• Proceedings of the KIEE Conference
• /
• 2004.11a
• /
• pp.194-196
• /
• 2004

$BaTiO_3/SrTiO_3$ heterolayered thick films on the $Al_2O_3$ substrate by screen printing method with stacking periodicity. The stacking periodicity of $BaTiO_3/SrTiO_3$ heterolayer structure was varied from $(BaTi_O_3)_1/(SrTiO_3)_1$ to $(BaTi_O_3)_3/(SrTiO_3)_3$. The total thickness of the $BaTiO_3/SrTiO_3$ films was about $120{\mu}m$. There was an interdiffusion at the interface of the $BaTiO_3$ and $SrTiO_3$ layers. The dielectric constant of $BaTiO_3/SrTiO_3$ heterolayered thick films was increased with decreasing stacking periodicity of the $BaTiO_3/SrTiO_3$. The dielectric constant of the ($(BaTi_O_3)_1/(SrTiO_3)_1$ herterolayered thick films was about 1780.

• Proceedings of the KIEE Conference
• /
• 2004.11a
• /
• pp.58-60
• /
• 2004

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated on alumina substrate by screening printing method. The obtained films were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The structural and electrical properties of $BaTiO_3/SrTiO_3$ heterolayered thick films were compared with pure $BaTiO_3$ and $SrTiO_3$ films. The (Ba,Sr)$TiO_3$ phase was appeared at the $BaTiO_3/SrTiO_3$ heterolayered thick films. The thickness of $BaTiO_3/SrTiO_3$ heterolayered thick film, obtained by one printing, was about $50{\mu}m$. The dielectric constant and dielectric loss of the $BaTiO_3/SrTiO_3$ heterolayered thick films were about 1964, 5.5% at 1KHz, respectively.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1850-1852
• /
• 2005

$SrTiO_3$ and $BaTiO_3$ sol-liquids and powders were prepared by the sol-gel method. $SrTiO_3/BaTiO_3$ heterolayered thin/thick films have been prepared on the $Al_2O_3$ substrates by screen printing and spin-coating method. The thin films were sintered at $750^{\circ}C$ in the air for 1 hour and the thick films sintered at $1325^{\circ}C$ in the air for 2 hours, respectively. The $SrTiO_3/BaTiO_3$ thin/thick films's structural and dielectric properties were investigated. Increasing the spin-coating times, (110), (200), (211) peaks of the $SrTiO_3$ were increased. The X-ray diffraction(XRD) patterns and SEM photographs indicated that the $SrTiO_3$ phase were formed in the surface of $BaTiO_3$ thick films. The average thickness of a $BaTiO_3$ thick films and $SrTiO_3$ thin films were $50{\mu}m$ and 400nm, respectively The dielectric constant and dielectric loss of the $SrTiO_3/BaTiO_3$ thin/thick films with $SrTiO_3$ coated 5 times were 1598 and 0.0436 at 10KHz.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.210-213
• /
• 2005

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated by the screen printing method on alumina substrates. The effect of the sintering temperature on the microstructure and dielectric properties of the $BaTiO_3/SrTiO_3$ thick films has been investigated. The relative dielectric constant and dielectric loss at 1 MHz of the $BaTiO_3/SrTiO_3$ heterolayered thick films with sintering temperature of $1350^{\circ}C$ were about 751 and 1.74, respectively. The remanent polarization $(P_r)$ of the pure $(Ba_{0.5}Sr_{0.5})TiO_3$ and $BaTiO_3/SrTiO_3$ heterolayered films are approximately $5.1\;{\mu}C/cm^2$ and $10\;{\mu}C/cm^2$. This study suggests that the design of the $BaTiO_3/SrTiO_3$ heterolayered thick films capacitor with different phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.609-612
• /
• 2002

In this study, the electrical properties were investigated for the deposited Ba,Sr)(Nb,Ti)$O_3$[BSNT] thin films grown on $Pt/TiO_2/SiO_2/Si$ substrate by RF sputtering method. The structural properties of the BSNT thin films affected by the $Ar/O_2$ rates were investigated. In the case of the BSNT thin films deposited with condition of 60/40$(Ar/O_2)$ ratio, the $BaTiO_3$, $SrTiO_3$ and $BaNbO_3$ phases were showed. The composition ratio of Nb and Ti in the BSNT thin films were nearly equivalent. Also, in the BSNT thin films deposited with condition of 60/40 and 80/20$(Ar/O_2)$ ratios, the composition of Ba, Sr, Nb and Ti were relatively uniform. The Ba, Sr, Nb and Ti in the BSTN thin films were not diffused into the Pt layer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.4
• /
• pp.317-321
• /
• 2003

In this study, the structural properties were Investigated for the deposited (Ba,Sr)(Nb,Ti)O$_3$[BSNT] thin films grown on Pt/TiO$_2$/SiO$_2$/Si substrate by RF sputtering method. The structural properties of the BSNT thin films affected by the Ar/02 ratios were Investigated. In the case of the BSNT thin films deposited with condition of 60/40(Ar/O$_2$) ratio, the BaTiO$_3$, SrTiO$_3$ and BaNbO$_3$ phases were showed. The composition ratio of Nb and Ti in the BSNT thin films were nearly equivalent. Also, in the BSNT thin films deposited with condition of 60/40 and 80/20(Ar/O$_2$) ratios, the composition of Ba, Sr, Nb and Ti were relatively uniform. The Ba, Sr, Nb and Ti in the BSTN thin films were not diffused into the Pt layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.400-403
• /
• 2004

The dielectric properties of $BaTiO_3/SrTiO_3$ multilayered thick films with printing times were investigated. $BaTiO_3/SrTiO_3$ thick films were deposited by Screen-printing method on alumina substrates. The obtained films were sintered at $1400^{\circ}C$ with bottom electrode(Pt) for 2hours. The structural and the dielectric properties were investigated for various printing times. The BST phase appeared in all of the $BaTiO_3/SrTiO_3$ mutilayered thick films. The $BaTiO_3/SrTiO_3$ multilayered thick film thickness, obtained by one printings, was $50{\mu}m$. The dielectric constant and dielectric loss of the $BaTiO_3/SrTiO_3$ multilayered thick film, obtained by five printings, were about 266, 0.8% at 1Mhz, respectively.

• Journal of Magnetics
• /
• v.13 no.2
• /
• pp.57-60
• /
• 2008

This study examined the effect of various types of epitaxial strain on the magnetic properties of $SrRuO_3$ thin films. Epitaxial $SrTiO_3$ (001), $SrTiO_3$ (110), and $SrTiO_3$ (111) substrates were used to apply different crystal symmetries to the grown films. The films were grown using pulsed laser deposition. The X-ray diffraction patterns of the films grown under optimum conditions showed very clear peaks for the $SrRuO_3$ film and $SrTiO_3$ substrates. The saturated magnetic moment at 5 K after 7 Tesla field cooling was $1.2-1.4\;{\mu}_B$/Ru. The magnetic easy axis for all three types of films was along the surface normal. The magnetic transition temperature for the $SrRuO_3$ film with lower symmetry was slightly larger than the $SrRuO_3$ film with higher symmetry.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.6
• /
• pp.429-435
• /
• 1999

The $SrTiO_3$ thin films were prepared on Ag/TiN-coated and p-type bare Si(100) substrates by r.f. magnetron sputtering deposition technique. The electrical properties of the deposited films were investigated, which controlling deposition parameters such as substrate temperature and film thickness. The electrical properties ofthe $SrTiO_3$ films were measured using the capacitance-voltage(C-V) technique. The thickness dependence of the electrical properties of the $SrTiO_3$ films was analyzed of the connection with the films in series. The substrate affected the crystal structure and texture characteristics of the $SrTiO_3$ films. The resistivity of the film, sandwiched between Al and Ag films was measured, as a function of the temperature.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.4
• /
• pp.543-548
• /
• 2018

Ferroelectric $Bi_4Ti_3O_{12}$ films were deposited on $SrTiO_3(100)$ and Si(100) substrate by using conductive $SrRuO_3$ films as underlayer, and their ferroelectric and electrical properties were investigated depending on crystal structure and orientation. C-axis oriented $Bi_4Ti_3O_{12}$ films were grown on well lattice-matched pseudo-cubic $SrRuO_3$ films deposited on $SrTiO_3(100)$ substrate, while random-oriented polycrystalline $Bi_4Ti_3O_{12}$ films were grown on $SrRuO_3$ films deposited on Si(100) substrate. The random-oriented polycrystalline film showed a good ferroelectric hysteresis property with remanent polarization ($P_r$) of $9.4{\mu}C/cm^2$ and coercive field ($E_c$) of 84.9 kV/cm, while the c-axis oriented film showed $P_r=0.64{\mu}C/cm^2$ and $E_c=47kV/cm$ in polarizaion vs electric field curve. The c-axis oriented $Bi_4Ti_3O_{12}$ film showed a dielectric constant of about 150 and lower thickness dependence in dielectric constant compared to the random-oriented film. Furthermore, the c-axis oriented $Bi_4Ti_3O_{12}$ film showed leakage current lower than that of the polycrystalline film. The difference of ferroelectric properties in two films was explained from the viewpoint of depolarization effect due to orientation of spontaneous polarization and layered crystal structure of bismuth-base ferroelectric oxide.