrogen yield than the other catalysts. Also TGA showed that the resistance of carbon deposition increase to Co addition.

• Journal of Korean Society for Atmospheric Environment
• /
• v.8 no.1
• /
• pp.84-91
• /
• 1992

Hydrodesulfurization of thiophene was studied over $Ni-W/TiO_2-ZrO_2$ catalysts in a fixed bed flow reactor. The ranges of experimental conditions were at the temperatures between 200$^\circ$C and 360$^\circ$C, the pressures between 20 X $10^5$ Pa. The catalysts were reduced with the flow of 10 L/hr of $H_2$ at the temperature of 350$^\circ$C. It was found that $TiO_2-ZrO_2$ supported catalysts had similar activity to $\gamma-Al_2O_3$ supported. The largest surface areas and the highest acidity occured as the binary oxides were mixed with equal molar ratios. The HDS increased with increasing temperatures, pressures and contact times.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.699-706
• /
• 1998

현재까지 박막코팅 분야에 주로 이용해 오던 플라즈마 용융분사법을 이용하여 고밀도의 두꺼운 세라믹 침적물을 제조하였다. 용융점이 2910K인 ZrO2-20wt%Y2O3분말을 이용하여 최적조건에서 이론밀도의 약 97%의 침적물을 얻었다. 고밀도 침적에 영향을 미치는 변수는 챔버 내부압력, 플라즈마동력, 플라즈마 가스조성, 분사거리, 분말입자 크기 등이었으며, 침적밀도 및 침적된 splat의 형태는 분말의 용융정도 및 챔버 내부압력에 크게 좌우되었다. 높은 밀도으 침적물을 만들기 위해서는 분말을 완전히 용융시키는 것이 중요하며, 완전히 용융된 조건에서는 챔버 내부압력이 낮고 분말분사거리가 짧은 조건 즉, 분사되는 분말이 높은 모멘텀을 가질수록 침적물의 밀도가 증가함을 알 수 있었다. 실험에서 얻어진 결과는 ANOVA 통계방법으로 분석하여 단일변수의 영향뿐만 아니라 이들 변수가 서로 조합하여 밀도에 미치는 영향도 분석하였다.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.10
• /
• pp.2835-2840
• /
• 2010

A series of $MoO_3/CeO_2-ZrO_2$ catalysts with different Mo content (8 - 20 wt %) were prepared by simple co-precipitation followed by impregnation method and were characterized by X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM), energy dispersive spectroscopic (EDS) techniques. The prepared materials were tested for catalytic activity by the synthesis of benzimidazole derivatives using condensation of aromatic aldehydes and o-phenylenediamine by conventional and microwave method. Obtained results reveal that the catalytic activity increases with increase in Mo wt % loading. The best catalytic activity was obtained with 20 wt % $MoO_3/CeO_2-ZrO_2$. The particle size or crystallite size was estimated using Debye-Scherrer equation. After completion of reaction, the catalyst can be recovered efficiently and reused with consistent activity.