• Proceedings of the KIEE Conference
• /
• 2007.11c
• /
• pp.138-140
• /
• 2007

$TiO_2-V_2O_5$ sol was fabricated using sol-gel method and $TiO_2-V_2O_5$ thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mo1e, 0.03mo1e, 0.05mo1e into $TiO_2$ sol. Viscosity of sol increased fast from about 1,000 minutes and sol began gelation from about 10,000 minutes. As a results of crystalline properties, $V_2O_5$ peaks were not found despite of $V_2O_5$ addition. Endothermic reaction occurred due to evaporation of solvent and dissociation of OH at $80^{\circ}C$. Exothermic reaction occurred due to combustion and oxidation of solvent at $230^{\circ}C$, occurred to combustion and oxidation of alkyl group at $350^{\circ}C$. Thickness of thin films increased $0.1{\sim}0.25{\mu}m$ every a dipping.

• Journal of Environmental Science International
• /
• v.30 no.6
• /
• pp.501-505
• /
• 2021

V₂O₅-TiO₂ catalysts were prepared by various methods. V₂O₅-TiO₂ were prepared by sol-gel method with different drying conditions (aerogel and xerogel), and V₂O₅ supported on TiO₂ obtained by sol-gel method with precipitation-deposition method and impregnation method. The performance of the V₂O₅-TiO₂ catalysts was investigated for the selective oxidation of hydrogen sulfide in the stream containing both ammonia and excess water. All the catalysts showed good dispersion of vanadium and they had high H₂S conversion with no or little production of sulfur dioxide. The V₂O₅-TiO₂ aerogel catalyst prepared by sol-gel method with drying under super critical condition had the highest surface area which led to better catalytic activity compared to those by other synthesis methods.

• Proceedings of the KIEE Conference
• /
• 2008.05a
• /
• pp.161-163
• /
• 2008

$TiO_2-V_2O_5$ sol was fabricated using sol-gel method and $TiO_2-V_2O_5$, thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mole, 0.03mole, 0.05mole into $TiO_2$ sol. Capacitance of thin films decreased with increasing $V_2O_5$ additive and it increased largest at 0.01mole. Because adsorption time and desorption time of thin films was about 2 minutes 40 seconds and about 3 minutes 40 seconds respectively, adsorption time was faster about 1 minutes than desorption time.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.7
• /
• pp.1255-1260
• /
• 2007

[ $TiO_2-V_2O_5$ ] sol was prepared using sol-gel method. Sol changed to gel with hydrolysis and polymerization. DTA properties of gel powder had endothermic reaction due to evaporation of propanol about $80^{\circ}C$, had exothermic reaction due to combustion of propanol about $230^{\circ}C$ and had exothermic reaction due to combustion of alkyl group about $350^{\circ}C$. Crystalline properties of gel powder retained amorphous phase at $50^{\circ}C$, retained anatase phase from $400^{\circ}C\;to\;600^{\circ}C$ and had all rutile phase over $700^{\circ}C$ at 0.01mole $V_2O_5$ additive. The capacitance of thin films increased with increasing heat treatment temperature and thin films had best properties at $700^{\circ}C$. The capacitance of thin films increased a lot with decreasing measurement frequency.

• Journal of Sensor Science and Technology
• /
• v.4 no.3
• /
• pp.15-21
• /
• 1995

In this paper, $TiO_{2}-V_{2}O_{5}$ humidity sensors are fabricated by Sol-Gel method. For the establishment of optimum processing condition which is good humidity sensitive characteristics for specimens, their microstructures and crystalline-structures are analysed. Grain size increases with substitution rate of $V^{5+}$ on $Ti^{4+}$ site. From the analysis of XRD, $V^{5+}$ peak can't confirm with $V_{2}O_{5}$ rate. Their humidity sensitive characteristics is good at 1mol% of $V_{2}O_{5}$ rate and heat-treated at $700^{\circ}C$. The capacitance of specimens decreases with frequency.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.57 no.6
• /
• pp.1012-1016
• /
• 2008

[ $TiO_2-V_2O_5$ ] sol was fabricated using sol-gel method and $TiO_2-V_2O_5$ thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mole, 0.03mole, 0.05mole into $TiO_2$ sol. As a results of crystalline properties, $V_2O_5$ peaks were not found in spite of $V_2O_5$ additive. Thickness of thin films increased $0.1{\sim}0.25{\mu}m$ every a dipping. Capacitance of thin films increased with increasing heat treatment temperature and it increased largest at $700^{\circ}C$. Capacitance of thin films decreased with increasing $V_2O_5$ additive and it increased largest at 0.01mole. Because adsorption time and desorption time of thin films was about 2 minutes 40 seconds and about 3 minutes 40 seconds respectively, adsorption time was faster about 1 minutes than desorption time.

• Clean Technology
• /
• v.14 no.3
• /
• pp.204-210
• /
• 2008

A series of $V_{2}O_{5}-TiO_2$ xerogel catalysts were prepared by nonhydrolytic sol-gel method and analysed by various characterization techniques. These catalysts showed much higher surface areas and total pore volumes than conventional V$V_{2}O_{5}-TiO_2$ xerogel and impregnated $V_{2}O_{5}/TiO_2$ catalysts. It was found that the textural property of $V_{2}O_{5}-TiO_2$ material varies with the method and conditions of synthesis. Surface vanadates and $TiO_2$ anatase phase are the crucial factors to obtain high catalytic activities. The selective oxidation of hydrogen sulfide in the presence of excess water and ammonia was studied over these catalysts. Xerogel catalysts prepared by non-hydrolytic sol-gel method showed very high conversion of $H_{2}S$ without harmful emission of $SO_2$. The highest catalytic activity shown by these $V_{2}O_{5}-TiO_2$ catalysts may be due to their high surface area and good dispersion of vanadia species in the titania matrix.

• Applied Chemistry for Engineering
• /
• v.7 no.2
• /
• pp.269-279
• /
• 1996

The porous armophous catalysts, composed of $SiO_2-TiO_2-V_2O_5$ were prepared through SOL-GEL process by differing the preparation parameters. Selected the optimum SOL-GEL catalyst which has the best NO removal activity through the screening test, and repeated coating it on the cordierite monolith which is the freely through and inert. And examined the NOx, SOx simultaneous removal effect under S. C. R. condition. In addition to its characterization performances by the DTA, TGA, BET, $NH_3$ and NO TPD, ESCA, XRD etc.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.58 no.2
• /
• pp.327-331
• /
• 2009

Nano-porous $TiO_2$ powder was fabricated using Acetylene black, applied photo voltaic device based on the Dye-sensitized Solar Cells (DSCs) was investigated experimentally. $TiO_2$-powder was fabricated using Ti-isopropoxide and 2-propanol by sol-gel combustion method. For cases of variable Acetylene black, characteristic of porosity, size of particle and crystallite of obtained $TiO_2$ nano-powder was investigated. The photovoltaic efficiency of the prepared DSCs was measured using $TiO_2$ film which prepared on each different heat treatment temperature($400^{\circ}C{\sim}700^{\circ}C$) with paste of $TiO_2$ powder. The porosity and size of particle of $TiO_2$ powder made with Acetylene black 0.4g was influenced significantly effect to DSCs characteristic. Heat treatment at $500^{\circ}C$ makes the better photovoltaic efficiency which 5.02%($J_{sc}=11.79mA/cm^2$, $V_{oc}=0.73V$, ff=0.58). The sol-gel combustion method was useful to DSCs fabrication.

• Applied Chemistry for Engineering
• /
• v.32 no.6
• /
• pp.599-606
• /
• 2021

In this study, an experiment and a reaction characteristic study were conducted to enhance the reaction activity of V₂O₅/WO₃/TiO₂ at 300 ℃ or less by adding selenium to the support, in a selective catalytic reduction method using ammonia as a reducing agent to remove nitrogen oxides. Se-TiO₂ and TiO₂ were synthesized using the sol-gel method, and used as a support when preparing V₂O₅/WO₃/TiO₂ and V₂O₅/WO₃/Se-TiO₂ catalysts. The reaction activity of our catalyst was compared with that of a commercial catalyst. The denitration efficiency of the catalyst using TiO₂ prepared by the sol-gel method was lower than that of the catalyst prepared using commercial TiO₂, but was improved by the addition of selenium. Thus, the effect of selenium addition on the catalyst structure was analyzed using BET, XRD, Raman, H₂-TPR, and FT-IR measurements and the effect of the increase in specific surface area by selenium addition and the formation of monomer and complex vanadium species on reaction characteristics were confirmed.