ZrSiO4 powders were prepared from partially hydrolyzed solution of Si(OC2H5)4 and ZrOCl2.8H2O solution by the sol-gel method and formation rate of ZrSiO4 on the reaction parameter was investigated. In order to prepare homogeneous ZrSiO4 precursor gels, the H2O/Si(OC2H5)4 molar ratio of about 2, the pH of the ZrOCl2.8H2O solution fo about 4 and stirring time of the mixed solutions of about 2 hrs were appropriate. Formation of temperature of ZrSiO4 reduced about 15$0^{\circ}C$ by milling and formation of ZrSiO4 at 1300~135$0^{\circ}C$ showed an accelerative increase through the hedvall effect by silica.

• 한국세라믹학회지
• /
• 제24권4호
• /
• pp.397-403
• /
• 1987

Pb(Zr0.52Ti0.48)O3 powders were prepared by hydrothermal synthesis. Using soluble salts such as Pb(NO3)2, TiCl4 and ZrOCl2$.$8H2O and oxide such as PbO and TiO2 as starting materials, PZT powder was hydrothermally synthesized at the temperature range between 150$^{\circ}C$ and 200$^{\circ}C$. The result showed that reactivity by alkali was decreased in the sequence of Pb(NO3)2, TiCl4, ZrOCl2, PbO, TiO2 and ZrO2. Using the first three soluble salts, PZT powder was synthesiged at 150$^{\circ}C$ for 1hr. In PbO-TiCl4-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 8rs. In Pb(NO3)2-TiO2-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 16hrs, in PbO-TiO2-ZrOCl2 system, the powder was synthesized at 200$^{\circ}C$ for 8hrs.

• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.497-504
• /
• 2000

In this study, mullite-zirconia comosite was fabricated by adding ZrOCl2.8H2O using of boehmite gel coating to Hadong kaolin (pink A grade) in order to enhance strength of the mullite specimens. The influence of ZrOCl2.8H2O content and fireing temperature on the crystall phase, microstructure, bulk density, strength of the specimens was investigated. Mullite-zirconia composite was produced in the process of coating zirconia to mullite powder synthesized thereafter and mixing simultaneously of starting materials with boehmite-zirconia gel. Maximum strength with in this study was 251 sintered at 1$600^{\circ}C$ for 2h. Bulk density and strength of the composite with zirconia coated mullite was higher than simultaneous on mixture of starting materials.

• 대한화학회지
• /
• 제57권4호
• /
• pp.472-475
• /
• 2013

An efficient and environmentally benign protocol for the three-component synthesis of triazoloindazoles and indazolophthalazines via condensation of dimedone, aldehydes and urazole or phthalhydrazide catalyzed by $ZrOCl_2.8H_2O$ as an inexpensive and eco-friendly catalyst with high catalytic activity under solvent-free conditions is reported. This protocol provides a new and improved method for obtaining triazoloindazoles and indazolophthalazines in terms of good yields, simple experimental procedure and short reaction time.

• 한국세라믹학회지
• /
• 제27권3호
• /
• pp.361-368
• /
• 1990

The properties of the powder of ZrO2＋3m/o Y2O3 system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide near by Zr(OH)4 structure showed more excellent crystallinity and lower formation temperature of tetragonal ZrO2. In the range of this study, cubic ZrO2 was not formed and stability of tetragonal ZrO2 prepared in the conditiion of pH 7 was most excellent. Average particle sizes and specific surface areas of tetragonal ZrO2 powders, prepared as calcining amorphous zirconium hydroxides at $600^{\circ}C$ for 1h, were 0.6-0.8${\mu}{\textrm}{m}$ and 45-70$m^2$/g, respectively.

• 한국세라믹학회지
• /
• 제23권3호
• /
• pp.44-52
• /
• 1986

$Al_2O_3-ZrO_2$ ceramics was obtained by the co-precipitation method using $Al_2(SO_4)_2$.$18H_2O$ and $ZrOCl_2$.$8H_2O$ as starting materials $MgCl_2$.$6H_2O$ as a sintering aid and NH4OH as a hydrolyzing agent. The coprecipitate from the above raw materials was calcined at 125$0^{\circ}C$ for 1h and again sintered at 1$650^{\circ}C$ for 2h before measurements of strength hardness and fracture toughness. MgO addition was found to increase mechanical properties of the $Al_2O_3-ZrO_2$ system. The strength and frac-ture toughness of $Al_2O_3-ZrO_2$ ceramics were considered to be increased by stress-induced phase tranforma-tion of $ZrO_2$.

• 한국세라믹학회지
• /
• 제24권2호
• /
• pp.186-192
• /
• 1987

ZrO2 powders having high purity were prepared from domestic zircon sand using the caustic fusion method and the soda ash sintering process. In the caustic fusion method, ZrO2 recovery was reached to 96% when 100/140 mesh zircon was reacted with NaOH at the NaOH/Zircon mole ratio 6 and at 650$^{\circ}C$ for 2 hours. And in the soda ash sintering process, ZrO2 was recovered to 88.5% when -325 mesh zircon was reacted with Na2CO3 at the Na2CO3/Zircon mole ratio 1.1 and 1050$^{\circ}C$ for 2 hours. In both cases, Zr component was extracted to ZrOCl2, subsequently crystallized to ZrOCl2$.$8H2O to increase the purity, and converted to ZrO2 by precipitation. And to increase the sinter ability of powder, Cl- ion was removed and strong agglomeration was avoided by methanol distribution of Zr(OH)4 precipitates.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.102-108
• /
• 1997

수용성 ZrOCl2.8H2O, YCl3.6H2O 및 Ce(NO3)3.6H2O를 사용하여 공침법으로 다양한 조성의 Y2O3-CeO2-ZrO2 분말을 합성하고, 이들의 압분체를 1400, 150$0^{\circ}C$에서 2시간동안 공기 중에서 상압소결하였다. 2mol%Y2O3-ZrO2 조성의 140$0^{\circ}C$ 소결체는 강도(1003MPa)와 미세경도(12.6GPa) 면에서 제일 우수하였으나, 인성은 10mol%CeO2-ZrO2의 경우가 13.3MPa.m1/2로 제일 높았다. CeO2-ZrO2에Y2O3의 첨가는 소결체의 평균 결정입자의 크기를 감소시켰고, 이로 인하여 강도와 경도는 증가하지만 인성은 감소하였다. 반면에 Y2O3-ZrO3에 CeO2의 첨가는 수열분위기에서 장시간 저온시효동안 정방정상의 안정화를 향상시키는 효과를 나타내었다.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.210-220
• /
• 1989

The properties of the powder of Al2O3-15v/o ZrO2(＋3m/o Y2O3) system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide decreased the specific surface area of aluminum hydroxide of AlOOH type, while increased the specific surface area of aluminum hydroxide of Al(OH)3 type, and formed co-network structure of Al-O-Zr type with the aluminum hydroxides. The rate of transition to $\alpha$-Al2O3 from co-precipitated materials occurred in the order of 7≒10, 9 and 11 of pH values. Al2O3 and ZrO2 interacted to bring about coupled grain growth, and the growth of ZrO2 crystallite size rapidly occurred within $\theta$-Al2O3 matrix. Segregation did not occur in the system Al2O3-15v/o ZrO2(＋3m/o Y2O3) and Y2O3 acted as a stabilizer to ZrO2. The lattice strain of tetragonal ZrO2 was increased by the constraint effect of Al2O3 matrix.

• 한국세라믹학회지
• /
• 제26권1호
• /
• pp.109-115
• /
• 1989

The properties of the powders of ZrO2-MgO system prepared by co-precipitation method using ZrOCl2.8H2O and MgCl2.6H2O as starting materials were investigated after calcination from $600^{\circ}C$ to 120$0^{\circ}C$. The crystallization temperature of amorphous ZrO2 was increased as MgO contents increased. The crystallite size of ZrO2 was increased with increasing calcination temperature. The crystallite size of tetragonal ZrO2 calcined at 100$0^{\circ}C$ for 1hr wa about 45nm, and MgO contributed effectively to promoting stability of tetragonal Zirconia.