• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.12
• /
• pp.1099-1107
• /
• 1998

In this study, the microstructure and electric conductivity of 5mol% $Gd_2O_3$-5mol% $Y_2O_3-ZrO_2$ system(5G5YZ) with a variation of sintering time at $1600^{\circ}C$ were investigated. By the result of TEM analysis of 5G5YZ sintered for 12h, a microcrack was observed near grain boundary. The change of the sintering time did not affect the lattice conductivity, but the grain boundary contribution was varied with the sintering time. The grain boundary conductivity of the sample sintered for 1h showed the highest value. Furthermore, the activation energy of the total conductivity was independent upon the sintering time and showed approximately 1.01eV. The highest conductivity measured at $1000^{\circ}C$ was 0.0197S/cm with the sample sintered for 1h. Comparing to 0h’s, the thickness ration of grain boundary as a function of sintering time were 0.88, 1.11 and 1.29 for 1h, 5h and 12h, respectively. In case of the sample sintered for 1h, the thickness of the grain boundary showed the lowest value. The increase of the sintering time over 1h made the decrease of the electric conductivity as well as the increase of the grain growth and the thickness of the grain boundary. As a result, it seemed that the proper sintering time for 5G5YZ composition was 1h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.341-342
• /
• 2006

Gadolinium-substituted bismuth titanate, $Bi_{3.3}Gd_{0.7}Ti_3O_{12}$ (BGT), thin films were successfully fabricated on Pt(111)/Ti/$SiO_2$/Si substrates by a sol-gel method and their structural and ferroelectric properties have been characterized. Fabricated BGT thin films were found to be random orientations, which were confirmed by X-ray diffraction experiment and scanning electron microscope analysis. The remanent polarization ($2P_r$)) of BGT thin film annealed at $720^{\circ}C$ was $25.85\;{\mu}C/cm^2$ at an applied voltage of 5 V. The BGT thin films exhibited a 11 % reduction in their switching charge after no less than $10^{11}$ switching cycles at a frequency of 1 MHz.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.213-221
• /
• 1998

$BaCe_{0.9}Gd_{0.1_O_{2.95}$ powder was synthesized by oxalate coprecipitation method. Precipitate with a stoichimetric ratio of the cations was prepared by adding a mixture of Ba, Ce and Gd nitrate solution to an oxalic acid solution at pH 4. Reaction between the constituent oxides to form a perovskite phase was initiated at $800^{\circ}C$ and a single phase $BaCe_{0.9}Gd_{0.1_O_{2.95}$ powder having good sinterability was obtained after calcination at $1000^{\circ}C$. Sintering green compacts of this powder for 6 h showed a considerable densification to start at $1100^{\circ}C$ and resulted in 93% and 97% relative densities at $1300^{\circ}$ and at $1450^{\circ}C$, respectively. Whereas the power compacts prepared by solid state reaction had lower relative densities, 78% at $1300^{\circ}$and 90% at $1450^{\circ}C$. Fine particles of $CeO_2$ second phase were observed in the surface of the sintered compacts. This was attributed to the evaporation of BaO from the surface that had been exposed during thermal etching.

• Proceedings of the Optical Society of Korea Conference
• /
• 2003.07a
• /
• pp.284-285
• /
• 2003

Significant research interest in the growth and characterization of $Y_2$O$_3$：Eu$^{3+}$ thin films has been shown over the last few years because of the promise for applications of display devices. Although an Eu-doped oxysulfide (Eu： $Y_2$O$_2$S) which has an efficiency of 13％ has been used for a traditional cathode ray tube (CRT) red phosphor, the sulfide system is known to degrade rapidly under the high current densities needed for field-emission display (FED) technology. (omitted)d)

• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.232-236
• /
• 2006

The Y1.99-xMxCe0.01SiO5(M=Li, La, Nd, and Gd) phosphors were synthesized by solid-state reaction at 1350oC for 10h under reducing atmosphere in order to improve properties of blue emitting phosphors. Compared with commercial blue phosphors, the Y2SiO5:Ce blue phosphors substituted with various elements showed significant enhancement of the emission intensity. Particularly, 1 mol% Li doped Y2SiO5:Ce phosphors indicated the maximum emission intensity in the photoluminescence spectra. Thanks to SEM analyses revealed that the morphology of Y2SiO5:(Ce,Li) blue phosphors was a pseudo-spherical with particle size of 3m.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.10
• /
• pp.2992-2994
• /
• 2010

• Journal of the Korean Ceramic Society
• /
• v.49 no.1
• /
• pp.118-123
• /
• 2012

GDC20($Ce_{0.8}Gd_{0.2}O_{1.9}$) powder was synthesized from Ce and Gd nitrate solutions using ammonium carbonate($(NH_4)_2CO_3$) as a precipitant. Attrition-milling of the powder, which had been calcined at $700^{\circ}C$ for 4 h, decreased an average particle size of 2.2 ${\mu}m$ to 0.5 ${\mu}m$. The milled powder consisted of nano-sized spherical primary particles. Due to the excellent sinterability of the powder, sintering of the powder compacts for 4 h showed relative densities of 80% at 1000 $^{\circ}C$ and 96.5% at $1200^{\circ}C$, respectively. Densification was found to almost complete at $1300^{\circ}C$, resulting in a dense and homogeneous microstructure with a relative density of 99.5%. The grains of ~0.2 ${\mu}m$ in size at $1200^{\circ}C$ grew to ~1 ${\mu}m$ in size at $1300^{\circ}C$ as a result of a rapid grain growth.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.44-44
• /
• 2008

GdBCO coated conductor have been fabricated using reactive co-evaporation. The batch type co-deposition system was specially designed and was named EDDC (evaporation using drum in dual chamber) that is possible to deposit superconducting layer with optimum composition ratio of materials at temperature over $700^{\circ}C$ and several mTorr of oxygen. The IBAD-MgO substrate with the architecture of LaMnO3(LMO)/IBAD-MgO/Hastelloy was used for coated conductor. In this study, GdBCO superconducting layer was deposited on IBAD-MgO substrate at optimal oxygen partial pressure (pO2) and deposition temperature. After fabrication of GdBCO coated conductor, critical current density was measured by 4-probe method. Surface morphology and texture of GdBCO coated conductors were analyzed by the SEM and XRD, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05a
• /
• pp.157-159
• /
• 2005

본 연구에서는 저온 액상반응법을 이용하여 활성제 Eu의 농도를 10wt%로 도핑하고 열처리를 각각 450, 700, $900^{\circ}C$로 1h 유지하여 $Gd_2O_3:Eu^{3+}$ 나노형광체를 합성하였다. 제조된 형광체의 결정화, 입자크기를 XRD, BET로 분석하였고, 이들이 발광 휘도에 미치는 영향을 확인하였다. 또한 합성된 형광체의 PL(photoluminescence) 특성을 알아보기 위해 여기파장 254nm 의한 발광스펙트럼, 611nm에 의한 여기스펙트럼을 조사하였다. 발광 특성은 611nm에서 주 peak을 갖는 $Eu^{3+}$ 이온에 의한 $^5D_0-^7F_{J(J=0,1,2)}$ 전이에 기인된 전형적인 Red 형광체의 특성을 나타냈고, 입자크기는 평균 20-60nm 정도이고, 발광강도는 열처리 온도가 증가함에 따라 향상되었다.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.6
• /
• pp.2017-2022
• /
• 2012

Three isostructural lanthanide coordination polymers, $[Ln(L)_3(H_2O)_2](H_2O)_3$ {Ln = Eu (1), Tb (2), Gd (3); L = $trans$-3-(3-pyridyl)acrylate, (3-py)-CH=CH-COO}, were prepared from HL, lanthanide nitrate, and NaOH in $H_2O$ by microwave heating. In all coordination polymers, the metal is bonded to eight oxygen atoms, and all pyridyl nitrogen atoms do not coordinate to the metals. All polymers have a 1-D loop-connected chain structure. The hydrogen atoms in the aqua ligands and lattice water molecules all participate in the hydrogen bonds of the O-$H{\cdots}O$ or O-$H{\cdots}N$ type. The hydrogen bonds connect the 1-D chains to create a 2-D network. Polymer 1 exhibited red luminescence in the solid state at room temperature.