• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.665-670
• /
• 1998

Ferroelectric anomaly in PbO-{{{{ { {B }_{2 }O }_{3 } }}-{{{{ {TiO }_{3 } }}-BaO glasses which is observed in DAT measurements was in-vestigated together with the effect of BaO content on the shift of Cuire temperature. The temperature where the ferroelectric anomaly apperars on cooling in DTA decreased in proportion with increasing BaO content,. For as-crystallized samples the ferroelectric anomaly was not observed on heating but on cooling whilist for powder samples leached chemically from the crystallized samples both endothermic and ex-otehrmic peaks were observed. This fact suggests that the appearance of the ferroelectric anomaly in DAT largely depends on glassy phases surrounding individual {{{{ {PbTiO }_{3 } }} crystals rather than effects of grain size and crystallinity.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.418-424
• /
• 2000

Pure $TiO_2$and 10 mol % Pb-doped $TiO_2(Pb_xTi_{1-x}O_2$(x = 0.1)) powder and thin films have been prepared by the sol-gel method. Titanium isopropoxide and ethanol are used for pure $TiO_2$, lead acetate trihydrate and titanium triisopropoxide monoacethylacetonate are used for Pb-doped $TiO_2$, respectively. Films are coated on p-type Si(100) wafer and ITO glass substrates by the sol-gel spin-coating method. The powder and multi-coated films are annealed at different temperature (400~$800^{\circ}C$) for phase formation and crystallization. TGA/DTA, XRD analysis, SEM and UV-visible transmission spectroscopy have been used to study the characteristics of the powder and films. XRD results show that the films are polycrystalline, anatase type and oriented predominantly to the A(101) plane. A slight shift in the d-spacing for the Pb-doped film indicates the incorporation of the Pb into $TiO_2$lattice. A shift of the absorption wavelength in the transmission spectrum towards longer wavelength has been observed about $Pb_xT_{1-x}O_2$(x = 0.1) thin film, which indicates a decrease in the bandgap of $TiO_2$upon Pb-doping.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.8
• /
• pp.858-868
• /
• 1992

0.085Ba(LaS11/2TNbS11/2T)OS13T-0.915Pb(ZrS1yTTiS11-yT)OS13T (0.45$\leq$y$\leq$0.65) transparent electrooptic ceramics were fabricated by two-stage sintering method. The structural, ferroelectric and electrooptic properties were investigated varying composition and second sintering time. Also the possibility of application to electrooptic device was studied. If we increase the PbZrOS13T contents, dielectric constants were increased and Curie temperature was decreased. In the composition of 0.55[mol] PbZrOS13T, electromechanical coupling factor and piezoelectric charge constant were the highest values of 43[%] and 173x10S0-12T[C/N], respectively. Mechanical quality factors were decreased with the increasing PbZrOS13T contents. Light transmittance was increased with wavelength when measured from 300[nm] to 900[nm], and with PbZrOS13T contents in the range of 0.50[mol]-0.65[mol], and had the highest value of 67[%] in the composition of 0.65[mol] PbZrOS13T. From the results of ferroelectric hysteresis loop and transmitted light intensity with electric field, the specimens with compositions of 0.65,0.60,0.55[mol] PbZrOS13T were applicable to electrooptic memory device and those with compositions of 0.50,0.45[mol] PbZrOS13T were applicable to linear electrooptic device.

• Electrical & Electronic Materials
• /
• v.10 no.2
• /
• pp.134-140
• /
• 1997

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb $_{2}$3/O$_{3}$)(PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol rates of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20) and #4(40:40:20), respectively. The spin-coated PZT-PNN films were sintered at the temperature from 500.deg. C to 600.deg. C for crystallization. The P-E hysteresis curve was drawn by Sawyer-Tower circuit with PZT-PNN film. The coercive field and the remanent polarization of #4(40:40:20 mol%) PZT-PNN film were 28.8 kV/cm and 18.3 .mu.C/cm$^{2}$, respectively. Their dielectric constants were shown between 128 and 1120, and became maximum value in MPB(40:40:20 mol%). The leakage currents of PZT-PNN films were about 9.4x 10$^{-8}$ A/cm$^{2}$, and the breakdown voltages were about 0.14 and 1.1 MV/cm. The Curie point of #3(45:35:20 mol%, sintered at 600.deg. C) film was 330.deg. C.

• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.581-586
• /
• 1994

Effect of excess and deficiency of PbO on the sintering and electrical properties of tetragonal Pb(Zr0.5Ti0.5)O3 were investigated. Fired density revealed maximum value with 4 wt% of excess PbO, and decreased with increasing amount of both excess and deficient PbO. Grain size increased with excess PbO, and decreased with deficiency of PbO. It appeared that excess PbO forms a liquid phase to enhance grain growth and completely volatilizes after sintering, whereas ZrO2 particles formed in PbO-deficient PZT inhibit grain growth. The change in the values of the equivalent circuit elements of PZT corresponded well with thar of porosity formed by excess and deficiency of PbO; kp, Co and Cm decreased while Qm, Rm and Lm increased conosiderably with porosity. This change was more pronounced in PbO-deficient type probably due to change in Zr/Ti ratio of PZT.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.2
• /
• pp.71-76
• /
• 1992

Piezoceramic filters were fabricated by adding $MnO_2 and FeZ0_3$ to the $0.05Pb(Al_{2/3}W_{1/3})O_3-0.95Pb(Zr_{0.52}Ti0.48)O_3$ system using photolithography method. As the amounts of $MnO_2$ increased, the electro-mechanical coupling factor(Kp) decresed. On the other hand, for $Fe_2O_3$ added samples, Kp was 57%, but mechanical quality factor(Qm) showed relatively low value. The passband widths were 155kHz for 0.3wt % $MnO_2$ addition and 260kHz for 0.1 wt % $Fe_2O_3$ addition, and were inversely propotional to Qm values. Group delay time characteristics showed Gausian for $MnO_2$ additions and Butterworth for$Fe_2O_3$ additions.

• Electrical & Electronic Materials
• /
• v.1 no.2
• /
• pp.152-161
• /
• 1988

Pb(Zr, Ti)O$^{3}$-Pb(Mg, Nb)O$^{3}$계에 MnO$_{2}$첨가량을 변화시켜 소결성, 미세구조, 유전상수, 비저항 및 압전특성에 미치는 영향을 XRD, EDAX 및 SEM을 이용하여 미세구조를 관찰하고 실험을 통하여 전기적 성질에 미치는 영향을 밝혔다. 비저항의 변화없이 그레인 성장이 억제되는 $MnO_{2}$의 첨가량은 0.4wt%이었으며 이때 분말의 합성이 촉진되어 소성된 시편의 밀도가 증가하였다. 그러나 고상반응의 범위를 벗어나는 과잉 $MnO_{2}$는 편석이 되어 그레인 경계상에 모임이 확인되었고 또한 기공을 형성하여 밀도를 낮추었다. $Mn^{+4}$는 $Mg^{+2}$ 와 치환되어 페로브스카이트 구조의 "A" 결핍을 유발하였으며 이것이 비저강을 감소시키는 원인으로 밝혀졌다.감소시키는 원인으로 밝혀졌다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1993.11a
• /
• pp.10-13
• /
• 1993

ln this study, x PSN - y PT - z PZ ceramics doped with w MnO$_2$were fabricated by the mixed oxide method at 1250[$^{\circ}C$] for 2[hr] and then the dielectric and pyroelectric properties were investigated. In the 0.05 PSN - 0.4 PT - 0.55 PZ specimen with 0.5[wt.%] MnO$_2$, the pyroelectric coefficient was 6.6${\times}$10$\^$-8/[C/cm$^2$$.$$^{\circ}C$], respectibly.

• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.286-291
• /
• 1998

Dielectric properties of $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$, ceramics prepared by the columbite precursor method have been investigated as a function of the sintering temperature in the range of 1000∼$1250^{\circ}C$. The $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$ ceramics show typical relaxor ferroelectric behavior. As the sintering temperature increased, the dielectric constant increased and the phase transition temperature shifted to lower temperature. The TCK(temperature coefficient of dielectric constant) and VRK (variation rate of dielectric constant) increased with increasing sintering temperature. The $Pb(Mg_{1/3}Nb_{2/3})O_{3}-PbTiO_{3}$ compositions sintered at $1250^{\circ}C$ appear to be suitable for ferroelectric bolometer.

• Electrical & Electronic Materials
• /
• v.6 no.3
• /
• pp.241-247
• /
• 1993

본 연구에서는 투광성 0.085Ba(L $a_{1}$2/N $b_{1}$2/) $O_{3}$- 0.915Pb(Z $r_{y}$ $Ti_{1-y}$) $O_{3}$(0.45.leq.y.leq.0.70)세라믹을 2단 소성법으로 제작한 후, PbZr $O_{3}$조성 및 온도에 따른 구조적, 강유전적특성을 측정하였다. XRD측정 결과, PbZr $O_{3}$조성이 감소할수록 결자상수 및 단위격자 체적은 감소하였으며 시편의 결정구조는 입방정계에서 능면체정계, 정방정계로 변화되었다. 8.5/60/40시편의 경우 포화분극, 잔류분극 및 항전계가 각각 33.28[.mu.C/$cm^{2}$], 4.15[kV/cm]로 전형적인 메모리 특성을 나타내었으며 PbZr $O_{3}$조성이 증가함에 따라 강유전 이력곡선은 slim loop특성을 나타내었다. 잔류분극은 온도가 증가함에 따라 감소하였으며 특히 PE-FE상경계 부근에 위치한 조성의 경우, 상전이 온도 이하의 온도에서 급격히 감소하는 경향을 나타내었다.다.