• 한국표면공학회지
• /
• 제26권2호
• /
• pp.87-107
• /
• 1993

The grain size of the final products of WC-Co and WC-Ni composite powders is dependent on the size of the starting material and the conditions employed for the reduction and carburization. APT-Co and -Ni com-plex salts were prepared by the substitution reaction between ammonium ions in APT and the metal ions in Co(NO3)2 and Ni(NO3)2 solutions of different concentrations(0.1 to 0.7M) at $50^{\circ}C$ and the grain sizes of the com-plex salts was $0.54~0.76\mu\textrm{m}$. The complex which calcined the complex salts at $700^{\circ}$~80$0^{\circ}C$ for 60min. were 0.2~0.5$\mu\textrm{m}$. W-Co($5.92^{\circ}C$) and -Ni(6.95%) powders which reduced the complex oxides with H2d atmo-sphere(flow rate;600cc/min.) at $700^{\circ}$~$800^{\circ}C$ for 60min. were $0.5~0.6\mu\textrm{m}$. The mean grain sizes of WC-Co and WC-Ni composite powders which carburized both complex metals of W-Co and W-Ni at $800^{\circ}C$ for 60min. were $0.5~0.6\mu\textrm{m}$, and take place the coarsening of the grain above $800^{\circ}C$ and the optmium ratio of C3H8 and H2 was 0.2 for the control of the free carbon. The effect of Co contents on the particle sizes decreased from 0.4 to $0.25\mu\textrm{m}$ with increasing the content from 2.0 to 7.6w%. The activation energies on the reductions of oxides and the formations of carbides were as follows ; W-Co : Q = 8.7 kcal/mole, W-Ni : Q = 8.1 kcal/mole, WC-Co pow-der : Q = 17.8 kcal/mole, WC-Ni powder : Q = 16.6 kcal/mole.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.208-215
• /
• 2015

Fe-TiC composite powders were fabricated by planetary ball mill processing. Two kinds of powder mixtures were prepared from the starting materials of (a) (Fe, TiC) powders and (b) (Fe, $TiH_2$, Carbon) powders, respectively. Milling speed (300, 500 and 700 rpm) and time (1, 2, and 3 h) were varied. For (Fe, $TiH_2$, Carbon) powders, an in situ reaction synthesis of TiC after the planetary ball mill processing was added to obtain a homogeneous distribution of ultrafine TiC particulates in Fe matrix. Powder characteristics such as particle size, size distribution, shape, and mixing homogeneity were investigated.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.418-424
• /
• 1996

(Ti.W)C complex carbide was synthesized by self-propagating high temperature synthesis (SHS) chemical furnace. Attempt to find the optimal condition for synthesis of (Ti.W)C the effects of molar ratio of Ti:W:C on the synthesized powders and mechanical properties were investigated, Optimum molar ratio of these synthe-sized powder was Ti:W:C=0.7:0.2:1.0 The bulk density M,O.R Hardness Fracture toughness of (Ti.W)C complex carbide sintered at 200$0^{\circ}C$ for 60 min by hot-pressing under the pressure of 20 MPa were 7.6g/cm3, 475 MPa, 17,.7 GPa respectively.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.387-390
• /
• 2009

This study was designed to fabricate the micro-electro-mechanical systems (MEMS) parts such as micro spur gears using hot extrusion of gas atomized Al-78Zn powders. For this purpose, it is important to develop new methods to fabricate micro-dies and choose suitable extrusion conditions for a micro-forming. Micro-dies with Ni were fabricated by LIGA technology. LIGA technology was capable to produce micro-extrusion dies with close tolerances, thick bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro formability with average strain rates ranging from $10^{-3}$ to $10^{-2}\;s^{-1}$ and constant temperatures ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape (${\Phi}3{\times}h10$) under compressive force of 10kN and, subsequently, the compacted powders were extruded at 563k in a hot furnace. Micro-extrusion has succeeded in forming micro-gear shafts.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1998년도 추계학술대회 및 발표대회 강연 및 발표논문 초록집
• /
• pp.48-48
• /
• 1998

• 한국세라믹학회지
• /
• 제36권11호
• /
• pp.1252-1260
• /
• 1999

The defect chemistry and electrical characteristics of the grain boundaries of semiconducting SrTiO3 ceramics synthesized with wet-chemically surface-coated powders were investigated. The starting powders were separated into groups of 1-10${\mu}{\textrm}{m}$ 10-20${\mu}{\textrm}{m}$ etc by sedimentation and sieving methods. Na+ ions were absorbed on the powder surfaces by wet chemical-treatment method. The width of the grain boundary ranged up to several nm and the intergranular materials was amorphous. The additives coated on the surface of the powders were observed to be present at the grain boundaries of the ceramics. The diffusion depth of the additives into grains was about 30nm for the SrTiO3 ceramics synthesized with 5w/o coated materials, The threshold voltage grain boundary resistance and boundary potential barrier of the ceramics increased from 0.67V/cm 2.27k$\Omega$ and 0.05eV to 80.9V/cm 13.0k$\Omega$ 1.44eV with increasing the amount of the additives from 0 to 5 w/o respectively .

• Progress in Superconductivity
• /
• 제3권1호
• /
• pp.91-94
• /
• 2001

By varying fabricating process, precursor powders with different initial conditions were prepared. Subsequently, Bi-2223/Ag tapes were made through these powders. The effects of precursor powders on the phase evolution and Jr properties of Bi-2223/Ag tapes were studied along with several thermomechanical cycles. Our results showed that the initial conditions of precursor powders could strongly influence the phase formation rate and $J_{c}$ value in final tapes. The factors of precursor powders that influence the phase formation and $J_{c}$ of Bi-2223/Ag tapes must be studied and optimized in combination.ion.

• 마이크로전자및패키징학회지
• /
• 제17권2호
• /
• pp.49-54
• /
• 2010

n형 $Bi_2(Te,Se)_3$ 분말을 용해/분쇄법으로 제조하여 가압소결 후, 가압소결체의 열전특성을 $Bi_2(Te,Se)_3$ 잉곳과 비교하였으며, $Bi_2(Te,Se)_3$ 열전분말의 기계적 밀링처리가 가압소결체의 열전특성에 미치는 영향을 분석하였다. $Bi_2(Te,Se)_3$ 잉곳은 $24.2{\times}10^{-4}W/m-K^2$의 power factor를 나타내었으며, 이를 가압소결함으로써 power factor가 $27.3{\sim}32.3{\times}10^{-4}W/m-K^2$로 향상되었다. 기계적 밀링처리한 분말로 제조한 $Bi_2(Te,Se)_3$ 가압소결체는 $100^{\circ}C$에서 1.02의 무차원 성능지수를 나타내었으며, $130^{\circ}C$에서 외인성-내인성 천이거동을 나타내었다.

• 한국분말재료학회지
• /
• 제12권4호
• /
• pp.266-272
• /
• 2005

Transition metal ions($Ni^{2+}$, $Cr^{3+}$ and $V^{5+}$) doped $TiO_2$ nanostructured powders were synthesized by mechanical alloying(MA) to shift the adsorption threshold into the visible light region. The synthesized powders were characterized by XRD, SEM, TEM and BET for structural analysis, UV-Vis and photoluminescence spectrum for the optical study. Also, photocatalytic abilities were evaluated by decomposition of 4-chlorophenol(4CP) under ultraviolet and visible light irradiations. Optical studies showed that the absorption wavelength of transition metal ions doped $TiO_2$ powders moved to visible light range, which was believed to be induced by the energy level change due to the doping. Among the prepared $TiO_2$ powders, $NiO^{2+}$ doped $TiO_2$ powders, showed excellent photooxidative ability in 4CP decomposition.

• 한국분말재료학회지
• /
• 제5권3호
• /
• pp.178-183
• /
• 1998

Ultrafine WC-10wt.%Co cemented carbides powders were synthesized by direct carburization. W-Co composite powders and carbon black powders were mixed by wet ball milling and dried. The mixed powders were heated to 800 $^{\circ}C$ with heating rate of 8.2$^{\circ}C$/min and held for various times in flowing $H_2$. For carbon addition of 140%, the carburization was completed by heating at 80$0^{\circ}C$ for 4 hours. The carburization time decreased with increasing amount of carbon and carburization was completed by heating at 800 $^{\circ}C$ for 2 hours with carbon addition of 150%. WC-10 wt%Co cemented carbides powders fabricated by direct carburization have nanoscale WC($\/leqq$100 nm) size.