• Korean Journal of Materials Research
• /
• v.10 no.7
• /
• pp.471-477
• /
• 2000

Corrosion behavior of Fe-Ni-Cr alloy in molten salts of LiCl and LiCl-$Li_2O was investigated in the tempera-ture range of $650~850^{\circ}C$. In the molten salt of LiCl, and internal oxidation of Fe occurred in the KSA(Kaeri Superalloy)-1 alloy without containing Cr, while a dense protective oxide scale of $LiCrO_2$ was formed in the KSA-4, Incoloy 800H and KSA-5 alloys. In the mixed molten salt of LiCl-$Li_2O$, internal oxidation of Fe and Cr took place in the KSA-1 and KSA-4 alloys, respectively. Non-protective porous oxide scales consisting of $LiCrO_2$ and Ni were formed in the Incoloy 800H and KSA-5. The corrosion rate of the alloys increased with the increase in Cr content and the corrosion rate followed the parabolic law for the alloy containing Cr content less than 8%, and the linear law for the alloy containing Cr content more than 8%. Such a corrosion behavior of the alloy in the mixed molten salt of LiCl-$Li_2O$ was interpreted in terms of the basic fluxing mechanism of protective oxide scale of $Cr_2O_3$.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1303-1305
• /
• 1998

In order to reduce or avoid oxidation problem at operation the interconnects in SOFCs have so far mostly been made of ceramic material. It has high chemical stability both under cathode and anode condition, relatively thermal expansion coefficient that matchs that of electrolyte material YSZ. But this material shown rather weak in the low oxygen atmosphere and thermal shock, and it has lower mechanical strength than alloys. To avoid these problems one may consider to use metals or alloys as materials for interconnects. Metallic interconnects are advantageous because of their high thermal and electronic conductivities. But it has some problems, Those are high thermal expansion and oxidation at high temperature in air. To solve these problems in the interconnection material in this study, $LaCrO_3$-dispersed Cr alloys for metallic interconnector of SOFC have been investigated as a fuction of $LaCrO_3$ content in the range of 5 to 25 vol.%. The Cr alloy were prepared by mixing Cr and $LaCrO_3$ powders in high-energy ball mill for 48h and by sintering under Ar atmosphere with 5vol.% $H_2$ for 10h at $1500^{\circ}C$. The alloys had a relative density of 95% and above. The Cr alloys in composed of two kind of small $LaCrO_3$ and large Cr particles. As the $LaCrO_3$ content increased, the Cr particle size decreased but the $LaCrO_3$ particle size remained contant. Also the oxidation tests show that the $LaCrO_3$-dispersed Cr is very resistant to oxidation in air. These results means that $LaCrO_3$-dispersed Cr is a useful material for metallic interconnect of planar SOFC.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.2
• /
• pp.91-98
• /
• 1994

For the plasma sprayed as well as the EB-PVD thermal barrier coatings, the fracture paths within the oxidation products developed at the interface between the partially stabilized zirconia ceramic coating and NiCoCrAlY bond coat during cyclic thermal oxidation has been investigated. It was observed that the fracture in the oxidation products primarily took place within the oxide such as $Ni_{1-x}Co_3(Al_,Cr)_2O_4$ or at the interface between the oxide and $Al_2O_3$. It was found that Al2O3 developed first, followed by the Ni/Co/Cr rich oxides such as ,,$Ni_{1-x}Co_x(Al_,Cr)_2O_4$ $Cr_2O_3$and NiO at the interface between the ceramic coating and the bond coat in a cyclic high temperature environment. It was therfore concluded that the formation of the oxide containing Ni, Cr and Co was a life-limiting event for thermal barrier coatings during cyclic thermal oxidation.

• Korean Chemical Engineering Research
• /
• v.46 no.1
• /
• pp.99-105
• /
• 2008

Core-shell structured $BaTiO_3$ powders were produced via nano-coating of $Cr_2O_3$ and $Mn_2O_3$ to barium titanate powder system for MLCCs. From preliminary experiments, the optimal solution reaction condition employing using $KMnO_4$, $K_2Cr_2O_4$ and sulfur was established. Not only powders of $Cr_2O_3$ and $Mn_2O_3$ were synthesized but also their coating on $BaTiO_3$ powders were peformed under the same reaction condition. The coating was carried out in two ways, one-step and two-step, and its results were characterized for comparison. Conclusively speaking, two oxide additives were coated onto the $BaTiO_3$ powder surface with high quality and excellent reaction yield even under mild condition, which indicates that the contents as well as the properties of additive shell layer can be precisely controlled with rather ease.

• The Korea Journal of Herbology
• /
• v.21 no.1
• /
• pp.101-107
• /
• 2006

Objectives : It is well known that hexavalent chromium has toxic effect on normal cells. Recently, toxic effect of hexavalent chromium is diminished by the some extracts derived from herbs or plants. But, the toxic or protective mechanism of hexavalent chromium is well unknown. This study was performed to examine the protective effect of poncirin against $Na_2Cr_2O_7$-induced cytotoxicity on NIH3T3 fibroblasts. Methods : The protective effect of the cytotoxicity induced by $Na_2Cr_2O_7$ was measured by the cell viability after NIH3T3 fibroblasts were cultured with or without $Na_2Cr_2O_7$ for 48 hours. Antitoxic effects of poncirin on the cytotoxicity induced by $Na_2Cr_2O_7$ were examined by colorimetric assays such as MTT or XTT assay. Results : $Na_2Cr_2O_7$ decreased cell viability by the decreased absorbance in MTT or XTT assay, but, the poncirin increased cell viability which was decreased by $Na_2Cr_2O_7$-induced cytotoxicity on NIH3T3 fibroblasts. Conclusion : These results suggest that $Na_2Cr_2O_7$ showed cytotoxicity effect on NIH3T3 fibroblasts by the decrease of cell viavility, and poncirin was effective in the protection of $Na_2Cr_2O_7$-induced cytotoxicity in these cultures.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.129-136
• /
• 2006

The high velocity oxy-fuel sprayed coatings of 38Ni-23Co-20Cr-11Al-3Y-5Ta, 25Ni-34Co-20Cr-11Al-3Y-2Re and 32Ni-34.5Co-22Cr-11Al-0.5Ir (in wt%) were oxidized at 1000 and $1100^{\circ}C$ in air in order to find the alloying effect of Ta, Re and Ir on the oxidation properties of the NiCoCrAlY-base coatings. The primary phase of the coatings was $Ni_3Al$. The oxides formed on the coatings consisted primarily of ${\alpha}-Al_2O_3$, together with some $CoCr_2O_4,\;CoAl_2O_4$, and $Al_5Y_3O_{12}$. Tantalum oxidized to $Ta_2O_5$ and $Ta_2O_{22}$. However, no oxides of Re and Ir were detected by XRD owing to their thermodynamic inertness and/or their small amount.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.898-901
• /
• 2004

[ $ZnCr_2O_4$ ]를 모물질로 하고 MgO, $TiO_2$를 몰비로 2:1, 4:1, 6:1, 및 8:1이 되게 정량적으로 조합한 후, 조사하였다. $ZnCr_2O_4$-MgO와 $ZnCr_2O_4-TiO_2$를 X-선 분석한 결과 Spinel 결정구조를 형성하였으며, 또한 SEM과 EDX 분석결과 각각 $Li_2CrO_4$와 $Li_3VO_4$의 형성으로 인하여 저항 특성이 나타나는 것을 알 수 있었다. $ZnCr_2O_4-MgO$, $ZnCr_2O_4-TiO_2$에서 MgO의 양이 증가할수록 저항값은 약간 감소하는 반면, $TiO_2$의 양이 증가할수록 저항값이 급격히 증가하는 특성을 나타내었고, 감습 특성에서도 M??보다 TiO2가 더 높게 나타내었다. 습에 따른 복원 특성의 경우 $700^{\circ}C$에서 소결한 ($ZnCr_2O_4:MgO=4:1$)과 ($ZnCr_2O_4:TiO_2=6:1$) 조성의 센서가 가장 양호하였다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2004.04b
• /
• pp.38.3-38.3
• /
• 2004

• Journal of the Korean institute of surface engineering
• /
• v.27 no.2
• /
• pp.74-82
• /
• 1994

The structure and properties such as adhesion and corrosion resistance of Cr and $Cr_2O_3$ films, deposited on steel plates by the vacuum evaporation method, were investigated. According to the ESCA and AES analy-sis, it could be concluded that chromium oxide with uniform composition could be formed on the steel sub-strate. The deposited Cr and $Cr_2O_3$ films had high adhesion strength, and they did not peeled off by the tape test. The adhesion property, however, was deteriorated as the film thciknes increased. After bending of the deposited specimen many cracks were observed by SEM, and they were assumed to have propagated along co-lumnar boundaries by the bending test. The corrosion resistance of the films was not generally good, which in-dicates that the films had a porous structure with a large number of defects such as pin holes and voids.