• Proceedings of the Korea Crystallographic Association Conference
• /
• 2003.11a
• /
• pp.32-32
• /
• 2003

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.6
• /
• pp.403-407
• /
• 2018

In this study, double layer KTN/STO thin films were fabricated on $Pt/Ti/SiO_2/Si$ substrate, their structural and electrical properties were measured according with the number of STO coatings, and their applicability to microwave materials was investigated. The average grain size was about 80~90 nm, the average thickness of the 6-coated KTN thin film was about 320 nm, and the average thickness of the STO thin film coated once was about 45~50 nm. The dielectric constant decreased with increasing frequency, and as the number of STO coatings increased, the rate of change of the dielectric constant with the applied electric field decreased. The tunability of the KTN thin film showed a maximum value of 19.8% at 3 V. The figure of merit of the KTN/1STO thin film was 9.8 at 3 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.1
• /
• pp.29-32
• /
• 2012

Lead-free $0.98(Na_{0.5},K_{0.5})NbO_3-0.02Li(Sb_{0.17}Ti_{0.83})O_3$ (hereafter 0.98NKN-0.02LST) ceramics doped with $Ag_2O$ were prepared using a conventional mixed oxide method. The specimen showed superior structural and electrical properties when 1 mol% $Ag_2O$ was doped. For the 0.98NKN-0.02LST+1.0mol%$Ag_2O$ ceramics sintered at $1,100^{\circ}C$, piezoelectric constant ($d_{33}$) of sample showed the optimum values of 207 pC/N. The 0.98NKN-0.02LST+1.0 mol%$Ag_2O$ ceramics are a promising candidate for lead-free piezoelectric materials.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.93-93
• /
• 2009

In this study, in order to develop excellent lead-free composition ceramics for piezoelectric transformer, $(K_{5.4}Cu_{1.3}Ta_{10}O_{29})$ added $(K_{0.5}Na_{0.5}](Nb_{0.97}Sb_{0.03})O_3$ were fabricated using conventional mixed oxide method. At the 0.9mol% KCT added specimen, electromechanical coupling factor(kp) and mechanical quality factor ($Q_m$) showed the optimal values of 0.437 and 727.07, respectively, for piezoelectric transformer application.

• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.360-364
• /
• 2003

$Sr_{l}$ $\pm$x/$Bi_{2}$ $\pm$y/$Ta_2$ $O_{9}$ and $Sr_{l}$ $\pm$$Bi_{x}$ $2\pm$y$Nb_2$$O_{9}$ ceramics were prepared by a solid state reaction method. X-ray diffraction analysis indicated that single-phase of Bi-layered perovskite was obtained. According to Sr/Bi content ratio, Curie temperature( $T_{c}$), electromechanical factor($K_{p}$ ) and mechanical quality factor($Q_{m}$ ) were measured. The Curie temperature of SBN(SBT) rose from $414^{\circ}C$(314$^{\circ}C$) to $494^{\circ}C$(426$^{\circ}C$) when Sr/Bi content ratio was increased. In the case of Sr/Bi content ratio = 0.55/2.3, the maximum value of the mechanical quality factor $Q_{m}$ of SBT and SBN were obtained 3320 and 1010, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.707-711
• /
• 2006

ZnO was doped up to 0.3 wt% for improving the electrical properties of lead-free $[Li_{0.04}(Na_{0.44}Ko_{0.52})-(Nb_{0.86}\;Ta_{0.10}\;Sb_{0.04})]O_3$ piezoelectric ceramics. The ceramics were fabricated with the conventional sintering processes. Crystal structure of the samples was tetragonal phase regardless of ZnO amount. However, the piezoelectric properties were varied with the ZnO amount. The electro-mechanical coupling factor $(k_p)$ was with the ZnO amount up to 0.2 wt% but decreased with the further addition. the maximum value of $k_p$ was 0.475. Density, piezoelectric charge constant and relative dielectric constant was also showed maximum value at 0.2 wt%. The maximum values are $4.75g/cm^3$, 275 pC/N, 1403, respectively. In contrast, the mechanical quality factor $(Q_m)$ was not varied with increasing the ZnO addition up to 0.2 wt% but rapidly increased at 0.3 wt%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.8
• /
• pp.622-626
• /
• 2011

Lead-free piezoelectric ceramics with the composition of $(Na_{0.54}K_{0.46})_{0.96}Li_{0.04}(Nb_{1-0.10-x}Ta_{0.10}Sb_x)O_{3}$ (x= 0~8 mol%) were fabricated by nomal sintering at $1,090^{\circ}C$ for 5 h. the phase structure, microstructure and electrical properties were investigated with a emphasis on the influence of the Sb content. All samples exhibit a single perovskite phase over the whole compositional range. For the ceramics with x= 4 [mol%], two phase transitions are observed at $75^{\circ}C$ and $366^{\circ}C$, corresponding to the phase transitions of orthorhombic to tetragonal (To-t) and tetragonal to cubic (Tc), respectively. high electrical properties of $d_{33}$= 210.83 pC/N, kp= 40%, ${\varepsilon}_r$= 1,091.35, $\rho$= 4.54 g/$cm^2$ were obtained from the specimen with x= 4 [mol%], which suggests that the composition ceramics is a promising lead-free piezoelectric material.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.218-219
• /
• 2005

In this paper, in order to develop Pb-free piezoelectric ceramics, $[Li_{0.04}(Na_{0.44}K_{0.52})-(Nb_{0.86}Ta_{0.10}Sb_{0.04})]O_3$ ceramic was fabricated with the variation of ZnO addition. Piezoelectric properties of the ceramic were varied with the amount of ZnO addition and showed the maximum kp value at 0.2 wt% ZnO addition. Qm of ZnO added ceramics showed lower values than the non-added ceramics, however, the kp was increased by the addition of ZnO up to 0.2 wt%. At the sintering temperature of 1110$^{\circ}C$ and the calcination temperature of 850$^{\circ}C$, the optimal values of density=473g/$cm^3$, kp=0.473, $\varepsilon_r$=1403 were obtained.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.9
• /
• pp.646-650
• /
• 2013

$(Na,K)NbO_3$-based piezoelectric ceramics were synthesized by a liquid phase sintering method with a selected glass frit. The effects of the content of the glass frit and the sintering temperature on the microstructure and the electrical properties of the samples were investigated. With the 0.1 wt% of glass frit content, $(Na_{0.52}K_{0.44}Li_{0.06})(Nb_{0.84}Ta_{0.10}Sb_{0.06})O_3$ (NKL-NTS) ceramics showed the maximum values of the relative density (99.1%) and the electro-mechanical coupling factor ($k_p$: 0.32) at the sintering temperature of $1,050^{\circ}C$. It might mean that a liquid phase sintering with a suitable glass frit having the lower flow temperature could improve the relative density and the piezoelectric properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.83-83
• /
• 2009

우수한 압전성을 가지는 PZT는 인체에 유해한 다량의 PbO을 함유하여 심각한 환경문제를 야기함은 물론 제조 공정 중 PbO 휘발 억제 시설 구비에 따른 경제적 부담 등 문제점이 지적되었다. 따라서 환경오염 및 가격경쟁력을 갖추기 위해 현재 무연 조성 세라믹스에 대한 많은 연구가 진행되고 있다. 최근 비납계 압전 세라믹의 연구는 비스무스 레이어형과 페로브스카이트 형 비납계 세라믹스의 연구가 활발히 진행되고 있다. 특히 $(Na,K)NbO_3$ 계는 페로브스카이트 구조를 가지는 비납계 세라믹으로 현재 많은 연구가 진행되고 있다. 이 물질은 PZT계와 유사하게 상전이(morphotropic phase boundary:MPB)영역을 가지고 있 으며 이 영역에서 높은 압전 특성을 보여주고 있다. 최근 $Na_{0.5}K_{0.5}NbO_3$에 $LiTaO_3$를 치환하여 우수한 압전 특성을 지니는 조성이 개발되고 있지만, 보통 소성법으로 제조된 세라믹스는 PZT계 세라믹스와 비교하여 특성이 떨어진다. 본 연구에서는 압전성이 우수한 $(Na_{0.44}K_{0.52}Li_{0.44})(Nb_{0.90}Sb_{0.06}Ta_{0.04})O_3$ 조성에 도너 도핑과 억셉터 도핑을 한 다음 전기기계결합계수, 압전상수, 유전상수의 변화를 평가하고, hardener 와 softener 특성이 본조성에서 나타나는지를 관찰하였다. 실험방법은 보통 소성법을 사용하였으며, 분쇄와 혼합은 직경 3 mm zirconia ball을 사용하여 볼밀 하였다. $850^{\circ}C$ 에서 5h 하소 후 $1100{\sim}1200^{\circ}C$ 에서 소결하고, 두께 1 mm로 연마한 다음 silver paste를 $650^{\circ}C$ 에서 소부하여 전극을 형성하였다. 제작된 시편은 $90^{\circ}C$의 실리콘유에서 3~4 kV/mm의 전계를 가해 20분간 분극 처리를 수행하였다. 제작된 시편의 압전전하 상수 값은 d33-meter(APC-8000)를 이용하여 측정하였고, 유전율, 전기기계결합계수 및 기계적품질계수 등은 임피던스 분석기 (impedance/gain phase analyzer)를 이용하여 특성을 측정 하였다. 또한 전압-분극 특성의 평가에는 강유전특성 측정기(ferroelectric tester: Precision-LC, Radiant Technologies, USA)를 이용하였다.