• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1056-1064
• /
• 1995

95Pb(Mg1/3Nb2/3)O3-5PbTiO3 (hereinafter designated as 95PMN-5PT) system was prepared by the columbite-precursor method with 2 mol% excess PbO to compensate the PbO loss during thermal process. The amount of CuO was 1~10 mol%, and the effects of CuO addition on the dielectric properties of this system have been investigated. From the microstructures, XRD analysis and dielectric measurements, the solubility limit of CuO in 95PMN-5PT was found to be around 3 mol%. Lattice parameter and Curie temperature were found to be decreased as the amount of CuO increased up to the solubility limit. This result confirmed that the Cu2+-ions substituted the Pb2+-ions. It was revealed that the addition of CuO on 95PMN-5PT promoted the sinterability and properties. The room temperature dielectric constant, the loss factor and the specific resistivity of the specimens processed with optimum conditions were 23000, 1%, and 8$\times$1011Ω.cm, respectively.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.103-104
• /
• 2007

$CuInO_2$ 단일상은 합성조건이 매우 까다롭기 때문에 일반적인 고상법으로 얻기 힘든 것으로 알려저 있다. 투명전도성 $CuInO_2$ 박막을 증착하기 위하여 일반적인 고상법으로 Cu와 In의 비율이 1:1인 $Cu_2O-In_2O_3$ composite target 및 In 대신 Ca, Mg, Ti가 각각 1mol% 도핑된 target을 제작하였다. 제작된 각각의 composite target을 이용하여 pulsed laser deposition(PLD) 공정으로 투명전도성 $CuInO_2$ 박막을 증착하였다. Cu와 In이 1:1 인 $Cu_2O-In_2O_3$ composite target을 사용한 경우, 증착된 박막이 Cu와 In의 비율이 1:1인 c-axis 배향된 단일상의 $CuInO_2$ 박막임을 확인하였다.

• Applied Chemistry for Engineering
• /
• v.10 no.1
• /
• pp.154-159
• /
• 1999

EDTA (ethylenediaminetetraacetic acid), a chelating agent is most widely used in industrial applications, especially for cleaning of metals in water, frequently prohibits metal removal from water in conventional water treatment technologies. It could be easier to remove aqueous metal ions by the breakdown of DETA complexed bonds first. This study investigated the availability of $TiO_2$ photo-catalysis for the aqueous phase oxidation of Cu(II)-EDTA, under an aerobic condition at $20^{\circ}C$ with $TiO_2$ (Degussa P-25) and 1.79mM of Cu(II)-EDTA. When $TiO_2$ loading was 2.0 g/L, the photo-catalytic oxidation of Cu(II)-EDTA was maximal. The tendency of EDTA adsorption onto the catalyst surface was affected by $TiO_2$ surface charge, and the oxidation rate of Cu(II)-EDTA by photo-catalysis was shown to be dependent upon the tendency of EDTA adsorption before photo-irradiation.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.9
• /
• pp.2813-2817
• /
• 2014

A new magnetic semiconductor material was synthesized to enable separation after a liquid-type photocatalysis process. Core@shell-structured $CuFeS_2@TiO_2$ magnetic nanoparticles were prepared by a combination of solvothermal and wet-impregnation methods for photocatalysis applications. The materials obtained were characterized using X-ray diffraction, transmission electron microscopy, ultraviolet-visible, photoluminescence spectroscopy, Brunauer-Emmett-Teller surface area measurements, and cyclic voltammetry. This study confirmed that the light absorption of $CuFeS_2$ was shifted significantly to the visible wavelength compared to pure $TiO_2$. Moreover, the resulting hydrogen production from the photo-splitting methanol/water solution after 10 hours was more than 4 times on the core@shell structured $CuFeS_2@TiO_2$ nanocatalyst than on either pure $TiO_2$ or $CuFeS_2$.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.571-576
• /
• 2011

Activity carbon (AC), Cu and $Cu_2O$ modified $TiO_2$ composites (Cu/$Cu_2O$-AC/$TiO_2$) were prepared using a sol-gel method. The characteristics of the composites were evaluated using Brunauer-Emmett-Teller (BET) surface area measurements, X-ray diffraction (XRD), energy dispersive X-ray (EDX) analysis and scanning electron microscope (SEM) analysis. A methyl orange (MO) solution under visible light irradiation was used to determine the photocatalytic activity. The degradation of MO was determined using UV/Vis spectrophotometry. $Cu_2O$, Cu and the cooperative effect of the AC increased the photo-absorption effect, thus increasing in photocatalytic activity.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1046-1054
• /
• 2001

Effects of B$_2$O$_3$and CuO addition on the microwave dielectric properties of the PbWO$_4$-TiO$_2$ceramics were investigated in order to use this material as an LTCC material for fabrication of a multilayered RF passive components module. We found that PbWO$_4$could be used as an LTCC material because of its low sintering temperature (8$50^{\circ}C$) and fairy good microwave dielectric properties($\varepsilon$$_{r}$=21.5, Q$\times$f$_{0}$=37200 GHz and $\tau$$_{f}$ =-31 ppm/$^{\circ}C$). In order to stabilize $\tau$$_{f}$ of PbWO$_4$, TiO$_2$was added to the PbWO$_4$and the mixture was sintered at 8$50^{\circ}C$. A near zero $\tau$$_{f}$ value (+0.2 ppm/$^{\circ}C$) was obtained with 8.7 mol% TiO$_2$addition. $\varepsilon$r and Q$\times$f$_{0}$ values were 22.3 and 21400 GHz, respectively. It was believed that the decrement of Q$\times$f$_{0}$ value with TiO$_2$addition was resulted from increasing grain boundary. In order to improve Q$\times$f$_{0}$, various amounts of B$_2$O$_3$and CuO were added to the 0.913PbWO$_4$-0.087TiO$_2$mixture. The optimum amount of CuO was 0.05 wt%. At this addition, the 0.913PbWO$_4$-0.087TiO$_2$ceramic showed $\varepsilon$$_{r}$=23.5, $\tau$$_{f}$ =-2.2ppm/$^{\circ}C$, and Q$\times$f$_{0}$=32900 GHz after sintered at 8$50^{\circ}C$. In case of B$_2$O$_3$addition, the optimum amount range was 1.0~2.5 wt% at which we could obtain following results; $\varepsilon$$_{r}$=20.3~22.1, Q$\times$f$_{0}$=48700~54700 GHz, and $\tau$$_{f}$ =+2.4~+8.2ppm/$^{\circ}C$.

• Journal of Sensor Science and Technology
• /
• v.32 no.4
• /
• pp.238-245
• /
• 2023

0.75(Bi_1/2Na_1/2)TiO₃-0.25SrTiO₃ (BNT-25ST) ceramics with high densities were successfully prepared at a sintering temperature of 1,000℃ by adding a mixture of 1 mol% CuO and 0.5 mol% Na₂CO₃ or 0.5 mol% CuO and 0.25 mol% Na₂CO₃. Double polarization-electric field (P-E) hysteresis curves and sprout-shaped bipolar strain-electric field (S-E) hysteresis curves with small negative strains were observed in the pristine and CuO-added BNT-25ST ceramics whereas the Na₂CO₃-added sample showed similar P-E and S-E curves to a typical ferroelectric. The pristine BNT-25ST ceramics showed an extremely large strain and a large-signal piezoelectric strain constant (d₃₃^*): 0.287 % at 80 kV/cm and 850 pm/V at 20 kV/cm. Similar values, 0.248 % at 80 kV/cm and 655 pm/V at 20 kV/cm, were obtained in the CuO-added sample. However, the pristine and CuO-added samples showed large hysteresis in unipolar S-E curves at an electric field of less than 20 kV/cm. The Na₂CO₃-added sample showed smaller values of the strain and d₃₃^* but displayed a linear change and small hysteresis in the unipolar S-E curve. The co-added sample with CuO and Na₂CO₃ displayed intermediate P-E and S-E hysteresis curves.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.2
• /
• pp.70-76
• /
• 2014

$Zn_2TiO_4$, using an anatase form of $TiO_2$ on zinc crystalline glaze, was shown as effective nuclear agent. Thus the effects on glaze were studied with synthesized $Zn_2TiO_4$ at low temperature. First, the chromophore elements were employed in synthesized $Zn_2TiO_4$ then add them in the zinc crystalline glaze. Crystal creation and development of color by $Zn_2TiO_4$ addition on the zinc crystalline glaze were more effective. Addition of $Zn_2TiO_4$, which is developed in low range temperature, is effected as zinc crystalline nuclear in the willemite glaze. When 5 wt% of synthesized $Zn_2TiO_4$ was added to the willemite glaze, nuclear creation increases and steadily retains. Therefore addition of respectively doped $Zn_2TiO_4$ with CoO, NiO, and CuO would increase doped effects in the glaze, various color willemite crystal were obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.679-683
• /
• 2004

[ $BaO-Sm_2O_3-4TiO_2$ ] 세라믹을 LTCC용 재료로 사용하기 위해 $B_2O_3$와 CuO를 소결조제로 첨가하여 소결온도를 낮추었다. 10.0 mol%의 $B_2O_3$만을 첨가하였을 경우 $1000^{\circ}C$에서 2시간 소결시 er=72.23, Qf=4,050GHz, ${\tau}f=-0.574ppm/^{\circ}C$의 우수한 유전 특성값을 얻을 수 있었지만, $960^{\circ}C$이하에서는 소결이 잘 이루어지지 않았다. $B_2O_3$와 CuO를 동시에 소결조제로 첨가하였을 경우에는 $900^{\circ}C$에서 2시간 소결시 10.0 mol% $B_2O_3$, 15.0 mol% CuO의 첨가조성에서 ${\varepsilon}r$=70.09, Qf=4,728GHz의 우수한 유전특성을 보여 고유전율을 가진 저온 동시 소결용 재료로서의 가능성을 보여주었다. 이처럼 BaO-$Sm_2O_3-4TiO_2$ 세라믹의 소결온도를 낮출 수 있었던 요인은 소결온도보다 용융점이 낮은 2차상들이 액상을 형성하여 액상소결이 진행되었기 때문이며 이때 소결에 기여한 이차상들은 결정화되지 못하고 비정질 상태로 남아있는 것으로 추정된다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.663-663
• /
• 2013

We prepared Cu oxides, and Ni and Pd-TiO2@SiO2 core-shellnanostructures, and tested their CO oxidation performances by temperature-programmed mass spectrometry. We found the starting temperatures of CO oxidation are around $200^{\circ}C$ and $300^{\circ}C$ for Ni and Pd-TiO2@SiO2 nanostructures, respectively. Cu oxides are cubes with 50~200 nm with, prepared with different concentrations of NaOH and ascorbic acid. For the core-shell structures, we prepared 100 nm SiO2 spheres, first coated the surface with TiO2 precursor, and then coated with Ni and Pd. Their characteristics are further examined by scanning electron microscopy, optical microscope, FT-IR, and UV-Vis absorption spectroscopy.