• E2M - 전기 전자와 첨단 소재
• /
• 제9권9호
• /
• pp.906-910
• /
• 1996

Ferroxplana N $i_{2}$Y(B $a_{2}$N $i_{2}$F $e_{12}$ $O_{22}$ ) magnetic particles, which is one of the hexagonal ferrite were synthesized by a coprecipitation method. The coprecipitates were prepared by adding aqueous solution of BaC $I_{2}$ - 2 $H_{2}$O, NiC $I_{2}$ - 6 $H_{2}$O and FeC $I_{3}$ - 6 $H_{2}$O(of which the mole ratio is $Ba^{+2}$ : N $i^{+2}$ : F $e^{3+}$= 1 : 1 : 6) to a mixture of NaOH and N $a_{2}$C $O_{3}$. The shape of Ferroxplana N $i_{2}$Y magnetic particles obtained at 1, 100(.deg. C) was hexagonal plate-like, average particle size and aspect ratio were 2(.mu.m) and 7, respectively.y.

• 한국전기화학회:학술대회논문집
• /
• 한국전기화학회 2001년도 연료전지심포지움 2001논문집
• /
• pp.37-42
• /
• 2001

The electrooxidation of methanol was studied using Pt, PtNi(1.1 and 3:1), PtRuNi and PtRu(1:1) alloy nanoparticles in sulfuric acid solution for application to a direct methanol fuel cell. The PtNi and PtRuNi alloys showed excellent catalytic activities compared to those of pure Pt and PtRu. The role of Ni in the electrocatalytic activity was investigated using cyclic voltammetry (CV), chronoamperometry (CA), X-ray photoelectron spectroscopy (XPS). The XPS data confirm that the chemical states of Pt are exclusively metal as well as the presence of metallic Ni, NiO, $Ni(OH)_2$, NiOOH, metallic Ru, $RuO_2$, and $RuO_3$. Negative shifts of the binding energies of Pt for the PtNi alloy nanoparticles were determined by XPS measurements. This can be explained based by assuming that the enhanced activities of PtNi alloys for methanol electrooxidation were caused by the oxide states of Ni and by the change in the electronic structure of Pt component in the alloys.

• 한국연소학회:학술대회논문집
• /
• 한국연소학회 2014년도 제49회 KOSCO SYMPOSIUM 초록집
• /
• pp.355-356
• /
• 2014

Catalytic steam reforming of tar produced from biomass gasification was conducted using several Ni-based catalysts. K and Mn were used as a promoter over $Ni/Ru/Al_2O_3$ catalyst. The pellet and monolith type catalysts were prepared and applied to lab and bench-scale biomass gasification system. The $Ni/Ru-K/Al_2O_3$ catalyst shown higher performance than $Ni/Ru-Mn/Al_2O_3$ catalyst at low temperature range.

• 한국세라믹학회지
• /
• 제38권6호
• /
• pp.506-508
• /
• 2001

The ferrite plating with applying power ultrasound waves of 19.5 kHz and 600W enabled us to encapsulate entirely MnZn ferrite cores for transformers with Ni$\sub$x/Zn$\sub$y/Fe$\sub$3-x-y/O$_4$coating. Supplying a NH$_4$OH solution during the plating broke the limit of the solubility of Ni ions to ferrite-plated films. The electrical resistivity of the NiZn ferrite coating increased with increasing the Ni and Zn content, reaching 2.3${\times}$10$\^$5/Ωcm at the composition of Ni$\sub$0.24/Zn$\sub$0.30/Fe$\sub$2.46/O$_4$. The saturation magnetization was 540 emu/㎤. As a result, the MnZn ferrite cores were successfully encapsulated with the NiZn ferrite coatings for an insulation layer.

• Korean Chemical Engineering Research
• /
• 제59권2호
• /
• pp.232-238
• /
• 2021

The development of a low cost catalyst with high performance and small amount of carbon deposition on catalyst from toluene steam reforming were investigated by using coal ash as a support material. Ni-loaded coal ash catalyst showed similar catalytic activity for toluene steam reforming compared with the Ni/Al2O3. At 800 ℃, the toluene conversion was 77% for Ni/TAL, 68% for Ni/KPU and 78% for Ni/Al2O3. Ni/TAL showed similar toluene conversion to Ni/Al2O3. However, Ni/KPU produced higher hydrogen yield at relatively lower toluene conversion. Ni/KPU catalyst showed a remarkable ability of suppressing the carbon deposition. The difference in coke deposition and hydrogen yield is due to the composition of KPU ash (Ca and Fe) which increase coke resistance and water gas shift reaction. This study suggests that coal ash catalysts have great potential for the application in the steam reforming of biomass tar.

• 마이크로전자및패키징학회지
• /
• 제12권3호
• /
• pp.253-258
• /
• 2005

도금전류밀도에 따른 Ni박막의 결정립 크기, 전기비저항, 솔더 wetting angle 및 금속간화합물의 성장속도를 분석하였다. 도금전류밀도를 $5\;mA/cm^2$에서 $40\;mA/cm^2$로 증가시킴에 따라 Ni 박막의 표면 nodule의 크기가 감소하고 결정립이 미세화 되었으며, 전기비저항이 $7.37\mu\Omega-cm$에서 $9.13\mu\Omega-cm$로 증가하였다. $5\;mA/cm^2$ 및 $10\;mA/cm^2$에서 도금한 Ni 박막이 $40\;mA/cm^2$에서 형성한 Ni 박막에 비해 전기비저항이 낮고 dense하며 계면 금속간화합물의 성장속도가 느리기 때문에 무연솔더의 UBM 용도로 더 적합할 것이다.

• 대한화학회지
• /
• 제18권3호
• /
• pp.194-201
• /
• 1974

네자리 schiff리간드는 salicylaldehyde와 m-phenylenediamine을 Duff-반응 시킴으로써 N,N-bis(salicylaldehyde)-m-phenylenediimine을 합성하고 이 리간드와 Cu(II), Ni(II), Co(II) 및 Zn(II) 이온들과의 새로운 착물 Cu(II)$[C_{20}H_{14}O_2N_2]{\cdot}2H_2O, Co(II)[C_{20}H_{14}O_2N_2]{\cdot}2H_2O$ 및 Zn(II)$[C_{20}H_{14}O_2N_2]{\cdot}4H_2O$들을 합성하였다. 이들 착물에 대하여 가시부 흡수스펙트럼, 적외선스펙트럼, TGA, X-ray 회절 및 원소분석 결과에 의하여 Cu(II), Ni(II) 및 Co(II) 착물들은 리간드와 금속이 1:1 몰비 및 2수화물의 6배위 착물로 주어지며 Zn(II) 착물은 1:2 몰비 4배위 착물로 주어짐을 알았다

• Korean Chemical Engineering Research
• /
• 제53권3호
• /
• pp.372-381
• /
• 2015

본 연구에서는 $Ni/Al_2O_3$ 촉매를 사용한 에틸렌글리콜의 수증기 개질반응에서 제조 방법에 따른 영향을 알아보았다. 촉매들은 건식 함침법, 습식 함침법 그리고 공침법을 사용하여 제조하였다. 공침법을 사용하여 촉매 제조시 침전제를 KOH, $K_2CO_3$, $NH_4OH$를 각각 사용하여 침전제에 따른 영향 또한 알아보았다. 제조한 촉매들은 질소 물리흡착, 유도결합 플라즈마 질량분석법(ICP-AES), X선 회절법(XRD), 수소 승온 환원법(TPR), 수소 화학흡착, 승온 산화법(TPO), 주사전자현미경(SEM), 열분석법(TGA)을 사용하여 촉매의 물리화학적인 특성을 분석하였다. 773 K에서 환원한 촉매의 경우 KOH 혹은 $K_2CO_3$를 침전제로 사용하여 공침법으로 제조한 촉매가 가장 높은 활성을 보였다. 촉매 제조 방법은 Ni의 입자크기, Ni 산화물의 환원도, 반응에서의 활성과 안정성, 반응 중 탄소 침적의 형태 등에 영향을 끼치는 것을 확인할 수 있었다. KOH를 침전제로 사용하여 공침법으로 제조한 촉매의 경우 환원온도를 773~1173 K까지 증가시켰을 때, Ni 입자크기의 증가에도 불구하고 Ni 산화물의 환원도가 증가하므로 반응활성이 증가하는 것으로 나타났다.

• 한국표면공학회지
• /
• 제56권5호
• /
• pp.320-327
• /
• 2023

In this study, the nickel hydroxide (Ni(OH)₂) electrode for supercapacitor was prepared via hydrothermal method. Based on the nickel (Ni) foam, the electrode does not require any additional binder material or post-processing. Nickel nitrate (Ni(NO₃)₂) and hexamethylenetetramine (C₆H₁₂N₄) were used for synthesis, and the synthesis condition was 12 hours at 80 ℃. X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM) were used to analyze the structural characteristics of the electrode, and it shown that the nickel hydroxide was successfully prepared after only the one-step hydrothermal synthesis. The electrochemical properties were analyzed through the half-cell test. The prepared electrode shown a pair of oxidation/reduction peaks, indicating that the driving method included the redox reaction on the electrode surface. After the charge/discharge test, the specific capacitance was calculated as the value of 438 F/g at 3 A/g.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2008년도 춘계학술대회 논문집
• /
• pp.499-502
• /
• 2008

고정층반응기에서 니켈이 치환된 하이드로탈사이트($Ni_3Mg_3Al_2(CO_3)(OH)_{{16}{\cdot}n}H_2O$ ; n=3$\sim$5)를 합성하고 여기에 세리아를 첨가 후 소성하여 얻은 촉매를 사용하여($Ce_xNi_3$-HTlc ; x=0.3$\sim$1.2) 메탄의 부분산화 반응실험을 수행하였다. 세리아가 첨가되지 않은 촉매는 반응 초기 활성이 세리가가 소량 첨가된 ($Ce_{0.3}Ni_3$-HTlc) 촉매보다 우수하였으나 장시간 반응에서는 차차 활성이 저하되었으나, $Ce_{0.3}Ni_3$-HTlc의 활성은 30시간까지 일정하게 유지 되었다. 세리아 함량이 많아 질수록 촉매 활성은 점차 저하되었으며, $Ce_{1.2}Ni_3$-HTlc 는 촉매활성이 매우 낮았다.