• Journal of Sensor Science and Technology
• /
• v.5 no.5
• /
• pp.47-54
• /
• 1996

Highly sensitive $WO_{3}$ doped with $SnO_{2}$ and Pt thick-film sensors for NOx gas were fabricated. The sensors had a maximum sensitivity at operating temperature of $250^{\circ}C$, but the optimum operation temperature, considering recovery desorption time, was at $330^{\circ}C$. These sensors improved sensitivity, response and recovery time, selectivity and stability, as compared to $WO_{3}$ sensors. The good linearity of sensitivity as a function of the gas concentration exhibited the possibility to be used for concentration meter.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.1
• /
• pp.32-36
• /
• 2005

[ $WO_3$ ] and $NiO-WO_3$ thin films were deposited on a Si (100) substrate by using high vacuum thermal evaporation. The effects of various film thicknesses on the surface morphology $WO_3$ and $NiO-WO_3$ thin films were investigated. X-ray diffraction (XRD), Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy(XPS) were employed to characterize the deposited films. The results suggest that as $WO_3$ thin films became thick, their grain grew up to a $0.6{\mu}m$. On the other hand, NiO-doping to $WO_3$ thin films inhibited the grain growth five times less than undoped $WO_3$ thin films. This results show that NiO doping inhibited the grain growing of $WO_3$ thin films. Also, the variation of NOx sensitivity $(R_{NOx}/R_{air})$ to the thickness of $WO_3$ and $NiO-WO_3$ thin films were measured according to the thickness change of thin films and the working temperature of sensor in 5ppm NOx gas. As a result, $NiO-WO_3$ thin films showed more excellent properties than $WO_3$ thin films for NOx sensitivity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.99-102
• /
• 1997

An electronic nose system is an instrument designed far mimicking human olfactory system. It consists generally of gas (odor) sensor array corresponding to olfactory receptors of human nose and artificial neural network pattern recognition technique based on human biological odor sensing mechanism. Considerable attempts to develop the electronic nose system have been made far applications in the fields of floods, drinks, cosmetics, environment monitoring, etc. A portable electronic nose system has been fabricated by using oxide semiconductor gas sensor array and pattern recognition technique such as principal component analysis (PCA) and back propagation artificial neural network The sensor array consists of six thick film gas sensors whose sensing layers are Pd-doped WO$_3$ Pt-doped SnO$_2$ TiO$_2$-Sb$_2$O$_3$-Pd-doped SnO$_2$ TiO$_2$-Sb$_2$O$_{5}$-Pd-doped SnO$_2$+Pd filter layer, A1$_2$O$_3$-doped ZnO and PdCl$_2$-doped SnO$_2$. As an application the system has been used to identify CO/HC car exhausting gases and the identification has been successfully demonstrated.d.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.33.1-33.1
• /
• 2009

To date, nanostructured tungsten oxides with a variety of stoichiometries, such as WO3, WO2.9, W18O49, and WO2, have been prepared, because they are promising candidates for applications such as gas sensors, photocatalysts, electrochromic devices, and field emission devices. Among them, W18O49 and WO2 have been widely studied due to their outstanding chemical sensing, catalytic, and electron emissive properties. Here we report, for the first time, a one-pot solution-phase route to synthesizing a novel composite hierarchical hollow structure without adding catalysts, surfactants, or templates. The products, consisting of a WO2 hollow core sphere surrounded by a W18O49 nanorod shell (yielding a sea urchin-like structure), were generated as discrete structures via Ostwald ripening. To our knowledge, this type of composite hierarchical core/shell structure has not been reported previously. The morphological evolution and the detailed growth mechanism were carefully studied. We also demonstrate that the size of the hollow urchins is readily tunable by controlling the reactant concentrations.Interestingly, although bulk tungsten oxides are weakly paramagnetic or diamagnetic, the as-prepared products show unusual ferromagnetic behavior atroom temperature. The urchin structures also show a very high Brunauer-Emmet-Teller (BET) surface area, suggesting that they may potentially be applied to chemical sensor or effective catalyst technologies.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.1
• /
• pp.12-16
• /
• 2005

Chemical mechanical polishing (CMP) process is one of the most useful methods for improving the surface roughness of films. The effects of CMP on the surface morphology of WO$_3$ films prepared by RF sputtering system were investigated in this paper. A removal rate of films increased, and the uniformity performance of surface decreased with the addition of an oxidizer to the tungsten slurry. Non-uniformity performance of surface was superior as its value was below 5 % when oxidizers of 5.0 vol% and 2.5 vol%, respectively, were added to the tungsten slurry. The optimized oxidizer concentration, reflected both the improved roughness values and hillock-free surface with the good uniformity performance, was 5.0 vol% as an atomic force microscopy(AFM) analysis of thin film topographies. Our CMP results will be a useful reference for advanced technology of thin films for gas sensor applications in the near future.

• Korean Journal of Materials Research
• /
• v.12 no.12
• /
• pp.930-934
• /
• 2002

Nanosized $WO_3$ powders were synthesized by the sol-precipitation process using $WCl_{6}$ as the starting material, ethanol as a solvent and $NH_4$OH solution as a precipitant, followed by a washing-drying treatment and calcination. The effects on the powder crystallinity and microstructure of calcination temperature were investigated with XRD and FE-SEM. The $WO_3$ powders calcined at $500^{\circ}C$ and $700^{\circ}C$ showed good crystallinity and their mean particle size was 30nm and 70nm, respectively. These powders were used for the preparation of pastes which were printed as thick films on alumina substrates with comb-type Pt electrodes. The particle size strongly influenced the $NO_2$ gas sensing property of the thick films. A significant reduction in the $NO_2$ sensitivity was observed for the film prepared from larger particle size, having thus a larger grain size. For the film having a smaller grain size, on the other hand, the higher $NO_2$ sensitivity was observed and the sensitivity increased with $NO_2$ concentration.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.2 s.17
• /
• pp.81-87
• /
• 2004

Semiconductor thick film gas sensors based on tin oxide are fabricated and their gas response characteristics are examined for four simulant gases of chemical warfare agent (CWA)s. The sensing materials are prepared in three different sets. 1) The Pt or Pd $(1,\;2,\;3\;wt.\%)$ as catalyst is impregnated in the base material of $SnO_2$ by impregnation method.2) $Al_2O_3\;(0,\;4,\;12,\;20\;wt.\%),\;In_2O_3\;(1,\;2,\;3\;wt.\%),\;WO_3\;(1,\;2,\;3\;wt.\%),\;TiO_2\;(3,\;5,\;10\;wt.\%)$ or $SiO_2\;(3,\;5,\;10\;wt.\%)$ is added to $SnO_2$ by physical ball milling process. 3) ZnO $(1,\;2,\;3,\;4,\;5\;wt.\%)$ or $ZrO_2\;(1,\;3,\;5\;wt.\%)$ is added to $SnO_2$ by co-precipitation method. Surface morphology, particle size, and specific surface area of fabricated sensing films are performed by the SEM, XRD and BET respectively. Response characteristics are examined for simulant gases with temperature in the range 200 to $400^{\circ}C$, with different gas concentrations. These sensors have high sensitivities more than $50\%$ at 500ppb concentration for test gases and also have shown good repetition tests. Four sensing materials are selected with good sensitivity and stability and are fabricated as a sensor array A sensor array Identities among the four simulant gases through the principal component analysis (PCA). High sensitivity is acquired by using the semiconductor thick film gas sensors and four CWA gases are classified by using a sensor array through PCA.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.25.2-25.2
• /
• 2011

The tungsten oxide wire-like nanostructure is fabricated by deposition and thermal oxidation of tungsten metal on porous single wall carbon nanotubes (SWNTs). The morphology and crystalline quality of materials are investigated by SEM, TEM, XRD and Raman analysis. The results prove that $WO_3$ wire-like nanostructure fabricated on SWNTs show highly porous structures. Exposure of the sensors to NH3 gas in the temperature range of 150~300$^{\circ}C$ resulted in the highest sensitivity at $250^{\circ}C$ with quite rapid response and recovery time. Response time as a function of test concentrations and NH3 gas sensing mechanism is reported and discussed.

• Journal of Sensor Science and Technology
• /
• v.18 no.1
• /
• pp.54-62
• /
• 2009

${Co_3}{O_4}$ and ${Co_3}{O_4}$-based thick films with additives such as ${Co_3}{O_4}-{Fe_2}{O_3}$(5 wt.%), ${Co_3}{O_4}-{SnO_2}$ (5 wt.%), ${Co_3}{O_4}-{WO_3}$(5 wt.%) and ${Co_3}{O_4}$-ZnO(5 wt.%) were fabricated by screen printing method on alumina substrates. Their structural properties were examined by XRD and SEM. The sensitivities to iso-${C_4}H_{10}$, $CH_4$, CO, $NH_3$ and NO gases were investigated with the thick films heat treated at $400^{\circ}C$, $500^{\circ}C$ and $600^{\circ}C$. From the gas sensing properties of the films, the films showed p-type semiconductor behaviors. ${Co_3}{O_4}-{SnO_2}$(5 wt.%) thick film heat treated at $600^{\circ}C$ showed higher sensitivity to i-${C_4}H_{10}$ and CO gases than other thick-films. ${Co_3}{O_4}-{SnO_2}$(5 wt.%) thick film heat treated at $600^{\circ}C$ showed the sensitivity of 170 % to 3000 ppm iso-${C_4}H_{10}$ gas and 100 % to 100 ppm CO gas at the working temperature of $250^{\circ}C$. The response time to i-${C_4}H_{10}$ and CO gases showed rise time of about 10 seconds and fall time of about $3{\sim}4$ minutes. The selectivity to i-${C_4}H_{10}$ and CO gases was enhanced in the ${Co_3}{O_4}-{SnO_2}$(5 wt.%) thick film.

• Journal of Hydrogen and New Energy
• /
• v.16 no.1
• /
• pp.9-16
• /
• 2005

We studied the electrochromic properties of hydrated amorphous ruthenium oxide ($RuO_2{\cdot}xH_2O$) thin films using in-situ Raman spectroscopy during electrochemical charging/discharging cycles. We have found that the principal effect of hydrogen insertion into $RuO_2{\cdot}xH_2O$ is reduction of $Ru^{4+}\;to\;Ru^{3+}$, and not formation of new bonds involving hydrogen. We compared the changes in the Raman spectrum of a gasochromic $Pd/RuO_2{\cdot}xH_2O$ film as it is exposed to hydrogen gas with that of electrochemical hydrogen insertion. We tested the changes in the optical transmission of the $Pd/RuO_2{\cdot}xH_2O$ film when exposed to hydrogen gas.