• Journal of Energy Engineering
• /
• v.8 no.2
• /
• pp.256-264
• /
• 1999

The performance of the Pt-B/cordierite catalysts (2 wt%) Pt, 70 wt% Alumina, 28 wt%) Ceria and Zirconia, B: base metal) loaded with 6∼12 wt% Mn, Cu, V, Co, Cr and Ba, respectively was studied for partial oxidation of methane reaction and compared with that of Ni loaded catalyst. As a results, it was found that Ba, Co, Cr as well as Ni loaded catalysts showed higher activity for methane partial oxidation of methane than the Mn, Cu and V loaded catalyst. But it was known that catalysts having good activity for methane showed the good activity for coke formation, too. A XRD analysis of the catalyst before and after the reaction using 5 wt% Ni/Al$_2$O$_3$) showed that there were three Ni phases. In these results, it was found that methane oxidation reaction occulted at the front of the catalyst bed consisted of NiAl$_2$O$_4$and NiO and reforming reaction occurred at the rear part of the catalyst bed consisted of reduced Ni.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.631-635
• /
• 2012

Nickel oxide was doped with a wide range of concentrations (mol%) of Aluminum (Al) by solvothermal synthesis; single-phased nano powder of nickel oxide was generated after calcination at$900^{\circ}C$. When the concentration of Al dopant was increased, the reduced intensity was confirmed through XRD analysis. Lattice parameters of the synthesized NiO powder were decreased after treatment of the dopant; parameters were increased when the concentration of Al was over the doping limit (5 mol% Al). The binding energy of $Ni^{2+}$ was chemically shifted to $Ni^{3+}$ by doping $Al^{3+}$ ion, as confirmed by the XPS analysis. The tilted structure of the synthesized NiO with 5 mol% Al dopant and the polycrystalline structure of the $Ni_{0.75}Al_{0.25}O$ were observed by HR-TEM analysis. The electrical conductivity of the newly synthesized NiO was highly improved by Al doping in the conductivity test. The electrical conductivity values of the commercial NiO and the synthesized NiO with 5 mol% Al dopant ($Ni_{0.95}Al_{0.05}O$) were 1,400 s/cm and 2,230 s/cm at $750^{\circ}C$, respectively. However, the electrical conductivity of the synthesized NiO with 10 mol% Al dopant ($Ni_{0.9}Al_{0.1}O$) decreased due to the scattering of free-electrons caused by the large number of impurity atoms; the electrical conductivity of $Ni_{0.9}Al_{0.1}O$ was 545 s/cm at $750^{\circ}C$.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.208-208
• /
• 2009

메탄의 수증기-이산화탄소 복합개질반응에서 니켈 촉매의 탄소 침적 저항성에대한 Ce 증진 효과를 살펴보기 위해, Ni-Ce/${\alpha}-Al_2O_3$ 촉매를 제조하였다. Ce/Ni 비율 변화에 따른 촉매 비표면적, Ni 입자 분산도 및 촉매 활성 변화를 살펴보았고, Ce 첨가량을 최적화 할 수 있었다. Ce/Ni 비율 증가에 따라 NiO 결정크기가 감소하고 표면적과 Ni 분산도는 증가하였다. 특히, Ce/Ni=0.5 첨가 시, 촉매는 가장 넓은 비표면적과 Ni 분산도를 가졌으며, 우수한 촉매 활성 및 높은 탄소 침적 저항성을 보였다. 또한, 본 연구에서는 Ni과 Ce 담지 방법에 따른 Ni 분산도 향상과 Ni과 Ce간의 접촉 면적 극대화를 통한 활성산소 공급 향상에 대한 영향을 함께 살펴보았다. Ni과 Ce를 동시 함침법과 연속 함침법으로 담지하여 비교한 결과, 동시 함침법으로 제조한 Ni-Ce/${\alpha}-Al_2O_3$ (Ce/Ni=0.5) 촉매가 가장 우수한 촉매 성능 및 높은 탄소 침적 저항성을 보였다. 이는 동시 함침법으로 고분산된 Ni 입자와 담체간의 강한 상호작용 형성과 원활한 활성 산소 공급에 기인한 것이다.

• Journal of the Korean Ceramic Society
• /
• v.15 no.2
• /
• pp.66-71
• /
• 1978

The cobalt blue spinel stains (main composition; CoO:$Al_2O_3$=1 : 1) in CoO-NiO-$Al_2O_$3 and $CoO-Al_2O_3-Cr_2O_3$ system were prepared by the calcination of each component oxides to be adequate for the factory. The color development, the change of the lattice constnat of the spinel and its application to colored glazes were studied. The results were summarized as follows. 1) In CoO-Al_2O_3$ spinel, the excess addition of each component hardly made any variation in lattice constantand alumina-rich spinel specimens caused the brilliant blue color fade. 2) An increase of $Ni^{2+}$ in $CoO-NiO-Al_2O_3$ system, made the lattice constnat of the $CoO-Al_2O_3$ spinel smaller, and an increase of $Cr^{3+}$ in $CoO-Al_2O_3-Cr_2O_3$, larger. 3) Glazed stains under lead glaze were colored nearly same dark blue color fade.

• Clean Technology
• /
• v.13 no.4
• /
• pp.287-292
• /
• 2007

[ $M/Al_2O_3$ ] (M = Mn, Fe, Co, Ni, Cu) catalysts supported on commercial alumina ($Al_2O_3$) were prepared by an impregnation method, and were applied to the hydrogen production by auto-thermal reforming of ethanol. It was revealed that each catalyst retained its own metallic phase and product distribution strongly depended on the identity of active metal. Among the catalysts prepared, $Ni/Al_2O_3$ and $Co/Al_2O_3$ showed the best catalytic performance in the auto-thermal reforming of ethanol. However, the reaction mechanisms over these two catalysts were different. Ni/Al_2O_3 catalyst showed 100% ethanol conversion at $500^{\circ}C$, but it exhibited a rapid decrease in hydrogen selectivity. Although $Co/Al_2O_3$ catalyst showed an excellent performance in hydrogen selectivity, on the other hand, no significant improvement in hydrogen yield was observed due to the low ethanol conversion over the catalyst.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.3
• /
• pp.236-243
• /
• 1995

Since amorphous alloys have been known to have better mechanical and chemical properties than crystalline alloys of the same composition, a great number of studies on the formation of Al-based amorphous alloys have been carried out actively. However, little has been obtained about the effect of Rare-Earth metal and Transition metal addition on amorphous phase formed by melt spinning method. This study included fabrication of amorphous alloy $Al_{85}Ce_5Ni_{10}$ by melt spinning methods and DTA, XRD, TEM analysis to determine crystalization behavoir. Annealing treatments were carried out in Ar atmosphere under isothermal and nonisothermal conditions. The diffraction pattern of non-heated ribbons showed broad form characteristic of glass metallic alloy. The crystallization of amorphous $Al_{85}Ce_5Ni_{10}$ takes place eutedtoidly by homogeneous formation of Al and MS-1, followed by precipitation of the $Al_{11}Ce_3$ and later $MS-1{\rightarrow}Al_3Ni$ transformation.

• Korean Journal of Materials Research
• /
• v.15 no.8
• /
• pp.503-507
• /
• 2005

Microstructure and wear behavior of A1203-based nanocomposites with Cu and Ni-Co dispersions were investigated. $Al_2O_3/Cu$ and $Al_2O_3/Ni-Co$ nanocomposites were fabricated by hydrogen reduction and sintering method using metal oxide and metal nitrates. The nanocomposites showed increased mechanical properties compared with monolithic $Al_2O_3$. In particular, high toughness and hardness were measured for the $Al_2O_3/Ni-Co$ nanocomposite consolidated by spark plasma sintering. A minimum value of wear coefficient comparable to the monolithic $Al_2O_3$ was obtained for $Al_2O_3/Ni-Co$ nanocomposite. Wear behavior is discussed in terms of microstructure and mechanical properties of nanocomposites

• Journal of the Korean Electrochemical Society
• /
• v.19 no.3
• /
• pp.57-62
• /
• 2016

The over-discharging phenomena in sodium-nickel chloride batteries were investigated in relation to decomposition of molten salt electrolyte and consequent metal co-deposition. From XRD analysis, the material deposited on graphite cathode current collector was revealed to be by-product of molten salt electrolyte decomposition. In particular, the result showed that the Ni-Al alloys ($Al_3Ni_2$, $Ni_3Al$ and $Al_3Ni$) were electrochemically deposited on graphite current collectors in line with over-discharging behaviors. It is assumed that the $NiCl_2$ solubility in molten salt electrolytes leads to the co-deposition of Ni-Al alloys by increasing metal deposition potential above 1.6 V (vs. $Na/Na^+$). The cell tests have revealed that the composition of molten salt electrolytes modified by various additives makes a decisive influence on the over-discharging behaviors of the cells. It was revealed that NaOCN addition to molten salt electrolytes was advantageous to suppress over-discharge reactions by modifying the characteristics of molten salt electrolytes. NaOCN addition into molten salt electrolytes seems to suppress Ni solubility by maintaining basic melts. The cell using modified molten salt electrolyte with NaOCN (Cell D) showed relatively less cell degradation compared with other cells for long cycles.

• Journal of Korea Foundry Society
• /
• v.7 no.4
• /
• pp.352-357
• /
• 1987

Recently there were many studies on the development of cast iron for increasing strength, thermal resistance and mechanical properties, etc. The effects on mechanical properties and variation of solidification structure of hypo-eutectic cast iron was investigated when Ni(Al) was added with a fixed quantity of Al(Ni) content. The conclusions are as follows. 1) Tensile strength was the maximum(over 41 kg/ $mm^2$) when Al is added about 0.72%. 2) Torsional strength and angle were increased with increasing Al content and represents maximum value, when Al and Ni content are 1.5 and 2.0%. 3) With increasing Ni content, tensile strength decreased because of the effect of graphite coarsening. But torsional strengths were increased with the appropriate addition of (Ni%+Al%) content because of the effect of strengthened matrix.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.7 s.166
• /
• pp.1245-1252
• /
• 1999

The sliding wear behavior of $Al_2O_3/NiCr$ coating deposited on steel(SM45C) was investigated under lubrication. The parameters of sliding wear are normal loads, coating thickness. As a result, the wear resistance of $Al_2O_3/NiCr$ coating was remarkably greater than that of $Al_2O_3$ coating. The optimized coating thickness was found to be $300{\mu}m$ to ensure good anti-wear. The bond coating played important role in decreasing residual stress. The residual stress had much influence on wear mechanism. These results were correlated with the stress state of coating and the microstructure of coating.