A Synthesis of Spherical Shape $TiO_2-SiO_2$ Complex via Solvothermal Process and Thermal Properties at Non-Isothermal

용매열합성을 이용한 구형 $TiO_2-SiO_2$ 복합체 제조 및 열적특성

  • Cho Tae-Hwan (Dept. of Industrial Chemistry, Dankook University) ;
  • Park Seong-Jin (Dept. of Industrial Chemistry, Dankook University)
  • 조태환 (단국대학교 공학대학 공업화학) ;
  • 박성진 (단국대학교 공학대학 공업화학)
  • Published : 2005.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

Nanomaterial $TiO_2-SiO_2$ was synthesized by hydrolysis and condensation process using 2-propanol(2-PrOH) and was characterized by FT-IR, DSC, XRD and FE-SEM. FT-IR spectra were measured to investigate Ti-0-Si absorption peak. DSC thermal analysis results appllied to Ozawa equation were used to calculate to activation energy of crystallization. It was found that the changes of X-ray diffraction patterns and FWHM obtained XRD measurement depended on calcination temperature. In FE-SEM analysis, particle size changed by quantity changes of Ti-alkokide.

나노재료 $TiO_2-SiO_2$는 2-prOH(2-propanol)를 용매로 사용하여 가수분해와 축합반응으로 제조하였고, FT-IR, DSC, XRD, FE-SEM을 사용하여 $TiO_2-SiO_2$의 특성을 조사하였다. FT-IR분석으로부터 Ti-0-Si의 흡수피크에 대해 설명하였으며, DSC분석 결과를 Ozawa 방정식에 적용하여, 결정화에 필요한 활성화 에너지를 계산하였다. 결정학적 특징은 XRD를 이용하여 하소 온도의 변화에 따른 시료의 회절패턴과 반가폭의 변화 등에 관련하여 설명하였다. FE-SEM을 통하여 Ti mol$\%$가 증가할수록 입자크기가 커지는 것을 확인 할 수 있었다.