• Journal of the Korean Magnetics Society
• /
• v.13 no.1
• /
• pp.36-40
• /
• 2003

We have grown D $y_{x}$B $i_{3-x}$F $e_{5}$ $O_{12}$ (x = 0.5,1.0, 1.5,2.0) magnetic garnet thin films upon $Al_2$O3i and GGG substrate using Pechini process. The annealing temperature to get single phase D $y_{x}$B $i_{3-x}$F $e_{5}$ $O_{12}$ garnet is dependent on substrate, i.e. the annealing temperature for GGG substrate il 5$0^{\circ}C$ lower than that for $Al_2$ $O_3$ substrate. The grains of garnet thin film grown on GGG (111) plane align along [111] direction, and in this case the hysteresis curve does not saturate up to H : 5000 Oe. We attribute this phenomenon to rotation magnetization process. The maximum amount of Bi substitution in polycrystalline D $y_{x}$B $i_{3-x}$F $e_{5}$ $O_{12}$ thin film prepared by Pechini process is restricted to 2.0 Bi atom/unit cell, and this value is less than that in single garnet crystall grown by LPE method.own by LPE method.ethod.

• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.186-190
• /
• 2005

The $Al_{0.2}CoFe_{1.8}O_4$ ferrite films and powders were prepared by the sol-gel method. The crystallographic and magnetic properties of the samples were examined with annealing temperature by X-ray diffraction, $M\ddot{o}ssbauer$ spetroscopy and vibrating sample magnetometry. The powder samples showed the presence of spinel structure at annealing temperatures above 673 K, while the film samples indicated the spinel structure above 873 K, also the particle size increased with rising annealing temperatures. The $M\ddot{o}ssbauer$ spectra of $Al_{0.2}CoFe_{1.8}O_4$ powder annealed above 873 K could be fitted as the superposition of two Zeeman sextets due to ferrimagnetic phase. And the spectra of annealed at 673 K exhibited the superposition of ferrimanetic and paramagnetic phase and those of annealed at 473 K showed only a paramagnetic phase. The magnetic behaviour of powders appeared that the coercivity increased until annealed at 673 K but decreased above this temperature. The coercivity of the film samples decreased from 1.084 kOe at 873 K to 0.540 kOe at 1073 K with increasing annealing temperatures.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.742-748
• /
• 2004

Isopropanol of low boiling point was used as a solvent to prepare Al-doped ZnO(AZO) thin films. A homogeneous and stable sol was made from Zn acetate a solute whose mole concentration was 0.7mol/$\iota$ and Al chloride as a dopant. Al-doped ZnO thin films were prepared by sol-gel method as a function of post-heating temperature from 500 to $700^{\circ}C$ and the optical and electrical properties were investigated. The c-axis orientation along (002) plane was enhanced with the increasing of post-heating temperature and the surface morphology of the films showed a homogeneous and nano-sized microstructure. The optical transmittance of the films post-heated below $650^{\circ}C$ was over $86\%$, but decreased at $700^{\circ}C$. The electrical resistivity of the thin films decreased from 73 to 22 $\Omega$-cm as the post-heating temperature increased up to $650^{\circ}C$, but increased greatly to 580 $\Omega$-cm at $700^{\circ}C$. XPS analysis indicated that the deterioration of electrical and optical properties was attributed to the precipitation of $Al_2O_3$ phase on the surface of AZO thin film. This result suggests that the optimum post-heating temperature to improve electrical and optical properties is $600^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.338-341
• /
• 2002

$(Ba_{1-x}Sr_{0.4}Ca_x)TiO_{3}$ (x=0.10, 0.15, 0.20) powders were prepared by the sol-gel method and BSCT thick films were fabricated by the screen-printing method. Their structural and dielectric properties were investigated with variation of composition ratio and $Al_{2}O_{3}$ doping contents. As results of the X-ray diffraction and microstructure analysis, the grain size of BSCT thick films was decreased with increasing $Al_{2}O_{3}$ amount. The thickness of BSCT thick films by 4-coating/drying is about $110{\sim}120{\mu}m$. The tunability increased with decreasing Ca content, and the BSCT(50/40/10) specimen doped with 1.0wt% $Al_{2}O_{3}$ showed the highest value of 12.94% at 5kV /cm.

• Korean Journal of Materials Research
• /
• v.28 no.7
• /
• pp.371-375
• /
• 2018

The manganese-, nickel-, and aluminum-doped cobalt ferrite powders, $Mn_{0.2}Co_{0.8}Fe_2O_4$, $Ni_{0.2}Co_{0.8}Fe_2O_4$, and $Al_{0.2}CoFe_{1.8}O_4$, are fabricated by the sol-gel method, and the crystallographic and magnetic properties of the powders are studied in comparison with those of $CoFe_2O_4$. All the ferrite powders are nano-sized and have a single spinel structure with the lattice constant increasing in $Mn_{0.2}Co_{0.8}Fe_2O_4$ but decreasing in $Ni_{0.2}Co_{0.8}Fe_2O_4$ and $Al_{0.2}CoFe_{1.8}O_4$. All the $M{\ddot{o}}ssbauer$ spectra are fitted as a superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. The values of the magnetic hyperfine fields of $Ni_{0.2}Co_{0.8}Fe_2O_4$ are somewhat increased in the A and B sites, while those of $Mn_{0.2}Co_{0.8}Fe_2O_4$ and $Al_{0.2}CoFe_{1.8}O_4$ are decreased. The variation of $M{\ddot{o}}ssbauer$ parameters is explained using the cation distribution equation, superexchange interaction and particle size. The hysteresis curves of the ferrite powders reveal a typical soft ferrite pattern. The variation in the values of saturation magnetization and coercivity are explained in terms of the site distributions, particle sizes and the spin magnetic moments of the doped ions.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.682-690
• /
• 1989

Fine mullite powder was prepared by colloidal sol-gel route. Boehmite as a starting material of Al2O3 and silica sol or fumed silica as a starting material of SiO2 were used. $\alpha$-Al2O3, TiO2 and ZrO2 were used as seeding materials. The combination of boehmite and silica was found to be the stoichiometric mullite powder. Techniques for drying used were spray drying, freeze drying, reduced pressure evaporation and drying in a oven. The gelled powder was heated at 130$0^{\circ}C$ for 100min and was attrition-milled for 1~3hrs. The mullite powder obtained was composed of submicrometer, uniform and spherical particles with a narrow size distribution. The mullite powder was characterized by BET, SEM, XRD and IR spectroscopy.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.477-480
• /
• 2014

An $Al_2O_3$-CuO-ZnO (ACZ) precursor powder was synthesized by a facial sol-gel process using a nonionic surfactant span 80 as the chelating agent to improve the surface area and morphology. When creating a hydrogen membrane, several kinds of properties are required, such as easy dissociation of hydrogen molecules, fast hydrogen diffusion, high hydrogen solubility, and resistance to hydrogen embrittlement. ACZ-Ni composite membranes (cermet) were prepared with this precursor and pure Ni powder via the hot press sintering (HPS) method. The ACZ powder was characterized by XRD, BET, and FE-SEM. Hydrogen permeation experiments were performed by Sievert's type of hydrogen permeation membrane equipment. The hydrogen permeability of ACZ/Ni 10 wt% and ACZ/Ni 20 wt% was obtained as 7.2 and $10molm^{-2}s^{-1}$ at RT, respectively. These values of the corresponding membranes were slightly increased with increasing pressures.

• Journal of the Korean Society of Combustion
• /
• v.11 no.2
• /
• pp.7-14
• /
• 2006

Catalytic combustion is one of the suitable methods for micro power source due to high energy density and it can be applied to micro structured chamber without consideration of quenching since it is flameless combustion. Catalyst loading in the micro structured combustion chamber is one of the most important issues in the development of micro catalytic combustors. In this research, to coat catalyst on the chamber wall, two methods were investigated. First, $Al_2O_3$ was selected as a support of Pt and $Pt/Al_2O_3$ was synthesized through the alumina sol-gel procedure. To improve the coating thickness and adhesion between catalyst and substrate, heat resistant and water solvable organic-inorganic hybrid binder was used. Porous silicon was also investigated as a catalyst support for platinum. Through the parametric studies of current density and etching time, fabrication process of $1{\sim}2{\mu}m$ of diameter and about $25{\mu}m$ depth pores was confirmed. Coated substrates were test in the micro channel combustor which was fabricated by the wet etching and machining of SUS 304. Using $Pt/Al_2O_3$ coated substrate and Pt coated porous silicon substrate, conversion rate of fuel was over 95 % for $H_2/Air$ premixed gas.

• Korean Journal of Materials Research
• /
• v.26 no.3
• /
• pp.160-165
• /
• 2016

To increase the capacitance of an Al electrolytic capacitor, the anodic oxide film, $Al_2O_3$, was partly replaced by an $Al_2O_3-ZrO_2$ (Al-Zr) composite film prepared by the vacuum infiltration method and anodization. The microstructure and composition of the prepared samples were investigated by scanning electron microscopy and transmission electron microscopy. The coated and anodized samples showed multi-layer structures, which consisted of an inner Al hydrate layer, a middle Al-Zr composite layer, and an outer $Al_2O_3$ layer. The thickness of the coating layer could go up to 220 nm when the etched Al foil was coated 8 times. The electrical properties of the samples, such as specific capacitance, leakage current, and withstanding voltages, were also characterized after anodization at 100 V and 600 V. The capacitances of samples with $ZrO_2$ coating were 36.3% and 27.5% higher than those of samples without $ZrO_2$ coating when anodized at 100 V and 600 V, respectively.

• 한국연소학회:학술대회논문집
• /
• 2006.10a
• /
• pp.235-241
• /
• 2006

Catalytic combustion is one of the suitable methods for micro power source due to high energy density and no flame quenching. Catalyst loading in the micro structured combustion chamber is one of the most important issues in the development of micro catalytic combustors. In this research, to coat catalyst on the chamber wall, two methods were investigated. First, $Al_2O_3$ was selected as a support of Pt and $Pt/Al_2O_3$ was synthesized through the alumina sol-gel procedure. To improve the coating thickness and adhesion between catalyst and substrate, heat resistant and water solvable organic-inorganic hybrid binder was used. Porous silicon was also investigated as a catalyst support for platinum. Through the parametric studies of current density and etching time, fabrication process of $1{\sim}2{\mu}m$ of diameter and about $25{\mu}m$ depth pores was confirmed. Coated substrates were test in the micro channel combustor which was fabricated by the wet etching and machining of SUS 304. Using $Pt/Al_2O_3$ coated substrate and Pt coated porous silicon substrate, conversion rate of fuel was over 95% for $H_2$/Air premixed gas.