• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.2
• /
• pp.116-123
• /
• 2007

[ $La_{0.5}Ce_{0.5}Co_{1-x}Cu_xO_{3-{\alpha}}$ ](X=0, 0.1, 0.3, 0.5) perovskites were prepared by coprecipitation method at pH 7 or pH 11 and its catalytic activity of selective CO oxidation was investigated. The characteristics of these catalysts were analyzed by $N_2$ adsorption, X-ray diffraction(XRD), SEM, $O_2$-temperature programmed desorption(TPD). The pH value at a preparation step made effect on particle morphology. The smaller particle was obtained with a condition of pH 7. The better catalytic activity was observed using catalysts prepared at pH 7 than pH 11. The maximum CO conversion of 98% was observed over $La_{0.5}Ce_{0.5}Co_{0.7}Cu_{0.3}O_{3-{\alpha}}$ at $320^{\circ}C$. Below $200^{\circ}C$, the most active catalyst was $La_{0.5}Ce_{0.5}Co_{0.9}Cu_{0.1}O_{3-{\alpha}}$, of which conversion was 92% at $200^{\circ}C$. By the substitution of Cu, the evolution of ${\alpha}$-oxygen was remarkably enhanced regardless of pH value at preparation step according to $O_2$-TPD. Among the different ${\alpha}$-oxygen species, the oxygen species evolved between $400^{\circ}C$ and $500^{\circ}C$, gave the better catalytic performance for selective CO oxidation including $La_{0.5}Ce_{0.5}CoO_3$ in which Cu was absent.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.21-26
• /
• 2004

Deposition condition of YBa$_2$Cu$_3$$O_{7-x}$ (YBCO) films on moving IBAD templates (CeO$_2$/IBAD-YSZ/SS) was studied in a hot-wall type metal organic chemical vapor deposition (MOCVD) process using single liquid source. The reel velocity was 40 cm/hr and the source mole ratios of Y(tmhd)$_3$:Ba(tmhd)$_2$:Cu(tmhd)$_2$ were 1:2.3:3.1 and 1:2.1:2,9, Two different types of IBAD templates with thin CeO$_2$ and thick CeO$_2$ layers were used, The YBCO films were successfully deposited at the deposition temperatures of 780~89$0^{\circ}C$ ; the a-axis growth was observed together with the c-axis growth up to 83$0^{\circ}C$. while the c-axis growth became dominant above 83$0^{\circ}C$. The top surface of the c-axis film was fairly dense and included a small amount of the a-axis growth, although the peaks of the a-axis grains were not observed in XRD pattern, The YBCO film deposited on IBAD template with thin CeO$_2$ layer showed low critical current of 2.5 A/cm-width. while the YBCO film deposited on IBAD template with thick CeO$_2$ layer showed higher critical current of 50 A/cm-width. This result indicates that thick CeO$_2$ layer is thermally more stable than thin CeO$_2$ layer at the high deposition temperature of the MOCVD process.s.

• Progress in Superconductivity
• /
• v.6 no.1
• /
• pp.37-40
• /
• 2004

We investigated the effects of impurity doping on the electrical transport and magnetic properties of TEX>$(Ru, Sn)(Sr, La)<_2$$EuCeCu_2$$O_{z}$ samples. We found that Sn substitution fur Ru causes a significant decrease of the volume fraction of ferromagnetic phase, as well as a decrease of the temperature where the ferromagnetic component is observed. La substitution for Sr leads to an increase of the magnetic ordering temperature with a moderate change of ferromagnetic component. The experimental results are discussed in conjunction with the structural data, transport properties and a possible change of oxygen content.

• Clean Technology
• /
• v.13 no.1 s.36
• /
• pp.54-63
• /
• 2007

Even traces of CO in the hydrogen-rich feed gas to proton exchange membrane fuel cells (PEMFC) poison the platinum anode electrode and dramatically decrease the power output. In this work, a variety of catalytic materials consisting of $Cu/Ce_xZr_{1-x}O_2$, (x = 0.0-1.0) were synthesised, characterized and tested for CO oxidation and preferential oxidation of CO (PROX). These catalysts prepared by hydrothermal and deposition-precipitation methods. The catalysts were characterized by XRD, XRF, SEM, BET, $N_2O$ titration and oxygen storage capacity (OSC) measurement. The effects of composition of the support and degree of excess oxygen were investigated fur activity and $CO_2$ selectivity with different temperatures. The composition of the support markedly influenced the PROX activity. Among the various $Cu/Ce_xZr_{1-x}O_2$ catalysts having different composition, $Cu/Ce_{0.9}Zr_{0.1}O_2$ and $Cu/Ce_{0.7}Zr_{0.3}O_2$ showed the highest activities (>99%) and selectivities (ca.50%) in the temperature range of $150{\sim}160^{\circ}C$. It was found that by using of $Ce_xZr_{1-x}O_2$ mixed oxide support which possesses a high oxygen storage capacity, oxidation-reduction activity of Cu-based catalyst was improved, which resulted in the increase of catalytic activity and selectivity of CO oxidation in excess $H_2$ environments.

• Progress in Superconductivity
• /
• v.13 no.3
• /
• pp.163-168
• /
• 2012

The effects of Ta substitution on the superconducting and magnetic properties of the $(Ru_{1-x}Ta_x)Sr_2(Gd_{1.4}Ce_{0.6})Cu_2O_z(0{\leq}x{\leq}0.5)$ system have been investigated. The X-ray diffraction measurements indicate that the Ta ion replaces Ru sites up to x = 0.4. It is found that the Ta substitution for Ru significantly reduces the weak-ferromagnetic component of the field-cooled magnetic susceptibility without an appreciable change of room temperature thermopower at lower Ta doping level below x = 0.2. The resistive transition temperature tends to decrease monotonically from 27 K for the x = 0 sample to 16 K (9 K) for the x = 0.4 (x = 0.5) sample. These results suggest that superconductivity of the $(Ru_{1-x}Ta_x)Sr_2(Gd_{1.4}Ce_{0.6})Cu_2O_z$ compound is not significantly affected by the magnetic state of the Ru sublattice. The experimental results are discussed in connection with previous reports on the effects of Nb substitution.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.152-157
• /
• 2001

For the fabrication of YBa$_2$Cu$_3$O$_{x}$ thick film using diffusion process between $Y_3$BaCuO$_{5}$ and BaO+CuO, each material was selected as substrate and doping material. In this paper, we investigated the characteristic of YBa$_2$Cu$_3$O$_{x}$ thick film due to both addition of CeO$_2$into substrate and initial particle size of doping material. Through X-ray diffraction patterns and SEM photographs, the variation of composition and thickness of the formed phase was observed. It was from the experiment obtained that the addition of CeO$_2$into $Y_2$BaCuO$_{5}$ substrate and the initial particle size of doping material play important part in promoting the reaction between substrate and doping material.aterial.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.128-132
• /
• 2009

Polycrystalline samples of $(Ru_{0.8}Nb_{0.2})Sr_2(Gd_{1.5-x}Nd_xCe_{0.5})Cu_2O_z$($ 0{\leq}x{\leq}1.25$) have been synthesized by a solid-state reaction route. The X-ray diffraction data revealed that the Nd solubility limit can be placed between x=0.5 and x=0.75. The superconducting transition temperature decreased with increasing Nd content, confirming that Nd entered the lattice. Room-temperature thermoelectric power measurements showed that all the samples are in the underdoped state and the partial substitution of Nd for Gd resulted in a decrease in the carrier density on the superconducting layers.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.3
• /
• pp.190-198
• /
• 2016

Application of fuel cell to produce renewable energy for commercial purpose is limited by the high cost of Pt based electrode materials. Development of inexpensive, high energetic electrode is the need of the hour to produce pollution free energy using bio-fuel through a fuel cell. Ni-Cu and Ni-CeO₂-Cu electrode materials, electro synthesized by pulse current have been developed. The surface morphology of the electrode materials is controlled by different deposition parameters in order to produce a high current from the electro-oxidation of the fuel, the ethanol. The developed materials are electrochemically characterized by Cyclic Voltammetry (CV), Chronoamperometry (CA) and Potentiodynamic polarization tests. The results confirm that the high current is due to their enhanced catalytic properties viz. high exchange current density (i₀), low polarization resistance (R_p) and low impedance. It is worthwhile to mention here that the addition of CeO₂ to Ni-Cu has outperformed Pt as far as the high electro catalytic properties are concerned; the exchange current density is about eight times higher than the same on Pt surface. The morphology of the electrode surface examined by SEM and FESEM exhibits that the grains are narrow and sub spherical with 3D surface, containing vacancies in between the elongated grains. The fact has enhanced more surface area for electro oxidation of the fuel, giving rise to an increase in current. Presence of Ni, CeO₂, and Cu is confirmed by the XRD and EDXS. Fuel cell fabricated with Ni-CeO₂-Cu material electrode is expected to produce clean electrical energy at cheaper rates than conventional one, using bio fuel the derived from biomass.

• Korean Journal of Materials Research
• /
• v.22 no.10
• /
• pp.526-530
• /
• 2012

Silica-based ceramic-matrix composites have shown promise as advanced materials for many applications such as chemical catalysts, ceramics, pharmaceuticals, and electronics. $SiO_2$-CuO-$CeO_2$ multi-component powders and their thin film, using an oxalic acid template as a chelating agent, have larger surface areas and more uniform pore size distribution than those of inorganic acid catalysts. $SiO_2$-CuO-$CeO_2$ composite powders were synthesized using tetraethylorthosilicate, copper (II) nitrate hemi (pentahydrate), and cerium (III) nitrate hexahydrate with oxalic acid as template or pore-forming agent. The process of thermal evolution, the phase composition, and the surface morphology of these powders were monitored by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), field-emission scanning electron microscopy (FE-SEM), and energy dispersive X-ray spectrometry (EDXS). The mesoporous property of the powders was observed by Brunner-Emmett-Teller surface (BET) analysis. The improved surface area of this powder template with oxalic acid was $371.4m^2/g$. This multi-component thin film on stainless-steel was prepared by sol-gel dip coating with no cracks.