• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.9
• /
• pp.752-757
• /
• 1998

Rotational Magnetization-vector measurements have been performed on a polycrystalline $Y_1Ba_2Cu_3O_{7-\delta}$ sample in field-cooled condition at 4.2 K. The experimental results show that vortex flux density(B) consists of 3 groups :(1) a weak pinning part ($B_w$) which stays at a fixed angle relative to the magnetic field f(H) ; (2) a strong pining part($B_s$) which rotates rigidly with the sample and has same magnitude with the sample rotation, and(3) and intermediated pining part ($B_i$) which rotates rigidly with the sample, but whose magnitude changes with the sample rotation Our results have been explained in terms of a distribution in the strength of the vortex pinning torque and a repulsive intervortex torque.

• The Korean Journal of Ceramics
• /
• v.2 no.2
• /
• pp.95-101
• /
• 1996

Variations of the leakage current behaviors and interface potential barrier $({\Phi}_B)$ of rf-sputter deposited (Ba, Sr)$TiO_3$ (BST) thin films with thicknesses ranging from 20 nm to 150nm are investigated as a function of the thickness and bias voltages. The top and bottom electrodes are dc-sputter-deposited Pt films. ${\Phi}_B$ critically depends on the BST film deposition temperature, postannealing atmosphere and time after the annealing. The postannealing under $N_2$ atmosphere results in a high interface potential barrier height and low leakage current. Maintaining the BST capacitor in air for a long time reduces the ${\Phi}_B$ from about 2.4 eV to 1.6 eV due to the oxidation. ${\Phi}_B$ is not so dependent on the film thickness in this experimental range. The leakage conduction mechanism is very dependent on the BST film thickness; the 20 nm thick film shows tunneling current, 30 and 40 nm thick films show Shottky emission current.

• 전기의세계
• /
• v.21 no.6
• /
• pp.17-20
• /
• 1972

The magnetic properties of Ba-Ferrite ( $M^{+2}$O.nF $e_{2}$ $O_{3}$ is highly improved under the condition of composition ratio n=4.4 when B $i_{2}$ $O_{3}$ is added to Ferrite, the adding amount and sintering temperature which affect the magnetic properties were investigated and the following results; were obtained; 1. Magnetic properties are varied with B $i_{2}$ $O_{3}$ content and singering temperature, and coercive force and residual induction can be improved with B $i_{2}$ $O_{3}$. 2. The optimal content of B $i_{2}$ $O_{3}$ amount is about 4 mol %, 3. Without the addition of B $i_{2}$ $O_{3}$, the optimal sintering temperature is about 1300.deg. C, but when 4 mol % of B $i_{2}$ $O_{3}$ is added, the optimal sintering temperature falls to the range of 900.deg. C to 1100.deg. C and it also improves magnetic properties. 4. Residual induction increases as the singering temperature is raised to 1100.deg. C. Coercive force also increased as the sintering temperature is raised to 1000.deg. C, but it rapidly decreases when sintering temperature goes beyond 1000.deg. C. 5. Only a negligible change may be noticed in the decrease of Curie temperature by the addition of about 4 mol % of B $i_{2}$ $O_{3}$.

• Progress in Superconductivity and Cryogenics
• /
• v.18 no.4
• /
• pp.1-4
• /
• 2016

We investigated the relation between the Cu-O bond length and the superconducting properties of $BaSnO_3$ (BSO)-added $GdBa_2Cu_3O_{7-x}$ (GdBCO) thin films by using extended x-ray absorption fine structure (EXAFS) spectroscopy. 4 wt.% $BaSnO_3$ (BSO) added $GdBa_2Cu_3O_{7-x}$ (GdBCO) thin films with varying thickness from $0.2{\mu}m$ to $1.0{\mu}m$ were fabricated by using pulsed laser deposition (PLD) method. The transition temperature ($T_c$) and the residual resistance ratio (RRR) of the GdBCO films increased with increasing thickness up to $0.8{\mu}m$, where the crystalline BSO has the highest peak intensity, and then decreased. This uncommon behaviors of $T_c$ and RRR are likely to be created by the addition of BSO, which may change the ordering of GdBCO atomic bonds. Analysis from the Cu K-edge EXAFS spectroscopy showed an interesting thickness dependence of ordering behavior of BSO-added GdBCO films. It is noticeable that the ordering of Cu-O bond and the transition temperature are found to show opposite behaviors in the thickness dependence. Based on these results, the growth of BSO seemingly have evident effect on the alteration of the local structure of GdBCO film.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.640-646
• /
• 1998

Nucleation and crystallzation of a quaternary glass system for lead titanate glass-ceramics were in-vestigated using DTA(differential thermal analysis ) with variation of nucleation temperature and crystal growth time. Glass samples containing 60mol% of PbO-{{{{ { TiO}_{2 } }} were prepared from melts by the conventional normal cooling method in a cylindrical brass mould. The glass sample was nucleated between 40$0^{\circ}C$ and 50$0^{\circ}C$ for a given time and showed the maximum nucleation rate at 46$0^{\circ}C$ The DTA crystallization peak temperature decreased with increasing nucleating time and decreasing heating rate during DTA runs which indicated an increase of the number of nuclei produced in the system.

• Journal of the Microelectronics and Packaging Society
• /
• v.2 no.1
• /
• pp.29-34
• /
• 1995

Glass 물질을 첨가하여 저온소결한(Ba, Sr, Ca) TiO3 세라믹 유전체의 전기 및 기계 적 특성을 조사하였다. PbO-ZnO-B2O3 계 glass를 첨가하여 소결온도를 135$0^{\circ}C$ to 105$0^{\circ}C$ With 4wt% of glass material the sintered specimen at 115$0^{\circ}C$ for 2hrs showed a dielectric constant over 8000 with low dissipation factor. As fired ceramic capacitor satisfied the Z5U( +10~ +85$^{\circ}C$; +22% ~-56%) specifications of the EIAs. The mechanical hardness and toughness of glass reacted ceramics slightly decreased but it hows higher hardness and toughness values than Lead perovskite dielectrics.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.12
• /
• pp.2270-2275
• /
• 2011

The sintering behavior and microwave properties of ferrite ($Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics) were investigated for microwave applications. Also PIFA type antenna with ferrite was simulated. All samples were prepared by the solid state reaction method and sintered at $1350^{\circ}C$. All ceramics had relatively density above of 92% compare with theoretical density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics. From the XRD pattens, the Z-type phase was existed as main phase in $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics. The permittivity and permeability of $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics were increased with Zn additions and decreased rapidly over frequency of 200~600 MHz. Several PIFA type antennas with ferrite and FR4 were simulated. All antenna structure had return loss of less than -10 dB at each resonant frequency. Simulated antenna using both ferrite and FR4 showed size reduction of 25% without a significant decrement of efficiency.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.438-445
• /
• 2002

In this study, the glass frit of $PbO-TiO-2-SiO_2-BaO-ZnO-Al_2O-3-CaO-B_2O_3-Bi_2O_3-MgO$ system was manufactured. The glass was melted at $1,400{\circ}C$, quenched and attrition-milled. The glass frit powder was pressed and fired for 2h at the range of $750~1,000{\circ}C$. The crystallization of glass frit began at about $750{\circ}$ and at low temperature, the main crystal phases were hexagonal celsian($BaAl_2Si_2O_8$) and alumina. As the firing temperature increased, the crystal phases of monoclinic celsian, zinc aluminate, zinc silicate, calcium titanium silicate and titania appeared. And the increase of firing temperature led to transformation of hexagonal celsian to monoclinic. The only glass frit containing 15wt% PbO had the crystal phase of solid solution of $PbTiO_3-CaTiO_3$. At the frequency of 1 MHz, the dielectric constant of glass frit crystallized was in the range of 11~16 and the dielectric loss less than 0.020. But the glass frit containing 15wt% PbO had the dielectric constant of 17~26 and loss of 0.010~0.015 because of crystal phase of solid solution of $PbTiO_3-CaTiO_3$.

• Fire Science and Engineering
• /
• v.16 no.4
• /
• pp.15-19
• /
• 2002

This dissertation is about the development of $BaTiO_3$-type PTC(Positive Temperature Coefficient) thermistor by composition method. A multilayer-type PTC samples were fabricated under optimal conditions after setting the experimental composition equation as ($Ba_{0.95-x}$S $r_{0.05}$$Ca_{x}$ )$TiO_3$-$0.01TiO_2$-$0.01SiO_2$-$\alpha$$MnCO_3$-$\beta$N $b_2$ $O_{5}$.) and their testing results were analyzed. The optimal sin-tering and cooling temperatures were 13$50^{\circ}C$ for two hours and $100^{\circ}C$/h for an hour, respectively; By composing Ca and Mn, dopants to lower the resistivity at room temperature, and Nb, a dopant to raise peak resistivity(Ca:5 mol%, Mn:0.08 mol%, Nb:0.18 mol%), appropriately, a PTC thermistor, having the characteristics of relatively low resistivity at room temperature and high peak resistivity and a good temperature coefficient, has been developed. And we find that it is possible of application for fire detection sensor.r.r.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1286-1293
• /
• 1998

${SO_4}^{2-}$ ions present in industrial waste water if combined with other metal ions in the water can cause serious scale problem in a transporting pipe. In this study therefore ${SO_4}^{2-}$ ions in an acidic solution have been removed by using surface active glasses. Glasses with various compositions of $SiO_2-Na_2O-B_2O_3-RO$ (R=Mg, Ca, Sr, Ba) system were reacted in a ${SO_4}^{2-}$ ion-containing solution with various pHs ranging from 1 to 4 for various time the reacted glass surfaces were analyzed by XRD and SEM and all ions in the reacted solution were also measured ${SO_4}^{2-}$ ions in the solution were combined with divalent ions leached out of glass and precipitated on the glass surface as sulfate crystals. In this was the surface ion could be removed from the acidic solution. The sulfate ion removal capacity is closely related to the solubility product con-stants of the newly formed sulfate crystals. Almost no sulfate crystal was formed on the MgO-containing glass while sulfate crystals were easily formed on the glass containing either SrO or BaO This indicates that those glasses have strong removal efficiency of ${SO_4}^{2-}$ ions from the solution.