• Journal of Powder Materials
• /
• v.27 no.5
• /
• pp.406-413
• /
• 2020

Ti_0.5Al_0.5N/CrN nano-multilayers, which are known to exhibit excellent wear resistances, were prepared using the unbalanced magnetron sputter for various periods of 2-7 nm. Ti_0.5Al_0.5N and CrN comprised a cubic structure in a single layer with different lattice parameters; however, Ti_0.5Al_0.5N/CrN exhibited a cubic structure with the same lattice parameters that formed the superlattice in the nano-multilayers. The Ti_0.5Al_0.5/CrN multilayer with a period of 5.0 nm exceeded the hardness of the Ti_0.5Al_0.5N/CrN single layer, attaining a value of 36 GPa. According to the low-angle X-ray diffraction, the Ti_0.5Al_0.5N/CrN multilayer maintained its as-coated structure up to 700℃ and exhibited a hardness of 32 GPa. The thickness of the oxidation layer of the Ti_0.5Al_0.5N/CrN multilayered coating was less than 25% of that of the single layers. Thus, the Ti_0.5Al_0.5N/CrN multilayered coating was superior in terms of hardness and oxidation resistance as compared to its constituent single layers.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.105-114
• /
• 2001

$Al_2$$O_3$ coatings were deposited on M2 high speed steels by the plasma enhanced chemical vapor deposition (PECVD) process, using a gas mixture of AlC1$_3$, $H_2$, $CO_2$ and Ar $Al_2$$O_3$ coatings had interference color and showed amorphous phase. $A1_2$X$A1_3$/($Ti_{0.5}$ /$Al_{0.5}$ )N double layer coatings were produced in the sequence of substrate $NH_3$ plasma pretreatment, ($Ti_{0.5}$$Al_{0.5}$)N depoition process, $Al_2$$O_3$ deposition process. $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings showed NaCl structure in ( $Ti_{0.5}$A $l_{0.5}$)N layer and amorphous phase in A1$_2$ $O_3$ layer. It was shown that $Al_2$ $O_3$ columns continuously grew onto ( $Ti_{0.5}$A $l_{0.5}$)N columns. ( $Ti_{0.5}$A $l_{0.5}$)N single coating and $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coating were oxidized at $700^{\circ}C$, 80$0^{\circ}C$, 90$0^{\circ}C$ for 1hr, 3hr in atmosphere. At 80$0^{\circ}C$, single layer coatings were oxidized, which were examined substrate oxide particle. But $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings maintained the asdeposited state. Therefore, $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings have moreexcellent oxidation resistance than ( $Ti_{0.5}$A $l_{0.5}$)N single layer coatings.X> 0.5/)N single layer coatings.s.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.6
• /
• pp.329-334
• /
• 2003

Microstructure and mechanical properties of $(Ti_{1-x}Alx)N$ films, Produced by the the Ion Beam Sputtering(IBS) method, were studied by changing the Ti, Al contents. The compositions of films determined by RBS were $(Ti_{0.75}Al_{0.25})N$, $(Ti_{0.61}Al_{0.39})N$ and $(Ti_{0.5}Al_{0.5})N$, and XPS binding energies of Ti2P, A12p and N1s shifted to higher energies than those of pure Ti, Al and N, which indicated that nitrides were formed. XRD results indicated that the NaCl structure for $$x{\leq_-}0.39$$ changed into amorphous structure at x=0.5. For films with $$x{\leq_-}0.39$$, the lattice parameter decreased in proportion to the Al content. Nanoindentation hardness value were above HV=3300 at Al content up to x=0.39. However, the hardness of films with x=0.5 abruptly decreased to HV=1800, and this lower hardness values were attributed to different crystal structure. Critical load(Lc) in scratch test showed 23N at x=0.25, 22N at x=0.39 and 22N at x=0.5, which indicated that films with different Al contents showed similar adhesion behavior.

• Corrosion Science and Technology
• /
• v.5 no.2
• /
• pp.52-61
• /
• 2006

Recently, much of the current development in surface modification engineering are focused on multilayered coatings. Multilayered coatings have the potential to improve the tribological properties. Four different multilayered coatings were deposited on AISI D2 steel. The prepared samples are designed as $WC-Ti_{0.6}Al_{0.4}N$, $WC-Ti_{0.53}Al_{0.47}N$, $WC-Ti_{0.5}Al_{0.5}N$ and $WC-Ti_{0.43}Al_{0.57}N$. The multilayered coatings were investigated with respect to coating surface and cross-sectional morphology, roughness, adhesion, hardness, porosity and tribological behavior. Especially, wear tests of four multilayered coatings were performed by using a ball-on-disc configuration with a linear sliding speed of 0.017 m/sec, 5.38 N load. The tests were carried out at room temperature in air by employing AISI 52100 steel ball ($H_R=66$) having a diameter of 10 mm. The surface morphology, and topography of the wear scars of samples and balls have been determined by using scanning electron spectroscopy (SEM). Results have showed an improved wear resistance of the $WC-Ti_{1-x}Al_xN$ coatings with increasing of Al concentration. $WC-Ti_{0.43}Al_{0.57}N$ coating with the lower surface roughness and porosity with good adhesion enhanced wear resistance.

• Journal of the Korean Ceramic Society
• /
• v.56 no.1
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.1
• /
• pp.79-84
• /
• 2003

$WC-Ti_{1}$ -xA $l_{x}$ N multilayered coatings are performed by their periodically repeated structures of lamellae of WC-Ti/$WC-Ti_{1}$ -xA $l_{x}$ Nmaterials. The $WC-Ti_{1}$ -xA $l_{x}$ N coatings with variable Al content were deposited onto AISI D2 steel by cathodic arc deposition (CAD) method. The electrochemical behavior of multilayered $WC-Ti_{1}$ -xA $l_{x}$ N coatings with different phases (WC- Ti$0.6/Al_{0.4}$ N, $WC-Ti_{0.53}$$Al_{0.47}$N, $WC-Ti_{0.5}$ $Al_{0.5}$ N and $WC-Ti_{ 0.43}$$Al_{0.57}$ N) was investigated in deaerated 3.5% NaCl solution at room temperature. The corrosion behaviors for the multilayered coatings were investigated by electrochemical techniques (potentiodynamic polarization) and surface analyses (X-ray diffraction (XRD), scanning electron microscopy (SEM), and glow discharge optical emission spectroscopy (GDOES)). In the petentiodynamic polarization test, the corrosion current density of $WC-Ti_{0.5}$$Al_{0.5}$N was lower than others.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.3
• /
• pp.187-196
• /
• 1995

TiN and AlN are ceramic materials with mechanical and chemical properties for use in structural applications at elevated temperature. The purpose of this research is to develop the technology for the synthesis of (Ti, Al)N power, which shows simultancously the excellent properties of TiN and AlN, from the mixed powder($Ti_{0.25}Al_{0.75}$, $Ti_{0.5}Al_{0.5}$ and $Ti_{0.75}Al_{0.25}$) by the direct nitriding method. The effects of variables such as temperature, mixing ratio of Al to Ti in raw material were investigated. The(Ti, Al)N powder can be easily synthesized from the mixed powder by the direct nitriding method. Among the mixed powdres, the nitriding behavior decreased with increasing the ratio of Al to Ti. This behavior is well explained by the nitriding mechanism presented in this research.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.512-518
• /
• 1997

The high temperature oxidation behaviors of titanium nitride films prepared by PACVD technique were studied in the temperature range of from 50$0^{\circ}C$ to 80$0^{\circ}C$ under air atmosphere. Ti0.88Al0.12N film, which showed the excellent microhardness from the previous work, was investigated on its oxidation resistance compared with pure TiN film. Ti-Al-N film showed superior oxidation resistance up to $700^{\circ}C$, whereas TiN film was fast oxidized into rutile TiO2 crystallites from at 50$0^{\circ}C$. It was found that an amorphous layer having AlxTiyOz formula was formed on the surface region due to outward diffusion of Al ions at the initial stage of oxidation. The amorphous oxide layer played a role as a barrier against oxygen diffusion, protected the remained nitride layer from further oxidation, and thus, resulted in the high oxidation resistive characteristics of Ti-Al-N film.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.435-444
• /
• 2001

WC-( $Ti_{1-x}$ A $l_{x}$) N coatings of constant changing Al concentration were deposited on S45C substrates by high-ionization sputtered PVD method. The Al concentration could be controlled by using evaporation source for Al and fixing the evaporation rate of the metals (i.e, WC- $Ti_{0.86}$A $l_{0.14}$N, WC- $Ti_{0.72}$A $l_{0.28}$N, and WC- $Ti_{0.58}$A $l_{0.42}$N). The corrosion behavior of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings in a deaerated 3.5% NaCl solution was investigated by electrochemical corrosion tests and surface analyses. The measured galvanic corrosion currents between coating and substrate indicated that WC- $Ti_{0.72}$A $l_{0.28}$N coating showed the best resistance of the coating tested. The results of potentiodynamic polarization tests showed that the WC- $Ti_{0.72}$A $l_{0.28}$N coating deposited with 32W/c $m^2$ of Al target revealed higher corrosion resistance. This indicated that the WC- $Ti_{0.72}$A $l_{0.28}$N coating is effective in improving corrosion resistance. In EIS, the WC- $Ti_{0.72}$A $l_{0.28}$N coating showed one time constant loop and increased a polarization resistance of coating ( $R_{coat}$) relative to other samples. Compositional variations of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings were analyzed by EDS and XRD analysis was performed to evaluate the crystal structure and compounds formation behavior. Surface morphologies of the films were observed using SEM and AFM. Scratch test was performed to measure film adhesion strength.strength. adhesion strength.strength.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.505-511
• /
• 1997

The effects of sintering atmospheres(air, O2, N2) on the sintering and microwave dielectric properties of (1-x)CaTiO3-xLaAlO3 system was investigated. The sintered density of (1-x)CaTiO3-xLaAlO3 under air atmosphere increased linearly with increasing x, but it decreased in the range of x>0.5 under O2 atmosphere and x>0.6 under N2 atmosphere in spite of the increament of the smaller La(1.06$\AA$) and Al(0.5 $\AA$) ion than Ca(0.99$\AA$) and Ti(0.6$\AA$). In case of the air sintering atmosphere of (1-x)CaTiO3-xLaAlO3 the two phases of orthorhombic and rhombohedral crystal system were coexisting, and the XRD peak of rhombohedral crystalsystem was to be higher with increasing x. However, the sintering atmosphere of O2 and N2 made the monophasic crystal system of orthorhombic keep up by x=0.5 and x=0.6, respectively, and it transformed to pseudo-cubic crystal system in x>0.5 and x>0.6. The XRD peak intensity of (1-x)CaTiO3-xLaAlO3 was to be gradually higher with increasing x under the air atmosphere of sintering. Whereas, its XRD peak intensity increased till x=0.6 but decreased with increasing x in the range of x>0.6 under O2 and N2 atmosphere. The relative dielectric constant of (1-x)CaTiO3-xLaAlO3 sintered under air atmosphere decreased linearly and the Q.f0 value increased according as x increased. On the other hand, the relative dielectric constant of (1-x)CaTiO3-xLaAlO3 under O2 and N2 atmosphere decreased in the range of x$\leq$0.5 with increasing x, but increased rapidly in the range of x$\geq$0.6. And the Q.f0 value increased till x=0.6 but decreased in the range of x>0.6 with increasing x. The temperature coefficient of resonant frequency had no relation to sintering atmosphere.