• 한국세라믹학회지
• /
• 제27권5호
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.

• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.37-41
• /
• 2012

A lithium ion conducting borosilicate glass was fabricated by a conventional melt quenching technique from a mixture of Li2CO3, B2O3 and SiO2 powders. The Li ion conductivity of the lithium borosilicate glasses was evaluated in terms of the SiO2/B2O3 ratio. In the Li2O-B2O3-SiO2 ternary glass, the glass forming region decreases with an increasing Li2O content. At the same Li2O, the crystallization tendency of the glass samples increases with the SiO2/B2O3 ratio, resulting in a reduced glass forming region in the Li2O-B2O3-SiO2 ternary glass. The electrical conductivity moderately depends on the SiO2/B2O3 ratio in the Li2O-B2O3-SiO2 ternary glass. The conductivity of the glasses slightly increases with the SiO2/B2O3 ratio. The observed phenomenon can be explained by the modification of the glass structure as a function of the SiO2 content.

• 한국세라믹학회지
• /
• 제11권3호
• /
• pp.19-26
• /
• 1974

Mechanical properties of the system PbO-B2O3-V2O5 low melting glass during crystallization by heat-treatment were investigated. Wettability of the system PbO-B2O3-V2O5 was excellent and appropriate for commercial sealing as a low melting solder glass. Crystals, during heat-treated at 30$0^{\circ}C$ of the system PbO-B2O3-V2O5 were $\beta$-4PbO.B2O3, 5PbO.4B2O3, and Pb2V2O7 mainly. The percent of crystallinity was 82$\pm$5%. Mechanical properties of the system PbO-B2O3-V2O5 were influenced not only by the differences of density and coefficient of thermal expansion and the stress induced from the difference in the density and coefficient of thermal expansion between glass phase and crystals but also crystallization conditions.

• 한국결정성장학회지
• /
• 제14권3호
• /
• pp.123-128
• /
• 2004

융제(flux)로서 $B_2O_3$의 농도를 0-10 wt%까지 변화시킨 $SrAl_2O_4$ : $Eu^{+2}$, $Dy^{+3}$계 장잔광 형광체를 고상반응법으로 합성한 후, $B_2O_3$의 첨가량에 따른 결정특성과 장잔광 축광재료로서 가장 중요한 발광 및 장잔광 특성을 조사하였다. $SrAl_2O_4$ : Eu$^{+2}$, $Dy^{+3}$계 형광체는 $B_2O_3$의 농도에 관계없이 520nm 파장을 최대 발광파장으로 하는 발광스펙트럼을 나타내었고, 3wt%의 $B_2O_3$ 농도에서 최대 발광강도를 나타내었다. 그리고 $SrAl_2O_4$ : Eu$^{+2}$, $Dy^{+3}$ 형광체의 잔광강도 역시 $B_2O_3$의 농도에 무관하게 시간에 따라 모든 시료에서 지수 함수적으로 감소하였으나, $B_2O_3$의 농도가 3wt%인 경우에 발광의 감쇠속도가 작은 뛰어난 장잔광특성을 나타내었다.

• 멤브레인
• /
• 제25권2호
• /
• pp.115-122
• /
• 2015

졸겔법에 의해서 trimethylborate (TMB)/tetraethylorthosilicate (TEOS) 몰비 0.01, 온도 $800^{\circ}C$에서 $SiO_2{\cdot}B_2O_3$가 제조되었다. 그리고 제조된 $SiO_2{\cdot}B_2O_3$와 PDMS[poly(dimethylsiloxane)]로부터 PDMS-$SiO_2{\cdot}B_2O_3$ 복합막을 제조하고 막의 물리화학적 특성을 TG-DTA, FT-IR, BET, X-ray, SEM에 의해 조사하고 그리고 $H_2$와 $N_2$의 투과도와 선택도를 조사하였다. TG-DTA, BET, X-ray, FT-IR 측정에 의하면 $SiO_2{\cdot}B_2O_3$는 무정형의 다공성 $SiO_2{\cdot}B_2O_3$였으며, 기공의 평균직경은 $37.7821{\AA}$, 표면적은 $247.6868m^2/g$이었다. TGA 측정에 의하면 PDMS 내에 $SiO_2{\cdot}B_2O_3$가 첨가되었을 때 PDMS-$SiO_2{\cdot}B_2O_3$ 복합막의 열적 안정성은 향상되었다. SEM 관찰에 의하면 $SiO_2{\cdot}B_2O_3$는 약 $1{\mu}m$ 크기로 PDMS 내에 덩어리 상태로 뭉쳐서 분산되어 있었다. 기체투과실험에 의하면 PDMS 내에 $SiO_2{\cdot}B_2O_3$ 함량이 증가하면 $H_2$와 $N_2$의 투과도는 증가하였고, 질소보다 Lenard Jones 분자지름이 작은 $H_2$의 투과도는 $N_2$의 투과도보다 컸으며, 선택도($H_2/N_2$)는 감소하였다.

• 한국세라믹학회지
• /
• 제36권7호
• /
• pp.767-772
• /
• 1999

The effect of B2O3 addition on the sintering behavior dielectric and ferroelectric properties of Ba0.7Sr0.3TiO3 ceramics were investigated. The sample with 0.5wt% B2O3 was sintered under 115$0^{\circ}C$. The dielectric and ferroelectric properties of BST with 0.5wt% B2O3 was as good as BST without B2O3 sintered at 135$0^{\circ}C$ and its dielectric loss was even better When B2O3 was added over 1.0wt% the overdoped B2O3 remained in the specimens and formed a second phase which degraded the sintering behaivor dielectric properties of BST.

• 한국세라믹학회지
• /
• 제50권1호
• /
• pp.57-62
• /
• 2013

We investigated the thermal and electrical properties of the $B_2O_3-ZnO-Bi_2O_3$ glass system as a sealing material in sheath heater modules. A composition with over 90 wt% $Bi_2O_3$ in the $B_2O_3-ZnO-Bi_2O_3$ system was glassified by controlling the cooling rate. The glass transition temperature and thermal expansion coefficient in bismate glass could be controlled by the minor ingredients of ZnO, $SiO_2$, $BaO_2$, and $K_2O$. The $B_2O_3-ZnO-Bi_2O_3$ glass system bonded well to metal, and bismate glass insulating properties were comparable to those of bismate glass $B_2O_3-ZnO-PbO$ glass system in a sheath heater module.

• 한국안광학회지
• /
• 제8권1호
• /
• pp.7-10
• /
• 2003

4성분 $SrO-B_2O_3-Al_2O_3-SiO_2$ 유리들을 $R({\equiv}SrO\;mole%/B_2O_3\;mole%)$과 $K({\equiv}(Al_2O_3+SiO_2)\;mole%/B_2O_3\;mole%)$에 의하여 제작하여 적외선 흡수(Infrared absorption)을 이용하여 유리들의 구조를 조사하였다. R의 증가에 따라 $1,200{\sim}1,600cm^{-1}$ 영역에서 대칭적 3배위 구조인 $BO_3$ 단위구조에 의한 B-O 결합의 신축떨기(stretching vibration)에 의한 흡수 띠의 세기가 감소되어지며, 사면체 구조인 $BO_4$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기는 $800{\sim}1,200cm^{-1}$ 영역에서 변화되어졌다. 그라고 K의 증가에 따라 대칭적 3배위 구조인 $BO_3$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기는 증가되어지며, 사면체 구조인 $BO_4$ 단위구조에 의한 B-O 결합의 신축떨기에 의한 흡수 띠의 세기가 감소되어졌다.

• 한국자기공명학회논문지
• /
• 제9권1호
• /
• pp.61-66
• /
• 2005

$^{11}B MAS NMR$ spectra of binary glass system $xV_2O5-B_2O_3$ and ternary glass system $xV_2O5-B_2O_3-yNa_2O$ (x = $V_2O_5 mol%/$B_2O_3$ mol%, y = $Na_2O$ mol$/$B_2O_3$ mol%) were acquired. $BO_3$ units are dominant components in the spectra of $xV_2O_5-B_2O_3$glass systems while both $BO_3$ and $BO_4$ unit appear in comparable amounts in the spectra of $xV_2O_5-B_2O_3-yNa_2O$ glass systems. More $BO_3$ units were monitored for higher $V_2O_5$ contents while more $BO_4$ unit for higher $Na_2O$ contents. Quadrupole parameters such as $e^2qQ$ and $\eta$ obtained form spectral simulation indicate that $e^2qQ$ has a maximum value at x = y 1 and $\eta$ decreases and increases as x or y grows, respectively. Our results suggest that $V_2O_5$ and $Na_2O$ play opposite roles in the ternary glasses.

• 멤브레인
• /
• 제14권4호
• /
• pp.312-319
• /
• 2004

졸겔법에 의해 Si(OC$_2$$H_5$/)$_4$-($CH_3$O)$_3$B-C$_2$$H_5$OH-$H_2O$계로부터 다공성의 SiO$_2$-B$_2$O$_3$ 막을 제조하였다. SiO$_2$-B$_2$O$_3$막의 특성을 BET, IR spectrophotometer, X-ray diffractometer, SEM 과 TEM을 사용하여 조사하였다. $700^{\circ}C$에서 얻어진 SiO$_2$-B$_2$O$_3$ 막의 평균 기공직경은 0.0048 $\mu\textrm{m}$이고, 표면적은 354.398 $m^2$/g이었으며, 입자의 크기는 7 nm인 무정형의 다공체이었다. SiO$_2$-B$_2$O$_3$ 막의 수소/질소 혼합 기체 분리 특성은 기체분리 압력을 달리하여 조사하였다. $25^{\circ}C$, ΔP 155.15cmHg에서 수소/질소 혼합 기체를 분리하여 본 결과 SiO$_2$-B$_2$O$_3$ 막의 수소에 대한 real separation factor($\alpha$)는 4.68이었다. 그리고 투과셀의 압력차(ΔP)값이 증가할수록 real separation factor($\alpha$), head separation factor($\beta$), tail separation factor((equation omitted))값이 증가하였다.