In order to develop alloy resistance in aggressive sulphat ion, the corrosion behavior of metallic glasses $Ni_{92{\cdot}3}Si_{4.5}B_{32}$, $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ (at %) at different concentrations of $H_2SO_4$ solutions was examined by electrochemical methods and Scanning Electron Microscope (SEM) and X-ray Photoelectron Microscopy (XPS) analyses. The corrosion kinetics and passivation behavior was studied. A direct proportion was observed between the corrosion rate and acid concentration in the case of $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloys. Critical concentration was observed in the case of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ alloy. The influence of the alloying element is reflected in the increasing resistance of the protective film. XPS analysis confirms that the protection film on the $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ alloy was NiS which is less protective than that formed on Cr containing alloys. The corrosion rate of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$. alloys containing 7% and 13% Cr are $7.90-26.1{\times}10^{-3}$ mm/y which is lower about 43-54 times of the alloy $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ (free of Cr). The high resistance of $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloy at the very aggressive media may due to thicker passive film of $Cr_2O_3$ which hydrated to hydrated chromium oxyhydroxide.

• 한국자기학회지
• /
• 제3권3호
• /
• pp.185-189
• /
• 1993

급속응고법으로 제작된 비정질 $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금의 열처리에 따른 구조 및 자기특성이 조사되었다. 비정질 $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금은 $600^{\circ}C$이하의 열처리온도에서 약 10 nm의 초미세결정립이 형성된다. $600^{\circ}C$이상의 열처리 조건에서는 결정립크기가 급격히 증가하여 자기특성을 열화시킨다. $Fe_{85-x}Co_{x}Zr_{7}B_{7}Cu_{1}$ 합금의 최적열처리온도는 Fe-Zr-B초미세결정립합금에 비하여 낮으며, 결정립크기 또한 감소한다. 이는 Cu의 첨가에 기인하는 것으로 판단된다. 최적열처리조건에서 $Fe_{80}Co_{5}Zr_{7}B_{7}Cu_{1}$ 초미세결정립합금의 포화자화 및 f=50 kHz, $B_{m}=0.2\;T$에서 측정한 투자율 및 철손은 각각 157.3 emu/g(1.5 T), $1.8{\times}10^{4}$ 및 13 W/kg으로 자기특성이 가장 우수하다.

• 한국자기학회지
• /
• 제9권6호
• /
• pp.285-290
• /
• 1999

고투자율 및 고포화자화 특성을 동시에 만족하는 새로운 연자성 박막을 개발하기 위해 Fe-Zr-B계 조성에 Fe원소와 비고용 원소인 Ag를 첨가시킨 Fe86.7Zr3.3B4Ag6 비정질 박막을 DC 마그네트론 스퍼터링법으로 제조한 후 일축 자장중에서 1시간 동안 진공 열처리를 한 후 fan을 이용하여 냉각하여 특성을 조사하였다. Fe86.7Zr3.3B4Ag6 박막을 40$0^{\circ}C$에서 열처리한 후 1.7T의 높은 포화자화와 1 Oe의 낮은 보자력으로 인해 50 MHz에서 투자율이 7,800(0.2 mOe)으로 우수한 연자기 특성을 나타내었으며, 1 MHz에서 손실이 1.4 W/cc(B=0.1T)로 매우 낮았다. 이러한 고주파 연자기 특성은 Ag 첨가에 의해 비정질 기지에 미세한 bcc $\alpha$-Fe cluster가 균일하게 형성되었기 때문이라 생각된다.

• 한국자기학회지
• /
• 제12권3호
• /
• pp.88-93
• /
• 2002

소량의 Zn및 Sn분말을 급냉응고된 NdFeB 자성합금 분말에 첨가한 후 CA-press공정에 의해 등방성 자석을 제조하고, 제조된 등방성 자석을 CA-deformation 공정에 의해 소성변형시켜 이방성 자석을 제조하였다. 원료분말만을 밀링하여 사용한 경우, 밀링시간에 관계없이 잔류자화값은 일정하였으며, 보자력은 초기원료 분말을 그대로 사용하는 경우에 비하여 감소하였다. 이에 반해 소량의 Zn및 Sn분말을 첨가하고 볼밀링에 의하여 혼합한 분말로부터 제조된 등방성 자석 및 이방성 자석의 보자력은 첨가원소가 없는 경우의 시편보다 증가하였으며, 0.3wt.% Zn및 Sn이 첨가된 이방성 자석에서는 보자력이 5kOe 정도 증가하였다.

• 한국초지조사료학회지
• /
• 제24권1호
• /
• pp.11-20
• /
• 2004

Orchardgrass 및 white clover의 단파 및 혼파 재배조건에서 미량요소 Fe, Mn, Cu, Zn, Mo및 B의 조합시비가 목초의 생육, 개화, 수량, 양분 함량 및 식생구성비율 등에 미치는 영향을 구명하였다. 다량요소 양분을 동일 량 시비한 조건에서 7 수준의 미량요소 조합시비는 $T_1$;대구조, $T_2$; Fe, $T_3$; Fe＋Mn, $T_4$: Fe＋Mn＋Cu, $T_5$; Fe＋Mn＋Cu＋Zn, $T_6$ ; Fe＋Mn＋Cu＋Zn＋Mo 및 $T_7$ ;Fe＋Mn＋Cu＋Zn＋Mo＋B로 하였다. 본 IV보에서는 조합시비가 목초 중 미량요소의 함량에 미치는 영향을 검토하였다. 1. 미량요소의 함량은 일반적으로 조합시비, 초종(grass-clover), 재배방법(단파-혼파), 예취 회수 및 추비 유무별 차이를 보였다. 단파재배와 비교해서 혼파에서 orchardgrass는 더 낮은 B와 Fe-함량, 더 높은 Mn, Zn-함량을 보였고 white clover는 이의 반대경향을 보였다. 그러나 Cu와 Mo-함량은 차이를 보이지 않았다. 2. 상대적인 함량 비교에서 일반적으로 $T_7$ 7처리로 orchardgrass의 경우 Cu, Zn 및 Mo-함량은 낮아졌고 Mn-함량은 높아졌다. 이에 비해서 white clover의 경우는 Fe, Mn 및 Cu-함량은 높아졌고 그리고 Mo-함량은 낮아졌다. 목초 중 Fe-함량은 $T_3$(Fe＋Mn)에서 Fe과 Mn 간의 길항작용으로 현저히 낮아졌다. 본 시험재배 조건별 Fe-함량의 변화는 white clover가 orchardgrass보다 상대적으로 더 큰 차이를 보였다. Mn-함량은 초종 간 큰 차이를 보였고 두 목초 공히 Mn을 함유한 조합시비로 크게 증가하였지만 이들 조합시비 간에는 차이가 경미하였다. 3. Mo-함량은 모든 경우 $T_6$ 6및 $T_7$ 에서 다소 높은 수준 이였다. $T_7$ 은 $T_6$ 에 비해서 Mo-함량이 다소 낮아졌다. Mo-과다피해는 B/Mo 비율의 조화 또는 B-시비를 통해서 경감되거나 방지할 수 있는 것으로 보였다. 모든 경우 white clover가 orchardgrass보다 B-함량이 높았고 $T_7$ 에서 B-함량이 크게 증가하였다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.786-787
• /
• 2006

The magnetic inductance of nanocrystalline $Fe_{73}Si_{16}B_7Nb_3Cu_1$ and an amorphous FeSiB powder sheet has been investigated to identify RFID performance. The powder was mixed with binder and solvent and tape-casted to form films. Results show annealing significantly influenced on the inductance of the material. The surface oxidation of the particles was the main reason for the reduced inductance. The maximum inductance of $Fe_{73}Si_{16}B_7Nb_3Cu_1$ alloy was about $88{\mu}H$ at 17.4 MHz, about 65% greater compared to the FeSiB alloy. The higher inductance in the nanocrystalline alloy indicates it may be used as a potential replacement of current RFID materials.

• 한국자기학회지
• /
• 제2권3호
• /
• pp.193-199
• /
• 1992

희토류 영구자석, $Nd_2Fe_{14}B$ 화합물에 대한 자체충족적 국재밀도함수근사 전자 구조 계산을 수행하여 이 물질의 전자기적 물성을 연구하였다. LMTO(Linearized Muffin-Tin Orbital)에너지 띠 방법을 사용하여 상자성, 강자성상에서 구한 $Nd_2Fe_{14}B$ 화합물의 에너지 띠구조를 토대로 하여 자성을 포함한 제반 물성, 즉 희토류금속과 천이금속의 결합(bonding)효과, 전기적, 자기적 구조등을 고찰하였다. Boron 원자의 역학은 근접 Fe 원자와의 혼합 상호작용을 통하여 Fe의 원자의 자기모멘트를 많이 줄이는 효과를 주며 또한 구조 안정성에 기여한다는 결과를 얻었다. 강자성상에서의 Fe 원자들의 평균 자기모멘트는 약 2.15 ${\mu}B$로 계산되었는데 이중 Boron 원자로 부터 가장 멀리 떨어져 있으며 12개의 Fe 원자들로 둘러싸인 Fe(j2-site)원자가 가장 큰 값(2.7 ${\mu}B$)의 자기모멘트를 갖고 Boron 원자와의 혼합 상호작용이 가장 큰 Fe(e-site)원자가 가장 작은 값(1.9 ${\mu}B$)의 자기모멘트를 갖는다.

• 한국자기학회지
• /
• 제12권1호
• /
• pp.30-33
• /
• 2002

초미세결정렵 Nd-Fe-B-Mo-Cu합금에서 Co 치환이 미세조직과 자기특성에 미치는 영향을 조사 하였다. 급속응고법으로 제조된 비정질 Nd-(Fe, Co)-B-Mo-Cu합금은 결정화에 의하여 $\alpha$-Fe기 초미세결정립 Nd-(Fe, Co)-B-Mo-Cu합금이 제조되었다. Co로의 Fe치환은 결정립 미세화에 기여하며, 이로 인하여 경자기특성이 개선되었다. 최적열처리된 초미세결정립 N $d_4$(F $e_{0.85}$ $Co_{0.15}$)$_{82}$ $B_{10}$M $o_3$Cul합금의 잔류자화, Curie온도는 Co가 치환되지 않은 합금에 비하여 개선된 우수한 특성을 나타내었다. 64$0^{\circ}C$, 10분 열처리된 초미세결정립 N $d_4$(F $e_{0.85}$ $Co_{0.15}$)$_{82}$ $B_{10}$M $o_3$Cu 합금의 평균결정립 크기는 약 15 nm이며, 이때 보자력, 잔류자화 및 최대에너지적은 각각 239kA/m, 1.4 T 및 103.5 kJ/ $m^3$이었다.

• 한국자기학회지
• /
• 제3권3호
• /
• pp.190-195
• /
• 1993

새로운 Fe기 초미세 결정립합금의 제조 가능성 및 자기특성에 관하여 조사하였다. 고포화자화 (Fe.$_{85}$Co.$_{15}$ )$_{80}$B$_{20}$ 비정질합금에서 천이금속을 약 10 at.% Al으로 치환한 (Fe.$_{85}$ Co.$_{15}$ )$_{70}$B$_{20}$Al$_{10}$ 합금은 급속응고에 의하여 비정질 기지내에 직접 .alpha. -Fe(Co)의 석출이 가능하다. 또한 (Fe.$_{85}$Co.$_{15}$ )$_{70}$B$_{20}$Al$_{10}$합금에 2~6 at.% Nb의 첨가는 급속 응고시 결정립성장을 억제하고 포화자왜를 약 6ppm이하로 감소시켜 자기 특성을 개선시킨다. 열처리에 의한 자기 특성은 Nb의 치환량이 증가할 수록 감소한다. 400 .deg. C에서 1시간 열처리한 (Fe.$_{85}$Co.$_{15}$ )$_{70}$ B$_{18}$ Al$_{10}$Nb$_{2}$합금은 평균 약 8nm이하의 .alpha. -Fe(Co) 결정립으로 구성된 초미세 결정립합금 으로 제조가 가능하며, 포화자속밀도, 철손 및 투자율 (f=50 kHz, B$_{m}$ =0.2 T)이 각각 1.2 T, 12W/kg 및 2.5 *$10^{4}$으로 가장 우수하다. 이는 Fe-Si-B-Nb-Cu 초미세결정립합금 및 영자왜 Co기 비정질합금과 거의 같은 자기특성을 나타낸다.다..다.다..낸다.다..

• 한국자기학회지
• /
• 제5권1호
• /
• pp.64-70
• /
• 1995

$ThMn_{12}$ 구조를 갖는 $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$의 결정학적 및 자기적 성질을 X선 회절법과 VSM, $M\"{o}ssbauer$분광법으로 연구하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$합금은 알곤가스 분위기의 아크 용해로에서 제조하였다. $NdFe_{10.7}TiM_{0.3}$의 결정구조는 순수 단일상의 tetragonal구조를 갖고 있으며 $a_{0}=8.587\;{\AA},\;c_{0}=4.788\;{\AA}$의 격자상수를 결정하였다. $M\"{o}ssbauer$ spectrum은 13 K 부터 770 K 영역까지 취하였으며 Curie 온도는 $NdFe_{10.7}TiM_{0.3}$의 경우 $570{\pm}3\;K$로 결정하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$은 $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f의 5 set의 Fe 이온의 subspectra로 분석하였다. $NdFe_{10.7}TiM_{0.3}$의 실온에서 Fe-site $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f는 16.4, 8.2, 14.8, 21.3 및 39.3%의 면적비를 각각 가지고 있었다. 초미세자기장은 $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$비로 감소함을 알았다.