• 방사선산업학회지
• /
• 제6권3호
• /
• pp.211-215
• /
• 2012

In this study, crosslinked polyethylene (PE) foam sheets were prepared through gamma-ray irradiation. PE foam sheets were prepared through a foaming process using sodium bicarbonate as a blowing and foaming agent. The prepared PE foam sheets were then crosslinked through gamma-ray irradiation. The crosslinking degree was increased to 86.0% with an increase in the absorption dose. The tensile strength of the crosslinked PE foam sheets was increased with an increase in the absorption dose. However, the elongation-at-break of the crosslinked PE foam sheets was decreased. The thermal decomposition temperature of the crosslinked PE foam sheets was increased to $421.2^{\circ}C$ with an increase in the absorption dose. The SEM analysis revealed that the morphology was not changed significantly after the crosslinking through gamma-ray irradiation.

• 접착 및 계면
• /
• 제2권3호
• /
• pp.9-15
• /
• 2001

표면 에너지가 낮아 접착이 어려운 EVA foam을 용해도 파라미터와 표면장력이 다른 용매로 표면처리하여 표면의 상태 변화를 SEM, 접촉각 측정 등으로 조사하였으며 표면의 변화가 접착력에 미치는 영향을 고찰하였다. Zismann plot에 의해 계산된 EVA foam의 임계표면장력 (${\gamma}_{c,0}$)은 27.08 dyne/cm이었다. 용매 처리에 의해 EVA foam 표면의 형태 및 임계포면장력이 변화하였으며 EVA foam의 팽윤도가 용해도 파라미터에 의해 영향을 받는 것에 비해 표면의 변화 정도는 용매의 표면장력에 더 크게 의존하였다. 표면의 변화는 용매의 표면장력 (${\gamma}_L$)이 EVA foam의 임계표면장력 보다 낮아 wetting이 잘될수록 커지는 것으로 나타났다. 용매 처리된 EVA foam을 접착한 결과 처리하지 않은 것에 비해 접착력이 600% 이상 크게 향상되었으며, ${\gamma}_c$가 프라이머의 ${\gamma}_{L,p}$에 근접하여 ${\gamma}_c/{\gamma}_{L,p}$가 1에 가까워질수록 접착력이 증가하였다.

• 한국태양에너지학회:학술대회논문집
• /
• 한국태양에너지학회 2012년도 춘계학술발표대회 논문집
• /
• pp.260-266
• /
• 2012

Syngas and hydrogen from the $CeO_2/ZrO_2$ coated foam devices were investigated under simulated solar radiation. The $CeO_2/ZrO_2$ coated SiC, Ni and Cu foam device were prepared using drop-coating method. Syngas production step was performed at $900^{\circ}C$, and hydrogen production process was performed for ten repeated cycles to compare the CeO2 conversion in syngas production step, $H_2$ yield in hydrogen production step and cycle reproducibility. The produced syngas had the $H_2$/CO ratio of 2, which was suitable for methanol synthesis or Fischer-Tropsch synthesis process. In addition, syngas and hydrogen production process is one of the promising chemical pathway for storage and transportation of solar heat by converting solar energy to chemical energy. After ten cycles of redox reaction, the $CeO_2/ZrO_2$ was analyzed using XRD pattern and SEM image in order to characterize the physical and chemical change of metal oxide at the high temperature.

• 폴리머
• /
• 제36권1호
• /
• pp.34-40
• /
• 2012

초임계 $CO_2(scCO_2)$를 사용하여 poly(butylene succinate) (PBS)를 발포하였다. PBS는 용융 강도를 높이기 위하여 반응 컴파운딩 기법으로 개질하였다. $scCO_2$로 포화된 PBS를 강하 융점 이상의 온도에서 빠르게 압력을 낮춤으로써 미세기포 발포체를 제조하였다. 발포체의 구조는 공정 조건을 변화시켜 제어할 수 있었다. 다른 변수들은 고정하고 발포 온도만 변화시킨 실험은 발포 온도가 높을수록 셀 크기는 증가하고, 셀 밀도는 감소함을 보여주었다. 포화 압력이 클수록 기핵 밀도가 높아졌으며, 그 결과로 셀의 크기는 감소하였다. 감압 속도가 느린 경우에는 셀이 장시간 동안 팽창함으로써 보다 큰 셀이 얻어졌다.

• 한국의류학회지
• /
• 제9권3호
• /
• pp.53-61
• /
• 1985

This paper has been studied on the method of washing without any damage on wool, namely foam washing method. Effect of washing was obtained with experimental equipment manufactured by way of trial. but some deflects were found that the volume of detergent solution and blow ratio changed with time passes by. This difficulties should be improved by farther studies. The solution mixed with sodium oleate ($0.5\%$) and sodium carbonate ($0.3\%$) was found suitable for detergent solution, and under the conditions of washing temperature at $50\~60^{\circ}C$ and washing time for 5 minutes, the washing effect was obtained good. Desoaping treatment with $Na_2CO_3$ solution after washing might be thought to be necessary, and from the scanning electron micrographs (SEM), no damage on wool and wool sureface washed was, observed. From the results of this study foam washing of wool may be expected to be very effective.

• KSBB Journal
• /
• 제26권1호
• /
• pp.83-86
• /
• 2011

The stability of cream containing lotus leaf extract (LLE) was evaluated. Stability pH and viscosity were measured at 3 different temperatures ($25^{\circ}C$, $45^{\circ}C$ and $65^{\circ}C$), and at room temperature under the sun light at 2 day intervals during 12 days. The cleansing cream and foam cleansing containing the extract did not show a significant pH change at the different temperatures. However, the pH of the cleansing cream and foam cleansing containing LLE slightly decreased at $25^{\circ}C$. They showed a high stability at temperature conditions ($45^{\circ}C$ and $65^{\circ}C$) and under the sun light condition. The cleansing cream and foam cleansing containing LLE did not show a significant viscosity change at $25^{\circ}C$, but had a tendency of decrease at $45^{\circ}C$ and $65^{\circ}C$. There was no significant offflavor and discoloration as well as physical changes such as creaming and cohesion at $25-65^{\circ}C$ and under the sun light condition. And this LLE could be used as a stable functional cosmetic material.

• 원예과학기술지
• /
• 제34권3호
• /
• pp.414-423
• /
• 2016

본 연구는 환경오염 감소와 암면 배지의 대체를 위해 새롭게 개발된 생육배지인 phenolic foam의 토마토 육묘용 배지로써의 이용가능성을 구명하기 위해 수행되었다. 토마토 'Madison' 품종을 4종류의 펠릿형 Grodan rockwool(GRW), UR rockwool(URW), phenolic foam LC(LC), phenolic foam LC-lite(LC-lite) 인공배지에 파종하여 육묘 후 19일 후에 4종류의 큐브형 인공배지에 이식하였다. 종자는 식물생장 챔버에($25{\pm}2^{\circ}C$, 상대습도 $90{\pm}5%$, 암발아) 4일 동안 발아시켰고, 발아가 시작 된 후에는 유리온실로 옮겨 두상 관수로 양액을 관수하였다. 토마토의 초장, 엽수, 엽면적, 생체중 및 건물중은 LC-lite 펠릿에서 육묘한 후 URW 큐브로 이식한 묘에서 생육이 우수하였다. 뿌리 등급은 LC 펠릿에서 육묘 후 LC와 LC-lite 큐브로 이식한 처리에서 가장 우수하였다. 배지의 화학성은 모든 배지에서 토마토의 생육에 안정적인 범위였다. URW의 물리성은 용기 용수량, 기상률, 총 공극에서 높은 값을 나타냈다. 그러므로, 신개발 배지인 phenolic foam은 토마토 묘의 초기 육묘와 뿌리 발달에 적합하여 암면 대체 가능성을 입증하였다.

• 한국미생물·생명공학회지
• /
• 제42권3호
• /
• pp.307-311
• /
• 2014

폴리우레탄 담체가 혼합폐기물을 이용한 연속식수소생산에 미치는 영향을 조사하였다. 당밀폐수와 하수슬러지를 혼합하여 연속 회분식 공정에서 발효시켰다. 담체를 넣지 않고 12 h의 수리학적 체류시간으로 운전하였을 때, 대부분의 바이오매스가 외부로 유실된 반면, 담체를 반응조에 투입하였을 때에는 미생물 유실이 현저히 저감하였다. 또한, 담체를 이용한 경우, 수소생산속도 $0.4L-H_2L^{-1}d^{-1}$로 높게 나타났다. 반응조 내 부유 바이오매스에 의한 비수소생산속도가 $241{\pm}4ml-H_2g-VSS^{-1}d^{-1}$로서 담체 표면 부착바이오매스($133{\pm}10ml-H_2g-VSS^{-1}d^{-1}$) 및 담체 내부 부착 바이오매스에 의한 값($95{\pm}14ml-H_2g-VSS^{-1}d^{-1}$)보다 높게 나타났다.

• 한국화재소방학회논문지
• /
• 제29권3호
• /
• pp.48-52
• /
• 2015

이 연구는 기존의 미터링 오리피스보다 유량계수가 작은 미터링 벤츄리를 이용하여 포소화약제 혼합장치를 실무에서 주로 사용하는 직경으로 제작하여 혼합비가 적정한지를 평가한 연구로써 3%용 혼합비의 경우 가압수 직경 76.2 mm(포원액 직경 31.75 mm)는 3.1~3.5%의 혼합비의 변화를 나타내었고, 가압수 직경 101.6 mm(포원액 직경 38.1 mm)는 3.3~3.7%의 변화를 나타내어 포소화약제혼합장치등의 성능인증 및 제품검사의 기술기준인 3.0~3.9%를 만족하는 것을 알 수 있었다. 6% 혼합비의 경우 가압수 직경 76.2 mm는 6.4~6.8%의 혼합비의 변화를 나타내었고, 가압수 직경 101.6 mm는 6.25~6.5%의 변화를 나타내어 포소화약제혼합장치등의 성능인증 및 제품검사의 기술기준인 6.0~7.0%를 만족하는 것을 알 수 있었다.

• 대한기계학회논문집A
• /
• 제33권4호
• /
• pp.337-345
• /
• 2009

This paper investigates the reliability of district heating pipes at thermo-elastic fatigue loading. District heating pipes, subjected to $120^{\circ}C$ and $16kg_f/cm^2$ due to water distributing service through inside the pipes, should endure long term cyclic thermal-mechanical loadings. The heating pipes are the co-centric tubes of steel pipe, poly urethane(PUR) insulator, and high density poly ethylene(HDPE) case. On installation, foam pad is externally wrapped for accommodating stress reduction near the bend sections of pipes. However, there have been frequent reports on the failures of bend sections in the middle of long term service. This study scrutinizes the observed failures near the bend sections through applying the finite element methods. Specially in this study, heating pipes are studied on the influence of foam padding on failures and proposed new designs for reinforced bend without foam pad.