• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.210-220
• /
• 1989

The properties of the powder of Al2O3-15v/o ZrO2(＋3m/o Y2O3) system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide decreased the specific surface area of aluminum hydroxide of AlOOH type, while increased the specific surface area of aluminum hydroxide of Al(OH)3 type, and formed co-network structure of Al-O-Zr type with the aluminum hydroxides. The rate of transition to $\alpha$-Al2O3 from co-precipitated materials occurred in the order of 7≒10, 9 and 11 of pH values. Al2O3 and ZrO2 interacted to bring about coupled grain growth, and the growth of ZrO2 crystallite size rapidly occurred within $\theta$-Al2O3 matrix. Segregation did not occur in the system Al2O3-15v/o ZrO2(＋3m/o Y2O3) and Y2O3 acted as a stabilizer to ZrO2. The lattice strain of tetragonal ZrO2 was increased by the constraint effect of Al2O3 matrix.

• The Journal of Natural Sciences
• /
• v.8 no.2
• /
• pp.111-118
• /
• 1996

In order to improve the chemical durability of glass in the $Na_2O$-CaO-$SiO_2$ system, it was investigated in the effect of $B_2O_3$ and ZnO addition and changing amount of each composition, $Na_2O$, $Al_2O_3$, $Li_2O$. In this minimize the change of softening point of glass was as follow.(wt%)$B_2O_3$:3.36%, ZnO:2.88%, $Na_2O$:9.93%, $Al_2O_3$, $Li_2O$:0.19%, $SiO_2$:70.56%, CaO:11.22%, $K_2O$:0.14%

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.305-314
• /
• 1991

This study was conducted to research the formation and the color development of NiO-ZnO-Fe2O3-TiO2-SnO2 system for the purpose of synthesizing the spinel pigments which are stable at high temperature. After preparing ZnO-Fe2O3 as a basic composition, {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.Fe2O3 system, {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.TiO2 system, and {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.SnO2 system were prepared with {{{{ chi }}=0, 0.2, 0.5, 0.7, 1 mole ratio respectively. The manufacturing was carried out at 128$0^{\circ}C$ for 30 minutes. The reflectance measurement and the X-ray analysis of these specimens were carried out and the results were summarized as follows. 1. In the specimens which included NiO, it was difficult for the spinel structure to be formed. 2. As increasing the contents of NiO and Fe2O3, all the groups which were yellow or green colored changed to brown. 3. NiO-ZnO-Fe2O3 system and NiO-ZnO-TiO2 system formed the spinel structure and the illmenite structure appeared in NiO-TiO2 system.

• Journal of the Korean Chemical Society
• /
• v.51 no.3
• /
• pp.240-243
• /
• 2007

The eight coordinated yttrium(III) complex Y(tpb)3(H2O)2 (Htpb=4,4,4-Trifluoro-1-phenyl-1,3-butanedione) has been synthesized and structurally characterized by X-ray diffraction method. The coordination polyhedron of Y(tpb)3(H2O)2 has a dodecahedron. The angle between two trapezia, Y-O2-O1-O5-O6 and Y-O4-O3-O8-O7, is 89.59°. The O1-O5 and O3-O8 distances are 2.965 and 2.995 A whereas the O2-O6 and O4-O7 distances are 4.256 and 4.403 A.

• Journal of the Korean Society of Safety
• /
• v.20 no.4 s.72
• /
• pp.29-33
• /
• 2005

In this paper, reflectance and the dielectric characteristics for $P_2O_5-ZnO-BaO$ system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ and the reflectance of $P_2O_5-ZnO-BaO$ system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5-ZnO-BaO$ system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can be explained as the space charge effects. These results are could be applied to the under plate dielectrics of PDP required high reflective ratio and breakdown strength.

• Journal of the Korean Ceramic Society
• /
• v.31 no.2
• /
• pp.213-219
• /
• 1994

The formations of spinel and colors of ZnO-Fe2O3-TiO2-SnO2 system have been researched on the basis of ZnO-Fe2O3 system. Specimens were prepared by substituting Fe3+, with Ti4+ or Sn4+ when mole ratios between Fe3+ and Ti4+ or between Fe3+ and Sn4+ were 0.2 mole. The reflectance measurement and X-ray diffraction analysis of the formation of spinel and the colors of there specimens were carried out. ZnO-Fe2O3 system in which Fe2O3 was substituted with SnO2 and TiO2 was formed the spinel structure of 2ZnO.TiO2, 2ZnO.SnO2, ZnO.Fe2O3. The stable stains which were colored with yellow and brown could be manufactured.

• Applied Chemistry for Engineering
• /
• v.18 no.4
• /
• pp.314-319
• /
• 2007

The destruction of synthetic acetic acid wastewater was carried out using UV, $O_3$, $H_2O_2$, $Fe^{2+}$ oxidants in various combinations by the advanced oxidation processes. $UV/H_2O_2$, $UV/H_2O_2/Fe^{2+}$, $O_3$, $O_3/H_2O_2$, $UV/O_3/H_2O_2$, $UV/O_3/H_2O_2/Fe^{2+}$ processes were tested. $UV/H_2O_2/Fe^{2+}$, $O_3/H_2O_2$, $UV/O_3/H_2O_2$, $UV/O_3/H_2O_2/Fe^{2+}$ processes shows the most effective destruction efficiency at low pH (3.5) condition of wastewater, but $UV/H_2O_2$ and $O_3$ processes were observed less than 20%. Destruction efficiency was gradually increased with the reaction time in the $O_3/H_2O_2$ and $UV/O_3/H_2O_2$ processes, in case of the $UV/H_2O_2/Fe^{2+}$ and $UV/O_3/H_2O_2/Fe^{2+}$ processes shows rapid increasing of destruction efficiency within 90 min, then slightly decreasing with time. The destruction efficiencies of $UV/H_2O_2/Fe^{2+}$, $O_3/H_2O_2$, $UV/O_3/H_2O_2$ and $UV/O_3/H_2O_2/Fe^{2+}$ processes were observed 55, 66, 66 and 64%, respectively.

• 전자공학회논문지 IE
• /
• v.43 no.4
• /
• pp.8-12
• /
• 2006

In this paper, reflectance and the dielectric characteristics for $P_2O_5$-ZnO-BaO system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ contents, and the reflectance of $P_2O_5$-ZnO-BaO system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5$-ZnO-BaO system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can explained as the space charge effects. These results are could be applied to the lower dielectrics layer of PDP required high reflective ratio and breakdown strength.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.11
• /
• pp.3991-3995
• /
• 2011

$TiO_2-SiO_2-In_2O_3$ nanocomposite thin film was deposited on the glass substrates using a dip coating technique. The morphology, surface composition, surface hydroxyl groups, photocatalytic activity and hydrophilic properties of the thin film were investigated by AFM, XPS, methyl orange decoloring rate and water contact angle measurements. The hydroxyl content for $TiO_2$, $TiO_2-SiO_2$ and $TiO_2-SiO_2-In_2O_3$ nanocomposite films was calculated to be 11.6, 17.1 and 20.7%, respectively. $TiO_2-SiO_2-In_2O_3$ film turned superhydrophilic after 180-min irradiation with respect to pure $TiO_2$ and $TiO_2-SiO_2$ thin films. The photocatalytic decomposition of methyl orange for $TiO_2$, $TiO_2-SiO_2$ and $TiO_2-SiO_2-In_2O_3$ thin films was measured as 38.19, 58.71 and 68.02%, respectively. The results indicated that $SiO_2$ and $In_2O_3$ had a significant effect on the hydrophilic, photocatalytic and self-cleaning properties of $TiO_2$ thin film.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.117-124
• /
• 1988

The properties of the powders of the system Al2O3-ZrO2-Y2O3 prepared by precipitation method were investigated. Al2(SO4)3$.$18H2O3, ZrOCl2$.$8H2O and YCl3$.$6H2O were used as starting materials. Amorphous aluminum hydrate prepared by precipitation method was completely transformed to alpha Al2O3 as a result of calcining at 1100$^{\circ}C$ for 1 hr and gamma, delta and theta phases appeared as transition phases. In ZrO2-Y2O3 system prepared by co-precipitation method, the crystallization temperature of ZrO2 was increase with Y2O3 contents. The coupled crystallization occured in coprecipitated Al2O3-ZrO2-Y2O3 system, therefore the formation temperature of alpha Al2O3 and ZrO2-Y2O3 system. In this ternary system, the powder morphology showed a particular shape which was composed of large Al2O3 grains having small spherical ZrO2 particles within large Al2O3 grain and relatively large ZrO2 particles along the grian boundaries.