• Journal of the Korean Society of Safety
• /
• v.20 no.4 s.72
• /
• pp.29-33
• /
• 2005

In this paper, reflectance and the dielectric characteristics for $P_2O_5-ZnO-BaO$ system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ and the reflectance of $P_2O_5-ZnO-BaO$ system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5-ZnO-BaO$ system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can be explained as the space charge effects. These results are could be applied to the under plate dielectrics of PDP required high reflective ratio and breakdown strength.

• 전자공학회논문지 IE
• /
• v.43 no.4
• /
• pp.8-12
• /
• 2006

In this paper, reflectance and the dielectric characteristics for $P_2O_5$-ZnO-BaO system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ contents, and the reflectance of $P_2O_5$-ZnO-BaO system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5$-ZnO-BaO system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can explained as the space charge effects. These results are could be applied to the lower dielectrics layer of PDP required high reflective ratio and breakdown strength.

• Korean Journal of Materials Research
• /
• v.1 no.4
• /
• pp.206-213
• /
• 1991

The crystallized solder glasses with the low melting temperature for electronic package were prepared with the compositions of 77-80wt% PbO, 4.5-6wt% ZnO, 7.5-8.5wt% $B_2O_3$, 1-2wt% CaO, and 0.5-2.0wt% $P_2O_5$ containing 3-7wt% $TiO_2$. The Characterization of the solder glasses were studied using DTA, SEM and XRD. Frit containing 3wt% $TiO_2$ had crytallzation temperature range of $420-440^{\circ}C$. The major crystalline phase was identified as $2PbO{\cdot}ZnO{\cdot}B_2O_3$ by X-ray diffraction. Frits containing 4 wt% $TiO_2$ consisted of crysalline Phases of $PbTiO_3$ and $2PbO{\cdot}ZnO{\cdot}B_2O_3$ in the temperature range of $420-440^{\circ}C$, When g1ass frit containing 5wt% $TiO_2$ were heat-treated in the temperature range of $440-460^{\circ}C$, major crytalline phase was perovskite lead titanate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.48-52
• /
• 2003

Low melting crystalline solder glasses for CRT sealing were prepared from the composition of PbO 73.0~75.5 wt%, ZnO 12~15 wt%, $B_2O_3$ 7.0~9.0 wt%, BaO 1.5~3.5 wt%, $P_2O_5$ 1.0~2.5 wt%, $Bi_2O_3$ 0.5~20 wt%. The nucleation and crystallization of the crystalline solder glasses were studied by DTA, SEM and XRD. $2PbO{\cdot}ZnO{\cdot}B_2O_3$ crystalline phase was formed from glass matrix by heat-treatment of glass frits Crystalline solder glasses developed from this paper have good firing condition of $430{\sim}440^{\circ}C$ for 10min and good physical properties

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.4
• /
• pp.55-59
• /
• 1999

One of lead free glass, Bi based solder glass is investigated for electronic packaging application. The melting temperature of glass about $550^{\circ}C$ at Bi based glass (70wt% $B_2O_3$ + l5wt%$B_2O_3$ + 8wt% $SiO_2$ + 2wt% $P_2O_5$ + 4wt% $A1_2O_3$ +lwt% ZnO) and varied with $P_2O_5$ content in this system. Crystallized glasses were obtainded after 1hr heat teratment at $450^{\circ}C$ with 10wt% of $P_2O_5$ addition. Much higher melting temperature was observed at $B_2O_3$ rich composition area.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.74.2-74
• /
• 2000

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.593-595
• /
• 2001

Zinc-phosphate glasses에 B$_2$O$_3$를 도입하여 borate, phosphate, boro-phosphate networks가 혼재되어 있는 highly cross-linked structures를 형성시켜 Phosphate glasses의 화학적 안정화를 검토하였다. Raman 측정 결과 B$_2$O$_3$와 P$_2$O$_{5}$는 잘 혼화된 polynary networks를 이루고 있으며, 이렇게 하여 증진된 구조적 cross-linking에 의하여 xB$_2$O$_3$.(1-x)Zn$_2$P$_2$O$_{7}$ glasses의 T$_{g}$, T$_{d}$는 증가하였고 동시에 CTE는 감소하는 결과를 가져왔다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2000.01a
• /
• pp.181-182
• /
• 2000

The glass compositions of $PbO-SiO_2-B_2O_3$ system and $P_2O_5-PbO-ZnO$ system for the transparent dielectric materials for front panel and $P_2O_5-ZnO-BaO$ and $SiO_2-ZnO-B_2O_3$ for the reflective dielectric materials for back panel of PDP(Plasma Display Panel) were investigated. As a transparent dielectric materials for front panel, $PbO-SiO_2-B_2O_3$ glass showed good dielectric properties, high transparency and proper thermal expansion matching to soda-lime glass substrate. And the reflective dielectric materials for back panel were prepared from parent glass of $SiO_2-ZnO-B_2O_3$ system and oxide filler. It was found that these glass-ceramics are useful materials for reflective dielectric layers, as those have a similar thermal expansion to soda-lime glass plate, high reflectance, low sintering temperature.

• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.235-240
• /
• 2006

We investigated the effect of ZnO filler on the microstructure of $BaO-B_2O_3-ZnO-P_2O_5$ glass system to find an etching mechanism of barrier ribs. The sintering behavior of composites heated in the temperature range $560-600^{\circ}C$ was studied by volumetric shrinkage rate and microstructure. The etching test was carried out in $HNO_3$ solution at $50^{\circ}C$ for 10 min. The volumetric shrinkage of sintered sample decreased with the increased firing temperature because of the formation of two crystals. Glass and ZnO filler react forming the $BaZn_2(PO_4)_2$ crystal phases during the sintering process. Etching phenomenon of sintered samples by $HNO_3$ showed that the $BaZn_2(PO_4)_2$ crystal phase was strongly leached compared to glass matrix, crystal phases and fillers. Therefore, the control of interface by condition of sintering is so important to achieve etching effect in barrier ribs.

• Journal of Information Display
• /
• v.2 no.3
• /
• pp.39-43
• /
• 2001

The glass compositions of $PbO-SiO_2-B_2O_3$ system and $P_2O_5-PbO-ZnO$ system for the transparent dielectric materials for front panel and $P_2O_5$-ZnO-BaO and $SiO_2-ZnO-B_2O_3$ for the reflective dielectric materials for back panel of PDP (Plasma Display Panel) were investigated. As a result, transparent dielectric materials for front panel showed good dielectric properties, high transparency, and proper thermal expansion matching to soda lime glass substrate. And the reflective dielectric layers for back panel were prepared from two series of parent glass and oxide filler. It was found that these glassceramics are useful materials for dielectric layers in PDP device, as they have similar thermal expansion to soda-lime glass plate, high reflectance, and low sintering temperature. In particular, the addition of $BPO_4$ and $TiO_2$ as fillers to $SiO_2-ZnO-B_2O_3$ system is considered to be the most effective for acquiring good properties of lower dielectric layer for PDP device.