• Journal of Biomedical Engineering Research
• /
• v.25 no.5
• /
• pp.383-389
• /
• 2004

A commercially pure Ti(CP-Ti) and Ti-25wt％Pd alloy for dental applications were cast into a phosphate-bonded Al$_2$ $O_3$/ $SiO_2$ investment mold and the surface of the casting specimens were investigated by means of SEM/EDS, XRD and XPS. The addition of 25wt％Pd in CP-Ti showed a moderate mold reaction owing to the considerable lowering of melting point. XRD analysis of the investment after burn-out treatment revealed that it consisted essentially of $SiO_2$, Al$_2$ $O_3$, P$_2$O$\_$5/, Mg$_3$(P $O_4$)$_2$, AlP $O_4$, Mg$_2$ $SiO_4$, MgAl$_2$ $O_4$ The mold reaction products were Ti$\_$5/Si$_3$ and Ti $O_2$ in case of CP-Ti casting and Ti $O_2$ and SiO$\_$x/ in case of Ti-25wt％ Pd casting.

• Applied Chemistry for Engineering
• /
• v.1 no.1
• /
• pp.35-43
• /
• 1990

A series of $TiO_2-SiO_2$catalysts were prepared by coprecipitation from the mixed solution of titanium tetrachloride and sodium silicate. Some of the samples were treated with 1N $H_2SO_4$ and used as modified catalysts. The catalytic activities of modified catalysts were higher than those of unmodified catalysts, and the effect of modification on the catalytic activity was higher for 2 - propanol dehydration than for cumene dealkylation. The catalytic activity of unmodified catalysts was correlated with their acid amount for the above two reactions. As $TiO_2-SiO_2$ catalysts had relatively large amount of weak acid sites and small amount of strong acid sites, the catalytic activity for 2 - propanol dehydration was higher than that for cumene dealkylation. The effect of modification on catalytic activity increased with increasing $TiO_2$content of the catalysts. Actually, $92-TiO_2-SiO_2/SO_4{^2}$had the highest increment in catalytic activity and $10-TiO_2-SiO_2/SO_4{^2}$had the lowest increment for the 2 - propanol dehydration.

• Particle and aerosol research
• /
• v.7 no.3
• /
• pp.79-85
• /
• 2011

Porous $TiO_2-SiO_2$ particles were synthesized by co-assembly of nanoparticles of $TiO_2$ and $SiO_2$ in evaporating aerosol droplets. Poly styrene latex (PSL) particles were employed as a template of porous particles. Flowrate of dispersion gas, weight ratio of $TiO_2/SiO_2$ and $SiO_2$ concentration in the precursor, and PSL size were chosen as process variables. The morphology, crystal structure, chemical bonding, and pore size distribution were analyzed by FE-SEM, XRD, FT-IR, BET. The morphology of porous $TiO_2-SiO_2$ particles was spherical and the average particle size range were from 1 to $10{\mu}m$. The particles were composed of meso and macro pores. The average particle diameter and pore volume of the as prepared particles were dependant on process variables. It was found that UV-Vis absorption of the porous particles was comparable with pure $TiO_2$ nanoparticles even though $TiO_2/SiO_2$ ratio is low in the porous particles.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.246-250
• /
• 2004

We have investigated the effects of boron added to Cu film on the Cu-Ti reaction and microstructural evolution of Cu(B) alloy film during annealing of Cu(B)/Ti/$SiO_2$/Si structure. The result were compared with those of Cu(B)/$SiO_2$ structure to identify the effects of Ti glue layers on the Boron behavior and the result grain growth of Cu(B) alloy. The vacuum annealing of Cu(B)/Ti/$SiO_2$ multilayer structure allowed the diffusion of B to the Ti surface and forming $TiB_2$ compounds at the interface. The formed $TiB_2$ can act as a excellent diffusion barrier against Cu-Ti interdiffusion up to $800^{\circ}C$. Also, the resistivity was decreased to $2.3\mu$$\Omega$-cm after annealing at $800^{\circ}C$. In addition, the presence of Ti underlayer promoted the growth Cu(l11)-oriented grains and allowed for normal growth of Cu(B) film. This is in contrast with abnormal growth of randomly oriented Cu grains occurring in Cu(B)/$SiO_2$ upon annealing. The Cu(B)/Ti/$SiO_2$ structure can be implemented as an advanced metallization because it exhibits the low resistivity, high thermal stability and excellent diffusion barrier property.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.14 no.1
• /
• pp.5-14
• /
• 1977

"Electrical Properties of Barium Titanates with Addition Sb2O3." PTC BaTiO3 in low resistance at room temperature was prepatred. Al2O3, SiO2 and TiO2 were doped with a view to improving reproduction. Sb2O3 was doped as impurity in order to control of resistivity of the specimens. The relations between the amount of Sb3O3 and electrical properties wereinvestigated. Of the compositions studied, additions of 3.75mole% Al2O3, 1.25mole% SiO2, 2.25mole% TiO2 and 0.16~0.25wt% Sb2O3 to BaTiC3 was low resistivity in 14-300 ohm-cm.00 ohm-cm.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1110-1111
• /
• 2006

[ $Ti_3SiC_2$ ] was coated with $Al_2O_3$, MgO and $SiO_2$ respectively by sol-gel method and cured at 900 and $1200^{\circ}C$. The coated oxides did not react with $Ti_3SiC_2$ at $900^{\circ}C$ but reacted with it to form $TiC_x$ at $1200^{\circ}C$. The specimen coated with $SiO_2$ at $900^{\circ}C$ formed a dense protecting layer and showed the best oxidation resistance at $800^{\circ}C$ in air. However, the dense protecting layers did not form in $Al_2O_3$ and MgO coated specimens cured even at $900^{\circ}C$. MgO coated specimen showed the worst improvement in the oxidation resistance because the reactivity of MgO with $Ti_3SiC_2$ was highest. On the other hand, the electrical conductivities were measured in MgO and $Al_2O_3$ coated specimens to have TiCx but could not be measured in the $SiO_2$ coated ones because of the nonconductive dense protected layers.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.141-147
• /
• 2005

Nanomaterial $TiO_2-SiO_2$ was synthesized by hydrolysis and condensation process using 2-propanol(2-PrOH) and was characterized by FT-IR, DSC, XRD and FE-SEM. FT-IR spectra were measured to investigate Ti-0-Si absorption peak. DSC thermal analysis results appllied to Ozawa equation were used to calculate to activation energy of crystallization. It was found that the changes of X-ray diffraction patterns and FWHM obtained XRD measurement depended on calcination temperature. In FE-SEM analysis, particle size changed by quantity changes of Ti-alkokide.

• Korean Journal of Materials Research
• /
• v.28 no.11
• /
• pp.620-626
• /
• 2018

Highly self-cleaning thin films of $TiO_2-SiO_2$ co-doped with Ag and F are prepared by the sol-gel method. The asprepared thin films consist of bottom $SiO_2$ and top $TiO_2$ layers which are modified by doping with F, Ag and F-Ag elements. XRD analysis confirms that the prepared thin film is a crystalline anatase phase. UV-vis spectra show that the light absorption of $Ag-F-TiO_2/SiO_2$ thin films is tuned in the visible region. The self-cleaning properties of the prepared films are evaluated by a water contact angle measurement under UV light irradiation. The photocatalytic performances of the thin films are studied using methylene blue dye under both UV and visible light irradiation. The $Ag-F-TiO_2/SiO_2$ thin films exhibit higher photocatalytic activity under both UV and visible light compared with other samples of pure $TiO_2$, Ag-doped $TiO_2$, and F-doped $TiO_2$ films.

• Journal of the Korean Ceramic Society
• /
• v.41 no.8
• /
• pp.593-598
• /
• 2004

To make the all-solid-state lithium thin film battery having less than 1 fm in thickness, LiCoO$_2$ thin films were deposited on Pt/TiO$_2$/SiO$_2$/Si substrate as a function of Li/Co mole ratio and the deposition temperature by Pulsed Laser Deposition (PLD). Especially, LiCoO$_2$ thin films deposited at 50$0^{\circ}C$ with target of Li/Co=1.2 mole ratio show an initial discharge capacity of 53 $\mu$Ah/cm$^2$-$\mu$m and capacity retention of 67.6％. The microstructural and electrochemical properies of (Li, La)TiO3 thin films grown on LiCoO$_2$Pt/TiO$_2$/SiO$_2$/Si structures by Pulsed Laser Deposition (PLD) were investigated at various deposition temperatures. The thin films grown at 10$0^{\circ}C$ show an initial discharge capacity of approximately 51 $\mu$Ah/cm$^2$-$\mu$m and moreover show excellent discharge capacity retention of 90％ after 100 cycles. An amorphous (Li, La)TiO$_3$ solid electrolyte is possible for application to solid electrolyte for all-solid-state lithium thin film battery below 1 $\mu$m.

• Journal of the Korean Ceramic Society
• /
• v.37 no.12
• /
• pp.1221-1228
• /
• 2000

TiO$_2$를 포함한 희토류 알루미노 규산염계 (NAS: Nd$_2$O$_3$-Al$_2$O$_3$-SiO$_2$) 유리의 상분리 현상에 대하여 연구되었다. 0~10wt%의 TiO$_2$포함한 NAS 조성은 유리전이온도(T$_{g}$) 부근에서 열처리하여 HF로 부식 후 주사전자현미경, 라만 및 IR 분석기로 상분리가 조사되었다. 그 결과로 상분리한 내부결정화는 8wt% 이상의 TiO$_2$를 포함한 NAS 조성에서 나타났다. 어닐링후 T$_{g}$ 부근에서 열처리의 결과는 투명 연핑크색의 유리를 불투명의 연푸른 우유빛 색으로 변하게 하였으며, Si와 Nd-Ti가 각각 풍부한 10$mu extrm{m}$ 이상과 0.1$\mu\textrm{m}$ 이하의 크기인 구형상의 영역으로 균일한 다상분리를 일으켰다. Nd$_2$O$_3$-Al$_2$O$_3$-SiO$_2$-TiO$_2$계에서 상분리는 내부 결정화와 관련하여 매우 중요한 인자로 확인되었다.