• Progress in Superconductivity and Cryogenics
• /
• v.13 no.4
• /
• pp.22-25
• /
• 2011

A single-coat $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) film of high critical currents ($I_c$) could be successfully fabricated by optimizing the viscosity of the coating solution in the metal-organic deposition (MOD) process. From a Ba-deficient coating solution (Y: Ba: Cu = 1: 1.5: 3) having the viscosity of 212 $mPa{\cdot}sec$, 0.9 ${\mu}m$-thick single coat YBCO film with the $I_c$ value of 289 A/cm-width ($J_c$ = 3.2 MA/$cm^2$) at 77 K was achievable on the $SrTiO_3$ (STO) substrate, which was superior to that of our previous report for 0.8 ${\mu}m$-thick single coat YBCO film from a stoichiometric coating solution (Y: Ba: Cu = 1: 2: 3) on the $LaAlO_3$ (LAO) substrate. This result might be attributed to denser and more homogeneous microstrcuture in the case of the YBCO film from the Ba-deficient coating solution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.43-46
• /
• 2000

In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$TiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Structure and electrical characteristics of specimen was analyzed by Fractal Process. Thickness of BST ceramics thin films are about 2800[$\AA$]. Dielectric constant and loss of thin films was little decreased at 1[kHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the relation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.2
• /
• pp.121-127
• /
• 1998

In this paper, to develop PTCR(Positive Temperature Coefficient of Resistance) thermistor with high withstanding voltage, Ca were added to. the compositions of $(Ba_{0.9165-X}-Sr_{0.08}-Ca_X-Y_{0.0035})TiO_3+MnO_2$ 0.02wt%+$SiO_2$ 0.5wt%. the effects of Ca additions were researched according the increasing of Ca from 0[mol%] to 20[mol%], and the electrical properties were investigated. As increasing Ca additions from 0[mol%] to 20[mol%], the grain size of the specimens was reduced from 11.1[${\mu}m$] to 6.15[${\mu}m$], and also the sintered density was reduced from 5.43[$g/cm^3$] to 5.05[$g/cm^3$] and their the breakdown voltages were increased from 163[V/mm] to 232[V/mm]. It is shown that the breakdown voltage was increased with amount of Ca additions.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.4
• /
• pp.15-20
• /
• 2013

We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the $SrTiO_3$ (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density ($J_c$) and pinning force density ($F_p$). The anisotropic $J_{c,min}/J_{c,max}$ ratio in the field-angle dependence of $J_c$ at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic $J_c$ values of 9.0 and $2.9MA/cm^2$ with the maximum $F_p$ ($F_{p,max}$) values of 19 and $5GN/m^3$ at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller $BaZrO_3$ (BZO) nanoparticles (the average size ${\approx}28.4$ nm) than $YBa_2SnO_{5.5}$ (YBSO) nanoparticles (the average size ${\approx}45.0$ nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.200-200
• /
• 2008

This paper reports on electrical characterization by IDC pattern using BST$(Ba_{0.5}Sr_{0.5}TiO_3)$ thin film. BST thin films have been deposited on $Al_2O_3$ Substrates by Nd-YAG pulsed laser deposition with a 355nm wavelength at $700^{\circ}C$. The post deposition annealing at $750^{\circ}C$ in flowing $O_2$ atmosphere for I hours. The capacitance of IDC patterns have been measured from 1 to 10 GHz as a function fo electric field (${\pm}40$ KV/cm) at room temperature using interdiigitated Au electrodes deposited on top of BST. The IDC patterns have three type of fingers number. For the finger paris was increased onto $Al_2O_3$, the capacitance increased. The capacitance of 5 pairs finger was 0.3pF and 10 pairs finger was 0.9pF.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Journal of Sensor Science and Technology
• /
• v.8 no.1
• /
• pp.10-15
• /
• 1999

White emission thin film electroluminescent device was fabricated using ZnS for phosphor layer and BST ferroelectric thin film for insulating layer. For fabrication conditions of BST thin film, stoichiometry of target was $Ba_{0.5}Sr_{0.5}TiO_3$, substrate temperature was $400^{\circ}C$, working pressure was 30 mTorr, and A:$O_2$ ratio was 9:1. At this time, dielectric constant was 209 at 1kHz frequency. For phosphor layer ZnS:Mn, ZnS:Tb, and ZnS:Ag were used. Mixing rates of activators were respectively 0.8, 0.8, and 1 wt%. Total thickness of phosphor tapers was 500 nm, thickness of lower insulating layer was 200 nm, and thickness of upper insulating layer was 400 nm. In this conditions, luminescence threshold voltage of thin film electroluminescent device was $95\;V_{rms}$, maximum brightness was $3,000\;cd/m^2$ at $150\;V_{rms}$. Luminescence spectrum peak was observed at region of blue(450 nm), green(550 nm), and red(600 nm).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.19-20
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_3$-MgO powder with $B_2O_3-Li_2CO_3$ were made by the Sol-Gel method. The thick films of BST-MgO with $B_2O_3-Li_2CO_3$ were fabricated on the $Al_2O_3$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_2O_3-Li_2CO_3$, addition were investigated. The structure of the BST-MgO with $B_2O_3-Li_2CO_3$ thick films were dense and homogeneous with no pores. The dielectric constant was increased and dielectric loss was decreased with increasing the sintering temperature.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1261-1262
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_{3}$-MgO powder with $B_{2}O_{3}-Li_{2}CO_{3}$ were made by the Sol-Gel method. And then the thick films of BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ were fabricated on the $Al_{2}O_{3}$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_{2}O_{3}-Li_{2}CO_{3}$ addition were investigated. The structure of the BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ thick films were dense and homogeneous with no pores. The dielectric constant and dielectric loss were increased with decreasing the $B_{2}O_{3}-Li_{2}CO_{3}$ addition ratio.

• The Journal of the Petrological Society of Korea
• /
• v.5 no.2
• /
• pp.142-160
• /
• 1996

Petrological and geochemical characteristics of A-type granite were studied from the Namsan and Tohamsan granites in the vicinity of Kyeongju city, southeastern Korea. The Namsan granite consists of hypersolvus alkali-feldspar granite in the northern part and subsolvus alkali-feldspar to biotite granite in the southern part. This hypersolvus granite usually has miarolitic cavities and is characteristically composed of quartz, single homogeneous one-feldspar (alkali feldspar) forming tabular microperthite crystals, or micrographic intergrowth with quartz, and interstitial biotite (Fe-rich annite), alkali amphibole (riebeckitic arfvedsonite) and fluorite. Petrographic and petrochemical characteristics indicate that the hypersolvus granite and subsolvus granite from the Namsan belogn to the A-type and I-type granitoid, respectively. The A-type granite is petrochemically distinguished from the I-type Bulgugsa granites of Late Cretaceous in South Korea, by higher abundance of $SiO_2$, $Na_2O$, $Na_2O+K_2O$, large highly charged cations such as Rb, Nb, Y, Zr, Ga, Th, Ce. U the REEs and Ga/Al ratio, and lower abundance of $TiO_2$, $Al_2O_3$, CaO, $P_2O_5$, MnO, MgO, Ba, Sr, Eu. The total abundance of REEs is 293 ppm to 466 ppm, showing extensively fractionated granitic compositon, and REEs/chondrite normalized pattern shows flat form with strong Eu '-' anomaly ($Eu/Eu^{\ast}$=0.03-0.05). A-type granite from the Namsan area is thought to have been generated late in the magmatic/orogenic cycle after the production of I-type granite and by direct, high-temperature partial melting of melt-depleted, relatively dry tonalitic/granulitic lower crustal material with underplating by mantle-derived basaltic magmas associated with subduction.