• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Journal of the Korean Magnetics Society
• /
• v.17 no.3
• /
• pp.124-127
• /
• 2007

Magnetic tunnel junctions (MTJs), which consisted of amorphous CoFeSiB layers, were investigated. The CoFeSiB layers were used to substitute for the traditionally used CoFe and/or NiFe layers with an emphasis given on understanding the effect of the amorphous free layer on the switching characteristics of the MTJs. CoFeSiB has a lower saturation magnetization ($M_s\;:\;560\;emu/cm^3$) and a higher anisotropy constant ($K_u\;:\;2800\;erg/cm^3$) than CoFe and NiFe, respectively. An exchange coupling energy ($J_{ex}$) of $-0.003\;erg/cm^2$ was observed by inserting a 1.0 nm Ru layer in between CoFeSiB layers. In the Si/$SiO_2$/Ta 45/Ru 9.5/IrMn 10/CoFe 7/$AlO_x$/CoFeSiB 7 or CoFeSiB (t)/Ru 1.0/CoFeSiB (7-t)/Ru 60 (in nm) MTJs structure, it was found that the size dependence of the switching field originated in the lower $J_{ex}$ using the experimental and simulation results. The CoFeSiB synthetic antiferromagnet structures were proved to be beneficial for the switching characteristics such as reducing the coercivity ($H_c$) and increasing the sensitivity in micrometer size, even in submicrometer sized elements.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.196-201
• /
• 2001

The dependence of CoFe interfacial layer thickness and plasma oxidation condition on tunneling magnetoresistance (TMR) in Ta/NiFe/FeMn/NiFe/Al$_2$O$_3$/NiFe/Ta tunnel junctions was investigated. As the CoFe layer thickness increases, TMR ratio rapidly increases to 13.7 % and decreases with further increase of the CoFe layer thickness. The increase of TMR with the CoFe thickness up to 25 was thought to be due mails to the high spin-polarization of CoFe. The maximum MR of 15.3% was obtained in the Si(100)/Ta(50 )/NiFe(60 )/FeMn(250 )/NiFe(70 )/Al$_2$O$_3$/NiFe(150 )/Ta(50 ) magnetic tunnel junction with a 16 Al oxidized for 40 sec using a Ar/O$_2$ (1:4) mixture gas.

• Journal of the Korean Chemical Society
• /
• v.25 no.5
• /
• pp.318-324
• /
• 1981

The effects of$ Fe_2O_3$ aggregation on the sintering of Ba-ferrite (BaFe$_{12}O_{19}$) were studied. $BaCO_3-Fe_2O_3$ mixtures were prepared by partial precipitation mixing and ball-mill mixing method using two different $Fe_2O_3 $powders. Techniques employed were TG, XRD and SEM. X-ray diffraction analysis showed that the over all reaction basically consists of the two consecutive reaction; $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$ It is also shown that the aggregation state of $Fe_2O_3$ raw materials, as well as the mixing method, has a remarkable effect on solid state reaction between $BaCO_3\;and\;Fe_2O_3$.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.210-219
• /
• 2000

The magnetoresistance characteristics of FeN/Co/Cu/Co and FeN/Co/Cu/Co/Cu/Co/FeN multilayers using ferromagnetic iron-nitrides (FeN) has been studied. The microstructure of FeN film is the mixed ${\alpha}$-Fe and $\varepsilon$-Fe$_3$N phase on the condition that the flow rate of N$_2$ gas is over 0.4 sccm. The magnetoresistance effect is observed because of shape magnetic anisotropy induced by needle-shaped $\varepsilon$-Fe$_3$N phase. This magnetoresistance effect changes, because the degree that the shape magnetic anisotropy adheres to the adjacent Co pinned layer is varied according to the flow rate of N$_2$ gas and the thickness of FeN film. The best magnetoresistance effect is obtained on the condition that the thickness of Co free layer is 70 ${\AA}$ and the maximum MR ratio(%) value of 3.2% shows in the FeN(250 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/Cu(25 ${\AA}$)/Co(70 ${\AA}$)/FeN(250 ${\AA}$) mutilayer film which is fabricated at the N, gas flow rate of 0.5 sccm and the FeN film thickness of 250 ${\AA}$. Four steps are observed in the magnetoresistance curve owing to this difference of coercive force, because respective magnetic layers in the multilayer possess different coercive forces. These effects observed in these mutilayer films can be expected to application to the memory device the same MRAM as can carry out simultaneously four signals.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.5
• /
• pp.183-189
• /
• 2014

This study was conducted to study the influence of Co and Fe on the color of glaze and diopside crystals in the diopside crystal glaze empirically produced and used by ceramic artists, in case of adding $Co_3O_4$ and $Fe_2O_3$. As a result, the color of glaze was blue when $Co_3O_4$ was added to the diopside crystal glaze and the diopside crystals appeared pastel violet with Co included. When $Fe_2O_3$ was added to the diopside crystal glaze, the color of glaze appeared brown and the color of diopside crystals was goldenrod with Fe included. The crystals precipitated on the surface of diopside consisted of diopside crystals and diopside precursors. With longer retention time, the amount of diopside precursors decreased and the amount of diopside crystals increased. Also, Co was more easily included by the diopside crystals than Fe was and crystallizability of dispside was improved in case of including Co. Including Fe lowered peak intensity of properties and partially dissolved the diopside crystals.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.154-158
• /
• 1999

Magnetic properties and microstructure of nanocrystalline $\alpha$-(Fe, Co)-based Nd-(Fe, Co)-B-Nb-Cu alloys have been investigated. $Nd_x(Fe_{0.9}Co_{0.1})_{90-x}B_6Nb_3Cu_1$(x=2, 3, 4, 5, 6) alloys prepared by rapid solidification process show amorphous phase except the one with x=2. By a proper annealing, the amorphous in the alloy is changed to a nanocrystalline phase. It is confirmed that the nanocrystalline alloys are composed of $\alpha$-(Fe, Co) and $Nd_2(Fe, Co)_{14}B_1$ phase. The optimally annealed $Nd_3(Fe_{0.9}Co_{0.1})_87B_6Nb_3Cu_1$ alloy shows the highest remanence of 1.55 T. The coercivity increases with the increase of Nd content The maximum coercivity of 4.6 kOe is obtained from an optimally annealed $Nd_6(Fe_{0.9}Co_{0.1})_84B_6Nb_3Cu_1$ alloy, resulting in the maximum energy product of 10.6 MGOe.

• Journal of the Korean Ceramic Society
• /
• v.19 no.3
• /
• pp.223-228
• /
• 1982

For the preparation of ferroxidure BaO.5.5 $Fe_2O_3$ with high coercive force, the green and calcined coprecipitates, which were obtained by neutralizing the mixed salt solution $FeCl_2-BaCl_2$ and $FeCl_3-BaCl_2$ with alkali solution $NaOH-Na_2CO_3$, were investigated about the thermal reaction, crystal growth, and the magnetic properties of the sintered specimens. The very single-domain crystallites of Ba-ferrite with high coercive force are formed from the coprecipitate of amorphous $Fe(OH)_3$ and amorphous $BaCO_3$ at lower temperature than that of subnucleus crystalline $\delta$-FeOOH and amorphous $BaCO_3$.

• Journal of the Korean Magnetics Society
• /
• v.16 no.1
• /
• pp.1-5
• /
• 2006

The crystallographic properties and cation distribution of oxyspinels ferrite $Co_xFe_{1-x}O_4$ thin films have been explored by X-ray diffraction, vibrating sample magnetometer (VSM), and conversion electron $M\"{o}ssbauer$ spectroscopy (CEMS). Thin films are prepared by sol-gel method. Normal spinel structure is transformed to inverse spinel structure with increasing Co concentration CEMS results indicate that most of $Fe^{3+}$ ions are substituted to $Co^{3+}$ions. Accordingly $Co^{2+}$ ions on octahedral site migrate to tetrahedral site. Magnetic moment is decreased with increasing Co concentration, which means high spin $Fe^{3+}$ ions are replaced by low spin $Co^{3+}$.

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.85-88
• /
• 2008

We calculated the electronic structures of substituted cobalt nitrides, that is $FeCo_3N$ and $NiCo_3Ni$, by using the all electron fullpotential linearized augmented plane-wave (FLAPW) energy band method, and investigated the influence on the magnetic properties of $Co_4N$ due to the substitution of Co atom located at corner sites by iron and nickel atoms. We found that the magnetic moments of CoII atoms located at the face-center positions in these compounds are almost same to that of $Co_4N$. The magnetic moments of Fe and Ni atoms in $FeCo_3N$ and $NiCo_3Ni$ are 3.086 and $0.795\;{\mu}_B$, and they have the localized nature of magnetism.