In this study, we conducted experiments to store $CO_2$ and produce $CaCO_3$ through indirect carbonation using paper sludge ash (PSA) and three chelating reagents (fumarate, IDA and EDTA). Fumarate and IDA used as solvents could facilitate the indirect carbonation reaction to store more $CO_2$ than water. When 0.1 M fumarate and IDA were used, $CO_2$ storage was 63 and $89kg-CO_2/ton-PSA$, respectively, and $CaCO_3$ yield was 144 and $202kg-CaCO_3/ton-PSA$. For the case of EDTA, however, the carbonation was hardly progressed. As either the concentration or Ca-ligand stabilization constant of each chelating reagent increased, the calcium extraction efficiency from PSA increased. In addition, the carbonation efficiency was influenced by the Ca-ligand stabilization constant. As the Ca-ligand stabilization constant increased, more calcium could be extracted from the PSA. With the constant larger than that of $CaCO_3$ ($10^{8.35}$), however, the carbonation reaction was not proceeded.

• Fashion & Textile Research Journal
• /
• v.23 no.2
• /
• pp.290-296
• /
• 2021

The effect of draw ratio (8, 10, 12, 14 times) and additive CaCO₃ content (0, 0.5, 1.0, 1.5, 2.0, and 3.0 wt%) on the properties of high-performance PE monofilament was investigated in this study. As the draw ratio increased (8-14 times), the melting enthalpy (ΔHf), crystallinity, specific gravity, and tensile strength increased significantly. However, the draw ratio had little effect on the melting temperature (Tm) and crystallization temperature (Tc). The seawater fastness (stain and fade) of the hydrophobic PE monofilament prepared in this study showed an excellent grade of 4-5 in all draw ratios. To investigate the effect of the additive CaCO₃ content on the properties of high-performance PE monofilament, the draw ratio was fixed at 14 times. It was found that the tensile strength of the PE monofilament sample containing 0.5 wt% of CaCO₃ was much greater compared to the sample without CaCO₃, but the elongation of the sample containing 0.5 wt% of CaCO₃ was much less than the sample with 0 wt% CaCO₃. However, in the case of the sample containing more than 0.5 wt% CaCO₃, the tensile strength slightly decreased and the elongation slightly increased as the CaCO₃ content increased. The seawater fastness (stain and fade) of the hydrophobic PE monofilament showed excellent grades of 4-5, regardless of the amount of additives. From the above results, it was found that the maximum draw ratio of 14 times with an additive of 0.5 wt% CaCO₃ are the optimal conditions for manufacturing high-performance marine fusion materials with various fineness (denier) with high strength and low elongation.

• Journal of Korea Foundry Society
• /
• v.6 no.4
• /
• pp.269-276
• /
• 1986

The effects of Se, $CaCO_3$ and CaO addition on the first stage graphization of malleable iron were evaluated. The results obtained in this work were as follows. 1. Many gas bubbles were found in the white cast iron under Se, $CaCO_3$ addition. 2. Nodular graphite were formed by annealing of the white cast iron with remained gas bubbles. 3. When specimens were annealed, bubbles provided the nucleation sites that were needed in graphite precipitation, so the nucleation rate of graphite was increased. 4. The remained gas bubbles and defects were more effective for the graphitization than metallic compounds.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.40 no.5
• /
• pp.665-672
• /
• 2011

We evaluated the effects of organic Ca supplements chelated with milk protein (CaMP) in ovariectomized osteoporotic rats. Eight week-old Sprague-Dawley female rats were ovariectomized and fed a low $CaCO_3$ diet (0.1%) for 4 weeks to create an osteoporotic model. At that point, L4-$CaCO_3$ rats were sacrificed and the rest of the rats were divided into 4 groups, each of which was fed an experimental diet for 4 weeks: low-$CaCO_3$ (0.1%; L8-$CaCO_3$) and CaMP at 3 Ca levels: low (0.1%; L8-CaMP), normal (0.5%; N8-CaMP), and high (1.5%; H8-CaMP). Daily weight gain, serum ALP, weight and breaking force of femurs, Ca content of the lumbar, and Ca absorption were measured. Daily weight gain increased in the N8-CaMP and H8-CaMP groups compared to the low Ca groups. The ALP activity in the CaMP-fed rats was significantly lower than in the $CaCO_3$-fed rats. Both breaking force and femur weight were higher in the N8-CaMP and H8-CaMP groups compared to the L8-$CaCO_3$ group. Ca content of the lumbar increased dose-dependently with Ca intake levels of CaMP. Ca absorption rates of the CaMP-fed rats increased more than that of the rats fed low Ca levels of $CaCO_3$. These results demonstrate that the CaMP supplement had positive effects on bone metabolism and Ca bioavailability in ovariectomized osteoporotic rats. Therefore, CaMP may be recommended as a useful Ca supplement to prevent bone loss in osteoporosis.

• Journal of Nutrition and Health
• /
• v.36 no.7
• /
• pp.684-690
• /
• 2003

This study has investigated the bioavailability of calcium in eggshell powder (ESP) for the purpose of reutilizing eggshells as the calcium source. The experiment was designed 2 ${\times}$ 2 factorial method with two sources, CaCO$_3$ and ESP, and two levels, 0.2% and 0.4% calcium. Weanling SD rats were assigned randomly to one of 4 groups and provided by one of the isocaloric, 20% casein based 4 different experimental diets for 4weeks. Deionized water was given and environment was kept from any contamination of minerals. The body weight, diet intake, feed efficiency ratio (FER), bone growth, Ca contents of bones, and apparent absorption were measured. FER (0.38 - 0.40) and kidney weight were not different among groups and the weight and length, Ca content, strength of two bones Tibia and Femur were not affected by Ca sources except Femur Ca content. Ca content of Femur was greater in ESP groups than that of CaCO$_3$ groups. The body weight gain, bone growth, the Ca contents and strength of bones were significantly greater in 0.4% calcium groups suggesting 0.2% calcium is not sufficient for the optimum growth in the growing rats. These results indicate that ESP be a proper Ca source comparable or superior to CaCO$_3$. However the apparent absorption rate of final 3 days of feeding did not support the observed results showing lower rate in ESP than CaCO$_3$ groups. Further study be needed in the absorption aspect.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.10 no.3
• /
• pp.200-207
• /
• 2007

Single base propellant using a nitrate ester compound NC decomposes naturally during storage time. Therefore, the research for storage life extension is necessary to single base propellant. In this research, $CaCO_3$ inorganic stabilizer had been added into single base propellants up to 0.3%, and the accelerated aging test of the propellant was started. And then, with applying the Arrhenius equation, the storage life of the test of the propellant was contrasted with that of reference propellant. As a result, the storage life of the propellant containing $CaCO_3$ inorganic stabilizer was about twice longer than the reference propellant.

• Journal of Sensor Science and Technology
• /
• v.15 no.3
• /
• pp.168-172
• /
• 2006

Potentiometric $CO_{2}$ sensors were fabricated using a NASICON ($Na_{1+x}Zr_{2}Si_{X}P_{3-X}O_{12}$, 1.8 < x < 2.4) thick film and auxiliary layers. The powder of a precursor of NASICON with high purity was synthesized by a sol-gel method. By using the NASICON paste, an electrolyte was prepared on the alumina substrate by screen printing and then sintered at $1000^{\circ}C$ for 4 h. A series of $Na_{2}CO_{3}-CaCO_{3}$ auxiliary phases were deposited on the Pt sensing electrode. The electromotive force (emf) values were linearly dependent on the logarithm of $CO_{2}$ concentration in the range between 1,000 and 10,000 ppm. The device attached with $Na_{2}CO_{3}-CaCO_{3}$ (1:2 in mol.%) showed good sensing properties in the low temperatures.

• Geomechanics and Engineering
• /
• v.31 no.3
• /
• pp.281-289
• /
• 2022

Bio-CaCO₃ is a blowout environment-friendly materials for soil improvement and sealing of rock fissures. To evaluate the chemical characteristics, shape, size and productivity of soybean urease induced CaCO₃ precipitates (SUICP), experimental studies were conducted via EDS, XRD, FT-IR, TGA, BET, and SEM. Also, the conversion rate of SUICP reaction at different time were determined and analyzed. The Bio-CaCO₃ product obtained by SUICP is comprehensively judged as calcite based on the results of EDS, XRD and FT-IR. The SUICP calcite precipitates are detected as spherical or ellipsoidal particles 3-6 ㎛ in diameter with nanoscale pores on their surface, and this morphology is novel. The median secondary particle size d₅₀ is 39-88 ㎛, indicating the agglomeration of the primary calcite particles. The Bio-calcite decomposes at 650-780℃, representing a medium thermal stability. The conversion rate of SUICP reaction can reach 80% in 24h, which is much more efficient than microbially induced CaCO₃ precipitation. These results reveal the knowledges of SUICP, and further direct its engineering applications. Moreover, we show an economic channel to obtain porous spherical calcite.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.404-412
• /
• 2020

Herein, the properties and self-healing performance of cement mortar incorporating calcium sulfoaluminate(CSA), crystalline admixture(CA), and magnesium oxide(MgO) were investigated. Mortar strength test and water permeability experiments were conducted to analyze self-healing performance of the mortar. Also, variation in crack width were measured via digital optical microscope observation. The hydration products formed in the crack via self-healing were analyzed using x-ray diffraction(XRD), thermogravimetry(TG), and digital optical microscope. The analysis revealed that compressive strength and tensile strength increased as CA substitutional ratio increased. However, in the case of MgO replacement, the compressive strength and tensile strength decreased as the CA substitution ratio increased. The products in the recovered cracks are found to be mostly Ca(OH)2, MgCO3, and CaCO3. CaCO3 was shown to be the main healing product and had a higher portion than Ca(OH)2 and MgCO3 in the recovery products. Moreover, the optimal mix derived via water permeability and crack width results was 8% CSA + 1% CA + 2.5% MgO.

• Journal of the Korean Society of Safety
• /
• v.19 no.1
• /
• pp.81-87
• /
• 2004

Composite particles using inorganic and organic chemicals were synthesized and the results of those reaction were compared to variation of temperature and agitation speed in presence of $CaCO_3$ which was adsorbed SDBS. Also the synthesises were optimized according to conversion rate of composite particles. In inorganic/organic core-shell composite particle polymerization, $CaCO_3$ adsorbed by 0.5wt% surfactant SDBS was prepared initially and then core $CaCO_3$ was encapsulated by sequential emulsion polymerization using MMA at the addition of APS 3.16${\times}$$10^{-3}$mol/L to minimize the coagulated PMMA particle itself during MMA shell polymerization. Encapsulated PMMA on $CaCO_3$ as inorganic/organic core-shell particles was verified by FT-IR and DSC analysis. It was found that the $CaCO_3$ was very well encapsulated by PMMA as shell. The surfaces were distinctly found as spindle shape and broad particle distribution after capsulation.