• Journal of the Korea Institute of Military Science and Technology
• /
• v.21 no.6
• /
• pp.760-766
• /
• 2018

The present study investigates the effect of PMMA and BN content on microstructure, mechanical and dielectric properties of silicon nitride($Si_3N_4$) ceramics in $Y_2O_3-Al_2O_3$ additive system. The total additive content was fixed at 8 wt.% and the amount of PMMA varies from 0 to 40 wt.% and BN varies from 0 to 36 wt.%, respectively. The crystalline phases of the samples were determined by X-ray diffraction analysis. All the sintered sample shows complete transformation of ${\alpha}$ to ${\beta}-Si_3N_4$ during the sintering process indicated that the phase transformation was unaffected by the PMMA or BN content. However, the microstructure shows that the residual porosity increased with increasing PMMA and BN content. In addition, the flexural strength and the dielectric constant decrease with addition of PMMA and BN due to the residual porosity. This article provides empirical study of design parameters for $Si_3N_4$-based radome materials.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.1 no.4
• /
• pp.202-208
• /
• 2001

In Recent results suggested that doping $Ta_2O_5$ with a small amount of $TiO_2$ using standard ceramic processing techniques can increase the dielectric constant of $Ta_2O_5$ significantly. In this paper, this concept is studied using RTCVD (Rapid Thermal Chemical Vapor Deposition). Ti-doped $Ta_2O_5$ films are deposited using $TaC_{12}H_{30}O_5N$, $C_8H_{24}N_4Ti$, and $O_2$ on both Si and $NH_3$-nitrided Si substrates. An $NH_3$-based interface layer at the Si surface is used to prevent interfacial oxidation during the CVD process and post deposition annealing is performed in $H_2/O_2$ ambient to improve film quality and reduce leakage current. A sputtered TiN layer is used as a diffusion barrier between the Al gate electrode and the $TaTi_xO_y$ dielectric. XPS analyses confirm the formation of a ($Ta_2O_5)_{1-x}(TiO_2)_x$ composite oxide. A high quality $TaTi_xO_y$ gate stack with EOT (Equivalent Oxide Thickness) of $7{\AA}$ and leakage current $Jg=O.5A/textrm{cm}^2$ @ Vg=-1.0V has been achieved. We have also succeeded in forming a $TaTi_x/O_y$ composite oxide by rapid thermal oxidation of the as-deposited CVD TaTi films. The electrical properties and Jg-EOT characteristics of these composite oxides are remarkably similar to that of RTCVD $Ta_2O_5, suggesting that the dielectric constant of $Ta_2O_5$ is not affected by the addition of $TiO_2$.

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.5
• /
• pp.527-534
• /
• 2006

The purpose of this study is the development of more effective filter-type polymer adsorbent for removal of anionic pollutants from wastewater. In order to synthesize the polymer adsorbent that possesses anionic exchangeable function, carboxyl(-COOH) group of PP-g-AA nonwoven fabric was converted into amine($-NH_2$) group by the chemical modification using diethylene triamine(DETA). FT-IR data indicate that amine group was introduced into PP-g-AA through amidation of grafted acrylic acid by reaction with DETA. The degree of amination increased with increase in the reaction time and temperature of the chemical modification process, and was significantly improved by the pre-swelling treatment of PP-g-AA with solvent and addition of metal chlorides as a catalyst in following order as $NH_4OH>MeOH{\geq}HCl{\geq}H_2O\;and\;AlCl_3>FeCl_3{\geq}SnCl_2{\gg}ZnCl_2{\geq}FeCl_2$, respectively. However, the addition of catalyst limited the reusability of DETA, hence was less useful from the viewpoint of cost effectiveness and waste management. The anion exchange capacity of the aminated PP-g-AA(PP-g-AA-Am) increased with increase in the degree of amination, but it reached maximum value at the degree of amination as about $50{\sim}60%$. The anion exchange capacity of PP-g-AA-Am was higher than those of commercial anion resins.

• Journal of Korean Society of Environmental Engineers
• /
• v.36 no.2
• /
• pp.96-102
• /
• 2014

To meet the reinforced discharge standards, effect of coagulant PAC (Poly aluminium chloride, 10.4% as $Al_2O_3$) on phosphorous removal in advanced wastewater treatment process (a modified $A^2$/O). 15 mg/L of PAC determined by jar-test was added to influent of settling basin in a modified $A^2$/O consists of anaerobic, anoxic, and oxic chamber which contains Bio-clod and porous polyurethane media. Performance of PAC was tested by supernatant after settling. The removal efficiencies of BOD, COD, TP (total phosphorus) and SP (soluble phosphorus) on biological process with PAC were 96.1%, 88.8%, 97.0% and 98.6%, compared with those on biological process without PAC were 95.4%, 72.4%, 71.6% and 59.5% respectively. 18.4% of TP and 39.1% of SP removal efficiency was increased, although increase of BOD and COD removal rate was not significant. Only PAC addition to influent of settling basin in $A^2O$ process can help total phosphorus removal to 0.13 mg/L with following discharge standard.

• Journal of Korean Society on Water Environment
• /
• v.30 no.3
• /
• pp.261-268
• /
• 2014

Four clays (both natural and commercial types) mainly used in Korea were tested for removal efficiency of Microcystis spp. and ecotoxicity on Daphnia magna and Vibrio fischeri. Four clays (clay A~D) were composed of 91.9~100% of sand (0.02~0.2 mm in particle size). Clay D consisted of lager particles than other clays. Major elements of the four clays were $SiO_2$ (45.3~62.8%), $Al_2O_3$ (18.5~29.7%) and $Fe_2O_3$ (5.4~7.9%). They contained kaolinite (clay mineral), quartz, muscovite, and so on. Clay C and D contained montmorillonite, one of the clay minerals improving clay-cell aggregation. For clay A, B and C, removal efficiency of Microcystis spp. was over 60% at 2 g/L. It reached about 100% at over 5 g/L. For clay D, it was over 60% and 95~100% at 5 g/L and 20 g/L respectively. After adding clays, pH decreased. The greatest drop of pH appeared at clay C. Except for addition of 100 g/L clay C, ecotoxicity on D. magna and V. fischeri didn't appeared at all dose of clays.

• Korean Journal of Agricultural Science
• /
• v.9 no.1
• /
• pp.250-259
• /
• 1982

The Larch was known unsuitable species for the wood cement board owing to its some inhibitory substances. Therefore this research was carried out to evaluate the effect of pretreatments and chemical additives on the properties of woodflake cement board from Japanese larch (Larix leptolepis) grown in Korea. In order to improve the board qualities, the woodflakes were treated by cold water or dilute NaOH solutions(0.1, 0.5, and 2.0%), and also some chemicals($CaCl_2$, $Al_2Cl_3$ and $Na_2SiO_4$) added to the wood cement mixture. The results obtained are summarized as follow; 1. The wood cement boards from the woodflake treated with 0.1% NaOH showed remarkable higher bending strengths and internal bonding strengths than those from the flake pretreated with cold water. 2. The bending strengths showed over $60kg/cm^2$, i.e. the standard strength of JIS A-5417, with pretreatments of NaOH over 0.1% and additive of $CaCl_2$ 3.0%. The maximum strengths showed at about 0.5 of every additives. 3. Addition of $CaCl_2$ and $Al_2Cl_3$, in the case of pretreated wood with NaOH above 0.1%, had effects on increasing the internal bonding strengths of sample boards. 4. The thickness swellings became decreasing along with the increasing NaOH pretreatment concentntration. 5. The equilibrium conditions of the sample boards pretreated with NaOH over 0.1% and added with $Al_2Cl_3$ and $CaCl_2$ were maintained at 9.0~10.5% moisture contents. 6. The specific gravity of the samples showed close relationships with strength properties.

• Journal of Environmental Health Sciences
• /
• v.49 no.5
• /
• pp.251-261
• /
• 2023

Background: This paper deals with the study of natural radioactivity in rocks from Ogun State in Southwestern Nigeria. The aim is to determine radiation emissions from rocks in order to estimate radiation hazard indices. Objectives: The following objectives were targeted: 1. To determine radiation emissions from each type of rocks; 2. To estimate radiation hazard indices based on the rocks; 3. To correlate the activity concentrations of radionuclides with major oxides. Methods: The samples were analyzed using a NaI (Tl) gamma ray spectrometric detector and PerkinElmer AAnalyst 400 AAS spectrometer. Results: The activity of ⁴⁰K, ²²⁶Ra, and ²³²Th were found in order of decreasing magnitude from pegmatite>granite>migmatite. In contrast, lower concentrations were found in shale, phosphate, clay stone, sandstone and limestone. The mean absorbed doses were 125±23 nGyh^-1 (migmatite), 74±13 nGy/h (granite), 72±13 nGyh^-1 (pegmatite), 64±09 nGyh^-1 (quartzite), 45±16 nGyh^-1 (shale), 41±09 nGyh^-1 (limestone), 41±11 nGyh^-1 (clay stone), 24±03 nGyh^-1 (phosphate), and 21±10 nGyh^-1 (sandstone). The outdoor effective dose rates in all rock samples were slightly higher than the world average dose value of 0.34 mSvy^-1. The percentage composition of SiO₂ in the rock samples was above 50 wt% except for in the limestone, shale and phosphate. Al₂O₃ ranged from 4.10~21.24 wt%, Fe₂O₃ from 0.39~7.5 wt%, and CaO from 0.09-46.6 wt%. In addition, Na₂O and K₂O were present in at least 5 wt%. Other major oxides, including TiO₂, P₂O₅, K₂O, MnO, MgO and Na₂O were depleted. Conclusions: The findings suggest that Ogun State may be described as a region with elevated background radiation. It is recommended that houses should be constructed with good cross ventilation and residences should use home radiation monitoring instruments to monitor radon emanating from walls.

• Journal of the Korean GEO-environmental Society
• /
• v.14 no.8
• /
• pp.23-27
• /
• 2013

In this study, efficiency of pre-treatment of turbid seawater was measured where micro-air bubbles were used to remove particles in seawater after input of natural coagulant PGA. Artificial seawater was prepared having the intended trubidity using marine sediments and microalgae. 73.7% of turbidity removal was achieved when 0.5g/L of $AlCl_3{\cdot}6H_2O$ was added in the artificial seawater, but 92.4% of turbidity removal was observed when 0.05g/L of PGA was added in the artificial seawater containing microalgae. In addition, much greater turbidity removal was achieved for microalage than sediments. For both cases, input of 0.1g/L PGA and following additional input of micro-air bubbles for 5 seconds resulted in the maximum removal efficiency where reaction time of coagulation was 1 min and flotation by micro-air bubbles was 10 min. From this study, we concluded that micro-air floation after coagulation could be a possible economical pre-treatment method for highly turbid seawater.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.410-416
• /
• 2015

Recently, a new $Y_2O_3$ coating deposited using the EB-PVD method has been developed for erosion resistant applications in fluorocarbon plasma environments. In this study, surface crack formation in the $Y_2O_3$ coating has been analyzed in terms of residual stress and elastic modulus. The coating, deposited on silicon substrate at temperatures higher than $600^{\circ}C$, showed itself to be sound, without surface cracks. When the residual stress of the coating was measured using the Stoney formula, it was found to be considerably lower than the value calculated using the elastic modulus and thermal expansion coefficient of bulk $Y_2O_3$. In addition, amorphous $SiO_2$ and crystalline $Al_2O_3$ coatings were similarly prepared and their residual stresses were compared to the calculated values. From nano-indentation measurement, the elastic modulus of the $Y_2O_3$ coating in the direction parallel to the coating surface was found to be lower than that in the normal direction. The lower modulus in the parallel direction was confirmed independently using the load-deflection curves of a micro-cantilever made of $Y_2O_3$ coating and from the average residual stress-temperature curve of the coated sample. The elastic modulus in these experiments was around 33 ~ 35 GPa, which is much lower than that of a sintered bulk sample. Thus, this low elastic modulus, which may come from the columnar feather-like structure of the coating, contributed to decreasing the average residual tensile stress. Finally, in terms of toughness and thermal cycling stability, the implications of the lowered elastic modulus are discussed.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.6
• /
• pp.354-359
• /
• 2015

Stainless steel has poor corrosion resistance in marine environment due to the breakdown of a passive film caused by chloride. It suffers electrochemical corrosion like pitting corrosion, crevice corrosion, and stress corrosion crack (SCC) in marine environment. In general, it indicates that the passive film of $Al_2O_3$ has better corrosion resistance than that of $Cr_2O_3$ in seawater. This paper investigated the damage behavior 304 stainless steel and hot-dip aluminized 304 stainless steel in seawater solution. Various electrochemical experiments were carried out including potential measurement, potentiodynaimic experiment, Tafel analysis and galvanostatic experiment. As a result of anodic polarization experiment, higher pitting damage depth was indicated at 304 stainless steel than hot-dip aluminized 304 stainless steel. In addition, relatively higher corrosion current density was shown at hot-dip aluminized stainless steel as a result of Tafel analysis.