• 센서학회지
• /
• 제18권1호
• /
• pp.48-53
• /
• 2009

$Eu^{2+}$-doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors have been synthesized by conventional solid state method. Photocurrent properties of $Eu^{2+}$ doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors, in order to elucidate $Dy^{3+}$ co-doping effect, during and after ceasing ultraviolet-ray (UV) irradiation have been investigated. The photocurrent of $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors during UV irradiation was 4-times lower than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ during UV irradiation, and 7-times higher than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ after ceasing UV irradiation. The photocurrent results indicated that holes of charge carriers captured in hole trapping center during the UV irradiation and liberated after-glow process, and made clear that $Dy^{3+}$ of co-dopant acted as a hole trap. The photocurrent of ${SrAl_2}{O_4}$ showed a good proportional relationship to UV intensity in the range of $1{\sim}5mW/cm^2$, and $Eu^{2+}$-doped ${SrAl_2}{O_4}$ was confirmed to be a possible UV sensor.

• 청정기술
• /
• 제13권4호
• /
• pp.287-292
• /
• 2007

상용 알루미나($Al_2O_3$)에 담지된 $M/Al_2O_3$ (M = Mn, Fe, Co, Ni, Cu) 촉매를 함침법에 의해 제조하였으며, 이를 에탄을 자열개질반응에 의한 수소제조에 적용하였다. 각각의 촉매는 고유한 금속상을 가지는 것으로 나타났으며, 생성물의 분포는 활성금속의 종류에 크게 의존하였다. 제조된 촉매 중에서, $M/Al_2O_3$ 및 Co/$Co/Al_2O_3$는 에탄을 자열개질반응에서 매우 우수한 촉매활성을 보였다. 그러나 두 촉매상에서의 반응메커니즘은 서로 다른 것으로 나타났다. $Ni/Al_2O_3$ 촉매는 $500^{\circ}C$의 반응온도에서 100%의 에탄올 전환율을 보였으나, 수소 선택도에서는 시간에 따라 급격한 저하현상을 나타내었다. 한편 $Co/Al_2O_3$ 촉매는 수소 선택도 면에서 우수한 활성을 보였으나, 에탄올 전환율이 저조하여 수소 수율에는 큰 변화가 나타나지 않았다.

• 한국분말재료학회지
• /
• 제5권4호
• /
• pp.334-339
• /
• 1998

In purpose of introducing the inverse magnetostrictive properties into the structural ceramics, $Al_2O_3$ based nanocomposites dispersed with nano-sized Ni-Co particles were studied. The composites were fabricated by the hydrogen reduction and hot-pressing of $Al_2O_3$ and NiO-CoO mixed powders. The mixtures were prepared by using Ni- and Co-nitrate $(Ni(NO_3)_2\;{\cdot}\;6H_2O\;and\;Co(NO_3)_2\;{\cdot}\6H_2O)$ as source materials for the Ni-Co particles. Microstructural observations revealed that nano-sized Ni-Co particles were dispersed homogeneously at $Al_2O_3$ grain boundaries. High strength above 1 GPa was obtained for the $Al_2O_3/10$ wt% Ni-Co nanocomposite fabricated by a controlled powder preparation process. The inverse magnetostrictive response to applied stress was obtained due to the presence of dispersed Ni-Co particles, which indicates a possibility to incorporate new functions into the structural ceramics without loosing the mechanical properties.

• 한국자기학회지
• /
• 제9권6호
• /
• pp.296-300
• /
• 1999

DC 마그네트론 스퍼터링 방법으로 금속 마스크를 사용하여 십자형태로 substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al2O3/CoFe/NiFe와 substrate/Ta/NiFe/CoFe/Al2O3/CoFe/NiFe/FeMn/NiFe 스핀 터널링 접합 구조를 제조하였다. 이러한 구조에서 절연층(Al2O3)의 형성조건과 각 층의 두께와 파워에 대한 증착율에 변화를 주어 24.3%의 자기 저항비를 얻었다. 두 종류의 구조에 대한 자기적 특성 비교와 Corning glass 7059와 Si(111) 기판의 종류에 따른 결과를 비교하였으며 소자 제조때 수반되는 온도변화에 대한 특성변화를 알아보고자 열처리를 하였다. 열처리 결과 자기 저항비는 15$0^{\circ}C$까지는 어느 정도 일정한 값을 유지하다가 18$0^{\circ}C$ 열처리 후 갑자기 감소하는 결과를 얻었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2018년도 춘계 학술논문 발표대회
• /
• pp.238-239
• /
• 2018

This paper presents the synthesis results of CaO-Al₂O₃ system clinker using the CaCO₃ and the Al₂O₃ according to the synthesis methods dependent on the temperature. The purpose of this study is the formation of the CaO-Al₂O₃ system clinker containing high ratio of CaO·2Al₂O₃ (CA₂). The maximum sintering temperature for the synthesis of CaO-Al₂O₃ compounds was 1250℃, 1300℃ and 1400℃. The CaO-Al₂O₃ compounds was sintered at the maximum sintering temperature for three hours. After sintering, the compounds was analyzed using X-ray diffraction method. The 12CaO·7Al₂O₃ (C1₂A₇) and CaO·Al₂O₃ (CA) increased as elevating the maximum sintering temperature whereas the CA₂ decreased. Especially, at the 1250℃ of maximum sintering temperature, the un-reacted CaO and Al₂O₃ was identified.

• Korean Chemical Engineering Research
• /
• 제48권6호
• /
• pp.776-783
• /
• 2010

수소생산을 위한 메탄의 부분산화용 촉매로 알루미나에 담지된 코발트와 니켈 촉매를 함침법으로 제조하였다. 메탄의 부분산화반응을 위한 이들 촉매의 반응활성은1기압, $CH_4/O_2=2.0$과 $450{\sim}650^{\circ}C$의 온도영역에서 조사하였다. 담지량이 다른 코발트촉매와 니켈촉매의 반응활성을 비교하고 코발트촉매에 니켈을 첨가한 이성분금속 촉매의 반응활성을 조사하였다. 그리고 코발트촉매와 니켈촉매에 첨가된 Ce와 La의 첨가효과를 조사하였다. 이들 촉매의 특성은 XRD와 SEM/EDX로 분석하였다. 코발트와 니켈은 10 wt%의 담지량이 적절한 것으로 나타났다. 이들 10 wt% 담지 코발트와 니켈촉매는 열역학적 평형값에 가까운 메탄의 전환율과 CO의 선택성을 나타내었으나 $H_2$의 선택성은 평형값보다 다소 낮게 나타났다. 코발트촉매에 니켈을 첨가한 이성분금속 촉매에서 $H_2$의 선택성은 증가하였으나 전환율을 고려하면 니켈을 첨가한 이점은 나타나지 않았다. 코발트촉매에서는 Ce의 첨가와 니켈촉매에서는La의 첨가로 메탄의 전환율과 수소의 선택성을 높일 수 있었다.

• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.423-437
• /
• 1989

Al2O3/ZrO2 composites were prepared by precipitation method using Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O as starting materials and NH4OH as a precipitation agent. Al2O3/ZrO2 composites(series A) were prepared by mixing Al2O3 powder obtained by single precipitation method with ZrO2(＋3m/o Y2O3) powder obtained by co-predipitation method. Al2O3/ZrO2 composites (series B) were prepared by co-precipitation method using the three starting materials. In all cases, the composition was controlled as Al2O3-15v/o ZrO2(＋3m/o Y2O3). The composites of series A showed higher final relative densities than those of series B and tetagonal ZrO2 in all cases was retained to about 95% at room temperature. ZrO2 particles were coalesced more rapidly in grain boundary of Al2O3 than within Al2O3 grain. ZrO2 particles were located at 3-and 4-grain junction of Al2O3 and limited the grain growth of Al2O3. It was observed that MgO contributed to densification of Al2O3 but limited grain growth of Al2O3 by MgO was not remarkable. In all Al2O3/ZrO2 composites, exaggerated grain growth of Al2O3 was not observed and Al2O3/ZrO2 composites were found to have homogeneous microstructures.

• 한국분말재료학회지
• /
• 제8권3호
• /
• pp.157-162
• /
• 2001

An optimum route to fabricate the ferrous alloy dispersed $Al_2O_3$ nanocomposites such as $Al_2O_3$/Fe-Ni and $Al_2O_3$/Fe-Co with sound microstructure and desired properties was investigated. The composites were fabricated by the sintering of powder mixtures of $Al_2O_3$ and nano-sized ferrous alloy, in which the alloy was prepared by solution-chemistry routes using metal nitrates powders and a subsequent hydorgen reduction process. Microstructural observation of reduced powder mixture revealed that the Fe-Ni or Fe-Co alloy particles of about 20 nm in size homogeneously surrounded $Al_2O_3$, forming nanocomposite powder. The sintered $Al_2O_3$/Fe-Ni composite showed the formation of Fe$Al_2O_4$ phase, while the reaction phases were not observed in $Al_2O_3$/Fe-Co composite. Hot-pressed $Al_2O_3$/Fe-Ni composite showed improved mechanical properties and magnetic response. The properties are discussed in terms of microstructural characteristics such as the distribution and size of alloy particles.

• 한국수소및신에너지학회논문집
• /
• 제23권6호
• /
• pp.640-646
• /
• 2012

The effect of Ce promotion over 1wt% $Pt/{\gamma}-Al_2O_3$ catalysts on the CO conversion and $CO_2$ selectivity was investigated in preferential CO oxidation (PrOx) to reduce the CO concentration less than 10 ppm in excess $H_2$ stream for polymer electrolyte membrane fuel cell (PEMFC). Ce-promoted 1wt% $Pt/{\gamma}-Al_2O_3$ catalysts were prepared by incipient wetness impregnation method and the loading amount of Pt was fixed at 1wt%. The content of Ce promoter which has excellent oxygen storage and transfer capability due to the redox property was adjusted from 0 to 1.5wt%. Ce-promoted 1wt% $Pt/{\gamma}-Al_2O_3$ catalysts exhibit high CO conversion and $CO_2$ selectivity at low temperatures below $150^{\circ}C$ due to the improvement of reducibility of surface PtOx species compared with the 1wt% $Pt/{\gamma}-Al_2O_3$ catalyst without Ce addition. When Ce content was more than 1wt%, the catalytic activity was decreased at over $160^{\circ}C$ in PrOx because of competitive $H_2$ oxidation. As a result, 0.5wt% Ce is optimal content not only to achieve high catalytic activity and good stability at low temperatures below $150^{\circ}C$ in the presence of $CO_2$ and $H_2O$ but also to minimize the $H_2$ oxidation at high temperatures.

• 청정기술
• /
• 제18권1호
• /
• pp.95-101
• /
• 2012

수소생산을 위한 메탄의 부분산화용 촉매로 알루미나에 담지된 코발트와 니켈 촉매를 함침법으로 제조하였다. 이들 코발트와 니켈 촉매에 조촉매 성분 Mg, Ce, La와 Sr을 첨가하여 초촉매 효과를 조사하였다. 메탄의 부분산화반응을 위한 촉매의 활성은 상압, $CH_4/O_2$ = 2.0에서 450~$650^{\circ}C$의 온도영역으로 조사하였다. 촉매의 특성은 BET, XRD와 SEM/EDX를 이용하여 조사하였다. 0.2 wt%의 조촉매 성분의 첨가로 촉매성능의 상승효과를 얻을 수 있었다. $500^{\circ}C$ 이상의 온도에서는 $Co/Al_2O_3$에 Mg을 첨가한 촉매가 가장 우수한 메탄 전환율과 수소 선택성을 나타내었다. 낮은 온도 영역에서는 $Ni/Al_2O_3$에 Ce와 Sr을 첨가한 촉매가 Co계 촉매보다 우수한 반응특성을 나타내었다. $Co/Al_2O_3$와 $Ni/Al_2O_3$에 조촉매를 첨가한 경우 촉매의 표면적이 증가하는 것으로 나타났다.