• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.35-36
• /
• 2008

PTC thermistor are characterized by an increase in the electrical resistance with temperature. The PTC materials of middle Curie point were produced or that of high Curie point (above $200^{\circ}C$), it was determined that compositional modifications of $Pb^{2+}$ for $Ba^{2+}$ produce change sin the Curie point to higher temperature. PTC ceramic materials with the Curie point above $120^{\circ}C$ were prepared by adding $PbTiO_3$, PbO or $Pb_3O_4$ into $BaTiO_3$. Thereby, adding $Pb^{2+}$ into $BaTiO_3$-based PTC material to improve Tc was studied broadly, however, weal know that PbO was poisonous and prone to volatilize, then to pollute the circumstance and hurt to people, so we should dope other innocuous additives instead of lead to increase Tc of composite PTC material. In order to prepare lead-free $BaTiO_3$-based PTC with middle Curie point, the incorporation on $Bi_{1/2}K_{1/2}TiO_3$ into $BaTiO_3$-based ceramics was investigated on samples containing 0, 1, 2, 3, 4, and 50mol% of $Bi_{1/2}K_{1/2}TiO_3$. $Bi_{1/2}K_{1/2}TiO_3$ was compounded as standby material by conventional solid-state reaction technique. The starting materials were $Bi_2O_3$, $K_2CO_3$, $BaCO_3$ and $TiO_2$ powder, and using solid-state reaction method, too. The microstructures of samples were investigated by SEM, DSC, XRD and dielectric properties. Phase composition and lattice parameters were investigated by X-ray diffraction.

• Journal of the Korean Ceramic Society
• /
• v.46 no.2
• /
• pp.200-210
• /
• 2009

It is necessary to minimize the mismatch of sintering shrinkage between dielectric ceramic and Ni inner electrode layers for the purpose of developing the ultra high-capacity multi layered ceramic condenser(MLCC). Thus, low temperature sintering of dielectric $BaTiO_3$ ceramic should be precedently investigated. In this work, the influence of the milling condition on sintering behavior and electrical properties of $BaTiO_3$ ceramics was investigated in the $BaTiO_3$(BT)-Mg-Dy-Mn-Ba system with borosilicate glass as a sintering agent. As milling time increased, specific surface area(SSA) of the powder increased linearly, while both sinterability and dielectric property were found to be drastically decreased with an increasing SSA. It was also revealed that the sinterability of the excessively milled $BaTiO_3$ ceramics could be recovered by increasing Ba content, rather than increasing glass addition. These results suggest that the sintering behavior of $BaTiO_3$ ceramics under the high SSA was more strongly dependent on the transient liquid phase caused by Ba addition, than the liquid phase from additional glass.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.1
• /
• pp.87-96
• /
• 2004

Polymer/ceramic composites are the most promising embedded capacitor material for organic substrates application. Predicting the effective dielectric constant of polymer/ceramic composites is very important for design of composite materials. In this paper, we measured the dielectric constant of epoxy/$BaTiO_3$ composite embedded capacitor films with various $BaTiO_3$ particles loading for 5 different sizes $BaTiO_3$ powders. Experimental data were fitted to several theoretical equations to find the equation useful for the prediction of the effective dielectric constant of polymer/ceramic composites and also to estimate the dielectric constant of $BaTiO_3$ powders. The Lichtenecker equation and the Jayasundere-Smith equation were useful for the prediction of the effective dielectric constant of epoxy/$BaTiO_3$ composites. And calculated dielectric constants of the $BaTiO_3$ powders were in the range of 100 to 600, which were lower than those of $BaTiO_3$ bulk ceramics.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.6
• /
• pp.367-371
• /
• 2014

We investigated dielectric relaxation properties of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics by addition (0~0.3 wt%) of $(Ba,Ca)SiO_3$ glass frit. All composition of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ added $(Ba,Ca)SiO_3$ glass frit showed the same crystallographic properties, coexistence of orthorhombic and tetragonal phase. By increasing addition of $(Ba,Ca)SiO_3$ glass frit, the Curie temperatures of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were decreased, whereas maximum dielectric constants of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were dramatically increased. Especially the deviations of Curie temperature $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were increased by increasing amount of $(Ba,Ca)SiO_3$ glass frit, and it indicated that $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics added $(Ba,Ca)SiO_3$ glass frit have relaxor characteristics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.68-69
• /
• 2005

BTO ($BaTiO_3$) thin film is one of the high dielectric materials for high-density dynamic random access memories (DRAMs) due to its relatively high dielectric constant. It is generally known that BTO film is difficult to be etched by plasma etching, but high etch rate with good selectivity to pattern mask was required. The problem of sidewall angle also still remained to be solved in plasma etching of BTO thin film. In this study, we first examined the patterning possibility of BTO film by chemical mechanical polishing (CMP) process instead of plasma etching. The sputtered BTO film on TEOS film as a stopper layer was polished by CMP process with the self-developed $BaTiO_3$- and $TiO_2$-mixed abrasives slurries (MAS), respectively. The removal rate of BTO thin film using the$ BaTiO_3$-mixed abrasive slurry ($BaTiO_3$-MAS) was higher than that using the $TiO_2$-mixed abrasive slurry ($TiO_2$-MAS) in the same concentrations. The maximum removal rate of BTO thin film was 848 nm/min with an addition of $BaTiO_3$ abrasive at the concentration of 3 wt%. The sufficient within-wafer non-uniformity (WIWNU%)below 5% was obtained in each abrasive at all concentrations. The surface morphology of polished BTO thin film was investigated by atomic force microscopy (AFM).

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.210-213
• /
• 2005

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated by the screen printing method on alumina substrates. The effect of the sintering temperature on the microstructure and dielectric properties of the $BaTiO_3/SrTiO_3$ thick films has been investigated. The relative dielectric constant and dielectric loss at 1 MHz of the $BaTiO_3/SrTiO_3$ heterolayered thick films with sintering temperature of $1350^{\circ}C$ were about 751 and 1.74, respectively. The remanent polarization $(P_r)$ of the pure $(Ba_{0.5}Sr_{0.5})TiO_3$ and $BaTiO_3/SrTiO_3$ heterolayered films are approximately $5.1\;{\mu}C/cm^2$ and $10\;{\mu}C/cm^2$. This study suggests that the design of the $BaTiO_3/SrTiO_3$ heterolayered thick films capacitor with different phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.6
• /
• pp.454-457
• /
• 2010

The influence of CuO addition on what of the $(Ba,Sr)TiO_3$ ceramics was studied. The sintering temperature of $(Ba,Sr)TiO_3$ ceramics was lowered by the addition of CuO additives. The 1 - 5 wt% CuO were selected and employed as the sintering aids. Low-Temperature Co-fired Ceramic technologies are popular technologies used in the manufacture of microwave devices. In this study, crystalline and electrical properties of CuO doped $(Ba,Sr)TiO_3$ ceramics were investigated to determine the low temperature sintering properties. The addition of CuO to $(Ba,Sr)TiO_3$ lowered the sintering temperature from $1350^{\circ}C$ to $1150^{\circ}C$. The dependence of the sintering temperature shrinkage rate and mechanism of CuO doped $(Ba,Sr)TiO_3$ ceramics are investigated and discussed. Also, the crystalline structure of CuO - doped $(Ba,Sr)TiO_3$ ceramics is discussed by the X-ray diffraction (XRD) method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.3
• /
• pp.205-209
• /
• 2009

In this study, in order to develop the composition ceramics for lead-free ultrasonic motor, (1-x-0.09)$NaNbO_{3-x}BaTiO_3-0,09LiNbO_3$ ceramics were fabricated using a conventional mixed oxide process and their piezoelectric and dielectric characteristics were investigated according to the $BaTiO_3$ substitution. All the specimens showed orthorhombic phase structure without secondary phase, $BaTiO_3$ substitution enhanced density, dielectric constant(${\epsilon}_r$) and electromechanical coupling factor($k_p$), However, mechanical quality factor was deteriorated. Curie temperature of specimens was observed as about $380^{\circ}C$. At the $BaTiO_3$ substitution of 4 mol%, density, electromechanical coupling factor($k_p$), dielectric constant(${\epsilon}_r$) and piezoelectric constant($d_{33}$) of specimen showed the optimum value of $4.493g/cm^3$, 0.236, 175, 70 pC/N, respectively.

• Electrical & Electronic Materials
• /
• v.10 no.3
• /
• pp.274-283
• /
• 1997

These days, according to surprising development of communication enterprises, every soft of devices is getting smaller and cheaper. Among these Devices, microwave dielectric ceramics are studied and progressed briskly as the materials of dielectric resonator. Dielectric properties of BaO-S $M_{2}$ $O_{3}$-Ti $O_{2}$, one of the BaO Lnsub 2/ $O_{3}$-Ti $O_{2}$ (Ln=La, Sm, Nd, Pr…) system, synthesized by solid-reaction and coprecipitation method were investigated. Disk-type samples were sintered at 1250-1400.deg. C for 2hrs. As a result, single phase was not synthesized in both method. First created the second phase of S $M_{2}$ $Ti_{2}$ $O_{7}$, and then the last phase of $Ba_{3.75}$S $m_{9.5}$ $Ti_{18}$ $O_{54}$, Ti $O_{2}$, and $Ba_{2}$ $Ti_{9}$ $O_{20}$. When the sample was sintered at 1280.deg. C (in solid reaction method) and at 1310.deg. C (in coprecipitation method), it obtained highest dielectric constant (72.96 and 71.70, respectively) and high Q value. Above that temperature, dielectric constant and Q value decreased because of lattice defect according to oxygen vacancies........

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.11
• /
• pp.959-962
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1${\mu}{\textrm}{m}$. When BaTiO$_3$ is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4$\times$10$^4$ A/$\textrm{cm}^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.