• 한국재료학회지
• /
• 제10권8호
• /
• pp.558-563
• /
• 2000

$Y_2SiO_5:Ce$ 형광체를 $In_2O_3$, $Al_2O_3$ 및 $SiO_2$로 코팅한 후 전계 방출 디스플레이에 요구되는 음극선 발광 특성을 조사하였다. $Al_2O_3$ 코팅으로 $Y_2$SiO(sub)5:Ce 형광체의 발광 효율과 에이징 특성은 감소되었다. 한편 $Al_2$$O_3$코팅으로 형광체의 발광효율은 증가하였으나 발광스펙트럼과 색좌표는 일부 변화하였다. 그러나 $Y_2SiO_5:Ce$ 청색 형과체의 발광 효율은 $SiO_2$코팅으로 크게 증가하였으며, 또한 $SiO_2$ 코팅한 $Y_2SiO_5:Ce$ 형광체의 에이징 특성은 코팅 전에 비하여 크게 향상되었다.

• 한국재료학회지
• /
• 제30권11호
• /
• pp.621-626
• /
• 2020

This study is aimed at preparing and evaluating the plasma resistance of YAS (Y₂O₃-Al₂O₃-SiO₂) coating layer with crystalline YAG phase contents. For this purpose, YAS frits with controlled phase contents are prepared and melt-coated on sintered Al₂O₃ ceramics. Then, the results of phase analysis of crystalline YAS coating layer are compared to that of YAS frits, and discussed with regard to the plasma resistance of the YAS coating layer. The phase contents of the YAS frit change in a manner different from that of the prepared YAS coating layer, presumably owing to the composition change of YAS frit during the melt-coating process. The plasma resistance of the YAS coating layer is shown to increase with the YAG phase contents in the coating layer. Comparing the weight loss of YAS coating layer with those of commercial Y₂O₃, Al₂O₃, and quartz ceramics, the plasma resistance of the prepared YAS coating layer is 8 times higher than that of quartz and 3 times higher than that of Al₂O₃; this layer shows 70 % of the resistance of Y₂O₃.

• 대한기계학회논문집A
• /
• 제33권7호
• /
• pp.652-657
• /
• 2009

Strength characteristics of $Si_3N_4$ composite ceramics has been studied as functions of heat-treatment temperature and additive $SiO_2$. $SiO_2$ colloidal could significantly increase the bending strength. Crack healing temperature decreased 300 K by additive $TiO_2$. Bending strength of specimen added $SiO_2$ is higher than that of non-added $SiO_2$. Moreover, bending strength of specimen with $SiO_2$ colloidal coating is much higher that of non-coated specimen. In in-situ observation, crack-healed specimen at 1,573 K shows phenomenon like a fog on the surface. By SPM, both crack-healed specimen, non-coating and coating of $SiO_2$ colloidal, at 1,273 K were healed completely but both of 1,573 K exist crack. This was made by evaporation of $SiO_2$ at high temperature. Crack-healing materials of $Si_3N_4$ composite ceramics is crystallized $Y_2Si_2O_7$, $Y_2Ti_2O_7$ and $SiO_2$. A large amount of Si and O, and little C were detected by EPMA. Si and O increase but C decreases according to heat treatment temperature. Specimens with additive $SiO_2$ were more detected Si and O than that of non-additive $SiO_2$. Specimen with $SiO_2$ colloidal coatings were much more detected O.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 추계학술대회 논문집
• /
• pp.590-593
• /
• 1999

$Y_2SiO_5$:Ce was considered as blue phosphor for field emission display because it had an excellent resistance against brightness saturation. But unfortunately It hadn't a sufficient brightness to be applied to FED. In this experiment It-$In_2O_3$, MgO and $SiO_2$ were coated onto $Y_2SiO_5$:Ce phosphor in order to improve the cathodoluminance(CL properties. The coating structures were identified to be the crystalline phases of $In_2O_3$ and MgO respectively. They had fine particle-like shape and were distributed on the surface of $Y_2SiO_5$:Ce phosphor. It was found that the CL efficiency of $Y_2SiO_5$:Ce phosphors were decreased after coatings with In20:j and MgO in voltage range from 500 V to 5 kV. But the brightness of $Y_2SiO_5$:Ce phosphor was increased after coating of 5 0 2 . And also the aging test showed that $In_2O_3$ coating improved the life time of $Y_2SiO_5$:Ce phosphor.

• ETRI Journal
• /
• 제31권6호
• /
• pp.675-679
• /
• 2009

$Ti_xSi_{1-x}O_y$ (TSO) thin films are fabricated using plasma-enhanced atomic layer deposition. The Ti content in the TSO films is controlled by adjusting the sub-cycle ratio of $TiO_2$ and $SiO_2$. The refractive indices of $SiO_2$ and $TiO_2$ are 1.4 and 2.4, respectively. Hence, tailoring of the refractivity indices from 1.4 to 2.4 is feasible. The controllability of the refractive index and film thickness enables application of an antireflection coating layer to TSO films for use as a thin film solar cell. The TSO coating layer on an Si wafer dramatically reduces reflectivity compared to a bare Si wafer. In the measurement of the current-voltage characteristics, a nonlinear coefficient of 13.6 is obtained in the TSO films.

• 한국표면공학회지
• /
• 제20권2호
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• 한국재료학회지
• /
• 제30권7호
• /
• pp.359-368
• /
• 2020

This study is aimed at improving the plasma resistance of Al₂O₃ ceramics on which plasma resistant YAS(Y₂O₃-Al₂O₃-SiO₂) frit is melt-coated using a simple heat-treatment process. For this purpose, the results of phase analysis and microstructural observations of the prepared YAS frits and the coating layers on the Al₂O₃ ceramics according to the batch compositions are compared and discussed with regard to the results of plasma resistance test. The prepared YAS frits consist of crystalline or amorphous or co-existing crystalline and amorphous phases according to the batch compositions, depending on the role and content of each raw material. The prepared YAS frit is melt-coated on the densely sintered Al₂O₃ ceramics, resulting in a dense coating layer with a thickness of at least ~ 80 ㎛. The YAS coating layer consists of crystalline YAG(Y₃Al₅O₁₂), Y₂Si₂O₇, and Al₂O₃ phases, and YAS glass phase. Plasma resistance of YAS coated Al₂O₃ ceramics is strongly dependent on the content of the YAG(Y₃Al₅O₁₂) and Y₂Si₂O₇ crystalline phases in the coating layer, especially on the content of the YAG phase. Comparing the weight loss of YAS coating ceramics with values obtained for commercial Y₂O₃, Al₂O₃, and quartz ceramics, the plasma resistance of the YAS coating ceramics is 6 times higher than that of quartz, 2 times higher than that of Al₂O₃, and 50 % of the resistance of Y₂O₃.

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.345-351
• /
• 2017

A double-layered anti-reflective coating with hydrophilic/abrasion-resistant properties was studied using anatase titanium dioxide($TiO_2$) and silicon oxycarbide($SiO_xC_y$) thin film. $TiO_2$ and $SiO_xC_y$ thin films were sequentially deposited on a glass substrate by DC sputtering and PECVD, respectively. The optical properties were measured by UV-Vis-NIR spectrophotometer. The abrasion-resistance and the hydrophilicity were observed by a taber abrasion tester and a contact angle analyzer, respectively. The $TiO_2/SiO_xC_y$ double-layer thin film had an average transmittance of 91.3%, which was improved by 10% in the visible light region (400 to 800 nm) than that of the $TiO_2$ single-layer thin film. The contact angle of $TiO_2/SiO_xC_y$ film was $6.9^{\circ}$ right after UV exposure. After 9 days from the exposure, the contact angle was $10.2^{\circ}$, which was $33^{\circ}$ lower than that of the $TiO_2$ single-layer film. By the abrasion test, $SiO_xC_y$ film showed a superior abrasion-resistance to the $TiO_2$ film. Consequently, the $TiO_2/SiO_xC_y$ double-layer film has achieved superior anti-reflection, hydrophilicity, and abrasion resistance over the $TiO_2$ or $SiO_xC_y$ single-layer film.

• Corrosion Science and Technology
• /
• 제7권4호
• /
• pp.233-236
• /
• 2008

Halide-activated pack cementation was utilized to deposit B-doped silicide coating. The pack powders were consisted of $3Wt.c/oNH_4Cl$, 7Wt.c/oSi, $90Wt.c/oAl_2O_3+TiB_2$. B-doped silicide coating was consisted of two layers, an outer layer of $NbSi_2$ and an inner layer of $Nb_5Si_3$. Isothermal oxidation resistance of B-doped silicide coating was tested at $1250^{\circ}C$ in static air. B-doped silicide coating had excellent oxidation resistance, because continuous $SiO_2$ scale which serves as obstacle of oxygen diffusion was formed after oxidation.

• 한국광학회지
• /
• 제13권5호
• /
• pp.396-399
• /
• 2002

전자선 증착기를 이용하여 1.3$\mu\textrm{m}$ 광모드 변환기가 집적된 반도체 레이저 출력 단면에 $SiO_2$와 $TiO_2$ 두 개의 박막 층으로 무반사 증착 하였다. 증착 단면의 최소 단면 반사율 $~ 10^{-5}$을 얻었고, $~ 10^{-4}$이하 단면 반사율 밴드 폭은 약 27nm임을 측정하였다. 이러한 코팅은 외부 공진기 레이저 광원 및 반도체 광 증폭기 등에 응용 가능하다.