Abstract
The authors have studied crystallographic and magrletic properties of $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$ by X-ray diffraction, VSM magnetometer, and Mossbauer spectrometer. The Alloys were prepared by arc-melting under argon atmosphere. The $NdFe_{10.7}TiM_{0.3}$ has pure single phase, whereas the $NdFe_{10.7}Ti_{1.3}$ contains some $\alpha-Fe$, from powder X-ray diffractometry. The $NdFe_{10.7}TiM_{0.3}$ has the $ThMn_{12}$-type tetragonal structure with $a_{0}=8.587\;{\AA}\;and\;c_{0}=4.788\;{\AA}$. The Curie temperature ($T_c$) is $570{\pm}3\;K$ from $M\"{o}ssbauer$ spectroscopy performed at various temperatures ranging from 13 to 770 K. Each spectrum of below $T_c$ was fitted with five subspectra of Fe sites in the structure ($8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}\;and\;8f$). The area fraction of the subspectra at room temperature are 16.4, 8.2, 14.8, 21.3 and 39.3 %, respectively. Magenetic hyperfine fields for the Fe sites decrease in the order, $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$.
$ThMn_{12}$ 구조를 갖는 $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$의 결정학적 및 자기적 성질을 X선 회절법과 VSM, $M\"{o}ssbauer$분광법으로 연구하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$합금은 알곤가스 분위기의 아크 용해로에서 제조하였다. $NdFe_{10.7}TiM_{0.3}$의 결정구조는 순수 단일상의 tetragonal구조를 갖고 있으며 $a_{0}=8.587\;{\AA},\;c_{0}=4.788\;{\AA}$의 격자상수를 결정하였다. $M\"{o}ssbauer$ spectrum은 13 K 부터 770 K 영역까지 취하였으며 Curie 온도는 $NdFe_{10.7}TiM_{0.3}$의 경우 $570{\pm}3\;K$로 결정하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$은 $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f의 5 set의 Fe 이온의 subspectra로 분석하였다. $NdFe_{10.7}TiM_{0.3}$의 실온에서 Fe-site $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f는 16.4, 8.2, 14.8, 21.3 및 39.3%의 면적비를 각각 가지고 있었다. 초미세자기장은 $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$비로 감소함을 알았다.