• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.588-593
• /
• 2006

Spinel phase $LiMn_2O_4$ is of great interest as cathode materials for lithium-ion batteries. In this study, SHS (Self propagating High-temperature Synthesis) method to synthesize spinel $LiMn_2O_4$ directly from lithium nitrate, manganese oxide, manganese and sodium chloride were investigated. The influence of Li/Mn ratio, the heat-treated condition of product have been explored. The resultant $LiMn_2O_4$ synthesized under the optimum synthesis conditions shows perfect spinel structure, uniform particle size and excellent electrochemical performances.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.3
• /
• pp.179-184
• /
• 1999

In the past ten years, $LiMn_2O_4$-based spinels have been extensively studied as positive electrode materials for lithium-ion batteries. To improve the cycle performance of spinel $LiMn_2O_4$ as the cathode of 4V class lithium secondary batteries, spinel phases $LiMn_2O_4$ were prepared at various temperatures ranging form 600-900$^{\cire}C$ in air. The results showed that charge.dischare capacity of $LiMn_2O_4$ varied at 1st temperature from $200^{\circ}C to 600^{\circ}C$ increase with increasing temperature. $LiMn_2O_4$ synthesized at 2nd temperature $750^{\circ}C$excellent charge.discharge capacity, efficiency and cyclability compared to the samplesynthesized different temperatures. The value of lst charge.discharge capacity was 121mAh/g, 118mAh/g, Also, the efficiency value was about 97%.

• Journal of Electrochemical Science and Technology
• /
• v.1 no.2
• /
• pp.97-101
• /
• 2010

In order to apply hybrid capacitor, $Li_2Mn_3O_7$ was synthesized by combustion method using $LiNO_3$, $Li(CH_3COO){\cdot}2H_2O$ and $Mn(CH_3COO){\cdot}4H_2O$. Spinel pattern was identified the samples calcined over $400^{\circ}C$ in XRD. Intensity of $Mn_2O_3$ peak increased as the calcination temperature increased. To decide n/p ratio and to investigate electrochemical properties, charge-discharge tests of Li/$Li_2Mn_3O_7$ and Li/AC half-cell were carried out. Applying to AC/$Li_2Mn_3O_7$ hybrid capacitor, it had high discharge capacitance of 32.8 F/cc at 100 mA/g.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.595-596
• /
• 2005

This research which it sees adds $LiMn_2O_4$ in the activated carbon electrode the test against the effect which it follows is. Test cells, which were $LiMn_2O_4$fabricated with active mass composite consisted of (100-X)% of MSP-20 and (X)% of $LiMn_2O_4$ (X=20,40,60,80,100), exhibits the better specific capacitance than those of the cells fabricated with single active mass that is MSP-20. The enhanced properties of composite active mass could be caused by capability of $LiMn_2O_4$ powders. But the resistance was increase by proportionate in $LiMn_2O_4$ addition and when mixture ratio of the activated carbon and the $LiMn_2O_4$ being similar, to be low rather to the after where had become the maximum it came.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.735-741
• /
• 2004

$LiMn_{1.92}Co_{0.08}O_4$ and $LiNi_{0.7}Co_{0.3}O_2$ synthesized by a simplified combustion method had good electrochemical properties. Mixtures $LiMn_{1.92}Co_{0.08}O_4$-x wt$\%$ $LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41, and 47) were prepared by milling for 30 min and their electrochemical properties were investigated. The electrode with x=9 had a relatively large first discharge capacity (109.9 mAh/g at 0.1 C) and good cycling performance. The decrease in the discharge capacity of the mixture electrodes with cycling is considered to result mainly from the degradation of $LiNi_{0.7}Co_{0.3}O_2$, caused by coating of $LiNi_{0.7}Co_{0.3}O_2$ with Mn dissolved from $LiMn_{1.92}Co_{0.08}O_4$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.4
• /
• pp.316-322
• /
• 2001

Cathode materials $LiMn_{2-y}$$M_{y}$ $O_4$(M=Zn and Mg) were obtained by reacting the mixture of LiOH.$H_2O$, Mn $O_2$ and MgO ar ZnO at 80$0^{\circ}C$ for 36h in an air atmosphere. These materials showed an extended cycle life in lithium-anode cells working at room temperatue in a 3.0 to 4.3V potential window. Among these materials, LiM $n_{1.9}$M $g_{0.1}$ $O_4$ showed the best cycle performance in terms of the capacity and cycle life. The discharge capacities of the cathode for the Li/LiM $n_{1.9}$ $M_{0.1}$ $O_4$ cell at the 1st cycle and at the 70th cycle were about 120 and 105mAh/g, respectively. This cell capacity is retained by 88% after 70th cycle. In cyclic voltammetry measurement, all cells revealed tow oxidation peaks and reduction peaks. However, Li/$LiMn_{2-y}$$M_{y}$ $O_4$ cell substituted with Zn and Mg showed new reaction peak during reduction reaction.eaction.ion.ion.

• Korean Chemical Engineering Research
• /
• v.47 no.1
• /
• pp.84-88
• /
• 2009

Al doped $LiMn_2O_4$ cathode powders with fine size were synthesized by an ultrasonic spray pyrolysis method from the spray solution with citric acid and ethylene glycol. The as-prepared powders with spherical shape, porous structure and micron size turned into $LiMn_{11/6}Al_{1/6}O_4$ powders with micron size and regular morphology after post-treatment above $800^{\circ}C$. The $LiMn_{11/6}Al_{1/6}O_4$ powders had low initial discharge capacity of 94 mAh/g at a post-treatment temperature of $700^{\circ}C$. As the post-temperature increased from $750^{\circ}C$ to $1,000^{\circ}C$, the initial discharge capacities of the $LiMn_{11/6}Al_{1/6}O_4$ powders changed from 103 to 117 mAh/g. The $LiMn_{11/6}Al_{1/6}O_4$ powders had the maximum discharge capacity at a post-treatment temperature of $750^{\circ}C$. However, the $LiMn_{11/6}Al_{1/6}O_4$ powders post-treated at a temperature of $900^{\circ}C$ had the good cycle properties. The discharge capacities of the $LiMn_{11/6}Al_{1/6}O_4$ powders dropped from 107 to 100 mAh/g (93% capacity retention) by the 70th cycle at a current density of 0.1 C.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.268-268
• /
• 2009

Li-Mn spinel의 고온수영 특성을 향상을 위해 졸-겔법으로 $V_2O_5$를 Li-Mn spinel 표면에 코팅을 하였다. $V_2O_5$의 코팅양은 1, 3, 5wt%로 조절하여 코팅 양에 따른 특성변화를 조사하였다. XRD분석결과 $V_2O_5$가 코팅된 Li-Mn spinel을 $400^{\circ}C$에서 열처리시 $Mn(VO_3)_2$가 생성되는 것을 확인하였다. 충방전 테스트결과, 고온에서 $V_2O_5$를 코팅한 Li-Mn spinel이 우수한 수명을 나타냈다. 하지만 코팅량이 1wt%까지는 용량의 변화가 거의 없었고, 5wt% 코팅시 현격히 용량이 감소하였다.

• Journal of the Korean Applied Science and Technology
• /
• v.20 no.1
• /
• pp.33-43
• /
• 2003

$LiMn_2O_4$ catalyst for $CO_2$ decomposition was synthesized by oxidation method for 30 min at 600$^{\circ}C$ in an electric furnace under air condition using manganese(II) nitrate $(Mn(NO_3)_2{\cdot}6H_2O)$, Lithium nitrate ($LiNO_3$) and Urea $(CO(NH_2)_2)$. The synthesized catalyst was reduced by $H_2$ at various temperatures for 3 hr. The reduction degree of the reduced catalysts were measured using the TGA. And then $CO_2$ decomposition rate was measured using the reduced catalysts. Phase-transitions of the catalysts were observed after $CO_2$ decomposition reaction at an optimal decomposition temperature. As the result of X-ray powder diffraction analysis, the synthesized catalyst was confirmed that the catalyst has the spinel structure, and also confirmed that when it was reduced by $H_2$, the phase of $LiMn_2O_4$ catalyst was transformed into $Li_2MnO_3$ and $Li_{1-2{\delta}}Mn_{2-{\delta}}O_{4-3{\delta}-{\delta}'}$ of tetragonal spinel phase. After $CO_2$ decomposition reaction, it was confirmed that the peak of $LiMn_2O_4$ of spinel phase. The optimal reduction temperature of the catalyst with $H_2$ was confirmed to be 450$^{\circ}C$(maximum weight-increasing ratio 9.47%) in the case of $LiMn_2O_4$ through the TGA analysis. Decomposition rate(%) using the $LiMn_2O_4$ catalyst showed the 67%. The crystal structure of the synthesized $LiMn_2O_4$ observed with a scanning electron microscope(SEM) shows cubic form. After reduction, $LiMn_2O_4$ catalyst became condensed each other to form interface. It was confirmed that after $CO_2$ decomposition, crystal structure of $LiMn_2O_4$ catalyst showed that its particle grew up more than that of reduction. Phase-transition by reduction and $CO_2$ decomposition ; $Li_2MnO_3$ and $Li_{1-2{\delta}}Mn_{2-{\delta}}O_{4-3{\delta}-{\delta}'}$ of tetragonal spinel phase at the first time of $CO_2$ decomposition appear like the same as the above contents. Phase-transition at $2{\sim}5$ time ; $Li_2MnO_3$ and $Li_{1-2{\delta}}Mn_{2-{\delta}}O_{4-3{\delta}-{\delta}'}$ of tetragonal spinel phase by reduction and $LiMn_2O_4$ of spinel phase after $CO_2$ decomposition appear like the same as the first time case. The result of the TGA analysis by catalyst reduction ; The first time, weight of reduced catalyst increased by 9.47%, for 2${\sim}$5 times, weight of reduced catalyst increased by average 2.3% But, in any time, there is little difference in the decomposition ratio of $CO_2$. That is to say, at the first time, it showed 67% in $CO_2$ decomposition rate and after 5 times reaction of $CO_2$ decomposition, it showed 67% nearly the same as the first time.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.3
• /
• pp.131-135
• /
• 2000

In order to investigate the origin of capacity fading with charge/discharge cycling in $LiMn_2O_4$ thin film battery, impedance studies have been performed with increasing cycling in $LiMn_2O_4/1M\;LiClO_4-PC/Li$ cells. The fitted values obtained from impedance data show good agreements with the experimental results. Especially, the element of charge transfer resistance of $LiMn_2O_4/liquid$ electrolyte interface initially increased, and then saturated with increasing the charge/discharge cycles, which could explain the cause of initial abrupt capacity fading of $LiMn_2O_4$ thin film with cycling due to interfacial reaction. The steady capacity fading is caused by the increasing of Warburg resistance. The chemical diffusion coefficient of Li ions decreased from $5.15\times10^{-11}cm^2/sec$ at 1st cycles to $6.3\times10^{-12}cm^2/sec$ at 800th cycles, which attributed to the Jahn-Teller distortion/Mn dissolution which diminishes tetra hedral sites necessary for Li diffusion in $LiMn_2O_4$.