A pellet of polycrystalline $CuGaO_2$ with a delafossite structure was prepared from $Ga_2O_3$ and CuO by high-temperature solid-state synthesis. The $CuGaO_2$ pellet was a p-type semiconductor for which the electrical conductivity, carrier density, carrier mobility and Seebeck coefficient were $5.34{\times}10^{-2}{\Omega}^{-1}cm^{-1}$, $3.5{\times}10^{20}cm^{-3}$, $9.5{\times}10^{-4}cm^2V^{-1}s^{-1}$ at room temperature, and $+360{\mu}V/K$, respectively. It also exhibited two optical transitions at about 2.7 and 3.6 eV. The photoelectrochemical properties of the $CuGaO_2$ pellet electrode were investigated in aqueous electrolyte solutions. The flat-band potential of this electrode, determined using a Mott-Schottky plot, was +0.18 V vs SCE at pH 4.8 and followed the Nernst equation with respect to pH. Under UV light illumination, a cathodic photocurrent developed, and molecular hydrogen simultaneously evolved on the surface of the electrode due to the direct reduction of water without deposition of any metal catalyst.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.48-48
• /
• 2007

P-type transparent conducting $CuGaO_2$ thin films have been prepared by DC/RF sputtering using Quartz(0001) and sapphire(0001) substrates. The target was fabricated by heating a stoichiometric mixture of CuO and $Ga_2O_3$ at 1373K for 12h under $N_2$ atmosphere. The film were deposited under mixture gas of Ar and $O_2(Ar:O_2=4:1)$ during 10~30min. and the as-deposited films were annealed at 1123K and $N_2$ atmosphere. Room temperature conductivity and the activation energy of the sintered body in the temperature range of 223K ~ 423K were 0 004S/cm, 1.9eV, respectively. XRD revealed that all of the as-deposited films were amorphous. Heating of the films deposited on Quartz substrates above 1123K resulted in crystallization with a second phase of $CuSiO_3$, which was assumed owing to reaction with Quartz substrate. The single phase of $CuGaO_2$ was obtained at the film deposited on the sapphire substrates. The transmittance after annealing of DC- and RF-sputtered films were 55~75% at 550nm. From the transmittance and reflectance measurement. the direct band gap of the DC/RF-sputtered films were 3.63eV and 3.57eV. and there was little difference between DC and RF sputtered films.

• Current Photovoltaic Research
• /
• v.5 no.4
• /
• pp.135-139
• /
• 2017

We fabricated two different transparent conducting oxide thin films of ZnO doped with Ga ($Ga_2O_3$ 0.9 wt%) as well as Al ($Al_2O_3$ 2.1 wt%) (GAZO) and ZnO doped only with Al ($Al_2O_3$ 3 wt%) (AZO). It was investigated how it affects the moisture resistance of the transparent electrode. In addition, $Cu(In,Ga)Se_2$ thin film solar cells with two transparent oxides as front electrodes were fabricated, and the correlation between humidity resistance of transparent electrodes and device performance of solar cells was examined. When both transparent electrodes were exposed to high temperature distilled water, they showed a rapid increase in sheet resistance and a decrease in the fill factor of the solar cell. However, AZO showed a drastic decrease in efficiency at the beginning of exposure, while GAZO showed that the deterioration of efficiency occurred over a long period of time and that the long term moisture resistance of GAZO was better.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.1-8
• /
• 2017

Catalytic synthesis and properties of ${\beta}-Ga_2O_3$ nanowires grown by metal organic chemical vapor deposition are reported. Au, Ni and Cu catalysts were suitable for the growth of $Ga_2O_3$ nanowires under our experimental conditions. The $Ga_2O_3$ nanowires grown by using Au, Ni and Cu catalysts showed different growth rates and morphologies in each case. We found the $Ga_2O_3$ nanowires were grown by the Vapor-Solid (VS) process when Ni was used as a catalyst while the Vapor-Liquid-Solid (VLS) was a dominant process in case of Au and Cu catalysts. Also, we found nanowires showed different optical properties depend on catalytic metals. On the other hand, for the cases of Ti, Sn and Ag catalysts, nanowires could not be obtained under the same condition of Au, Cu and Ni catalytic synthesis. We found that these results are related to the different characteristics of each catalyst, such as, melting points and phase diagrams with gallium metal.

• Progress in Superconductivity and Cryogenics
• /
• v.25 no.4
• /
• pp.14-18
• /
• 2023

We have investigated the behavior induced by Ga substitution in B-1212 system and observed an anomalous superconductor-like resistivity drop with an onset near 260 K and an offset at 248 K in the nominal (B_0.65Ga_0.35)(Ba_1.25Sr_0.75)(Er_0.5Ca_0.5)Cu₂O_z compound. However, this property degraded with repeated cycling. Systematic studies of the superconducting properties of the (B_1-xGa_x)(Ba_1.25Sr_0.75)(Er_0.5Ca_0.5)Cu₂O_z compounds are reported and discussed in the context of the anomalous resistivity transition.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1584-1586
• /
• 2002

CuIn$Se_2$ (CIS) and related compounds such as Cu($In_xGa_{1-x})Se_2$(CIGS) have been studied by their potential for use in photovoltaic devices. CIS thin film materials which have high absorption coefficient and wide bandgap, have attracted much attention as an alternative to crystalline and amorphous silicon solar cells currently in use. Cu-rich CIGS film have very low resistivity, due to coexistence of the semimetallic $Cu_{2-x}Se$. In-rich CIGS films show high resistivity, since these films are compensated films without the $Cu_{2-x}Se$ phase. Optical properties of the CIGS films also change in accordance with the resistivity for the Cu/(In+Ga) ratio. The Cu-rich films have different spectra from In-rich films in near infrared wavelengths.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.16 no.1
• /
• pp.39-43
• /
• 2016

The structural, electrical properties of Ga doped MgZnO transparent conductive oxide (TCO) films by ratio-frequency(RF) magnetron sputtering were investigated. Ga doped MgZnO TCO films were deposited on the sapphire substrates at $200^{\circ}C$ varying growth thickness 200 to 600 nm. The optical properties of Ga doped MgZnO TCO films were showed above 85% transmittance from 300 to 1000 nm region. In addition, the current density ($J_{SC}$) of $Cu(In,Ga)Se_2$ (CIGS) solar cells was improved by using the MgZnO:Ga films of 500 nm thickness because of outstanding electrical properties. The $Cu(In,Ga)Se_2$ solar cells with MgZnO:Ga transparent conducing layer yielded an efficiency of 9.8% with current density ($31.8mA/cm^2$), open circuit voltage (540.2 V) and fill factor (62.2) under AM 1.5 illumination.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.36.1-36.1
• /
• 2010

While the substrate-type solar cells with Cu(In,Ga)Se2 absorbers yield conversion efficiencies of up 20%[1], the highest published efficiency of Cu(In,Ga)Se2 superstrate solar cell is only 12.8% [2]. The commerciallized Cu(In,Ga)Se2 solar cells are made in the substrate configuration having the stacking sequence of substrate (soda lime glass)/back contact (molybdenum)/absorber layer (Cu(In,Ga)Se2)/buffer layer (cadmium sulfide)/window layer (transparent conductive oxide)/anti reflection layer (MgF2) /grid contact. Thus, it is not possible to illuminate the substrate-type cell through the glass substrate. Rather, it is necessary to illuminate from the opposite side which requires an elaborate transparent encapsulation. In contrast to that, the configuration of superstrate solar cell allows the illumination through the glass substrate. This saves the expensive transparent encapsulation. Usually, the high quality Cu(In,Ga)Se2 absorber requires a high deposition temperature over 550C. Therefore, the front contact should be thermally stable in the temperature range to realize a successful superstrate-type solar cell. In this study, it was tried to make a decent superstrate-type solar cell with the thermally stable ZnO:Al layer obtained by adjusting its deposition parameters in magnetron sputtering process. The effect of deposition condition of the layer on the cell performance will be discussed together with hall measurement results and current-voltage characteristics of the cells.

• Solar Energy
• /
• v.20 no.2
• /
• pp.43-54
• /
• 2000

We prepared and characterized $Cu(In_{1-x}Ga_x)Se_2$(CIGS) films using a elemental co-evaporation method for absorbing layer of high efficiency thin film solar cells. The CIGS films deposited on a soda-lime glass exhibited low resistivity because of higher carrier concentration. Na was accumulated at the CIGS surface and the 0 and Se were also accumulated at the surface, suggesting that oxidation is a driving force of Na accumulation. The structure of CIGS film was modified or a secondary phase was formed in the Cu-poor CIGS bulk films probably due to the incorporation of Na into Cu vacancy sites. As the Ga/(In+Ga) ratio increased, the diffraction peaks of $Cu(In_{1-x}Ga_x)Se_2$ films were shifted to larger angle and splitted, and the grain size of $Cu_{0.91}(In_{1-x}Ga_x)Se_2$ films became smaller. All $Cu_{0.91}(In_{1-x}Ga_x)Se_2$ films showed the p-type conductivity regardless of the Ga/(In+Ga) ratio. Ag/n-ZnO/i-ZnO/CdS/$Cu_{0.91}(In_{0.7}Ga_{0.3})Se_2$/Mo solar cells were fabricated. The currently best efficiency in this study was 14.48% for $0.18cm^2$ area ($V_{oc}=581.5mV,\;J_{sc}=34.88mA$, F.F=0.714).

• Bulletin of the Korean Chemical Society
• /
• v.19 no.4
• /
• pp.466-470
• /
• 1998

Catalytic hydrogenation of carbon dioxide for the simultaneous synthesis of methanol and dimethyl ether (together called oxygenates) over a combination of methanol synthesis and methanol dehydration catalysts has been studied. Various methanol synthesis and methanol dehydration catalysts were examined for this reaction. The addition of promotors like $Ga_2O_3\; and\; Cr_2O_3$ to Cu/ZnO catalyst gave much more enhanced yield on the formation of oxygenates. From the results, the promotional effect of $Cr_2O_3$ has been explained in terms of increase in the intrinsic activity of Cu while that of $Ga_2O_3$ being increase in the dispersion of Cu. Among the methanol dehydration catalysts examined, the solid acids bearing high population of intermediate-strength acid sites were found to be very effective for the production of oxygenates. HY zeolite which contains strong acid sites produce small amount of hydrocarbons as by-products. However, CuNaY zeolite in which the presence of strong acid sites are minimum gives very high oxygenates yield without the formation of hydrocarbons.