$Fe_2O_3$ Aggregation and Sintering of Ba-Ferrite

$Fe_2O_3$ 응집상태와 Ba-Ferrite의 소결성

  • Hyo-Duk Nam (Department of Electronics Engineering, College of Engineering) ;
  • Sang-Hee Cho (Department of Electronics Engineering, College of Engineering)
  • 남효덕 (경북대학교 공과대학 전자공학과) ;
  • 조상희 (경북대학교 공과대학 전자공학과)
  • Published : 1981.10.30

Abstract

The effects of$ Fe_2O_3$ aggregation on the sintering of Ba-ferrite (BaFe$_{12}O_{19}$) were studied. $BaCO_3-Fe_2O_3$ mixtures were prepared by partial precipitation mixing and ball-mill mixing method using two different $Fe_2O_3 $powders. Techniques employed were TG, XRD and SEM. X-ray diffraction analysis showed that the over all reaction basically consists of the two consecutive reaction; $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$ It is also shown that the aggregation state of $Fe_2O_3$ raw materials, as well as the mixing method, has a remarkable effect on solid state reaction between $BaCO_3\;and\;Fe_2O_3$.

일차입자의 크기와 응집상태가 다른 두 종류의 $Fe_2O_3$를 부분침전법과 ball-mill 혼합법으로 BaCO$_3$와 혼합한 $BaCO_3-Fe_2O_3$계의 고체반응에 있어 $Fe_2O_3$분체의 영향을 조사하였다. TG, XRD, SEM 등을 측정에 사용하였으며, X-선 회절분석결과 Ba-ferrite의 생성과정은 다음과 같은 연속적인 2단계로 이루어진다는 것을 알았다. $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$$Fe_2O_3$원료분체의 응집상태와 혼합방법은 고체반응에 현저한 영향을 미친다는 것을 확인했다.

Keywords

References

  1. Philips Tech. Rev. v.13 J. J. Went;G. W. Rathenau;E. W. Gorter
  2. Sumito Kinjoku v.10 no.4 K. Yasuhara;G. Asano
  3. Powder Metallurgy International v.4 no.2 Th. Maurer;H. G. Richter
  4. J. Amer. Ceram. Soc. v.56 no.4 J. S. Reed;R. M. Fulrath
  5. Sci. Papers I. P. C. R. v.54 no.2 M. Sugimoto;T. Takei
  6. J. Amer. Ceram. Soc. v.43 no.3 Y. Goto(et al.)
  7. J. Chem. Soc. no.A J. Beretka;M. J. Ridge
  8. J. Can. Ceram. Soc. v.36 R. E. Hamilton
  9. J. Amer. Ceram. Soc. v.44 no.12 S. L. Blum;P. C. Li
  10. Ceramic Bulletin v.59 no.4 T. Nomura;T. Yamaguchi
  11. Cermurgia Int. v.2 no.2 T. Yamaguchi;S. H. Cho