• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.362-368
• /
• 2006

Epitaxial $Ba_{0.5}Sr_{0.5}TiO_3$ (BSTO) thin films have been grown on TiN buffered Si (001) substrates by Pulsed Laser Deposition (PLD) method and the effects of substrate temperature and oxygen partial pressure during the deposition on their dielectric properties and crystallinity were investigated. The crystal orientation, epitaxy nature, and microstructure of oxide thin films were investigated using X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM). Thin films were prepared with laser fluence of $4.2\;J/cm^2\;and\;3\;J/cm^2$, repetition rate of 8 Hz and 10 Hz, substrate temperatures of $700^{\circ}C$ and ranging from $350^{\circ}C\;to\;700^{\circ}C$ for TiN and oxide respectively. BSTO thin-films were grown on TiN-buffered Si substrates at various oxygen partial pressure ranging from $1{\times}10^{-4}$ torr to $1{\times}10^{-5}$ torr. The TiN buffer layer and BSTO thin films were grown with cube-on-cube epitaxial orientation relationship of $[110](001)_{BSTO}{\parallel}[110](001)_{TiN}{\parallel}[110](001)_{Si}$. The crystallinity of BSTO thin films was improved with increasing substrate temperature. C-axis lattice parameters of BSTO thin films, calculated from XRD ${\theta}-2{\theta}$ scans, decreased from 0.408 m to 0.404 nm and the dielectric constants of BSTO epitaxial thin films increased from 440 to 938 with increasing processing oxygen partial pressure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.171-174
• /
• 1994

The drive towards ultra-large-scale integrated circuits a continuous intermetal dielectric films for multi layer interconection. Optimum condition of remote plasma enhanced chemical vapour deposition(RPECVD) was achieved by orthogonal array method. Chracteristics of SiO$_2$ films deposited by using remote PECVD with N$_2$O gas were investigated. Etching rate of SiO$_2$ films in P-echant was about 6[A/s] that was the same as the thermal oxide. The films a showed high breakdown voltage of 7(MV/cm) and a resistivity of Bx10$\^$13/[$\Omega$cm] at 7(MV/cm). The interface Trap density of SiO$_2$ has been shown excel lent properties of 5x10$\^$10/[/$\textrm{cm}^2$eV]. It was observed that the dielectric constant dropped to a value of 4. 29 for 150 [W] RF power.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.208-211
• /
• 2003

The dielectric carbon nitride thin films were deposited onto Si(100) using a pulsed laser ablation of pure graphite target combined with a high voltage discharge plasma in nitrogen gas atmosphere. We can be calculated dielectric constant, ${\varepsilon}_s$, with a capacitance Sobering bridge method. We reported to investigate the influence of the laser ablation of graphite target and DC high voltage source for the plasma. The properties of the deposited carbon nitride thin films were influenced by the high voltage source during the film growth. Deposition rate of carbon nitride films were found to increase drastically with the increase of high voltage source. Infrared absorption clearly shows the existence of C=N bonds and $C{\equiv}N$ bonds. The carbon nitride thin films were observed crystalline phase, as confirmed by x-ray diffraction data.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.160-161
• /
• 2005

The $(Sr_{1-x}Ca_x)TiO_3$(SCT) thin films are deposited on Pt-coated electrode (Pt/TiN/$SiO_2$/Si) using RF sputtering method with substitutional contents of Ca. The optimum conditions of RF power and $Ar/O_2$ ratio were 140[W] and 80/20, respectively. Deposition rate of SCT thin film was about 18.75$[{\AA}/min]$. The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mol%]. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200[kHz].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.92-95
• /
• 2000

The $(Sr_{1-x}Ca_x)TiO_3$(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/$SiO_2$/Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained at SCT15 thin film. The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mol%]. The dielectric constant changes almost linearly in temperature ranges of -80~+90$[^{\circ}C]$. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200[kHz].

• Proceedings of the KIEE Conference
• /
• 1999.11a
• /
• pp.31-34
• /
• 1999

In the present study, we fabricated stoichiometric $(Ba_{1-x}Sr_x)TiO_3$ thin films at various substrate temperature and contents using of magnetron sputtering method on optimized Pt-based electrodes (Pt/TiN/$SiO_2$/Si). The substate temperature deposited at 200[ $^{\circ}C$], 400[$^{\circ}C$] and 600[$^{\circ}C$] and crystalline BST thin films show above 400[$^{\circ}C$]. Also, the composition of $(Ba_{1-x}Sr_x)TiO_3$ thin films deposited on Si wafer substrate at 400[$^{\circ}C$] were closed to stoichiometry($1.015{\sim}1.093$ in A/B ratio), but compositional deviation from a stoichiometry is larger as $SrCO_3$ is added. The drastic decrease of dielectric constant and increase of dielectric loss in $(Ba_{1-x}Sr_x)TiO_3$thin films is observed above 100[kHz]. V-I characteristics of $(Ba_{1-x}Sr_x)TiO_3$ thin films show the decrease of leakage current with the increase of $SrCO_3$ contents.

• Transactions on Electrical and Electronic Materials
• /
• v.1 no.1
• /
• pp.22-25
• /
• 2000

Polycrystalline SBTN layered ferroelectric thin film with various Nb mole ratios were prepared by sol-gel method Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperature and characterized in terms of phase and microstructure. The films were crystallized with a high (105) diffraction intensity and had rodike structure, SBTN films fired at 800$^{circ}C$ revealed standard hysteresis loops with no fatigue for up to 10$^{10}$ cycles. At an applied voltage of 5V the dielectric constant($varepsilon$) , dissipation factor (tan $delta$), remanent polarization(ZPr) and coercive field(Ec) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$) $O_{9+}$$alpha$/ thin film(x=0.1) prepared on Pt/ $SiO_2$/Si (100) were about 277.7, 0.042, 3.74$mu$C/$textrm{cm}^2$, and 24.8kv/cm respectively.ly.y. respectively.ly.y.y..

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.325-329
• /
• 1998

In this paper, the (Sr$_{1-x}$ Ca$_{x}$)TiO$_3$(SCT) thin films were deposited at various substrate temperature using RF magnetron sputtering method on optimized Pt-coated electrodes (Pt/TiN/SiO$_2$/Si). An influence of substrate temperature and annealing temperature on the structural and dielectric properties are investigated. The substrate temperature changed from 100[$^{\circ}C$] to 500[$^{\circ}C$] and crystalline SCT thin films were deposited abode 400[$^{\circ}C$]. All thin films had (111) preferred orientation, the (100) oriented films were obtained at the substrate temperature above 400[$^{\circ}C$]. The dielectric constant changes almost linearly in the temperature region of -80~+90[$^{\circ}C$], the temperature characteristics of the dielectric loss exhibited a stable value within 0.1, then not affected by substitutional contents. The capacitance characteristics appears a stable value within $\pm$5[%].

• Journal of the Korea Institute of Military Science and Technology
• /
• v.21 no.6
• /
• pp.760-766
• /
• 2018

The present study investigates the effect of PMMA and BN content on microstructure, mechanical and dielectric properties of silicon nitride($Si_3N_4$) ceramics in $Y_2O_3-Al_2O_3$ additive system. The total additive content was fixed at 8 wt.% and the amount of PMMA varies from 0 to 40 wt.% and BN varies from 0 to 36 wt.%, respectively. The crystalline phases of the samples were determined by X-ray diffraction analysis. All the sintered sample shows complete transformation of ${\alpha}$ to ${\beta}-Si_3N_4$ during the sintering process indicated that the phase transformation was unaffected by the PMMA or BN content. However, the microstructure shows that the residual porosity increased with increasing PMMA and BN content. In addition, the flexural strength and the dielectric constant decrease with addition of PMMA and BN due to the residual porosity. This article provides empirical study of design parameters for $Si_3N_4$-based radome materials.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.10
• /
• pp.559-563
• /
• 2000

The $(Sr_{1-x}Ca_x)TiO_3(SCT)$ thin films are deposited on Pt-coated(Pt/TiN/$SiO_2$/Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained by substitution of Ca at 15[mol%]. Also the composition of SCT thin films were closed to stoichiometry(1.081∼1.117 in A/B/ ratio). The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mol%]. The dielectric constant changes almost linearly in temperature ranges of -80∼+90[^${\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 2000[kHz]. The current-voltage characteristics of SCT15 thin films showed the increasing leakage current as the measuring temperature increase.