• Journal of the Korean Ceramic Society
• /
• v.36 no.9
• /
• pp.982-990
• /
• 1999

YSZ/LSM composite cathode was fabricated by dip-coating of YSZ sol on the internal pore surface of a LSM cathode followed by sintering at low temperature (800-100$0^{\circ}C$) The YSZ coating significantly increased the TPB(Triple Phase Boundary) where the gas the electrode and the electrolyte were in contact with each other. Sinter the formation of resistive materials such as La2Zr2O7 or SrZrO3 was prevented due to the low processing temperature and TPB was increased due to the YSZ film coating the electrode resistance (Rel) was reduced about 100 times compared to non-modified cathode. From the analysis of a.c impedance it was shown that microstructural change of the cathode caused by YSZ film coating affected the oxygen reduction reaction. In the case of non-modified cathode the RDS (rate determining step) was electrode reactions rather than mass transfer or the oxygen gas diffusion in the experimental conditions employed in this study ($600^{\circ}C$-100$0^{\circ}C$ and 0,01-1 atm of Po2) for the YSZ film coated cathode however the RDS involved the oxygen diffusion through micropores of YSZ film at high temperature of 950-100$0^{\circ}C$ and low oxygen partial pressure of 0.01-0.03 atm.

• Journal of the Korean Ceramic Society
• /
• v.42 no.12 s.283
• /
• pp.793-799
• /
• 2005

A composite cathode of LSCF$(La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_3)\;and\;GDC\; (Gd_2O_3-doped\;CeO_2:Ce_{0.9}Gd_{0.1}O_{1.95_})$ was characterized in terms of an electrode response, using a point contact in an Yttria-Stabilized Zirconia (YSZ) electrolyte incorporated into AC two-point impedance spectroscopy. The point-contacted configuration amplifies the responses occurring near the YSZ/cathode interface through the aligned point contact on the planar LSCF/GDC electrode. The point contact interface increases the bulk resistance allowing the estimation of the point contact geometry and resolving the electrode-related responses. The resultant impedance spectra are analyzed through an equivalent circuit model constructed by resistors and constant phase elements. The bulk responses can be resolved from the electrode-related portions in terms of spreading resistance. The electrode-related polarizations are measured in terms of temperature and oxygen partial pressure. The modified impedance spectroscopy is discussed in terms of methodology and analytical aspects, toward resolving the electrode-polarization issues in solid oxide fuel cells.

• Environmental Sciences Bulletin of The Korean Environmental Sciences Society
• /
• v.4 no.2
• /
• pp.95-102
• /
• 2000

Methane combustion over perovskite-type oxides prepared using the malic acid method was investigated. To enhance the catalytic activity, the perovskite oxides were modified by the substitution of metal into their A or B site. In addition, the reaction conditions, such as the temperature, space velocity, and partial pressure of the methane were varied to understand their effect on the catalytic performance. With the LaCoO3-type catalyst, the partial substitution of Sr or Ba into site A enhanced the catalytic activity in the methane combustion. With the LaBO3(B=Co, Fe, Mn, Cu)-type catalyst, the catalytic activities were exhibited in the order of Co>Fe Mn>Cu. Futhermore, the partial substitution of Co into site B enhanced the catalytic activity, whereas an excess amount of Co decreased the activity. The surface area and catalytic activity of the perovskite catalysts prepared using the malic acid method showed higher values than those prepared using the solid reaction method. The catalytic activity was enhanced with decreased methane concentration and with a decrease in the space velocity.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1491-1500
• /
• 1994

Nonstoichiometry($\delta$) and the phase stability region of a ferrite spinel (Mg0.29Fe0.71)3-$\delta$O4 have been investigated by a coulometric titration method as a function of temperature(T) and oxygen partial pressure(Po2). It has been found that the spinel is thermodynamically stable in the ranges -8.0$\leq$log(PO2/atm)$\leq$-2.4, -7.0$\leq$log(PO2/atm)$\leq$-1.7 respectvely at 100$0^{\circ}C$. The nonstoichiometry extends over the ranges of -0.004$\leq$$\delta$$\leq$0.007, -0.008$\leq$$\delta$$\leq$0.006, -0.033$\leq$$\delta$$\leq$0.004 at 100$0^{\circ}C$, 120$0^{\circ}C$, respectvely. The observed PO2-dependence of $\delta$ suggests that the majority ionic defects are cation interstitials in the low PO2 region and cation vacancies in the high PO2 region.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.262-267
• /
• 2000

To tap the possibility of exploiting the precipitates as flux-pinning center in the Bi-2223 superconducting system, as-received Bi-2223/Ag tapes with the starting composition of Bi$_{1.8}$Pb$_{0.4}$Sr$_2$Ca$_{2.2}$Cu$_3$O$_8$ were post-annealed at various temperature, oxygen partial pressure, and annealing time. The 2$^{nd}$ phases in the annealed specimen were analysed with XRD, SEM, TEM, and EDS. The size and the distribution of the precipitates such as (Ca,Sr)$_2$(Pb,Bi)O$_4$ and Bi$_{0.5}$Pb$_3$Sr$_2$Ca$_2$CuO$_{12+{\delta}}$ (3221) in the Bi-2223 matrix was controllable by varying heat-treatment condition without breaking the connectivity of the 2223 grains. The nano-size precipitates within the 2223 grains are conjectured as working as flux-pinning sites, resulting in increased J$_c$ value.

• Journal of the Korean Vacuum Society
• /
• v.9 no.1
• /
• pp.30-35
• /
• 2000

Indium-Tin Oxide (ITO) thin films were deposited on the commercial glass substrate by rf-magnetron sputtering. The ITO films with the thickness of 2,000~2,400 $\AA$ were prepared by changing the oxygen partial pressures of 2, 3, and 5%, as well as by changing the substrate temperature of $300^{\circ}C$ and $500^{\circ}C$. spectrophotometer, XRD, SEM, AFM, 4-point probe and Hall effect system were employed to characterize the ITO films. The optimum deposition conditions were the substrate temperature of $500^{\circ}C$ and oxygen partial pressure of 2-3%. At theses conditions, the ITO film showed the transmittance of 91%, the resistivity of $5.4\times10^{-3}\Omega$cm, the carrier concentration of $1.0\times10^{19}\textrm{cm}^{-3}$, and the carrier mobility of 150$\textrm{cm}^2$/Vsec. In XRD spectra, the (222) and (400) $In_2O_3$ planes were dominant under the optimum deposition conditions When the substrate was cleaned only by the method of ultrasonic cleaning without both pre-annealing and chemical treatment of the substrate, the ITO film exhibited the transmittance of 86%, the carrier concentration of $5.4\times10^{19}\textrm{cm}^{-3}$ and the mobility of 24$\textrm{cm}^2$/Vsec.

• Korean Chemical Engineering Research
• /
• v.47 no.6
• /
• pp.734-739
• /
• 2009

Characteristics of pyrolysis, partial oxidation, combustion of chlorella, which is one species of micro-algae, were determined by using thermobalance reactor(I.D. 5.5 cm, Height 1 m). Effect of reaction temperature($500{\sim}800^{\circ}C$), water content in chlorella(0~60%), and oxygen content(0~21vol%) on thermal decomposition of chlorella were also determined and analyzed to investigate the kinetic characteristics of pyrolysis, partial oxidation and combustion. As the temperature and partial pressure increases, the carbon conversion increases. In case of pyrolysis, carbon conversion and reactivity sharply decreased with increasing moisture content. However, carbon conversion and reactivity decreased at 60% water content in case of partial oxidation and combustion. As reaction temperature and oxygen content increased, carbon conversion increased and the combustion reaction rate equation for chlorella has been presented. $\frac{dX}{dt}=(7.41{\times}10^{-1})$exp$\left(-\frac{19600}{RT}\right)(P_{O_{2}})^{0.209}(1-X)^{2/3}$.

• Journal of Powder Materials
• /
• v.23 no.4
• /
• pp.303-306
• /
• 2016

An optimum route to synthesize Ti-Mo system powders is investigated by analyzing the effect of the heat treatment atmosphere on the formation of the reaction phase by dehydrogenation and hydrogen reduction of ball-milled $TiH_2-MoO_3$ powder mixtures. Homogeneous powder mixtures with refined particles are prepared by ball milling for 24 h. XRD analysis of the heat-treated powder in a hydrogen atmosphere shows $TiH_2$ and $MoO_3$ peaks in the initial powders as well as the peaks corresponding to the reaction phase species, such as $TiH_{0.7}$, TiO, $MoO_2$, Mo. In contrast, powder mixtures heated in an argon atmosphere are composed of Ti, TiO, Mo and $MoO_3$ phases. The formation of reaction phases dependent on the atmosphere is explained by the partial pressure of $H_2$ and the reaction temperature, based on thermodynamic considerations for the dehydrogenation reaction of $TiH_2$ and the reduction behavior of $MoO_3$.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.2
• /
• pp.135-141
• /
• 2005

Nitric oxide(NO) reduction by methanol was investigated over $La_2O_3$ catalysts in the presence and absence of oxygen. In the absence of $O_2$, $CH_3OH$ reduced NO to both $N_2$ and $N_2O$, with selectivity to $N_2$ formation decreasing from 81-88% at 623K to 47-71% at 723 K. With 1.2% $O_2$ in the feed, the rates were 4-8 times higher, but the selectivity to $N_2$ dropped from 50% at 623 K to 9% at 723 K. The specific activities with $La_2O_3$ for this reaction were higher than those for other reductants; for example, at 773 K with hydrogen a specific activity of $34\;{\mu}mol\;NO/sec{\cdot}m^2$ was obtained whereas that for methanol was $638\;{\mu}mol\;NO/sec{\cdot}m^2$. The Arrhenius plots were linear under differential reaction conditions, and the apparant activation energy was consistantly near 15 kcal/mol with $CH_3OH$. Linear partial pressure dependencies based on a power rate law were obtained and showed a near-zero order in $CH_3OH$ and a near-first order in $H_2$.

• Progress in Superconductivity and Cryogenics
• /
• v.13 no.1
• /
• pp.6-11
• /
• 2011

The $BaHfO_3$ (BHO) buffer layer on the IBAD MgO template was turned to be effective for a successful fabrication of $GdBa_2Cu_3O_{7-{\delta}}$ (GdBCO) films with high critical current density ($J_c$). Both the BHO buffer layers and GdBCO films were prepared by pulsed laser deposition (PLD). The effects of the PLD conditions, including substrate temperature ($T_s$), oxygen partial pressure ($PO_2$), and deposition time on the in-plane texture, surface roughness, and microstructures of the BHO buffer layers on the IBAD MgO template were systematically studied for processing optimization. The c-axis oriented growth of BHO layers was insensitive to the deposition temperature and the film thickness, while the in-plane texture and surface roughness of those were improved with increasing $T_s$ from 700 to $800^{\circ}C$. On the optimally processed BHO buffer layer, the highest $J_c$ value (77 K, self-field) of 3.68 $MA/cm^2$ could be obtained from GdBCO film deposited at $780^{\circ}C$, representing that BHO is a strong candidate for the buffer layer on the IBAD MgO template.