• Journal of Ceramic Processing Research
• /
• v.20 no.1
• /
• pp.18-23
• /
• 2019

Chemical looping combustion (CLC) is a promising carbon capture and storage (CCS) technology whose efficiency and cost primarily relies on the oxygen carrier materials used. In this paper, gadolinium-doped ceria (GDC, Ce0.9Gd0.1O1.95) was added as a promoter to improve the oxygen transfer rate of MgMnO3-δ oxygen carrier materials. Increasing GDC content significantly increased the oxygen transfer rate of MgMnO3-δ-GDC composites for the reduction reaction due to an increase in the surface adsorption of CH4 via oxygen vacancies formed on the surface of the GDC. On the other hand, the oxygen transfer rate for the oxidation reaction decreased linearly with increasing GDC content due to the oxygen storage ability of GDC. Adsorbed oxygen molecules preferentially insert themselves into oxygen vacancies of the GDC lattice rather than reacting with (Mg,Mn)O to form MgMnO3-δ during the oxidation reaction.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.170-175
• /
• 2004

The ferroelectric (Y $b_{x}$ $Y_{1-x}$)Mn $O_3$ thin films were fabricated by sol-gel method using Y-acetate, Yb-acetate, and Mn-acetate as raw materials. The stable (Y $b_{x}$ $Y_{1-x}$)Mn $O_3$ precursor solution (sol) was prepared through the reflux process with acetylaceton as a catalyst and coated on Si(100) substrate by spin coating. The heat treatment temperature and, Rw ($H_2O$/alkoxide moi ratio) dependence on crystallinity of thin films were studied. The lowest temperature for obtaining YbMn $O_3$phase and the optimum heat-treatment conditions were proved as at 7$50^{\circ}C$ and 80$0^{\circ}C$, respectively. The hexagonal YbMn $O_3$with c-axis preferred orientation could be obtained at Rw=1 condition. The remanent polarization for the thin films of x=0 or 1 was about 200 nC/㎤ while, for the specimens ot 0< x< 1, were 50∼100 nC/$\textrm{cm}^2$.

• Proceedings of the Korea Crystallographic Association Conference
• /
• 2003.05a
• /
• pp.8-8
• /
• 2003

Electron-phonon interaction plays a significant role in forming of colossal magnetoresistance effect (CMR). Polaron formation was observed by neutron diffraction and by extended X-ray absorption fine structure (EXAFS) analysis. Local probe as given by the EXAFS is a useful method to study the polaronic charge and its dependence on temperature and ions size. Here we present the EXAFS study of polaronic charge in La/sub 0.7/Ca/sub 0.3-X/Ba/sub X/MnO₃ compositions. The single phase La/sub 0.7/Ca/sub 0.3-X/Ba/sub X/MnO₃ manganites (x=0; 0.03; 0.06, ..., 0.3) were prepared by ceramic technology [1]. The Curie temperature was determined by extrapolation of the temperature dependence of the magnetization (down to zero magnetization). EXAFS experiments were carried out at the 7C EC beam line of the Pohang Light Source (PLS) in Korea. The atomic pair distribution functions (PDF) were obtained by re-regularization method [2] from filtered spectra. The PDF for the x=0.3 sample showed a single peak function and for x=0.0, 0.03, 0.06, 0.09, 0.12 compositions were asymmetric in agreement with a small Jahn-Teller elongation of two (short and long) bonds of the MnO/sub 6/ octahedron. Dispersion, σ/sub Min-O//sup 2/, and asymmetry, σ/sub Min-O//sup 3/, of the Mn-O bond distances varied significantly with x and showed a maximums at x=0.09. The maximum of σ/sub Min-O//sup 2/ is caused by increase of dynamic rms displacements of the Mn-O distances near the T/sub C/. The observed x dependence of σ/sub Min-O//sup 3/ reflects the reduction of charge carriers mobility at approaching to T/sub C/ from low as well as high temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.3
• /
• pp.216-221
• /
• 2010

Employing statistical design of experiments, the difference in doping behaviors of rare-earth ions and their effects on the dielectric property and microstructure of $BaTiO_3$-MgO-$MnO_2$-($Ba_{0.4}Ca_{0.6}$) $SiO_3-Re_2O_3$ (Re = $Y_2O_3$, $Er_2O_3$) system were investigated. Through the statistical analysis we have found that the amount of $Re_2O_3$ are significantly affecting on the dielectric properties. The $Re_2O_3$ improved the dielectric constant, dielectric loss and R*C constant, so the appropriate contents of $Y_2O_3$ and $Er_2O_3$ were 0.8 ~ 1.2 mol% and 0.8 ~ 1.3 mol%, respectively. The MLCC(mutilayer chip capacitor) with $2.0{\times}1.2{\times}1.2mm$ size and 475 nF was also suited for X7R with the above composition. It showed that the dielectric constant and RC constant were 2,839 and 3,675 ${\Omega}F$, respectively in the sintering condition at $1250^{\circ}C$ in $Po_2$ $10^{-7}$ Mpa.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.297-297
• /
• 2008

Buffer layers play an important role in the development of high critical current density coated conductor. $LaMnO_3$, $SrTiO_3$ and $BaZrO_3$ buffer layers were compatible with MgO surfaces and also provide a good template for growing high current density REBCO(RE=Rare earth) films. Systematic studies on the influences of pulsed laser deposition parameters (deposition temperature, deposition pressure, processing gas, laser energy density, etc.) on microstructure and texture properties of $LaMnO_3$, $SrTiO_3$ and $BaZrO_3$ films as buffer layer deposited on ion-beam assisted deposition MgO (IBAD_MgO) template by pulse laser deposition method, were carried out. These results will be presented together with the discussion on the possible use of this material in HTS coated conductor as buffer.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.782-785
• /
• 1995

In this paper, $Mn^{2+}$ ion was doped in Y-Ba-Cu-O as an EPR probe. The following samples were prepared by conventional solid-state reaction method : $YBa_{2}Cu_{2.96}Mn_{0.04}O_{7-\delta}$ (MN-I), annealed $YBa_{2}Cu_{2.96}Mn_{0.04}O_{7-\delta}$ (AMN) and $YBa_{2}Cu_{2.94}Mn_{0.06}O_{7-\delta}$ (MN-II). AMN sample was obtained from MN-I by annealing for 1 hr under the Ar gas atmosphere at $600^{\circ}C$. X-band (~9.05 GHz) EPR spectra were measured from 103 K to room temperature by employing a JES-RE3X spectroscopy with a $TE_{0.11}$ cylindrical cavity and 100 kHz modulation frequency. In MN-I we have observed only the $Cu^{2+}$ signal. The fact that no $Mn^{2+}$ signal was observed, in spite of $Mn^{2+}$ being a very sensitive EPR probe, indicates that most likely isolated $Mn^{2+}$ ions don't exist in the MN-I sample. Most probably $Mn^{2+}$ ions in the MN-I sample interact antiferromagnetically and hence are EPR silent. The AMN spectra of at room temperature and 103 K indicate not only the $Cu^{2+}$ signal but also an extra signal, which increases with decreasing temperature. It is suggested that the extra signal originates from Mn ions that were antiferromagnetically coupled before the annealing process. In MN-II, from 103 K to room temperature, also, the extra signal was observed together with the $Cu^{2+}$ signal. The extra signal in MN-II, however, decreases with decreasing temperature and nearly disappears at 103 K. The signal originates from Mn ions in impurity phases that include $Mn^{2+}$ ions. We suppose that there exist at least two $Mn^{2+}$ doped phases in Y-Ba-Cu-O. The $Mn^{2+}$ signal of one phase is undectable at all temperature and that of another phase decreases with decreasing temperature and disappears around 103 K.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.216-219
• /
• 2011

Perovskite manganites such as $RE_{1-x}A_xMnO_3$ (RE = rare earth, A = Ca, Sr, Ba) have been the subject of intense research in the last few years, ever since the discovery that these systems demonstrate colossal magnetoresistance (CMR). The CMR is usually explained with the double-exchange (DE) mechanism, and CMR materials have potential applications for magnetic switching, recording devices, and more. However, the intrinsic CMR effect is usually found under the conditions of a magnetic field of several Teslas and a narrow temperature range near the Curie temperature ($T_c$). This magnetic field and temperature range make practical applications impossible. Recently, another type of MR, called the low-field magnetoresistance(LFMR), has also been a research focus. This MR is typically found in polycrystalline half-metallic ferromagnets, and is associated with the spin-dependent charge transport across grain boundaries. Composites with compositions $La_{0.7}(Ca_{1-x}Sr_x)_{0.3}MnO_3)]_{0.99}/(BaTiO_3)_{0.01}$ $[(LCSMO)_{0.99}/(BTO)_{0.01}]$were prepared with different Sr doping levels x by a standard ceramic technique, and their electrical transport and magnetoresistance (MR) properties were investigated. The structure and morphology of the composites were studied by X-ray diffraction (XRD) and scanning electronic microscopy (SEM). BTO peaks could not be found in the XRD pattern because the amount of BTO in the composites was too small. As the content of x decreased, the crystal structure changed from orthorhombic to rhombohedral. This change can be explained by the fact that the crystal structure of pure LCMO is orthorhombic and the crystal structure of pure LSMO is rhombohedral. The SEM results indicate that LCSMO and BTO coexist in the composites and BTO mostly segregates at the grain boundaries of LCSMO, which are in accordance with the results of the magnetic measurements. The resistivity of all the composites was measured in the range of 90-400K at 0T, 0.5T magnetic field. The result indicates that the MR of the composites increases systematically as the Ca concentration increases, although the transition temperature $T_c$ shifts to a lower range.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2008.02a
• /
• pp.340-340
• /
• 2008

• Journal of Korean Society of Environmental Engineers
• /
• v.27 no.5
• /
• pp.513-518
• /
• 2005

Catalytic oxidation of toluene on the manganese oxide catalysts and manganese-cerium oxide catalysts was investigated. The catalysts were characterised by X-ray diffraction(XRD), thermo gravimetric analyzer(TGA), toluene-temperature program reduction(Toluene-TPR). We found that the optimal manganese content was 18.2 wt.% and the optimal cerium content was 10.0 wt.% at catalytic oxidation of toluene. It is shown that ceria improves the activity of manganese oxide phases. From the XRD results, it was estimated that $MnO_2$ phase was active site in the monometallic and bimetallic catalysts. From the TGA and Toluene-TPR results, it show that ceria improves the mobility of the lattice oxygen, adequate oxidation state of the active phase, reduction ability at low temperature, and re-oxidation of the active site.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.814-817
• /
• 2005

In order to enhance energy efficiency in high electric conversion devices such as Power transformers, which need to have high power properties, an alloy design approach in $Pb(Zr,Ti)O_3(PZT)$ base ceramic system was attempted $0.03Pb(Sb_{0.5}Nb_{0.5})O_3-0.03Pb(Mn_{1/3}Nb_{2/3})O_3-(0.94-x)PbTiO_3-xPbZrO_3$[PSN-PMN- PZT] ceramics were synthesized by conventional bulk ceramic processing technique. To improve power properties, the various Zr/Ti ratio was varied ]lear their morphotropic phase boundary (MPB) composition of PSN-PMN-PZT system and their effects on subsequent piezoelectric and dielectric properties for the transformer application at high power were systematically investigated using an impedance analyzer. Microstructure and phase information were characterized using X-ray diffractometer (XRD), a scanning electron microscope (SEM) and others. When the Zr/Ti ratio was 0.415/0.465, the value of $Q_m\;and\;k_p$ were shown to reach to the maximum, indicating that this alloy design can be a feasible composition :or high power transformer.