• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.171-171
• /
• 2003

공정기술의 향상으로 DRAM(dynamic random acess memory)의 고집적화가 이루어지고 있으며, 각 개별소자 및 셀 영역의 점유면적의 감소가 요구되어지고 있다. 따라서 기존에 사용하던 NO (Si$_3$N$_4$/SiO$_2$)박막보다 유전율이 높은 고유전물질에 대한 연구가 진행되고 있다. Ta$_2$O$_{5}$, $Y_2$O$_3$, HfO$_2$, ZrO$_2$,Nb$_2$O$_{5}$, BaTiO$_3$, SrTiO$_3$ 및 (BaSr)TiO등이 고유전물질로 연구되고 있는데 그 중 공정의 안정성, 누설전류의 우수성으로 인해 Ta$_2$O$_{5}$이 많이 연구되고 있다. 본 실험에서는 TiO$_2$가 8 mol%가 첨가된 Ta$_2$O$_{5}$의 열처리 온도에 따른 전기적, 유전특성을 살펴보려고 한다살펴보려고 한다

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.472-478
• /
• 1998

Ferroelectric SrBi2Ta2O9(SBT) films were deposited on Pt/Ti/SiO2/Si substrates at 50$0^{\circ}C$ using a sintered SBT target Bi and Ta targets by modified rf magnetron sputtering and then were annealed at 80$0^{\circ}C$ for 10min in oxygen ambinet(760 torr) The composition of the SBT films could be easily controlled using the mul-ti-targets. The film composition of {{{{ {Sr }_{0.8 } {Bi }_{2.9 } {Ta}_{2.0 } {O }_{9 } }} was obtained with SBTd sputtering power of 100 W Bi of 25W and Ta of 10 W. A 250nm thick SBT films exhibited a dense and uniform microstructure and showed the remanent polarization(Pr) of 14.4 $\mu$C/cm2 and the coercive field({{{{ {E }_{c } }})of 60 kV/cm at applied voltage of 5 V. The SBT films show practically no polarization fatigue up to {{{{ {10 }_{10 } }} cycles under 5V bipolar pulse. The retention characteristics of the SBT films looked very promising and the leakage current density of the SBT films was about 1.23$\times${{{{ {10 }^{-7 } }}A/c{{{{ {m }^{2 } }} at 120kV/cm.

• Korean Journal of Materials Research
• /
• v.4 no.5
• /
• pp.550-555
• /
• 1994

The effects of RTA treatment on the leakage current have been studied for tantalum pentoxide( $Ta_2O_5$) films deposited by PECVD on P-type(100) Si substrate using $TaCl_5$(99.99%) and $N_2O$(99.99%) gaseous mixture. The refractive index increased with increasing the deposition temperature and the maximum deposition rate was obtained at $500^{\circ}C$. The Ta-0 bond peak intensity of as-deposited $Ta_2O_5$ increased with increasing the deposition temperature through FT-IR analysis and the leakage current value was decreased with increasing the deposition temperature. The small leakage current value obtained after RTA treatment of as-deposited $Ta_2O_5$ was found to be due to the reduction of 0-deficient structure in the film. The increases of the oxygen coacentration and the Ta-0 bond peak intensity in the film after RTA treatment were measured by AES and FT-IR analyses.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.5
• /
• pp.319-325
• /
• 1999

Direct current(d.c.)leakage current voltage characteristics of radio-frequencymagnetron sputtered BaTa\sub 2\O\sub 6\ film capacitors with aluminum(A1) top and indium tin oxide (ITO) bottom electrodes have been investigatedas a function of applied field and temperature. In order to study surfacetreatment effect on the electrical characteristics of as-deposited film weperformed exposure of oxygen plasma on $BaTa_2O_6$ surface. d. c.current-voltage (I-V), bipolar pulse charge-voltage (Q-V), d. c. current-time (I-t) andcapacitance-frequency (C-f) analysis were performed on films. All ofthe films exhibita low leakage current, a high breakdown field strength (3MV/cm-4.5MV/cm), and high dielectric constant (20-30). From the temperature dependence of leakage current,we can conclude that the dominant conduction mechanism is ascribed toSchottky emission at high electric field (>1MV/cm) and hopping conduction at lowelectric field (<1MV/cm). According to our results, the oxide plasma surfacetreatmenton as-deposited $BaTa_2O_6$ resulted in lowering interfacebarrier height and thus, leakage current when a negative voltage applied to the A1 electrode. This can be explained by reduction of surface contamination via etching surface and filling defects such as oxygen vacancies.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.300-300
• /
• 2008

In this study, the advanced DuoPIGatron-type ion beam (IB) system was applied to inorganic thin film for aligning liquid crystal (LC). LC alignment on $Ta_2O_5$ via IB irradiation was embodied. As a result of IB irradiation, the homogeneously aligned liquid crystal display (LCD) on $Ta_2O_5$ was observed with low pretilt angles. The $Ta_2O_5$ were deposited on indium-tin-oxide coated Coming 1737 glass substrates by rf magnetron sputtering at $200^{\circ}C$. The deposition process resulted in forming very uniform thin film on glass substrates without any defects. To confirm the application of the inorganic alignment on modem display optical devices, we fabricated twisted nematic LCD and measured optical property and response time. As a result of the experiment, the electro optical characteristics of the LCD fabricated by using IB irradiation on $Ta_2O_5$ alignment layer were similar with the other LCD fabricated by using rubbing process.

• Journal of the Korean Vacuum Society
• /
• v.12 no.1
• /
• pp.40-45
• /
• 2003

High quality $Ta_2O_5$ thin films have been obtained from the anodization of deposited tantalum (Ta). The as-deposited amorphous films of 750 $\AA$ thickness have excellent electrical properties. These properties include refractive indices 2.1~2.2 dielectric constants ~25, and leakage currents $10^{-8}$ /A$\textrm{cm}^{-2}$ at 1 MV$\textrm{cm}^{-1}$. We fabricated a MIM element with the $Ta_2O_5$ films. They have perfect current-voltage symmetry characteristics. A high performance MIM device was formed by newly developed processes based on our unique anodization and annealing treatment. The effects of various processing conditions (top-electrode metals, annealing conditions) on the MIM device performances will be extensively discussed throughout this work.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.290-294
• /
• 2000

ZnS:Mn TFEL devices were fabricated by electron-beam evaporation method and then the electro-optical properties were investigated. To investigate the capacitance which was due to oxygen vacancy at the $Ta_2O_5$ thin film, AES(Auger Electron Spectroscopy) and C-F(capacitance-frequency) measurements were used. It was found that the capacitance was decreased by annealing the $Ta_2O_5$ film in oxygen ambience. From EL emission measurement, we observed the EL emission spectrum which had the peak range from 550nm and 650nm. This emission is associated with the transition from $^4T_1(^4G)$ first excited state to $^6A_1(^6S)$ ground state in the $3d^5$ energy level configuration of $Mn^{2+}$ occurs. The threshold voltage of EL device with $Ta_2O_5$ insulator layer was found to be 24V~28V. The CIE color coordinates of these emission are X=0.5151, Y=0.4202 which is yellowish orange emitting. The EL device using $Ta_2O_5$ insulator layer can be driven with a low voltage which is beneficial to the practical application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.04b
• /
• pp.3-5
• /
• 2008

The $SrBi_2Ta_2O_9$ thin films are deposited on Pt-coated electrode(Pt/$TiO_2/SiO_2$/Si) using RF magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing temperatures were studied. Through the x-ray diffraction analysis and the scanning electron microscopy (SEM), it could be observed that crystallization of the SBT thin film started around $650^{\circ}C$ and complete crystallization was accomplished around $750^{\circ}C$ and grains grew from a small spheric form to rod-like. For the leakage current density of the SBT capacitor depending upon various annealing atmospheres, capacitor annealed in the oxygen atmosphere showed the most excellent characteristic, and they were respectively about $2.13\times10^{-9}[A/cm^2]$ at 5V and 340.

• Proceedings of the Optical Society of Korea Conference
• /
• 2000.02a
• /
• pp.320-321
• /
• 2000

전기장 발광현상(Electroluminescence, 이하 EL)은 1936년 Destriau$^{[1]}$ 가 ZnS:Cu 분말에서 처음 전기장 발광현상을 발견한 이래 TFEL(Thin Film EL)소자의 구동전압을 감소시키는 문제는 ACTFEL(Alternating Current Thin Film EL)소자의 개발이후 계속적인 관심의 대상이 되어왔다. TFEL 소자는 전기적으로 용량소자이므로 전기장 인가시 각 층의 정전용량의 역수에 비례하는 전압이 분배되므로 동일한 조건의 형광막 사용시 소자의 구동전압을 낮추기 위해서는 절연박막의 두께를 줄이는 방법과 유전율이 높은 물질을 사용하는 방법이 있으나, 전자의 경우에는 박막의 결함이 생기기 쉬워 한계가 있기 때문에 고유전율 특성을 갖는 새로운 물질을 개발하는 것이 바람직하다. Ta$_2$O$_{5}$ 박막의 경우 작은 누설전류 특성과 고유전율 특성으로 인해 고집적을 요하는 반도체 분야에서 많은 연구가 진행되어 왔다. 또한 EL소자 응용시 효율면에서 우수한 특성이 기대되며, 특히 수분에 강한 특성을 가지고 있어 EL소자의 안정성이 예견되는 바이다. 본 연구에서는 Ta$_2$O$_{5}$ 박막의 산소 결핍에 따른 전기적 특성에 대해 연구하였고 Ta$_2$O$_{5}$ 박막을 이용한 저전압에서 구동가능한 전기장 발광소자를 제작하여 전기광학적 특성에 대해 연구하였다. (중략

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.5
• /
• pp.335-340
• /
• 2013

In this study, the plasma etching of the TaN thin film with $CH_4/BCl_3/Ar$ gas chemistries was investigated. The etch rate of the TaN thin film and the etch selectivity of TaN to $SiO_2$ was studied as a function of the process parameters, including the amount of $CH_4$. X-ray photoelectron spectroscopy (XPS) and Field-emission scanning electron microscopy (FE-SEM) was used to investigate the chemical states of the surface of the TaN thin film.