Hydrogen Production by Auto-thermal Reforming of Ethanol over $M/Al_2O_3$ (M = Mn, Fe, Co, Ni, Cu) Catalysts

$M/Al_2O_3$ (M = Mn, Fe, Co, Ni, Cu) 촉매 상에서 에탄올 자열개질반응에 의한 수소 제조

  • Youn, Min-Hye (School of Chemical and Biological Engineering, Research Center for Energy Conversion and Storage, Seoul National University) ;
  • Seo, Jeong-Gil (School of Chemical and Biological Engineering, Research Center for Energy Conversion and Storage, Seoul National University) ;
  • Cho, Kyung-Min (School of Chemical and Biological Engineering, Research Center for Energy Conversion and Storage, Seoul National University) ;
  • Park, Sun-Young (School of Chemical and Biological Engineering, Research Center for Energy Conversion and Storage, Seoul National University) ;
  • Kim, Pil (School of Environmental and Chemical Engineering, Chonbuk National University) ;
  • Song, In-Kyu (School of Chemical and Biological Engineering, Research Center for Energy Conversion and Storage, Seoul National University)
  • 윤민혜 (서울대학교 공과대학 화학생물공학부) ;
  • 서정길 (서울대학교 공과대학 화학생물공학부) ;
  • 조경민 (서울대학교 공과대학 화학생물공학부) ;
  • 박선영 (서울대학교 공과대학 화학생물공학부) ;
  • 김필 (전북대학교 공과대학 환경화학공학부) ;
  • 송인규 (서울대학교 공과대학 화학생물공학부)
  • Published : 2007.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

[ $M/Al_2O_3$ ] (M = Mn, Fe, Co, Ni, Cu) catalysts supported on commercial alumina ($Al_2O_3$) were prepared by an impregnation method, and were applied to the hydrogen production by auto-thermal reforming of ethanol. It was revealed that each catalyst retained its own metallic phase and product distribution strongly depended on the identity of active metal. Among the catalysts prepared, $Ni/Al_2O_3$ and $Co/Al_2O_3$ showed the best catalytic performance in the auto-thermal reforming of ethanol. However, the reaction mechanisms over these two catalysts were different. Ni/Al_2O_3 catalyst showed 100% ethanol conversion at $500^{\circ}C$, but it exhibited a rapid decrease in hydrogen selectivity. Although $Co/Al_2O_3$ catalyst showed an excellent performance in hydrogen selectivity, on the other hand, no significant improvement in hydrogen yield was observed due to the low ethanol conversion over the catalyst.

상용 알루미나($Al_2O_3$)에 담지된 $M/Al_2O_3$ (M = Mn, Fe, Co, Ni, Cu) 촉매를 함침법에 의해 제조하였으며, 이를 에탄을 자열개질반응에 의한 수소제조에 적용하였다. 각각의 촉매는 고유한 금속상을 가지는 것으로 나타났으며, 생성물의 분포는 활성금속의 종류에 크게 의존하였다. 제조된 촉매 중에서, $M/Al_2O_3$ 및 Co/$Co/Al_2O_3$는 에탄을 자열개질반응에서 매우 우수한 촉매활성을 보였다. 그러나 두 촉매상에서의 반응메커니즘은 서로 다른 것으로 나타났다. $Ni/Al_2O_3$ 촉매는 $500^{\circ}C$의 반응온도에서 100%의 에탄올 전환율을 보였으나, 수소 선택도에서는 시간에 따라 급격한 저하현상을 나타내었다. 한편 $Co/Al_2O_3$ 촉매는 수소 선택도 면에서 우수한 활성을 보였으나, 에탄올 전환율이 저조하여 수소 수율에는 큰 변화가 나타나지 않았다.