• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.393-396
• /
• 2004

본 논문에서는 완충층용 MgO 박막을 P-type(100)Si 기판위에 작업가스 $Ar:O_2=80:20$, RF 파워 50W, 기판온도 $400^{\circ}C$, 10mtorr의 작업진공에서 $500{\AA}$ 증착하였다. 제작된 MgO/Si 기판위에 RF Magnetron sputtering법으로 작업가스 $Ar:O_2$의 비율을 90:10, 80:20, 70:30으로 변화하면서 $BST(Ba_{0.5}Sr_{0.5}TiO_3)$ 박막을 약 $2000{\AA}$ 증착하였다. XRD 측정결과 작업가스비의 변화에 관계없이(110)BST와 (111)BST 피크만이 관찰되었으며 작업가스 $Ar:O_2=80:20$에서 가장 양호한 결정성을 나타내었다. I-V 측정결과 인가전계 ${\pm}100kV/cm$에서 $10^{-7}A/cm^2$이하의 양호한 누설전류 특성을 보여주고 있으며 C-V 측정결과 작업가스 $Ar:O_2$의 비율 90:10, 80:20, 70:30에서의 비유전율은 각각 283, 305, 296으로서 작업가스비 80:20에서 제작된 박막의 특성이 가장 우수하였다. 작업가스비 80:20에서 제작된 박막의 SEM 측정결과 결정이 성장되었음을 확인할 수 있었고 그레인의 크기는 약 10nm였다.

• Proceedings of the Korean Society for Emotion and Sensibility Conference
• /
• 2001.05a
• /
• pp.147-155
• /
• 2001

Nasucon lamp and Russian ones, which are coated with some special materials on the glass bulb, gave good clinical results for a cancer therapy. They are experimentally studied with Automatic Bioelectric Response Recorder on the six placements of the electrodes (two feet, two hands and two foreheads). They reduced the current rather than the control (natural) state. However infrared lamp and Chinese God light did not reduced the value current. Hemoglobin in blood. Brown gas, Ti$_3$SiC$_2$ and Nasucon have planar crystallizing $\pi$-bonding bonding layer and covalent bonding one in sequence commonly and thus the alternating magnetic fields are protected. Nasucon lamp and Russian ones utilized electric bulbs in order to generate alternating magnetic fields and to produce absorbing force.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.124-124
• /
• 2015

Acoustic microscopy and scanning electron microscopy were applied to non-destructively evaluate the hydrogen-induced cracking of API X-80 steels and to find the initiation time of the crack. The API X-80 steel had the average grain size of about $4-10{\mu}m$. The hardness was reduced from 240 to 202 [Hv] after exposing in HIC environment for 2-days. Friction coefficient and wear loss were 0.745 and 0.392 mm, respectively. Empirical equation of corrosion potential and corrosion rate of the steel with HIC time in $5%NaCl-0.5%CH_3COOH$ at $25^{\circ}C$ were $Eh\;(up)=0.06^*t[day]+0.2951$, $Eh(down)=0.376^*t[day]+0.5938$, respectively. HIC grew with micro-size after 1-day exposure. The HIC tended to propagate on the surface with Al, Si, Ti, and Mn.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.5
• /
• pp.440-446
• /
• 2008

To manufacture the MLCC with X7R for high voltage stability, $BaTiO_3-MgO-MnO_2-Y_2O_3$ with $(Ba_{0.4}Ca_{0.6})SiO_3$ glass frit was formulated. Based on this composition, the addition of $Er_2O_3$ showed that TCC(Temperature Coefficient Capacitance) at $85^{\circ}C$ was improved from 5 % to ${\sim}0\;%$, but the dielectric constant and IR (Insulation Resistance) were decreased. The glass frit improved the dielectric constant and IR, so the appropriate contents of $Er_2O_3$ and glass frit were 0.6 mol% and 1 wt%, respectively. It showed that the dielectric constant and RC constant were 2,550 and 2,000 (${\Omega}F$), respectively in the sintering condition at $1250^{\circ}C$ in PO2 $10^{-7}$ Mpa. The MLCC with $3.2{\times}1.6$ (mm) size and $1\;{\mu}F$ was also suited for X7R with the above composition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.325-325
• /
• 2008

스크린 프린팅에 의한 압전 후막은 MEMS 공정을 이용하여 마이크로 펌프, 마이크로 벨브, 마이크로 센서, 마이크로 로봇 등 여러 초소형 기계부품에 응용되고 있으며, Sol-Gel, PLD를 이용해 증착된 막 등에 비해 수십${\mu}m$의 비교적 두꺼운 막을 형성시킬 수 있는 장점을 가지고 있다. 그러나 실리콘 기판을 사용하여 스크린 프린팅으로 형성된 압전 후막의 경우, 공정상 바인더를 연소시키는 과정을 거치게 되므로, 밀집된(Dense) 구조를 가지는 막을 만들기가 어렵다. 이로 인해 스크린 프린팅에 의한 후막은 전기적 특성 및 기계적 특성이 떨어지는 경향이 있다. 본 연구에서는 스크린 프린팅에 의한 압전 후막의 밀집된 구조 및 특성을 향상시키기 위해 0.01Pb$(Mg_{1/2}W_{1/2})$O3-0.41Pb$(Ni_{1/3}Nb_{2/3})O_3-0.35PbTiO_3-0.23PbZrO_3$의 powder와 Attrition 밀링 처리된 powder를 비율별로 혼합하여 입자의 크기를 변화시켜 막의 충진 밀도를 향상시켰으며, 열처리 효과를 극대화시키기 위해 RTA(Rapidly Thermal Annealing)를 통해 열처리 하였다. Attrition 밀링에 의한 파우더를 각각 비율별로 100%, 50%, 25%로 혼합하여 만든 압전 세라믹 페이스트는 P-type(100)Si Wafer sample 위에 $1{\mu}m$의 하부전극용($1100^{\circ}C$) Ag 전극을 screen print하여 소결했다. 그리고 다시 전극이 형성된 Si wafer 위에 스크린 프린팅하고, 건조 한 후 RTA로 300초 동안 열처리 한 결과 밀집된 구조를 가지는 압전 후막을 제작 수 있었다.

• Korean Journal of Environmental Agriculture
• /
• v.19 no.5
• /
• pp.401-418
• /
• 2000

1. Production of the artificial zeolite from coal ash Coal fly ash is mainly composed of several oxides including $SiO_2$ and $Al_2O_3$ derived from inorganic compounds remained after burning. As minor components, $Fe_2O_3$ and oxides of Mg, Ca, P, Ti (trace) are also contained in the ash. These components are presented as glass form resulting from fusion in the process of the combustion of coal. In other word, coal ash may refer to a kind of aluminosilicate glass that is known to easily change to zeolite-like materials by hydrothermal reaction. Lots of hot seawater is disposing near thermal power plants after cooling turbine generator periodically. Using seawater in the hydrothermal reaction caused to produce low price artificial zeolite by reduction of sodium hydroxide consumption, heating energy and water cost. As coal ash were reacted hydrothermally, peaks of quartz and mullite in the ash were weakened and disappeared, and new Na-Pl peaks were appeared strengthily. Si-O-Si bonding of the bituminous coal ash was changed to Si-O-Al (and $Fe^{3+}$) bonding by the reaction. Therefore the produced Na-Pl type zeolite had high CEC of 276.7 $cmol^+{\cdot}kg^{-1}$ and well developed molecular sieve structure with low concentration of heavy metals. 2. Utilization of the artificial zeolite in agro-environment The artificial zeolite(1g) could remove 123.5 mg of zinc, 164.7 mg copper, 184.4 mg cadmium and 350.6 mg lead in the synthetic wastewater. The removability is higher 2.8 times in zinc, 3.3 times in copper, 4.7 times in cadmium and 4.8 times in lead than natural zeolite and charcoal powder. When the heavy metals were treated at the ratio of 150 $kg{\cdot}ha^{-1}$ to the rice plant, various growth inhibition were observed; brownish discoloration and death of leaf sheath, growth inhibition in culm length, number of panicles and grains, grain ripening and rice yield. But these growth inhibition was greatly alleviated by the application of artificial zeolite, therefore, rice yield increased $1.1{\sim}3.2$ times according to the metal kind. In addition, the concentration of heavy metals in the brown rice also lowered by $27{\sim}75%$. Artificial Granular Zeolites (AGZ) was developed for the purification of wastewater. Canon exchange capacity was 126.8 $cmol^+{\cdot}kg^{-1}$. AGZ had Na-Pl peaks mainly with some minor $C_3S$ peaks in X-ray diffractogram. In addition, AGZs had various pore structure that may be adhere the suspended solid and offer microbiological niche to decompose organic pollutants. AGZ could remove ammonium, orthophosphate and heavy metals simultaneously. Mixing ratio of artificial zeolite in AGZs was related positively with removal efficiency of $NH_4\;^+$ and negatively with that of $PO_4\;^{3-}$. Root growth of rice seedling was inhibited severely in the mine wastewater because of strong acidity and high concentration of heavy metals. As AGZ(1 kg) stayed in the wastewater(100L) for 4days, water quality turned into safely for agricultural usage and rice seedlings grew normally.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.413-413
• /
• 2011

최근 전기, 전자, 반도체 산업의 발전으로 전 고상 박막리튬전지는 초소형, 초경량의 마이크로 소자의 구현을 위한 고밀도 에너지원으로 각광받고 있다. 현재 양극박막은 대부분LCO(LiCoO2)계열이 이용되고 있으나, 코발트는 높은 가격과 인체 유해성 뿐만 아니라 상대적으로 낮은 용량(~140 mAh/g)등의 단점을 갖고 있어 향후 보다 고용량의 양극박막이 요구된다. 3원계 양극활물질 LiMO2(M=Co,Ni,Mn,etc.)은 우수한 충방전 효율 과 열적 안정성 뿐 아니라 277mAh/g의 높은 이론용량을 갖고 있어 고용량 양극박막으로의 적용시 고용량 박막이차전지 제작이 가능하다. 본 연구에서는 전 고상 박막 전지의 구현을 위하여 RF 스퍼터링법을 사용하여 Li[Li0.2Mn0.54Co0.13Ni0.13]O2 박막을 증착하였다. Li/MnCoNi의 몰 비율을 변화시켜 높은 전기화학적 특성을 갖는 분말을 합성하여 제조한 타겟으로 Pt/TiO2/SiO2/Si 기판위에 RF 스퍼터법을 이용하여 박막을 성장시켰다. 박막 증착 시 가스의 비율은 Ar:O2=3:1로 하고 증착 압력의 조절(0.005~0.02 torr)을 통하여 박막의 두께와 표면 특성을 조절하며 성장시켰다. 또한 박막을 다양한 온도에서($400{\sim}550^{\circ}C$) 열처리하여 결정화도와 전기화학적 특성을 측정하였다. 증착 된 박막의 구조적 특성은 X-ray diffraction(XRD) 과 scanning electron microscopy(SEM)로 관찰되었다. 박막의 전기화학적 특성 평가를 위하여 Cyclic voltammatry를 측정하여 가역성의 정도를 확인하고 WBC3000 battery cycler를 이용한 half-cell 테스트를 통하여 박막의 용량을 평가하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.589-597
• /
• 2010

In the present study, the effect of variation in alloying elements on the carbide formation behavior during casting and homogenization treatment of M2 high speed steels was investigated. M2 high speed steels of various compositions were produced by vacuum induction melting. Contents of C, Cr, W, Mo, and V were varied from the basic composition of 0.8C, 0.3Si, 0.2Mn, 4.0Cr, 6.0W, 5.0Mo, and 2.0V in weight percent. Homogenization treatment at $1150^{\circ}C$ for 1.5 hr followed by furnace cooling was performed on the ingots. Area fraction and chemical compositions of eutectic carbide in as-cast and homogenized ingots were analyzed. Area fraction of eutectic carbide appeared to be higher in the ingots with higher contents of alloying elements the area fraction of eutectic carbide also appeared to be higher on the surface regions than in the center regions of ingots. As a result of the homogenization treatment, $M_2C$ carbide, which was the primary eutectic carbide in the as-cast ingots, decomposed into thermodynamically stable carbides, MC and $M_6C$. The latter carbide was found to be the main one after homogenization. Fine carbides uniformly distributed in the matrix was found to be MC type carbide and coarsened by homogenization.

• Journal of dental hygiene science
• /
• v.14 no.3
• /
• pp.319-324
• /
• 2014

The aim of this study was to evaluate influences of titanium dioxide ($TiO_2$) concentrations and irradiation times on growth of Streptococcus mutans when irradiated by visible light (405 nm wavelength) and by ultraviolet light (254 nm wavelength). To find the optimal antibacterial concentration of $TiO_2$, 0.01, 0.1, 1.0, and 10.0 mg/ml $TiO_2$ suspension was prepared with sterilized distilled water. S. mutans cultured media was added to $TiO_2$ solution to set the final cell count to $10^4CFU/ml$. The photocatalytic reaction was induced by irradiating 254 nm and 405 nm lights for 10 minutes. To compare the bactericidal activities according to irradiation times, all photocatalytic reaction was carried out with 0.1 mg/ml $TiO_2$ for 0, 10, 20, 30, and 40 minutes with both lights. After the photocatalytic reaction, $100{\mu}m$ of the reaction mixture was immediately plated on brain heart infusion agar. These plates were placed at 5% $CO_2$, $37^{\circ}C$, for 24 hours and the bacterial colonies were counted. All experiments were performed in quintuplicate. One-way ANOVA was used to determine whether there were any significant differences between the $TiO_2$ concentrations or the irradiation times. The most effective concentration of $TiO_2$ for its photocatalytic bactericidal effect on S. mutans was 0.1 mg/ml when irradiated with 254 nm and 405 nm lights. The longer the irradiation time, the bigger the bactericidal effect for both wavelengths. Over 99% of bacteria in the inoculum were killed after irradiation with 254 nm for 20 minutes and with 405 nm for 40 minutes. In conclusion, a photocatalytic reaction of $TiO_2$ induced by visible light of 405 nm constitutes the bactericidal effect on S. mutans.