• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.596-600
• /
• 1998

Reaction bonded $AI_2O_3$(RBAO)-SiC ceramics were prepared from the Al/$AI_2O_3$/SiC powder mixture. The calcined alumina and fused alumina were used as the raw $AI_2O_3$ powder. The same sized (3mm) and differently sized (3mm + Smm) $Zr0_2$ balls were used in attrition milling of starting powders. The effect of $AI_2O_3$ powder shapes on the milling efficiency and reaction sintering was investigated. After attrition milling, isopressed compacts were preheated to 1l00$^{\circ}$C with a heating rate l.5$^{\circ}C$/min and then sintered at the temperature range 1500 to 1$600^{\circ}C$ for S hours with a heating rate 5$^{\circ}C$/min. The powder mixture with fused alumina was effectively comminuted than the mixtures with calcined alumina. And the same sized balls milled more effctive than the differently sized balls. The reaction sintering behavior differed not depending on the shapes of $AI_2O_3$ powder.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.315-322
• /
• 1989

Li2O-Al2O3-SiO2 system glasses contained P2O5, TiO2 and ZrO2as the nucleating agents were melted and formed. The glass was subsequently heated first to nucleate and then to grow the crystals. At constant nucleating agent content the base glass compositions were varied and the influences of these variations on the crystallization behaviour were investigated. The study was made by measurement of thermal expansion coefficient, differential thermal analysis, X-ray diffraction analysis, scanning electron microscope observation and transmission measurement of crystallized glass specimen in visible region. It was shown that the content of crystalline phase decreased with increasing SiO2 content as well as decresing Li2O in the base glass compositions. As the result of X-ray diffrection analysis, the major crystal was $\beta$-quartz solid solution. The degree of crystallinity which was calculated using the noncrystalline scattering methods increased in S-shape with increasing heat treatment time. This change was similar to that in thermal expansion coefficient. The transmissions of 5mm thick samples were 80-90% in visible ray region.

• Korean Chemical Engineering Research
• /
• v.43 no.1
• /
• pp.140-145
• /
• 2005

The desulfurization abilities using GC/microreactor have been examined for $CuO-Fe_2O_3$ sorbents with respect to calcination temperatures of 700, 900 and $1,100^{\circ}C$. CuO was used as a main active component, $Fe_2O_3$ was used as an additive one and 25 wt% $SiO_2$ was used as a support. The desulfurization reaction temperature was $500^{\circ}C$ and the regeneration reaction temperature was $700^{\circ}C$. From the XRD results, the $CuFeO_2$ compound has been observed for the fresh sorbent calcined at $1,100^{\circ}C$ and the $CuFeS_2$ compound for the reacted sorbent calcined at $1,100^{\circ}C$. By the BET results, however any significant differences among sorbents calcined at the three different temperatures of 700, 900 and $1,100^{\circ}C$ haven't been observed. Especially CFS1 (CuO : $Fe_2O_3$ : $SiO_2$=67.5 wt% : 7.5 wt% : 25 wt%) sorbent calcined at $1,100^{\circ}C$ maintained about 10 g sulfur/100 g sorbent for 100 cycles by the cyclic test.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.99-99
• /
• 2003

최근들어 차세대 디스플레이 시장이 뜨겁게 달아오르고있다. 이에 따라서 보다 나은 발광특성 및 긴수명, 적정 잔광시간등 보다 우수한 형광체개발이 더욱 절실한 시점이다. 본 연구에서는 많은 형광체 후보물질중 하나인 yttrium silicate를 기상법으로 제조하였는데, 질산염 형태인 yttrium과 Tb에 소량의 질산에 용해시킨 Tetraethyl orthosilicate를 혼합하여 분무용액을 만든다음 분무 열분해법으로 제조하여 나온 $Y_2$SiO$_{5}$:Tb 입자들의 형상 및 발광특성등을 살펴보았다.

• Journal of Sensor Science and Technology
• /
• v.3 no.1
• /
• pp.5-11
• /
• 1994

This paper describes the characteristics of a piezoresistive pressure sensor fabricated on a SOI (Si-on-insulator) structure, in which the SOI structures of Si/$SiO_{2}$/Si and Si/$Al_{2}O_{3}$/Si were formed by SDB (Si-wafer direct bonding) technology and hetero-epitaxial growth, respectively. The SOI pressure sensors using the insulator of a SOI structure as the dielectrical isolation layer of piezoresistors, were operated at higher temperatures up to $300^{\circ}C$. In the case of pressure sensors using the insulator of a SOI structure as an etch-stop layer during the formation of thin Si diaphragms, the pressure sensitivity variation of the SOI pressure sensors was controlled to within a standard deviation of ${\pm}2.3%$ over 200 devices. Moreover, the pressure sensors fabricated on the double SOI ($Si/Al_{2}O_{3}/Si/SiO_{2}/Si$) structures formed by combining SDB technology with epitaxial growth also showed very excellent characteristics with high-temperature operation and high-resolution.

• Journal of Korean Ophthalmic Optics Society
• /
• v.9 no.2
• /
• pp.463-471
• /
• 2004

The Fabry-Perot interferometer filters for UV meter were designed using the design program of optical thin films. From the data obtained, two filters were fabricated. The transmittance of two filter were measured by spectrophotometer in order to analysis their optical property. The transmittance was controlled by the thickness of Ag reflector and the wavelength of the transmission was controlled by the thickness of $SiO_2$ spacer. The two UV filters were fabricated by the RF magnetron sputtering which are the multilayers of [air/$SiO_2$(174.6 nm)|Ag(78 nm)|$SiO_2$(68 nm)|Ag(78 nm)|Cr(5 nm)|glass] and [air/$SiO_2$(174.6 nm)|Ag(S8 nm)|$SiO_2$(56 nm)|Ag(58 nm)|Cr(S nm)|glass]. One filter has the maximum transmittance of 6% at the about 370nm and it has the transmittance of below 0.2% at 400nm. The other filter can be found that the transmittance is increased as the thickness of Ag is decreased and the wavelength of the transmission is controlled by the thickness of $SiO_2$ spacer layer.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.541-551
• /
• 1988

The purpose of this investigation was to prepare multicomponent monolithic Li-Al-Si gels of composition(mol%) 16.67 Li2O-16.67 Al2O3-66.67 SiO2 and to convert the gels to monolithic glass-ceramic at low temperature without melting. The hydrolysis, DTA, TGA, TMA, SEM, pore distribution, density and the activation energy for crystallization of the glass-ceramic formation with rawmaterials of which tetraethl orhosilicate of networkforming cation(Si) is partially hydrolyzed, aluminum isoproxide and lithium methoxide prepared by Li-metal react with methanol were studied. The results were as follows : 1) Monolithic gels which were added with additional water, resulting in a total water content 2.5 to 3.0 times the stoichiometric amount required to fully hydrolyze the alkoxides. 2) Specimens were dried to form crylinders 60mm in length and 40mm in diameter in about 800 hrs at 5$0^{\circ}C$. 3) $\beta$-eucryptite crystals and $\beta$-spodumene crystals were detected in samples heated above 75$0^{\circ}C$. 4) Within the temperature and range of 25-50$0^{\circ}C$ and 1,00$0^{\circ}C$ the thermal expansion coefficient for crystallized samples were shown as 2.6-5.7$\times$10-7/$^{\circ}C$ and 7.4-12.5$\times$10-7/$^{\circ}C$, respectively. 5) The activation energy for the crystal growth was 11.01kcal/mol at 794$^{\circ}C$ to 85$0^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.129-129
• /
• 2002

• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.323-333
• /
• 2005

Effects of gases to growth of $SiO_2$ nanowires were characterized. $N_2$, Ar, and $O_2$ gas's effect were determined. $SiO_2$ nanowires growth scheme was varied by kind and flow rates of gases because of amounts of $O_2$. Flow rates of gases and kind of substrates affected nanowires' diameters, lengths and morphologies of grown nano wires. With increasing flow rates of gases, nanowire's diameter increased because of additional VS and SLS reactions. By TEM characterization, We knows that, grown $SiO_2$ nanowires on Si substrate showed two shell structures. These shapes of nanowires were formed by reaction of additional SLS growth. Grown $SiO_2$ nanowires showed blue luminescence by PL characterization These Blue luminescence was due to quantum confinement effect and oxygen vacancies in the nanowires.

• Korean Journal of Soil Science and Fertilizer
• /
• v.6 no.2
• /
• pp.107-113
• /
• 1973

A pot experiment on paddy rice was carried out to investigate the effect of temperature after heading with application of phosphate, potash and silica on the yield and nutrient uptake. The results obtained are as follows: 1. The Grain yield was greatly affected by temperature during ripening. The yield at $20^{\circ}C$ and at $15^{\circ}C$ decreased to 62.3% and to 37.2% of that at $25^{\circ}C$ respectively. However, the application of phosphate, potash and silica at transplanting increased the grain yield even at low temperature of $15^{\circ}C$. 2. Percentage of ripened grain and weight of 1,000 grains decreased with decreasing temperature but they were increased by the application of phosphate, potash and silica at the low temperature of $15^{\circ}C$. 3. The grain filling rate was fast in the early stage of ripening at high temperature while it was fast in the later stage at low temperature. Low temperature damage was severe in the early stage of ripening. 4. Accumulation of carbohydrate in the grain was small at low temperature of $15^{\circ}C$ and the application of phosphate, potash and silica was effective to increase carbohydrate content in the grain at low temperature. 5. The content of T-N and $P_2O_5$ in straw grown at low temperature were high whereaas those of $K_2O$ and $SiO_2$ were low which were increased by the application of potash and silica. 6. There was a positive correlation between the grain yield and rate of ripening, 1,000 grain weight, contents of $K_2O$ and $SiO_2$, $K_2O/N$ and $SiO_2/N$ ratio, but a negative correlation between grain yield and contents of T-N and $P_2O_5$ in the straw at harvesting stage. 7. Ripening rate and weight of 1,000 grains showed a significant positive correlation with $K_2O$, $SiO_2$, $K_2O/N$ and $SiO_2/N$ ratio in the straw. Further, there was a negative correlation between ripening rate and the contents of T-N and $P_2O_5$ but a positive correlation between weight of 1,000 grains and these elements.